CN107522472A - A kind of blank for jardiniere - Google Patents
A kind of blank for jardiniere Download PDFInfo
- Publication number
- CN107522472A CN107522472A CN201710808678.6A CN201710808678A CN107522472A CN 107522472 A CN107522472 A CN 107522472A CN 201710808678 A CN201710808678 A CN 201710808678A CN 107522472 A CN107522472 A CN 107522472A
- Authority
- CN
- China
- Prior art keywords
- parts
- added
- jardiniere
- modifying agent
- heating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of blank for jardiniere, it is related to ceramic fabrication technique field, the present invention adds sodium bentonite, bamboo-carbon fibre using volcanic ash as primary raw material, and activated carbon, phosphate, oxidic polyethylene, nano-ceramic powder etc. are coordinated, and modifying agent, obtained blank is fine and smooth, smooth, has excellent gas permeability and water imbibition etc., and there is higher toughness and fastness, the flowerpot gas permeability made using the present invention is high, with beneficial to kind of a flower, has had concurrently attractive in appearance and practical.
Description
Technical field：
The present invention relates to ceramic fabrication technique field, and in particular to a kind of blank for jardiniere.
Background technology：
Ceramics are the general names of pottery and porcelain.Common ceramic material has clay, aluminum oxide, kaolin etc..Ceramic material
General hardness is higher, but plasticity is poor.Except being used in feeder, on decoration in addition to, ceramics science, technology development in also play the part of
Drill key player.Ceramic raw material is that the original ample resources clay of the earth forms by quenching to take.And the property tool toughness of clay,
Normal temperature chance water is plastic, and micro- do can carve, absolutely dry to grind；Water can be filled into pottery by burning to 700 degree；Burn to 1230 degree of then porcelain, can be several
Do not absorb water completely and corrosion-and high-temp-resistant.The elasticity of its usage, there is the application of various intention in culture today science and technology.
Flowerpot is that a common kind spends vessel used in life, from porcelain flowerpot than from clay flowerpot more
Attractive in appearance, artistry is higher, but the flowerpot of porcelain does not have clay flowerpot gas permeability height, good water absorption.
The content of the invention：
The technical problems to be solved by the invention are to provide a kind of blank for jardiniere.
The technical problems to be solved by the invention are realized using following technical scheme：
A kind of blank for jardiniere, it is made up of the raw material of following parts by weight：
Volcanic ash 25-30 parts, sodium bentonite 12-15 parts, bamboo-carbon fibre 10-15 parts, activated carbon 8-11 parts, phosphate 6-
10 parts, oxidic polyethylene 5-8 parts, nano-ceramic powder 5-8 parts, viscous glutinous agent 4-6 parts, plasticizer 3-5 parts, modifying agent 4-6 parts, paraffin
1-3 parts, epoxidized soybean oil 5-10 parts, nitrile rubber 1-2 parts, water 80-100 parts.
Further, the above-mentioned blank for jardiniere, the raw material of preferably following parts by weight are made：
28 parts of volcanic ash, 14 parts of sodium bentonite, 13 parts of bamboo-carbon fibre, 10 parts of activated carbon, 8 parts of phosphate, the poly- second of oxidation
7 parts of alkene, 6 parts of nano-ceramic powder, viscous glutinous 5 parts of agent, 4 parts of plasticizer, 5 parts of modifying agent, 2 parts of paraffin, 8 parts of epoxidized soybean oil, Ding Qing
2 parts of rubber, 90 parts of water.
Further, the modifying agent is made up of the component of following parts by weight：Potato starch 3-6 parts, plant ash 3-6 parts,
Straw 3-6 parts, litter decoration 2-4 parts, cotton 2-4 parts, sand 1-3 parts, sulphur 1-3 parts, limewash 8-14.
Further, the component of the preferably following parts by weight of the modifying agent is formed：5 parts of potato starch, 5 parts of plant ash, rice
4 parts of grass, 3 parts of litter decoration, 3 parts of cotton, 2 parts of sand, 2 parts of sulphur, limewash 12.
Its preparation method comprises the following steps：
(1) volcanic ash, sodium bentonite, bamboo-carbon fibre, activated carbon, nano-ceramic powder are added into water to be sufficiently mixed, enter
Row agitating and heating, it is heated to 90-100 DEG C of insulation and stands 10min, add paraffin, be further continued for being heated with stirring to 120-130 DEG C of insulation
5min is stood, produces material I；
(2) phosphate, oxidic polyethylene, plasticizer, nitrile rubber are uniformly mixed, soaks 30 minutes, be heated to flowing back
State isothermal holding 15min, viscous glutinous agent is added, continues isothermal holding 10min, produces material II；
(3) material II, modifying agent are added into material I, is sufficiently mixed uniformly, is added in ball mill, it is small to be milled to fineness
In 20 μm；
(4) mixture after polishing is added in mixer and is stirred heating, mixing speed 600-800r/min, added
Hot temperature is 120-150 degree；
(5) mixture after stirring being added in ball mill, is milled to fineness less than 10 μm, drying is moulding,
Form blank.
Further, the preparation method of the modifying agent comprises the following steps：
Potato starch, plant ash, straw, litter decoration, cotton, sand, sulphur, limewash are mixed, smashes, defibrination, stir
To mix uniformly, mixture is heated, heating-up temperature is 80-90 degree, and the heat time is 10-15 minutes, and insulation stands 10 minutes,
Mixture is continued into heating heating again, 120-140 degree is warming up to, feeds the mixture into and insulated and stirred is carried out in agitator, is stirred
Speed is 800-1000r/min, and mixing time is 15-20 minutes.
The beneficial effects of the invention are as follows：It is fine to add sodium bentonite, bamboo charcoal using volcanic ash as primary raw material by the present invention
Dimension, and coordinated activated carbon, phosphate, oxidic polyethylene, nano-ceramic powder etc., and modifying agent, obtained blank is fine and smooth, light
It is sliding, there is excellent gas permeability and water imbibition etc., and there is higher toughness and fastness, the flowerpot made using the present invention
Gas permeability is high, with beneficial to kind of a flower, has had concurrently attractive in appearance and practical.
Embodiment：
In order that the technical means, the inventive features, the objects and the advantages of the present invention are easy to understand, tie below
Specific embodiment is closed, the present invention is expanded on further.
Embodiment 1
A kind of blank for jardiniere, it is made up of the raw material of following parts by weight：
25 parts of volcanic ash, 12 parts of sodium bentonite, 10 parts of bamboo-carbon fibre, 8 parts of activated carbon, 6 parts of phosphate, oxidic polyethylene
5 parts, 5 parts of nano-ceramic powder, viscous glutinous 4 parts of agent, 3 parts of plasticizer, 4 parts of modifying agent, 1 part of paraffin, 5 parts of epoxidized soybean oil, the fine rubber of fourth
1 part of glue, 80 parts of water.
Further, the modifying agent is made up of the component of following parts by weight：3 parts of potato starch, 3 parts of plant ash, straw 3
Part, 2 parts of litter decoration, 2 parts of cotton, 1 part of sand, 1 part of sulphur, 8 parts of limewash.
Its preparation method comprises the following steps：
(1) volcanic ash, sodium bentonite, bamboo-carbon fibre, activated carbon, nano-ceramic powder are added into water to be sufficiently mixed, enter
Row agitating and heating, it is heated to 90 DEG C of insulations and stands 10min, add paraffin, is further continued for being heated with stirring to 120 DEG C of insulation standings
5min, produce material I；
(2) phosphate, oxidic polyethylene, plasticizer, nitrile rubber are uniformly mixed, soaks 30 minutes, be heated to flowing back
State isothermal holding 15min, viscous glutinous agent is added, continues isothermal holding 10min, produces material II；
(3) material II, modifying agent are added into material I, is sufficiently mixed uniformly, is added in ball mill, it is small to be milled to fineness
In 20 μm；
(4) mixture after polishing is added in mixer and is stirred heating, mixing speed 600r/min, heating temperature
Spend for 120 degree；
(5) mixture after stirring being added in ball mill, is milled to fineness less than 10 μm, drying is moulding,
Form blank.
Further, the preparation method of the modifying agent comprises the following steps：
Potato starch, plant ash, straw, litter decoration, cotton, sand, sulphur, limewash are mixed, smashes, defibrination, stir
Mix uniformly, mixture is heated, heating-up temperature is 80 degree, and the heat time is 10 minutes, and insulation stands 10 minutes, then will be mixed
Compound continues heating heating, is warming up to 120 degree, feeds the mixture into and insulated and stirred is carried out in agitator, mixing speed 800r/
Min, mixing time are 15 minutes.
Embodiment 2
A kind of blank for jardiniere, it is made up of the raw material of following parts by weight：
30 parts of volcanic ash, 15 parts of sodium bentonite, 15 parts of bamboo-carbon fibre, 11 parts of activated carbon, 10 parts of phosphate, the poly- second of oxidation
8 parts of alkene, 8 parts of nano-ceramic powder, viscous glutinous 6 parts of agent, 5 parts of plasticizer, 6 parts of modifying agent, 3 parts of paraffin, 10 parts of epoxidized soybean oil, Ding Qing
2 parts of rubber, 100 parts of water.
Further, the modifying agent is made up of the component of following parts by weight：6 parts of potato starch, 6 parts of plant ash, straw 6
Part, 4 parts of litter decoration, 4 parts of cotton, 3 parts of sand, 3 parts of sulphur, limewash 14.
Its preparation method comprises the following steps：
(1) volcanic ash, sodium bentonite, bamboo-carbon fibre, activated carbon, nano-ceramic powder are added into water to be sufficiently mixed, enter
Row agitating and heating, it is heated to 100 DEG C of insulations and stands 10min, add paraffin, is further continued for being heated with stirring to 130 DEG C of insulation standings
5min, produce material I；
(2) phosphate, oxidic polyethylene, plasticizer, nitrile rubber are uniformly mixed, soaks 30 minutes, be heated to flowing back
State isothermal holding 15min, viscous glutinous agent is added, continues isothermal holding 10min, produces material II；
(3) material II, modifying agent are added into material I, is sufficiently mixed uniformly, is added in ball mill, it is small to be milled to fineness
In 20 μm；
(4) mixture after polishing is added in mixer and is stirred heating, mixing speed 800r/min, heating temperature
Spend for 120-150 degree；
(5) mixture after stirring being added in ball mill, is milled to fineness less than 10 μm, drying is moulding,
Form blank.
Further, the preparation method of the modifying agent comprises the following steps：
Potato starch, plant ash, straw, litter decoration, cotton, sand, sulphur, limewash are mixed, smashes, defibrination, stir
Mix uniformly, mixture is heated, heating-up temperature is 90 degree, and the heat time is 15 minutes, and insulation stands 10 minutes, then will be mixed
Compound continues heating heating, is warming up to 140 degree, feeds the mixture into and insulated and stirred is carried out in agitator, mixing speed is
1000r/min, mixing time are 20 minutes.
Control group 1
A kind of blank for jardiniere, it is made up of the raw material of following parts by weight：
25 parts of volcanic ash, 12 parts of sodium bentonite, 10 parts of bamboo-carbon fibre, 8 parts of activated carbon, 6 parts of phosphate, oxidic polyethylene
5 parts, 5 parts of nano-ceramic powder, viscous glutinous 4 parts of agent, 3 parts of plasticizer, 1 part of paraffin, 5 parts of epoxidized soybean oil, 1 part of nitrile rubber, water 80
Part.
Its preparation method comprises the following steps：
(1) volcanic ash, sodium bentonite, bamboo-carbon fibre, activated carbon, nano-ceramic powder are added into water to be sufficiently mixed, enter
Row agitating and heating, it is heated to 90 DEG C of insulations and stands 10min, add paraffin, is further continued for being heated with stirring to 120 DEG C of insulation standings
5min, produce material I；
(2) phosphate, oxidic polyethylene, plasticizer, nitrile rubber are uniformly mixed, soaks 30 minutes, be heated to flowing back
State isothermal holding 15min, viscous glutinous agent is added, continues isothermal holding 10min, produces material II；
(3) material II is added into material I, is sufficiently mixed uniformly, adds in ball mill, is milled to fineness less than 20 μm；
(4) mixture after polishing is added in mixer and is stirred heating, mixing speed 600r/min, heating temperature
Spend for 120 degree；
(5) mixture after stirring being added in ball mill, is milled to fineness less than 10 μm, drying is moulding,
Form blank.
Control group 2
A kind of blank for jardiniere, it is made up of the raw material of following parts by weight：
30 parts of volcanic ash, 15 parts of sodium bentonite, 15 parts of bamboo-carbon fibre, 11 parts of activated carbon, 10 parts of phosphate, the poly- second of oxidation
8 parts of alkene, 8 parts of nano-ceramic powder, viscous glutinous 6 parts of agent, 5 parts of plasticizer, 6 parts of modifying agent, 3 parts of paraffin, 10 parts of epoxidized soybean oil, Ding Qing
2 parts of rubber, 100 parts of water.
Further, the modifying agent is made up of the component of following parts by weight：6 parts of potato starch, 6 parts of plant ash, straw 6
Part, 4 parts of litter decoration, 4 parts of cotton, 3 parts of sand, 3 parts of sulphur, limewash 14.
Its preparation method comprises the following steps：
(1) it is fully mixed that volcanic ash, sodium bentonite, bamboo-carbon fibre, activated carbon, nano-ceramic powder, paraffin are added into water
Close, be stirred heating, be heated to 130 DEG C of insulations and stand 5min, produce material I；
(2) phosphate, oxidic polyethylene, plasticizer, nitrile rubber, viscous glutinous agent are uniformly mixed, soaked 30 minutes, heating
To reflux state isothermal holding 15min, material II is produced；
(3) material II, modifying agent are added into material I, is sufficiently mixed uniformly, is added in ball mill, it is small to be milled to fineness
In 20 μm, drying is moulding, that is, forms blank.
Further, the preparation method of the modifying agent comprises the following steps：
Potato starch, plant ash, straw, litter decoration, cotton, sand, sulphur, limewash are mixed, smashes, defibrination, stir
Mix uniformly, mixture is heated, heating-up temperature is 140 degree, and the heat time is 15 minutes, and insulation stands 10 minutes.
Table 1 is the present invention and the Experimental Comparison result of control group
The blank for jardiniere that the present invention produces, obtained blank is fine and smooth, smooth, has excellent breathe freely
Property and water imbibition etc., and there is higher toughness and fastness, the flowerpot gas permeability made using the present invention is high, with beneficial to kind
Flower, has had concurrently attractive in appearance and practical, is a kind of high-quality blank for jardiniere.
The general principle and principal character and advantages of the present invention of the present invention has been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the simply explanation described in above-described embodiment and specification is originally
The principle of invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (6)
1. a kind of blank for jardiniere, it is characterised in that be made up of the raw material of following parts by weight：Volcanic ash 25-30
Part, sodium bentonite 12-15 parts, bamboo-carbon fibre 10-15 parts, activated carbon 8-11 parts, phosphate 6-10 parts, oxidic polyethylene 5-8
Part, nano-ceramic powder 5-8 parts, viscous glutinous agent 4-6 parts, plasticizer 3-5 parts, modifying agent 4-6 parts, paraffin 1-3 parts, epoxidized soybean oil 5-
10 parts, nitrile rubber 1-2 parts, water 80-100 parts.
2. the blank according to claim 1 for jardiniere, it is characterised in that the raw material of preferred following parts by weight
It is made：28 parts of volcanic ash, 14 parts of sodium bentonite, 13 parts of bamboo-carbon fibre, 10 parts of activated carbon, 8 parts of phosphate, oxidic polyethylene 7
Part, 6 parts of nano-ceramic powder, viscous glutinous 5 parts of agent, 4 parts of plasticizer, 5 parts of modifying agent, 2 parts of paraffin, 8 parts of epoxidized soybean oil, nitrile rubber
2 parts, 90 parts of water.
3. the blank according to claim 1 for jardiniere, it is characterised in that the modifying agent is by following parts by weight
Component form：Potato starch 3-6 parts, plant ash 3-6 parts, straw 3-6 parts, litter decoration 2-4 parts, cotton 2-4 parts, sand 1-3
Part, sulphur 1-3 parts, limewash 8-14.
4. the blank according to claim 1 for jardiniere, it is characterised in that the preferably following weight of modifying agent
The component of part is formed：5 parts of potato starch, 5 parts of plant ash, 4 parts of straw, 3 parts of litter decoration, 3 parts of cotton, 2 parts of sand, 2 parts of sulphur,
Limewash 12.
5. the blank according to claim 1 or 2 for jardiniere, it is characterised in that its preparation method includes as follows
Step：
(1) volcanic ash, sodium bentonite, bamboo-carbon fibre, activated carbon, nano-ceramic powder are added into water to be sufficiently mixed, stirred
Heating is mixed, 90-100 DEG C of insulation is heated to and stands 10min, add paraffin, is further continued for being heated with stirring to 120-130 DEG C of insulation standing
5min, produce material I；
(2) phosphate, oxidic polyethylene, plasticizer, nitrile rubber are uniformly mixed, soaks 30 minutes, be heated to reflux state
Isothermal holding 15min, viscous glutinous agent is added, continues isothermal holding 10min, produces material II；
(3) material II, modifying agent are added into material I, is sufficiently mixed uniformly, is added in ball mill, be milled to fineness and be less than 20 μ
m；
(4) mixture after polishing is added in mixer and is stirred heating, mixing speed 600-800r/min, heating temperature
Spend for 120-150 degree；
Mixture after stirring is added in ball mill, is milled to fineness less than 10 μm, drying is moulding, that is, forms base
Material.
6. the blank for jardiniere according to claim 3 or 4, it is characterised in that the preparation side of the modifying agent
Method comprises the following steps：Potato starch, plant ash, straw, litter decoration, cotton, sand, sulphur, limewash are mixed, smash,
Defibrination, stir, mixture is heated, heating-up temperature is 80-90 degree, and the heat time is 10-15 minutes, and insulation is stood
10 minutes, then mixture is continued into heating heating, 120-140 degree is warming up to, is fed the mixture into agitator and is carried out insulation and stir
Mix, mixing speed 800-1000r/min, mixing time is 15-20 minutes.