CN106167726A - A kind of ceramic bowl rotates base releasing agent - Google Patents

A kind of ceramic bowl rotates base releasing agent Download PDF

Info

Publication number
CN106167726A
CN106167726A CN201610513308.5A CN201610513308A CN106167726A CN 106167726 A CN106167726 A CN 106167726A CN 201610513308 A CN201610513308 A CN 201610513308A CN 106167726 A CN106167726 A CN 106167726A
Authority
CN
China
Prior art keywords
parts
releasing agent
ceramic
powder
volcanic ash
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610513308.5A
Other languages
Chinese (zh)
Inventor
宋从发
汪六
汪六一
马建健
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Zhibo New Material Technology Co Ltd
Original Assignee
Anhui Zhibo New Material Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Zhibo New Material Technology Co Ltd filed Critical Anhui Zhibo New Material Technology Co Ltd
Priority to CN201610513308.5A priority Critical patent/CN106167726A/en
Publication of CN106167726A publication Critical patent/CN106167726A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of ceramic bowl and rotate base releasing agent, relate to ceramic fabrication technique field, be made up of the raw material of following parts by weight: petroleum coke powder 20 25 parts, volcanic ash 12 17 parts, vermiculite power 10 15 parts, terpene resin 8 12 parts, flake asbestos 6 10 parts, Brazil wax 6 10 parts, ceramic 58 parts, sulfurized lard 58 parts, sodium polyacrylate 46 parts, titanate coupling agent 35 parts, Oleum Terebinthinae 35 parts, 23 parts of carbamide, charcoal powder 12 parts, n-butyl alcohol 15 20 parts, 80 100 parts of water.Releasing agent of the present invention can form one layer of smooth and hard isolating membrane after being sprayed at mould inside, base substrate gradually separates with isolating membrane in drying course, thus ensures that blank structure is complete；And this releasing agent uses the time long, once can carry out up to ten thousand bases and the demoulding after spraying.

Description

A kind of ceramic bowl rotates base releasing agent
Technical field:
The present invention relates to ceramic fabrication technique field, be specifically related to a kind of ceramic bowl and rotate base releasing agent.
Background technology:
Due to ceramic bowl simple in construction, the most usually use revolving-rolling molding.The column pug perfected is added mould In, make ceramic bowl base by revolving-rolling, and utilize blade to be pruned by unnecessary pug, then the demoulding after drying, after through executing Glaze, fire and polish prepared ceramic bowl finished product.Owing to manufacturing, the pug of ceramic bowl base is many to be made up of clay and mineral powder, has one Fixed viscosity, affects roll forming effect in the actual course of processing sometimes, causes bowl blank structure impaired, or the demoulding is stranded Difficulty, increases base substrate scrappage.
Summary of the invention:
The technical problem to be solved is that providing a kind of ensures that the smooth demoulding and bowl blank structure are without damage Ceramic bowl rotates base releasing agent.
The technical problem to be solved uses following technical scheme to realize:
A kind of ceramic bowl rotates base releasing agent, is made up of the raw material of following parts by weight:
Petroleum coke powder 20-25 part, volcanic ash 12-17 part, vermiculite power 10-15 part, terpene resin 8-12 part, flake asbestos 6-10 Part, Brazil wax 6-10 part, ceramic 5-8 part, sulfurized lard 5-8 part, sodium polyacrylate 4-6 part, titanate coupling agent 3-5 part, Oleum Terebinthinae 3-5 part, carbamide 2-3 part, charcoal powder 1-2 part, n-butyl alcohol 15-20 part, water 80-100 part.
Its preparation method comprises the steps:
(1) terpene resin, sodium polyacrylate and titanate coupling agent are added in n-butyl alcohol, be sufficiently mixed post-heating to returning Stream mode isothermal holding 15min, adds Brazil wax and sulfurized lard, continues isothermal holding 5min, obtains material I；
(2) in water, add carbamide and charcoal powder, stand 30min after being sufficiently mixed, be subsequently adding petroleum coke powder, volcanic ash And vermiculite power, at 0-5 DEG C, stand 1h after being uniformly dispersed, obtain material II；
(3) in material I, add material II, flake asbestos, ceramic and Oleum Terebinthinae, after being sufficiently mixed, add ball mill In, it is milled to fineness less than 30 μm.
Described volcanic ash uses front through pretreatment, and its processing method is: first 40-50 part volcanic ash is added 120-150 In part water, and add 3-6 part calcium citrate and 2-4 part nanometer titanium dioxide, in microwave frequency 2450MHz, power after being sufficiently mixed Microwave treatment 10min under 800W, after temperature is down to 40-50 DEG C filter, then in filtering residue add 8-11 part polyvinyl alcohol and 5-8 part epoxy soybean oil, ground and mixed 15min, it is ground into powder after last drying.
The invention has the beneficial effects as follows: the present invention, with petroleum coke powder as primary raw material, is aided with various fillers and merit Can prepare ceramic bowl rotation base releasing agent by auxiliary agent, this releasing agent is easy to use, only need to be sprayed in mould during use Portion, can form one layer of smooth and hard isolating membrane, and base substrate gradually separates with isolating membrane in drying course, thus ensures base Body structural integrity；And this releasing agent uses the time long, once can carry out up to ten thousand bases and the demoulding after spraying.
Detailed description of the invention:
For the technological means making the present invention realize, creation characteristic, reach purpose and be easy to understand with effect, below knot Close specific embodiment, the present invention is expanded on further.
Embodiment 1
(1) 8 parts of terpene resins, 4 parts of sodium polyacrylate and 3 parts of titanate coupling agents are added in 20 parts of n-butyl alcohol, fully Mixing post-heating, to reflux state isothermal holding 15min, adds 8 parts of Brazil waxs and 6 parts of sulfurized lard, continues at insulation Reason 5min, obtains material I；
(2) in 80 parts of water, add 3 parts of carbamide and 2 parts of charcoal powders, stand 30min after being sufficiently mixed, be subsequently adding 20 parts Petroleum coke powder, 12 parts of volcanic ash and 10 parts of vermiculite powers, stand 1h at 0-5 DEG C, obtain material II after being uniformly dispersed；
(3) in material I, add material II, 6 parts of flake asbestos, 5 parts of ceramics and 4 parts of Oleum Terebinthinaes, add after being sufficiently mixed Enter in ball mill, be milled to fineness less than 30 μm.
The pretreatment of volcanic ash: first 40 parts of volcanic ash are added in 120 parts of water, and add 3 parts of calcium citrates and 2 parts of nanometers Titanium dioxide, after being sufficiently mixed under microwave frequency 2450MHz, power 800W microwave treatment 10min, treat that temperature is down to 40-50 DEG C Rear filtration, then adds 8 parts of polyvinyl alcohol and 8 parts of epoxy soybean oils in filtering residue, and ground and mixed 15min, after last drying It is ground into powder.
Embodiment 2
(1) 10 parts of terpene resins, 5 parts of sodium polyacrylate and 3 parts of titanate coupling agents are added in 20 parts of n-butyl alcohol, fully Mixing post-heating, to reflux state isothermal holding 15min, adds 10 parts of Brazil waxs and 5 parts of sulfurized lard, continues insulation Process 5min, obtain material I；
(2) in 100 parts of water, add 3 parts of carbamide and 2 parts of charcoal powders, stand 30min after being sufficiently mixed, be subsequently adding 25 parts Petroleum coke powder, 15 parts of volcanic ash and 10 parts of vermiculite powers, stand 1h at 0-5 DEG C, obtain material II after being uniformly dispersed；
(3) in material I, add material II, 8 parts of flake asbestos, 5 parts of ceramics and 4 parts of Oleum Terebinthinaes, add after being sufficiently mixed Enter in ball mill, be milled to fineness less than 30 μm.
The pretreatment of volcanic ash: first 50 parts of volcanic ash are added in 150 parts of water, and add 5 parts of calcium citrates and 3 parts of nanometers Titanium dioxide, after being sufficiently mixed under microwave frequency 2450MHz, power 800W microwave treatment 10min, treat that temperature is down to 40-50 DEG C Rear filtration, then adds 10 parts of polyvinyl alcohol and 6 parts of epoxy soybean oils in filtering residue, and ground and mixed 15min, after last drying It is ground into powder.
The ultimate principle of the present invention and principal character and advantages of the present invention have more than been shown and described.The technology of the industry Personnel, it should be appreciated that the present invention is not restricted to the described embodiments, simply illustrating this described in above-described embodiment and description The principle of invention, without departing from the spirit and scope of the present invention, the present invention also has various changes and modifications, and these become Change and improvement both falls within scope of the claimed invention.Claimed scope by appending claims and Equivalent defines.

Claims (3)

1. a ceramic bowl rotates base releasing agent, it is characterised in that be made up of the raw material of following parts by weight:
Petroleum coke powder 20-25 part, volcanic ash 12-17 part, vermiculite power 10-15 part, terpene resin 8-12 part, flake asbestos 6-10 part, Brazil wax 6-10 part, ceramic 5-8 part, sulfurized lard 5-8 part, sodium polyacrylate 4-6 part, titanate coupling agent 3-5 Part, Oleum Terebinthinae 3-5 part, carbamide 2-3 part, charcoal powder 1-2 part, n-butyl alcohol 15-20 part, water 80-100 part.
Ceramic bowl the most according to claim 1 rotates base releasing agent, it is characterised in that: described volcanic ash uses front warp Crossing pretreatment, its processing method is: is first added in 120-150 part water by 40-50 part volcanic ash, and adds 3-6 part calcium citrate With 2-4 part nanometer titanium dioxide, after being sufficiently mixed under microwave frequency 2450MHz, power 800W microwave treatment 10min, treat temperature Filter after being down to 40-50 DEG C, in filtering residue, then add 8-11 part polyvinyl alcohol and 5-8 part epoxy soybean oil, ground and mixed 15min, is ground into powder after last drying.
Ceramic bowl the most according to claim 1 rotates base releasing agent, it is characterised in that its preparation method includes as follows Step:
(1) terpene resin, sodium polyacrylate and titanate coupling agent are added in n-butyl alcohol, be sufficiently mixed post-heating to the shape that refluxes State isothermal holding 15min, adds Brazil wax and sulfurized lard, continues isothermal holding 5min, obtains material I；
(2) in water, add carbamide and charcoal powder, stand 30min after being sufficiently mixed, be subsequently adding petroleum coke powder, volcanic ash and trematodiasis Stone powder, stands 1h at 0-5 DEG C, obtains material II after being uniformly dispersed；
(3) in material I, add material II, flake asbestos, ceramic and Oleum Terebinthinae, add after being sufficiently mixed in ball mill, ball It is milled to fineness less than 30 μm.
CN201610513308.5A 2016-06-30 2016-06-30 A kind of ceramic bowl rotates base releasing agent Pending CN106167726A (en)