CN1056395C - 纳米TiO2/矿石粉复合钛白的制备 - Google Patents

纳米TiO2/矿石粉复合钛白的制备 Download PDF

Info

Publication number
CN1056395C
CN1056395C CN98115376A CN98115376A CN1056395C CN 1056395 C CN1056395 C CN 1056395C CN 98115376 A CN98115376 A CN 98115376A CN 98115376 A CN98115376 A CN 98115376A CN 1056395 C CN1056395 C CN 1056395C
Authority
CN
China
Prior art keywords
titanium white
titanium
solution
composite titanium
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN98115376A
Other languages
English (en)
Other versions
CN1206727A (zh
Inventor
王子忱
赵敬哲
杨桦
杨少凤
刘艳华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jilin University
Original Assignee
Jilin University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jilin University filed Critical Jilin University
Priority to CN98115376A priority Critical patent/CN1056395C/zh
Publication of CN1206727A publication Critical patent/CN1206727A/zh
Application granted granted Critical
Publication of CN1056395C publication Critical patent/CN1056395C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明是一种纳米复合钛白的制备方法。
本发明是以我国富产的廉价的矿石粉为核心，表面均匀包覆一层纳米级超细TiO2，从而制得纳米复合钛白。经各种性能测试表明，此种复合钛白除具有钛白粉的白度外，其它性能也与钛白粉相当。本发明的纳米复合钛白制备过程简单，条件易控制，可在原有的钛白粉生产线上生产，大大降低成本，使钛白粉的应用更为广泛。

Description

纳米TiO2/矿石粉复合钛白的制备
本发明涉及一种纳米复合钛白的制备方法。
世界二氧化钛工业始于一九一六年，八十年来，世界二氧化钛工业蓬勃发展，年产超过300万吨/年，是世界第二或第三大无机化工产业，我国二氧化钛工业始于一九五六年，四十年来发展缓慢，产量、品种、质量与国外差距越来越大，消耗与成本越来越高。目前我国人均二氧化钛消费仅0.08公斤，距发达国家人均消费4公斤差50倍，距世界人均消费水平0.6公斤差7.5倍，因而我国钛白消费增加是必然趋势，降低钛白粉的成本也就成了摆在人们面前的一个关键问题。同时，随着TiO2用量的逐年增长，钛资源越来越少，钛白工业的发展将受到钛资源缺乏的限制，因此如何充分利用现有钛资源也就成为人们急待解决的问题。
本发明是采用自然界中含量丰富，几乎随处可得的矿石粉料为核心，表面均匀包覆一层纳米级超细TiO2制成纳米复合钛白。经各种性能测试表明，此种复合钛白除具有钛白粉的白度外，其它性能也与钛白粉相当。本发明的出现，可作为钛白粉的替代产品，大大降低成本，使钛白粉的应用范围更为广泛。
本发明是将硅灰石、高岭土、透闪石、钠长石等矿石粉碎成300～2000目的矿石粉，加入到浓度为0.2～2.0mol/L的TiOSO4或Ti(SO4)2、TiCl4等溶液中进行预处理1～12小时，然后将与钛溶液等摩尔浓度的NaOH溶液加入到不断搅拌的处理液中，反应时间1～6小时。反应温度为10～50℃时，表面层TiO2为无定型结构，其无定型结构可耐高温至800℃，具有良好的热稳定性，而一旦形成晶体后，易向金红石TiO2转化，900℃时已转化为完全的金红石结构；当反应温度为70～90℃时，直接可得到表面层TiO2为锐钛矿型结构的粉体。待钛沉淀完全后，复合物沉淀在母液中继续陈化2～10小时，经离心、洗涤、干燥、焙烧得纳米复合钛白。
实施例1：
称取1公斤硅灰石置于0.8mol/L Ti(SO4)2溶液16L中，不断搅拌4小时，0.8mol/L NaOH溶液64L加入到前面的预处理液中，反应温度为20℃，待沉淀完全，沉淀于母液中陈化5小时，复合沉淀经离心与母液分离，再用去离子水洗涤至用BaCl2检验无SO4 2-离子为止，沉淀在80℃于烘箱中烘干，再经500℃焙烧2小时得纳米复合钛白。实施例2：
称取10公斤高岭土置于1.6mol/L Ti(SO4)2溶液78L中，不断搅拌8小时，1.6mol/L NaOH溶液312L加入到前面的预处理液中，反应温度为30℃，待沉淀完全，沉淀于母液中陈化4小时，复合沉淀经离心与母液分离，再用去离子水洗涤至用BaCl2检验无SO4 2-离子为止，沉淀在80℃于烘箱中烘干，再经800℃焙烧2小时得纳米复合钛白。

Claims (1)

1  一种纳米复合钛白的制备方法，其特征在于将硅灰石或高岭土、透闪石、钠长石经粉碎成300目～2000目的矿石粉，置于浓度为0.2～2.0mol/L的TiOSO4或Ti(SO4)2、TiCl4溶液中进行预处理1～24小时，然后将与钛溶液等摩尔浓度的NaOH溶液加入到不断搅拌的处理液中，反应时间1～6小时，反应温度为10～50℃时表面层TiO2为无定型结构，其无定型结构可耐高温至800℃，具有良好的热稳定性，900℃时转化为完全的金红石结构；反应温度为70～90℃时直接得到的复合粉体表面层为锐钛矿型结构的TiO2；待钛沉淀完全后，复合物沉淀在母液中继续陈化2～10小时，经离心、洗涤、干燥、焙烧得纳米复合钛白。
CN98115376A 1998-07-03 1998-07-03 纳米TiO2/矿石粉复合钛白的制备 Expired - Fee Related CN1056395C (zh)