CN105664901A - 一种靶向二氧化钛光催化剂的制备方法 - Google Patents
一种靶向二氧化钛光催化剂的制备方法 Download PDFInfo
- Publication number
- CN105664901A CN105664901A CN201610093376.0A CN201610093376A CN105664901A CN 105664901 A CN105664901 A CN 105664901A CN 201610093376 A CN201610093376 A CN 201610093376A CN 105664901 A CN105664901 A CN 105664901A
- Authority
- CN
- China
- Prior art keywords
- titanium dioxide
- optical catalyst
- dioxide optical
- preparation
- template molecule
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种靶向二氧化钛光催化剂的制备方法,具体步骤为:(1)将异丙醇钛、模板分子和异丙醇混合均匀后于室温静置,然后在磁力搅拌下加水进行水解,再加入酸性溶液进行酸解形成凝胶;(2)将形成的凝胶于室温下真空干燥,再将干燥后的凝胶研磨,然后用溶剂进行清洗直至洗脱液通过高效液相色谱检测不到模板分子,再用超纯水清洗后干燥得到目标产物靶向二氧化钛光催化剂。本发明制得的靶向二氧化钛光催化剂对模板分子具有高度的选择性,能够在其它物质共存的条件下将模板分子进行选择性吸附和降解。
Description
技术领域
本发明属于二氧化钛光催化剂的制备技术领域,具体涉及一种靶向二氧化钛光催化剂的制备方法。
背景技术
二氧化钛是一种常见的光催化剂,可以在光照下将绝大多数有机物进行氧化分解,在各行各业应用广泛。但是,目前报道的二氧化钛光催化剂并不具备选择性,也不具备靶向识别功能。
发明内容
本发明解决的技术问题是提供了一种具有靶向识别功能的靶向二氧化钛光催化剂的制备方法,该制备方法简单实用、不需要大型仪器设备且无需高温反应过程。
本发明为解决上述技术问题采用如下技术方案,一种靶向二氧化钛光催化剂的制备方法,其特征在于具体步骤为:(1)将异丙醇钛、模板分子和异丙醇混合均匀后于室温静置,然后在磁力搅拌下加水进行水解,再加入酸性溶液进行酸解形成凝胶;(2)将形成的凝胶于室温下真空干燥,再将干燥后的凝胶研磨,然后用溶剂进行清洗直至洗脱液通过高效液相色谱检测不到模板分子,再用超纯水清洗后干燥得到目标产物靶向二氧化钛光催化剂。
进一步优选,步骤(1)中所述的模板分子为三氯生、双氯芬酸、布洛芬或环丙沙星。
进一步优选,步骤(1)中所述的酸性溶液为硝酸、磷酸、醋酸、硫酸或盐酸。
进一步优选,步骤(2)中所述的溶剂为氢氧化钠溶液、氢氧化钾溶液、碳酸钠溶液、碳酸钾溶液、碳酸氢钠溶液或碳酸氢钾溶液。
本发明所述的一种靶向二氧化钛光催化剂的制备方法,其特征在于具体步骤为:(1)将10mL异丙醇钛、0.8685g模板分子三氯生和2mL异丙醇混合均匀后于室温静置,然后在磁力搅拌下加水进行水解,再加入硝酸进行酸解形成凝胶;(2)将形成的凝胶于室温下真空干燥,再将干燥后的凝胶研磨,然后用摩尔浓度为0.05mol/L的氢氧化钠溶液进行清洗直至洗脱液通过高效液相色谱检测不到模板分子三氯生,再用超纯水清洗后干燥得到目标产物靶向二氧化钛光催化剂。
进一步优选,制得的靶向二氧化钛光催化剂具有锐钛矿晶型。
进一步优选,制得的靶向二氧化钛光催化剂能够对三氯生进行选择性吸附和降解。
本发明制得的二氧化钛光催化剂对模板分子具有高度的选择性,能够在其它物质共存的条件下将模板分子进行选择性吸附和降解。
具体实施方式
以下通过实施例对本发明的上述内容做进一步详细说明,但不应该将此理解为本发明上述主题的范围仅限于以下的实施例,凡基于本发明上述内容实现的技术均属于本发明的范围。
实施例1
(1)将10mL异丙醇钛、0.8685g模板分子三氯生和2mL异丙醇混合均匀后于室温静置,然后在磁力搅拌下加入水进行水解,再加入硝酸进行酸解形成凝胶;(2)将形成的凝胶于室温下真空干燥,再将干燥后的凝胶研磨,然后用摩尔浓度为0.05mol/L的氢氧化钠溶液进行清洗直至洗脱液通过高效液相色谱检测不到模板分子三氯生,再用超纯水清洗后干燥得到目标产物靶向二氧化钛光催化剂。
本实施例制得的靶向二氧化钛光催化剂对模板分子三氯生具有高度的选择性,当三氯生和结构相似的三氯卡班共存时,可以将三氯生进行选择性吸附和降解,其对三氯生的降解速率常数是三氯卡班的6.5倍。制得的靶向二氧化钛光催化剂不需要高温煅烧即具有锐钛矿晶型,光催化活性较好,所有工艺步骤均在室温下完成,能耗相对较低。
以上实施例描述了本发明的基本原理、主要特征及优点,本行业的技术人员应该了解,本发明不受上述实施例的限制,上述实施例和说明书中描述的只是说明本发明的原理,在不脱离本发明原理的范围下,本发明还会有各种变化和改进,这些变化和改进均落入本发明保护的范围内。
Claims (7)
1.一种靶向二氧化钛光催化剂的制备方法,其特征在于具体步骤为:(1)将异丙醇钛、模板分子和异丙醇混合均匀后于室温静置,然后在磁力搅拌下加水进行水解,再加入酸性溶液进行酸解形成凝胶;(2)将形成的凝胶于室温下真空干燥,再将干燥后的凝胶研磨,然后用溶剂进行清洗直至洗脱液通过高效液相色谱检测不到模板分子,再用超纯水清洗后干燥得到目标产物靶向二氧化钛光催化剂。
2.根据权利要求1所述的靶向二氧化钛光催化剂的制备方法,其特征在于:步骤(1)中所述的模板分子为三氯生、双氯芬酸、布洛芬或环丙沙星。
3.根据权利要求1所述的靶向二氧化钛光催化剂的制备方法,其特征在于:步骤(1)中所述的酸性溶液为硝酸、磷酸、醋酸、硫酸或盐酸。
4.根据权利要求1所述的靶向二氧化钛光催化剂的制备方法,其特征在于:步骤(2)中所述的溶剂为氢氧化钠溶液、氢氧化钾溶液、碳酸钠溶液、碳酸钾溶液、碳酸氢钠溶液或碳酸氢钾溶液。
5.根据权利要求1所述的靶向二氧化钛光催化剂的制备方法,其特征在于:(1)将10mL异丙醇钛、0.8685g模板分子三氯生和2mL异丙醇混合均匀后于室温静置,然后在磁力搅拌下加水进行水解,再加入硝酸进行酸解形成凝胶;(2)将形成的凝胶于室温下真空干燥,再将干燥后的凝胶研磨,然后用摩尔浓度为0.05mol/L的氢氧化钠溶液进行清洗直至洗脱液通过高效液相色谱检测不到模板分子三氯生,再用超纯水清洗后干燥得到目标产物靶向二氧化钛光催化剂。
6.根据权利要求1-5中任意一项所述的靶向二氧化钛光催化剂的制备方法,其特征在于:制得的靶向二氧化钛光催化剂具有锐钛矿晶型。
7.根据权利要求1-5中任意一项所述的靶向二氧化钛光催化剂的制备方法,其特征在于:制得的靶向二氧化钛光催化剂能够对三氯生进行选择性吸附和降解。