CN105696349A - 一种高强度纤维无纺布的加工方法 - Google Patents

一种高强度纤维无纺布的加工方法 Download PDF

Info

Publication number
CN105696349A
CN105696349A CN201510595308.XA CN201510595308A CN105696349A CN 105696349 A CN105696349 A CN 105696349A CN 201510595308 A CN201510595308 A CN 201510595308A CN 105696349 A CN105696349 A CN 105696349A
Authority
CN
China
Prior art keywords
processing method
woven fabrics
woven fabric
high strength
strength fibre
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510595308.XA
Other languages
English (en)
Inventor
吕绪林
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Yilin Plastic Industry Co Ltd
Original Assignee
Anhui Yilin Plastic Industry Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Yilin Plastic Industry Co Ltd filed Critical Anhui Yilin Plastic Industry Co Ltd
Priority to CN201510595308.XA priority Critical patent/CN105696349A/zh
Publication of CN105696349A publication Critical patent/CN105696349A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种高强度纤维无纺布的加工方法，高强度纤维无纺布的加工方法包括以下步骤：（1）制备纤维无纺布增强涂液：称取一定量的改性聚酰胺树脂，加入适量的丙酮搅拌均匀，根据涂液的粘稠情况加入适量的增稠剂，即制得增强涂料；（2）无纺布经去离子水浸泡处理以除去表面可能残留的胶浆类物质,将增强涂料均匀刷涂于无纺布上，室温固化，即得高强度纤维无纺布。本发明的高强度纤维无纺布强度高具有抗拉强度高、加工方法简单、透气防水、环保、柔韧、无毒无味，且价格便宜等优点。

Description

一种高强度纤维无纺布的加工方法
技术领域
本发明涉及一种高强度纤维无纺布的加工方法，属于新型无纺布材料技术领域。
背景技术
无纺布制品色彩丰富、鲜艳明丽、时尚环保、用途广泛、美观大方，图案和款式都多样，且质轻、环保、可循环再用，被国际公认为保护地球生态的环保产品。适用于农用薄膜、制鞋、制革、床垫、子母被、装饰、化工、印刷、汽车、建材，家具等行业。无纺布由包括化学纤维和植物纤维等在以水或空气作为悬浮介质的条件下在湿法或干法抄纸机上制成，虽为布而不经纺织故称其为无纺布。无纺布是新一代环保材料，具有强力好、透气防水、环保、柔韧、无毒无味，且价格便宜等优点。
本发明提供了一种高强度纤维无纺布，具有抗拉强度高、加工方法简单、透气防水、环保、柔韧、无毒无味，且价格便宜等优点。因此本发明的是很有必要的。
发明内容
本发明目的是补充现有技术，而提供一种高强度纤维无纺布的加工方法。
为了实现上述目的，本发明的技术方案如下：
一种高强度纤维无纺布的加工方法，其特征在于，加工方法包括以下步骤：（1）制备纤维无纺布增强涂液：称取一定量的改性聚酰胺树脂，加入适量的丙酮搅拌均匀，根据涂液的粘稠情况加入适量的增稠剂，即制得增强涂料；（2）无纺布经去离子水浸泡处理以除去表面可能残留的胶浆类物质,将增强涂料均匀刷涂于无纺布上，室温固化，即得高强度纤维无纺布。
所述增稠剂为羧甲基纤维素钠。
所述去离子水浸泡时间为1-2小时。
所述室温固化为4-6小时
本发明的有益效果如下：
本发明的高强度纤维无纺布具有抗拉强度高、加工方法简单、透气防水、环保、柔韧、无毒无味，且价格便宜等优点。
具体实施方式
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解，下面结合具体实施例，进一步阐述本发明。
实施例1：
一种高强度纤维无纺布的加工方法，其特征在于，加工方法包括以下步骤：（1）制备纤维无纺布增强涂液：称取100g改性聚酰胺树脂，加入5L丙酮搅拌均匀，根据涂液的粘稠情况加入适量的增稠剂，即制得增强涂料；（2）无纺布经去离子水浸泡处理1.5h以除去表面可能残留的胶浆类物质,将增强涂料均匀刷涂于无纺布上，室温固化5h，即得高强度纤维无纺布。
所述增稠剂为羧甲基纤维素钠。
本发明的高强度纤维无纺布具有抗拉强度高、加工方法简单、透气防水、环保、柔韧、无毒无味，且价格便宜等优点。
实施例2：
一种高强度纤维无纺布的加工方法，其特征在于，加工方法包括以下步骤：（1）制备纤维无纺布增强涂液：称取150g改性聚酰胺树脂，加入5L丙酮搅拌均匀，根据涂液的粘稠情况加入适量的增稠剂，即制得增强涂料；（2）无纺布经去离子水浸泡处理1.5h以除去表面可能残留的胶浆类物质,将增强涂料均匀刷涂于无纺布上，室温固化5h，即得高强度纤维无纺布。
所述增稠剂为羧甲基纤维素钠。
本发明的高强度纤维无纺布具有抗拉强度高、加工方法简单、透气防水、环保、柔韧、无毒无味，且价格便宜等优点。
实施例3：
一种高强度纤维无纺布的加工方法，其特征在于，加工方法包括以下步骤：（1）制备纤维无纺布增强涂液：称取200g改性聚酰胺树脂，加入5L丙酮搅拌均匀，根据涂液的粘稠情况加入适量的增稠剂，即制得增强涂料；（2）无纺布经去离子水浸泡处理1.5h以除去表面可能残留的胶浆类物质,将增强涂料均匀刷涂于无纺布上，室温固化6h，即得高强度纤维无纺布。
所述增稠剂为羧甲基纤维素钠。
本发明的高强度纤维无纺布具有抗拉强度高、加工方法简单、透气防水、环保、柔韧、无毒无味，且价格便宜等优点。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。

Claims (4)

1.一种高强度纤维无纺布的加工方法，其特征在于，加工方法包括以下步骤：（1）制备纤维无纺布增强涂液：称取一定量的改性聚酰胺树脂，加入适量的丙酮搅拌均匀，根据涂液的粘稠情况加入适量的增稠剂，即制得增强涂料；（2）无纺布经去离子水浸泡处理以除去表面可能残留的胶浆类物质,将增强涂料均匀刷涂于无纺布上，室温固化，即得高强度纤维无纺布。
2.根据权利要求1所述的一种高强度纤维无纺布的加工方法，其特征在于，所述增稠剂为羧甲基纤维素钠。
3.根据权利要求1所述的一种高强度纤维无纺布的加工方法，其特征在于，所述去离子水浸泡时间为1-2小时。
4.根据权利要求1所述的一种高强度纤维无纺布的加工方法，其特征在于，所述室温固化为4-6小时。
CN201510595308.XA 2015-09-18 2015-09-18 一种高强度纤维无纺布的加工方法 Pending CN105696349A (zh)