CN105778603A - Environment-friendly interior wall putty with indoor humidity adjustment function - Google Patents
Environment-friendly interior wall putty with indoor humidity adjustment function Download PDFInfo
- Publication number
- CN105778603A CN105778603A CN201610285069.2A CN201610285069A CN105778603A CN 105778603 A CN105778603 A CN 105778603A CN 201610285069 A CN201610285069 A CN 201610285069A CN 105778603 A CN105778603 A CN 105778603A
- Authority
- CN
- China
- Prior art keywords
- parts
- environment
- powder
- wall putty
- heated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses environment-friendly interior wall putty with an indoor humidity adjustment function, and relates to the technical field of building coatings. The environment-friendly interior wall putty comprises, by weight, 60-70 parts of gypsum powder, 20-25 parts of acrylic acid, 10-15 parts of tephra, 10-15 parts of plant starch, 8-12 parts of disproportionated rosin, 6-10 parts of ceramic micropowder, 6-10 parts of 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate, 5-8 parts of carbomer resin, 5-8 parts of polyacrylamide, 4-6 parts of fumed silica, 4-6 parts of sticky rice glue, 3-5 parts of microcrystalline wax, 3-5 parts of calamine powder, 2-3 parts of hydroxypropyl methyl celluloses, 2-3 parts of nano-powder, 2-3 parts of sodium hydroxide, 0.3-0.5 part of diethylenetriamine, 0.2-0.3 part of potassium peroxodisulfate and 50-70 parts of water. The environment-friendly interior wall putty has the advantages that the interior wall putty is highly environment-friendly, free of formaldehyde and poisonless, does not release harmful gas after being smeared onto interior walls and can adjust indoor humidity effectively.
Description
Technical field:
The present invention relates to building coating technical field, be specifically related to a kind of environment-friendly type scalable indoor humidity
Inner wall putty.
Background technology:
Inner wall putty is between body of wall leveling mortar and dope layer, rises the most levelling and forms dicoration
The assosting effect of textured pattern.Powder of lacquer putty for use on common on market is many to be added with white cement, inert filler, chemistry
Adding agent is main component, and by being uniformly mixed to get, this dry powder material the most directly adds water and stirs into
Paste gets final product knife-coat application, but the traditional putty with cement as cementitious matter is inevitably present cement based
The easy shrinkage cracking of material, flake, the defect such as peeling.In recent years, to build in some patents reported
Build Gypsum Fibrosum and desulfurated plaster, fluorgypsum prepares putty as base material, but it is the best, strong to still suffer from stability
Degree and hardness do not reach the shortcomings such as Specific construction requirement.
Summary of the invention:
The technical problem to be solved is that offer one is easy to use, rate of drying fast and performance
The inner wall putty of excellent environment-friendly type scalable indoor humidity.
The technical problem to be solved uses following technical scheme to realize:
The inner wall putty of a kind of environment-friendly type scalable indoor humidity, is made up of the raw material of following parts by weight:
Gypsum Fibrosum powder 60-70 part, acrylic acid 20-25 part, volcanic ash 10-15 part, plant amylum 10-15 part,
Disproportionated rosin 8-12 part, ceramic 6-10 part, Lauryl Alcohol ester 6-10 part, carbomer 5-8 part,
Polyacrylamide 5-8 part, aerosil 4-6 part, Oryza glutinosa glue 4-6 part, microwax 3-5 part, stove
Calamina powder 3-5 part, hydroxypropyl methyl cellulose 2-3 part, nanometer rubber powder 2-3 part, sodium hydroxide 2-3 part,
Diethylenetriamines 0.3-0.5 part, potassium peroxydisulfate 0.2-0.3 part, water 50-70 part.
Its preparation method is as follows:
(1) in water, add plant amylum, be stirred continuously down and be heated to 70-80 DEG C of insulation 30min, add
Sodium hydroxide stirring makes it be completely dissolved, and is subsequently adding acrylic acid, diethylenetriamines and potassium peroxydisulfate,
Mixture continues to be heated to reflux state insulated and stirred 1h, after naturally cool to sending into lyophilization after room temperature
Machine, the size-reduced machine of gained solid is made powder, is obtained material I；
(2) in disproportionated rosin, add microwax and nanometer rubber powder, be first heated to 80-90 DEG C of insulation mixing 10
Min, adds ceramic, Lauryl Alcohol ester and carbomer, continues to be heated to 120-130 DEG C of insulation mixed
Close 10min, after naturally cool to i.e. obtaining material II after room temperature；
(3) in Gypsum Fibrosum powder, add volcanic ash, aerosil and calamine stone, be heated to 100-110 DEG C
Insulation mixing 15min, after naturally cool to add after 40-50 DEG C material I, material II, polyacrylamide,
Oryza glutinosa glue and hydroxypropyl methyl cellulose, be fully ground and make its mix homogeneously.
The invention has the beneficial effects as follows:
(1) feature of environmental protection is strong: without formaldehyde, avirulence, will not discharge harmful gas after being applied in interior wall；
(2) regulation indoor temperature: absorb the moisture in air when indoor humidity is excessive, make the humidity of indoor
Reduce；Discharge moisture when indoor humidity is too small, make the humidity of indoor increase, thus play in conditioning chamber
The effect of humidity；
(3) easy to use: can to use after the stirring that directly adds water, solve the former of extemporaneous preparation putty existence
The problem that material quality is unstable and metering is inaccurate, and rate of drying is fast；
(4) excellent performance: can be firmly bonded with various basal planes, adhesion strength is not less than 0.25MPa, attachment
Power is strong, do not fire, do not rise powder, do not ftracture, do not fall off, bright and clean exquisiteness, and do not interfere with post-coatings
Coating, be not result in that colour-wash fades.
Detailed description of the invention:
For the technological means making the present invention realize, creation characteristic, reach purpose and effect and be readily apparent from
Solve, below in conjunction with specific embodiment, the present invention is expanded on further.
Embodiment 1
(1) in 50 parts of water, add 10 parts of plant amylums, be stirred continuously down and be heated to 70-80 DEG C of insulation 30
Min, adds the stirring of 2 parts of sodium hydroxide and makes it be completely dissolved, be subsequently adding 25 parts of acrylic acid, 0.3 part two
Ethylenetriamine and 0.2 part of potassium peroxydisulfate, mixture continues to be heated to reflux state insulated and stirred 1h, treats certainly
Sending into freezer dryer after being so cooled to room temperature, the size-reduced machine of gained solid is made powder, is obtained material I；
(2) in 8 parts of disproportionated rosins, add 5 parts of microwaxes and 2 parts of nanometer rubber powders, be first heated to 80-90 DEG C of guarantor
Temperature mixing 10min, adds 6 parts of ceramics, 8 parts of Lauryl Alcohol esters and 5 parts of carbomers, continues to add
Heat is to 120-130 DEG C of insulation mixing 10min, after naturally cool to i.e. obtaining material II after room temperature；
(3) in 70 parts of Gypsum Fibrosum powders, 10 parts of volcanic ash, 6 parts of aerosils and 3 parts of calamine stones are added,
Be heated to 100-110 DEG C of insulation mixing 15min, after naturally cool to add after 40-50 DEG C material I, material II,
6 parts of polyacrylamides, 5 parts of Oryza glutinosa glue and 2 parts of hydroxypropyl methyl celluloses, be fully ground and make its mix homogeneously.
Embodiment 2
(1) in 60 parts of water, add 15 parts of plant amylums, be stirred continuously down and be heated to 70-80 DEG C of insulation 30
Min, adds the stirring of 3 parts of sodium hydroxide and makes it be completely dissolved, be subsequently adding 25 parts of acrylic acid, 0.3 part two
Ethylenetriamine and 0.2 part of potassium peroxydisulfate, mixture continues to be heated to reflux state insulated and stirred 1h, treats certainly
Sending into freezer dryer after being so cooled to room temperature, the size-reduced machine of gained solid is made powder, is obtained material I；
(2) in 10 parts of disproportionated rosins, add 3 parts of microwaxes and 3 parts of nanometer rubber powders, be first heated to 80-90 DEG C
Insulation mixing 10min, adds 8 parts of ceramics, 6 parts of Lauryl Alcohol esters and 6 parts of carbomers, continues
It is heated to 120-130 DEG C of insulation mixing 10min, after naturally cool to i.e. obtaining material II after room temperature；
(3) in 60 parts of Gypsum Fibrosum powders, 10 parts of volcanic ash, 4 parts of aerosils and 4 parts of calamine stones are added,
Be heated to 100-110 DEG C of insulation mixing 15min, after naturally cool to add after 40-50 DEG C material I, material II,
8 parts of polyacrylamides, 4 parts of Oryza glutinosa glue and 3 parts of hydroxypropyl methyl celluloses, be fully ground and make its mix homogeneously.
The ultimate principle of the present invention and principal character and advantages of the present invention have more than been shown and described.One's own profession
Skilled person will appreciate that of industry, the present invention is not restricted to the described embodiments, above-described embodiment and explanation
The principle that the present invention is simply described described in book, without departing from the spirit and scope of the present invention,
The present invention also has various changes and modifications, and these changes and improvements both fall within claimed invention model
In enclosing.Claimed scope is defined by appending claims and equivalent thereof.
Claims (2)
1. the inner wall putty of an environment-friendly type scalable indoor humidity, it is characterised in that by following weight portion
The raw material of number is made:
Gypsum Fibrosum powder 60-70 part, acrylic acid 20-25 part, volcanic ash 10-15 part, plant amylum 10-15 part,
Disproportionated rosin 8-12 part, ceramic 6-10 part, Lauryl Alcohol ester 6-10 part, carbomer 5-8 part,
Polyacrylamide 5-8 part, aerosil 4-6 part, Oryza glutinosa glue 4-6 part, microwax 3-5 part, stove
Calamina powder 3-5 part, hydroxypropyl methyl cellulose 2-3 part, nanometer rubber powder 2-3 part, sodium hydroxide 2-3 part,
Diethylenetriamines 0.3-0.5 part, potassium peroxydisulfate 0.2-0.3 part, water 50-70 part.
The inner wall putty of environment-friendly type scalable indoor humidity the most according to claim 1, its feature exists
In, its preparation method is as follows:
(1) in water, add plant amylum, be stirred continuously down and be heated to 70-80 DEG C of insulation 30min, add
Sodium hydroxide stirring makes it be completely dissolved, and is subsequently adding acrylic acid, diethylenetriamines and potassium peroxydisulfate,
Mixture continues to be heated to reflux state insulated and stirred 1h, after naturally cool to sending into lyophilization after room temperature
Machine, the size-reduced machine of gained solid is made powder, is obtained material I；
(2) in disproportionated rosin, add microwax and nanometer rubber powder, be first heated to 80-90 DEG C of insulation mixing 10
Min, adds ceramic, Lauryl Alcohol ester and carbomer, continues to be heated to 120-130 DEG C of insulation mixed
Close 10min, after naturally cool to i.e. obtaining material II after room temperature；
(3) in Gypsum Fibrosum powder, add volcanic ash, aerosil and calamine stone, be heated to 100-110 DEG C
Insulation mixing 15min, after naturally cool to add after 40-50 DEG C material I, material II, polyacrylamide,
Oryza glutinosa glue and hydroxypropyl methyl cellulose, be fully ground and make its mix homogeneously.