CN102390933A - Dry grain for crystal throwing brick and method for preparing crystal throwing brick - Google Patents

Dry grain for crystal throwing brick and method for preparing crystal throwing brick Download PDF

Info

Publication number
CN102390933A
CN102390933A CN2011102284678A CN201110228467A CN102390933A CN 102390933 A CN102390933 A CN 102390933A CN 2011102284678 A CN2011102284678 A CN 2011102284678A CN 201110228467 A CN201110228467 A CN 201110228467A CN 102390933 A CN102390933 A CN 102390933A
Authority
CN
China
Prior art keywords
parts
brick
throwing brick
dry grain
crystal
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2011102284678A
Other languages
Chinese (zh)
Other versions
CN102390933B (en
Inventor
张翼
韦斐
况彩萍
余祖灯
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIANGXI HONGRUI NEW MATERIAL CO., LTD.
Original Assignee
GUANGDONG DOWSTONE TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by GUANGDONG DOWSTONE TECHNOLOGY Co Ltd filed Critical GUANGDONG DOWSTONE TECHNOLOGY Co Ltd
Priority to CN 201110228467 priority Critical patent/CN102390933B/en
Publication of CN102390933A publication Critical patent/CN102390933A/en
Application granted granted Critical
Publication of CN102390933B publication Critical patent/CN102390933B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses a dry grain for a crystal throwing brick, comprising the following components of Al2O3, SiO2, K2O, CaO, Na2O, MgO, ZnO, BaO, B2O3 and the like. The invention also discloses a method for preparing the crystal throwing brick by using the dry grain. The crystal throwing brick prepared by using the dry grain for the crystal throwing brick in the invention is sintered at one step, therefore, a biscuitfiring process can be omitted, the energy consumption is greatly reduced, pollution is effectively reduced, the production cost can be reduced by about 15%, and the production benefit can be greatly increased. The produced crystal throwing brick has high glaze transparency and fewer air bubbles. The dry grain for the crystal throwing brick provided by the invention has high initial vitrifying temperature and small high-temperature viscosity, a blank can keep good gas exhaust, the air bubbles can be removed at high temperature as much as possible, the usage temperature of a fusion cake can be adjusted by changing the contents of potassium and sodium, a series of dry grain products can be obtained, and the compatibility of the products is good.

Description

A kind ofly throw brilliant brick with dry granular and throw the preparation method of brilliant brick
Technical field
The present invention relates to a kind ofly throw brilliant brick with dry granular and use the preparation method of the brilliant brick of throwing of this dry granular.
Background technology
The texture of stone material is soft attractive in appearance serious, and elegant style is in a great variety, is the ideal material of decorating luxurious building, thereby high-grade fine stone material product is " distinguished guest " during many large-scale public spaces, villa big house are decorated always.But stone material is a kind of scarce resource, and high-grade fine stone material a thousand pieces of gold difficulty on market is asked.
Blemish in an otherwise perfect thing be; Lithotome has radioactivity, uses in the interior space not meet the environmental protection life idea, moreover; Because lithotome is exploited from natural rock mass; Formed pattern texture is difficult to nature and is connected, and can't realize the big area paving when therefore using, and is difficult to form unified and complete style.And the exploitation of stone material, not only wasted lot of manpower and material resources, and ecotope has been caused certain injury.
It is the NEW TYPE OF COMPOSITE sheet material that sytull is compounded in brick brick modelled after an antique surface one deck 2-5mm that imitative stone is thrown brilliant brick; It integrates glass, pottery, stone material advantage; Merge glass smelting technology, ceramic tile shaping and crystallization and thermal treatment, polishing, cutting technique in one, sytull piece pellet shop is applied on the ceramic tile base substrate formed compact product structure, clean mark, glittering and translucent through crystallizing and sintering; Stereoscopic sensation is strong, has the sensation as the beautiful matter.Soil pick-up not fully; Maintenance convenient for cleaning, wear resistance, aspects such as surface hardness, folding strength all are superior to granite and marble; Comprise the glass matrix structure again; Its acid-alkali-resistant degree, corrosion resistance all are far more than lithotome, and especially weather resisteant is more outstanding, stand to expose to the weather for a long time also can not fade and weathering.Compare the radiation pollution of lithotome; Imitative stone is thrown brilliant brick does not only have radioactivity; But also avoided the uneven shortcoming of its aberration intensity; Can make the linking harmony and natural more between the different ceramic tiles, not only avoid lithotome to have the shortcoming of flaw, also can be according to the paving of arbitrarily arranging in pairs or groups of individual's hobby.
Because the granularity of frit dry granular is between 20~100 orders, the ulking thickness of dry granular is 1~3mm, can not reach this thickness through drenching glaze or glaze spraying technology, and the transparency does not reach requirement yet.The preparation that at present imitative stone is thrown brilliant brick mainly is to adopt the secondary burning technology, behind the stamp through the high temperature biscuiting after the base substrate upper berth apply one deck glass ceramics frit dry granular, twice firing at low temperatures.
Along with world population increases and Economic development, the resource consumption and the disposal of pollutants of building and operation thereof economize on resources, protect environment, realize building and natural harmony coexistence, are the common issues that the whole world faces.In the face of earth natural resource constantly utilize and non-renewable objective problem, be a big bottleneck on the ceramic boundary of puzzlement.The traditional ceramics industry is very high to the degree of complying with of the resource and the energy, and ceramic industry will really become energy resource and practice thrift friendly type industry, energy-saving and emission-reduction, and consumption reduction is sharp useless etc., and the aspect also shoulders heavy responsibilities.Secondary is fired and is thrown brilliant brick fully, because base substrate will pass through the high temperature biscuiting earlier, again through the low temperature biscuiting; The process for producing bricks of more once painting enamel metal ware is loaded down with trivial details, and energy consumption is bigger, is standard by the kiln of 280 meters factories; The market coal price calculates with 1100 yuan/ton, and kiln is fired every square metre of product and wanted many 4.5 yuan with coal, by 1,000,000 square metres of calculating of YO; Then will increase by 4,500,000 yuan expense, and twice firing also can increase the cost of manual work, place, breakage etc.
Summary of the invention
The object of the present invention is to provide and a kind ofly once burn to throw brilliant brick with dry granular and use the preparation method of the brilliant brick of throwing of this dry granular.
The technical scheme that the present invention taked is:
The brilliant brick of a kind of throwing is used dry granular, by Al 2O 313~20 parts, SiO 256~63 parts, K 20.5~5 part of O, 8~18 parts of CaO, Na 23~6 parts of O, 0.5~3 part of MgO, 0.5~4 part of ZnO, 0~4 part of BaO, B 2O 30~4, Li 20 ~ 2 part of composition of O.
Preferably, the brilliant brick of said throwing with dry granular by Al 2O 314~17 parts, SiO 256~60 parts, K 21~4 part of O, 10~16 parts of CaO, Na 24~6 parts of O, 1~2 part of MgO, 1~4 part of ZnO, 0~2 part of BaO, B 2O 31~3, Li 20 ~ 2 part of composition of O.
A kind of preparation method who once burn to throw brilliant brick, be included in adobe compression moulding after, execute ground-coat enamel, cover-coat enamel, fancy glaze after, the above-mentioned dry granular of cloth one deck, 1150 ℃~1230 ℃ once-firings.
The time of preferably, firing is 60~120 minutes.
The brilliant brick of the throwing of the application of the invention use dry granular, the throwing crystalline substance brick that makes, and once-firing can save high temperature biscuiting process, greatly reduces energy consumption, has reduced pollution effectively, and it is nearly 15% to reduce production costs, and has improved productivity effect greatly.The brilliant brick of the throwing that production obtains, the glaze transparency is high, and bubble is few.
It is high to prepare the used frit initial melting temperature of this dry granular; High-temperature viscosity is little; Both can guarantee that the base substrate exhaust was good, the eliminating bubble that can at high temperature try one's best again, and the content of change potassium and the sodium use temperature that can regulate frit; Obtain a series of dry granular product, and the compatibility performance between product is good.
The brilliant brick of the throwing of the inventive method preparation, owing to be the high temperature once-firing, the brilliant brick product of the throwing of the equal lower temperature twice firing of wear resistance and resistance to acids and bases has significantly raising, and once-firing, less energy consumption, technology is simple.
Embodiment
Below in conjunction with instance, further specify the present invention.
In following examples, if no special instructions, said umber all refers to mass parts.
The melting method of dry granular is following:
Composition according to dry granular takes by weighing raw material, mixes, and founds in 1500~1580 ℃, is crushed to 20~100 orders afterwards.
Embodiment 1
The brilliant brick of a kind of throwing is used dry granular, by Al 2O 313 parts, SiO 260 parts, K 20.5 part of O, 14 parts of CaO, Na 25 parts of O, 1 part of MgO, 0.5 part of ZnO, 2 parts of BaO, B 2O 31 part, Li 22 parts of compositions of O.
Embodiment 2
The brilliant brick of a kind of throwing is used dry granular, by Al 2O 315 parts, SiO 263 parts, K 25 parts of O, 12 parts of CaO, Na 24 parts of O, 0.5 part of MgO, 2 parts of ZnO, B 2O 34 parts, Li 20.3 part of composition of O.
Embodiment 3
The brilliant brick of a kind of throwing is used dry granular, by Al 2O 320 parts, SiO 258 parts, K 23 parts of O, 8 parts of CaO, Na 25 parts of O, 1.5 parts of MgO, 1 part of ZnO, B 2O 34 parts, Li 21.5 parts of compositions of O.
Embodiment 4
The brilliant brick of a kind of throwing is used dry granular, by Al 2O 318 parts, SiO 256 parts, K 22 parts of O, 16 parts of CaO, Na 24 parts of O, 2 parts of MgO, 4 parts of ZnO, 2.5 parts of BaO, B 2O 32, Li 21 part of composition of O.
Embodiment 5
The brilliant brick of a kind of throwing is used dry granular, by Al 2O 316 parts, SiO 262 parts, K 23 parts of O, 11 parts of CaO, Na 26 parts of O, 3 parts of MgO, ZnO2 part, 0.5 part of BaO, B 2O 33 parts of compositions.
Embodiment 6
The brilliant brick of a kind of throwing is used dry granular, by Al 2O 316 parts, SiO 260 parts, K 21.5 parts of O, 15 parts of CaO, Na 24 parts of O, 2.5 parts of MgO, 3 parts of ZnO, 4 parts of BaO, Li 21.5 parts of compositions of O.
Embodiment 7
The brilliant brick of a kind of throwing is used dry granular, by Al 2O 316 parts, SiO 259 parts, K 23 parts of O, 14 parts of CaO, Na 23 parts of O, 2.0 parts of MgO, 2.5 parts of ZnO, 2 parts of BaO, Li 21 part of composition of O.
Embodiment 8
After the adobe compression moulding, execute ground-coat enamel, cover-coat enamel, fancy glaze after, the dry granular of cloth one deck 1.8mm, dry granular is mixed with the mass ratio of embodiment 4 said dry granulars by 1:2 by embodiment 1,1150 ℃, burns till in 120 minutes.
Embodiment 9
After the adobe compression moulding, execute ground-coat enamel, cover-coat enamel, fancy glaze after, the dry granular of cloth one deck 2.3mm, dry granular is mixed with the mass ratio of embodiment 5 said dry granulars by 2:1 by embodiment 2,1180 ℃, burns till in 90 minutes.
Embodiment 10
After the adobe compression moulding, execute ground-coat enamel, cover-coat enamel, fancy glaze after, the dry granular of cloth one deck 2mm, dry granular is mixed with the mass ratio of embodiment 3 said dry granulars by 1:1 by embodiment 1,1200 ℃, burns till in 90 minutes.
Embodiment 11
After the adobe compression moulding, execute ground-coat enamel, cover-coat enamel, fancy glaze after, the dry granular of cloth one deck 2.5mm, dry granular is mixed with the mass ratio of embodiment 4 said dry granulars by 2:3 by embodiment 2,1230 ℃, burns till in 50 minutes.
Embodiment 8~11 prepares and throws brilliant brick structure densification, transparency is high, bubble is few, greatly reduces production energy consumption, and environmental protection is attractive in appearance.
Embodiment 12
After the adobe compression moulding, execute ground-coat enamel, cover-coat enamel, fancy glaze after, the embodiment 6 described dry granulars of cloth one deck 2mm, burnt till in 50 minutes by 1150 ℃.
The brilliant brick of the throwing of the application of the invention use dry granular, can save the sintering procedure of a kiln of biscuiting, and the throwing crystalline substance brick that makes has the energy consumption of greatly reducing, and has reduced pollution effectively, and it is nearly 15% to reduce production costs, and has improved productivity effect greatly.The brilliant brick of the throwing that production obtains, the glaze transparency is high, and bubble is few.
It is high to prepare the used frit initial melting temperature of this dry granular; High-temperature viscosity is little; Both can guarantee that the base substrate exhaust was good, the eliminating bubble that can at high temperature try one's best again, and the content of change potassium and the sodium use temperature that can regulate frit; Obtain a series of dry granular product, and the compatibility performance between product is good.

Claims (4)

1. an once-firing is thrown brilliant brick and is used dry granular, by Al 2O 313~20 parts, SiO 256~63 parts, K 20.5~5 part of O, 8~18 parts of CaO, Na 23~6 parts of O, 0.5~3 part of MgO, 0.5~4 part of ZnO, 0~4 part of BaO, B 2O 30~4, Li 20~2 part of composition of O.
2. a kind of once-firing according to claim 1 is thrown brilliant brick and is used dry granular, by Al 2O 314~17 parts, SiO 256~60 parts, K 21~4 part of O, 10~16 parts of CaO, Na 24~6 parts of O, 1~2 part of MgO, 1~4 part of ZnO, 0~2 part of BaO, B 2O 31~3, Li 20~2 part of composition of O.
3. preparation method who once burn to throw brilliant brick, be included in adobe compression moulding after, execute ground-coat enamel, cover-coat enamel, fancy glaze after, cloth one deck claim 1 or 2 described dry granulars burn till at 1150 ℃~1230 ℃ next time, obtain throwing brilliant brick product.
4. a kind of preparation method who throws brilliant brick according to claim 3, it is characterized in that: product forms for once firing, and firing time is 60~120 minutes.
CN 201110228467 2011-08-10 2011-08-10 Dry grain for crystal throwing brick and method for preparing crystal throwing brick Active CN102390933B (en)