CN105778603B - A kind of environment-friendly type can adjust the inner wall putty of indoor humidity - Google Patents
A kind of environment-friendly type can adjust the inner wall putty of indoor humidity Download PDFInfo
- Publication number
- CN105778603B CN105778603B CN201610285069.2A CN201610285069A CN105778603B CN 105778603 B CN105778603 B CN 105778603B CN 201610285069 A CN201610285069 A CN 201610285069A CN 105778603 B CN105778603 B CN 105778603B
- Authority
- CN
- China
- Prior art keywords
- parts
- heated
- indoor humidity
- wall putty
- environment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses the inner wall putty that a kind of environment-friendly type can adjust indoor humidity, it is related to building coating technical field, is made up of the raw material of following parts by weight：60 70 parts of land plaster, 20 25 parts of acrylic acid, 10 15 parts of volcanic ash, 10 15 parts of plant amylum, 8 12 parts of disproportionated rosin, 6 10 parts of ceramic, 6 10 parts of Lauryl Alcohol ester, 58 parts of carbomer, 58 parts of polyacrylamide, 46 parts of aerosil, 46 parts of glutinous rice glue, 35 parts of microwax, 35 parts of calamine stone, 23 parts of hydroxypropyl methyl cellulose, 23 parts of rubber powder of nanometer, 23 parts of sodium hydroxide, 0.3 0.5 parts of diethylenetriamines, 0.2 0.3 parts of potassium peroxydisulfate, 50 70 parts of water.The inner wall putty feature of environmental protection of the present invention is strong：Without formaldehyde, nontoxicity, pernicious gas will not be discharged after being applied to interior wall, and can effectively adjust indoor humidity.
Description
Technical field：
The present invention relates to building coating technical field, and in particular to the interior wall that a kind of environment-friendly type can adjust indoor humidity is greasy
Son.
Background technology：
Inner wall putty is between wall leveling mortar and dope layer, plays further levelling and formation decorative textures pattern
Booster action.The common powder of lacquer putty for use on of in the market is more using white cement, inert filler, chemical addition agent as main component, by equal
It is even to be mixed to get, this dry powder material on request directly plus water stir into paste can knife-coat application, but using cement to be cementing
The defects of traditional putty of material is inevitably present the easy shrinkage cracking of cement-based material, flakes, peels off.In recent years, reporting
Putty is prepared as base-material using plaster of Paris and desulfurated plaster, fluorgypsum in some patents in road, but still suffers from stability not
Good, intensity and hardness do not reach the shortcomings of Specific construction requirement.
The content of the invention：
The technical problems to be solved by the invention are to provide a kind of easy to use, rate of drying soon and the ring of excellent performance
Guarantor's type can adjust the inner wall putty of indoor humidity.
The technical problems to be solved by the invention are realized using following technical scheme：
A kind of environment-friendly type can adjust the inner wall putty of indoor humidity, is made up of the raw material of following parts by weight：
Land plaster 60-70 parts, acrylic acid 20-25 parts, volcanic ash 10-15 parts, plant amylum 10-15 parts, disproportionated rosin 8-
12 parts, ceramic 6-10 parts, Lauryl Alcohol ester 6-10 parts, carbomer 5-8 parts, polyacrylamide 5-8 parts, gas phase titanium dioxide
Silicon 4-6 parts, glutinous rice glue 4-6 parts, microwax 3-5 parts, calamine stone 3-5 parts, hydroxypropyl methyl cellulose 2-3 parts, nanometer rubber powder
2-3 parts, sodium hydroxide 2-3 parts, diethylenetriamines 0.3-0.5 parts, potassium peroxydisulfate 0.2-0.3 parts, water 50-70 parts.
Its preparation method is as follows：
(1) plant amylum is added into water, is stirred continuously down and is heated to 70-80 DEG C of insulation 30min, add sodium hydroxide
Stirring is completely dissolved it, then adds acrylic acid, diethylenetriamines and potassium peroxydisulfate, and mixture continues to be heated to the shape that flows back
State insulated and stirred 1h, after naturally cool to freeze drier is sent into after room temperature, gained solid is made powder through pulverizer, produces thing
Expect I；
(2) microwax and nanometer rubber powder are added into disproportionated rosin, is first heated to 80-90 DEG C of insulation mixing 10min, then add
Enter ceramic, Lauryl Alcohol ester and carbomer, continue to be heated to 120-130 DEG C of insulation mixing 10min, after naturally cool to
Material II is produced after room temperature；
(3) volcanic ash, aerosil and calamine stone are added into land plaster, it is mixed to be heated to 100-110 DEG C of insulation
15min is closed, it is fine after naturally cool to material I, material II, polyacrylamide, glutinous rice glue and hydroxypropyl methyl is added after 40-50 DEG C
Dimension element, being fully ground makes it well mixed.
The beneficial effects of the invention are as follows：
(1) feature of environmental protection is strong：Without formaldehyde, nontoxicity, pernicious gas will not be discharged after being applied to interior wall；
(2) indoor humidity is adjusted：Moisture when indoor humidity is excessive in absorption air, makes the humidity of interior reduce；When
Moisture is discharged when indoor humidity is too small, makes the humidity increase of interior, so as to play a part of adjusting indoor humidity；
(3) it is easy to use：It directly plus after water stirring can be used, solve material quality existing for extemporaneous preparation putty not
The problem of stable and metering is inaccurate, and rate of drying is fast；
(4) excellent performance：It can be firmly bonded with various basal planes, adhesion strength is not less than 0.25MPa, and adhesive force is strong, non-ignitable,
Powder is not played, do not ftracture, fall off, bright and clean exquisiteness, and does not interfere with the coating of post-coatings, colour-wash will not be caused to take off
Color.
Embodiment：
In order that the technical means, the inventive features, the objects and the advantages of the present invention are easy to understand, tie below
Specific embodiment is closed, the present invention is expanded on further.
Embodiment 1
(1) 10 parts of plant amylums are added into 50 parts of water, is stirred continuously down and is heated to 70-80 DEG C of insulation 30min, add
2 parts of sodium hydroxide stirrings are completely dissolved it, then add 25 parts of acrylic acid, 0.3 part of diethylenetriamines and 0.2 part of persulfuric acid
Potassium, mixture continue to be heated to reflux state insulated and stirred 1h, and after naturally cool to freeze drier is sent into after room temperature, gained is solid
Powder is made through pulverizer in body, produces material I；
(2) 5 parts of microwaxes and 2 parts of nanometer rubber powders are added into 8 parts of disproportionated rosins, are first heated to 80-90 DEG C of insulation mixing
10min, 6 parts of ceramics, 8 parts of Lauryl Alcohol esters and 5 parts of carbomers are added, it is mixed to continue to be heated to 120-130 DEG C of insulation
10min is closed, after naturally cool to producing material II after room temperature；
(3) 10 parts of volcanic ash, 6 parts of aerosils and 3 parts of calamine stones are added into 70 parts of land plasters, are heated to
100-110 DEG C of insulation mixing 15min, after naturally cool to addition material I, material II, 6 parts of polyacrylamides, 5 after 40-50 DEG C
Part glutinous rice glue and 2 parts of hydroxypropyl methyl celluloses, being fully ground makes it well mixed.
Embodiment 2
(1) 15 parts of plant amylums are added into 60 parts of water, is stirred continuously down and is heated to 70-80 DEG C of insulation 30min, add
3 parts of sodium hydroxide stirrings are completely dissolved it, then add 25 parts of acrylic acid, 0.3 part of diethylenetriamines and 0.2 part of persulfuric acid
Potassium, mixture continue to be heated to reflux state insulated and stirred 1h, and after naturally cool to freeze drier is sent into after room temperature, gained is solid
Powder is made through pulverizer in body, produces material I；
(2) 3 parts of microwaxes and 3 parts of nanometer rubber powders are added into 10 parts of disproportionated rosins, are first heated to 80-90 DEG C of insulation mixing
10min, 8 parts of ceramics, 6 parts of Lauryl Alcohol esters and 6 parts of carbomers are added, it is mixed to continue to be heated to 120-130 DEG C of insulation
10min is closed, after naturally cool to producing material II after room temperature；
(3) 10 parts of volcanic ash, 4 parts of aerosils and 4 parts of calamine stones are added into 60 parts of land plasters, are heated to
100-110 DEG C of insulation mixing 15min, after naturally cool to addition material I, material II, 8 parts of polyacrylamides, 4 after 40-50 DEG C
Part glutinous rice glue and 3 parts of hydroxypropyl methyl celluloses, being fully ground makes it well mixed.
The general principle and principal character and advantages of the present invention of the present invention has been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the simply explanation described in above-described embodiment and specification is originally
The principle of invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (2)
1. a kind of environment-friendly type can adjust the inner wall putty of indoor humidity, it is characterised in that is made up of the raw material of following parts by weight：
Land plaster 60-70 parts, acrylic acid 20-25 parts, volcanic ash 10-15 parts, plant amylum 10-15 parts, disproportionated rosin 8-12 parts,
Ceramic 6-10 parts, Lauryl Alcohol ester 6-10 parts, carbomer 5-8 parts, polyacrylamide 5-8 parts, aerosil 4-6
Part, glutinous rice glue 4-6 parts, microwax 3-5 parts, calamine stone 3-5 parts, hydroxypropyl methyl cellulose 2-3 parts, nanometer rubber powder 2-3 parts,
Sodium hydroxide 2-3 parts, diethylenetriamines 0.3-0.5 parts, potassium peroxydisulfate 0.2-0.3 parts, water 50-70 parts.
2. environment-friendly type according to claim 1 can adjust the inner wall putty of indoor humidity, it is characterised in that its preparation method
It is as follows：
(1) plant amylum is added into water, is stirred continuously down and is heated to 70-80 DEG C of insulation 30min, add sodium hydroxide stirring
It is completely dissolved, then adds acrylic acid, diethylenetriamines and potassium peroxydisulfate, mixture continues to be heated to reflux state guarantor
Temperature stirring 1h, after naturally cool to freeze drier is sent into after room temperature, powder is made through pulverizer in gained solid, produces material I；
(2) microwax and nanometer rubber powder are added into disproportionated rosin, 80-90 DEG C of insulation mixing 10min is first heated to, adds pottery
Porcelain micro mist, Lauryl Alcohol ester and carbomer, continue to be heated to 120-130 DEG C of insulation mixing 10min, after naturally cool to room temperature
After produce material II；
(3) volcanic ash, aerosil and calamine stone are added into land plaster, is heated to 100-110 DEG C of insulation mixing
15min, after naturally cool to addition material I, material II, polyacrylamide, glutinous rice glue and hydroxypropyl methyl fiber after 40-50 DEG C
Element, being fully ground makes it well mixed.