CN105623131A - 一种防水电缆氯磺化聚乙烯护套橡皮配方 - Google Patents

一种防水电缆氯磺化聚乙烯护套橡皮配方 Download PDF

Info

Publication number
CN105623131A
CN105623131A CN201610054403.3A CN201610054403A CN105623131A CN 105623131 A CN105623131 A CN 105623131A CN 201610054403 A CN201610054403 A CN 201610054403A CN 105623131 A CN105623131 A CN 105623131A
Authority
CN
China
Prior art keywords
parts
chlorosulfonated polyethylene
rubber
polyethylene sheath
cable
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610054403.3A
Other languages
English (en)
Inventor
张晓飞
刘东兵
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Lieta Cable Group Co Ltd
Original Assignee
Anhui Lieta Cable Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Lieta Cable Group Co Ltd filed Critical Anhui Lieta Cable Group Co Ltd
Priority to CN201610054403.3A priority Critical patent/CN105623131A/zh
Publication of CN105623131A publication Critical patent/CN105623131A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种防水电缆氯磺化聚乙烯护套橡皮配方？，它由以下原料组成：按分量计取，氯磺化聚乙烯30-45份、防老剂25-？26份、二叔丁基？28-36份、甲基苯酚18-26份、阻燃剂采用含氯？20-40份、三氧化二锑10-20份、填充剂35-46份、超细滑石粉8.9-10.6份、高耐磨炭黑12-24份、氢氧化镁22-36份、低水硼酸锌15-17份、高岭土21-23份、硅灰石18-22份、蒙脱土、16-21份、云母粉中11-15份。本发明配方合理、科学，耐辐照性能、防水性能，且机械性能优异，氯磺化聚乙烯护套橡皮的用于水声换能器电缆的护套，可采用连续硫化挤橡工艺，生产出的成品电缆不仅机械物理性能比普通橡皮高，而且具有阻燃、耐磨、使用安全性和较长的使用寿命。

Description

一种防水电缆氯磺化聚乙烯护套橡皮配方
技术领域
本发明涉及一种防水电缆氯磺化聚乙烯护套橡皮配方。
背景技术
电缆绝缘材料广泛使用的电缆具有机械强度极高，邵氏硬度大，抗撕裂，耐电蚀损和起痕能力强等优点。但随着电力工业的发展，电气产品的功率消耗提高，其火灾出现的频率提高，硫化橡皮的长期使用温度可达90~105℃；具有优异的耐气候老化性能，能经受各种生物和微生物的侵蚀和破坏，可以在热带和湿热带使用；耐湿性好，硫化橡皮对湿度不敏感，吸水性很小因此传统的电缆绝缘材料已不能满足对安全性能的要求，而且传统的电缆的耐老化性能相对较差，易受紫外线影响。
鉴于以上现有技术中存在的缺陷，有必要将其进一步改进，使其更具备实用性，才能符合实际使用情况。
发明内容
为了克服上述现有技术的缺陷，本发明的目的是提供一种防水电缆氯磺化聚乙烯护套橡皮配方。
发明是采取以下技术方案来实现的：一种防水电缆氯磺化聚乙烯护套橡皮配方，它由以下原料组成：按分量计取，氯磺化聚乙烯30-45份、防老剂25-26份、二叔丁基28-36份、甲基苯酚18-26份、阻燃剂采用含氯20-40份、三氧化二锑10-20份、填充剂35-46份、超细滑石粉8.9-10.6份、高耐磨炭黑12-24份、氢氧化镁22-36份、低水硼酸锌15-17份、高岭土21-23份、硅灰石18-22份、蒙脱土、16-21份、云母粉中11-15份。
具体地，本发明它由以下原料组成：按分量计取，氯磺化聚乙烯32份、防老剂26份、二叔丁基30份、甲基苯酚22份、阻燃剂采用含氯28份、三氧化二锑18份、填充剂37份、超细滑石粉10.2份、高耐磨炭黑15份、氢氧化镁26份、低水硼酸锌15份、高岭土22份、硅灰石21份、蒙脱土、18份、云母粉中13份。
本发明的有益效果：用氯磺化聚乙烯护套橡皮配方生产的氯磺化聚乙烯护套橡皮的用于水声换能器电缆的护套，可采用连续硫化挤橡工艺，生产出的成品电缆不仅机械物理性能比普通橡皮高，而且具有阻燃、耐磨、防水性性和耐油性好、耐高低温等特性，延长了电缆的使用寿命。
具体实施方式
为使本发明现的技术手段、创作特征、达成目的与功效易于明白了解，下面结合具体实施方式，进一步阐述本发明。
本发明是采取以下技术方案来实现的：一种防水电缆氯磺化聚乙烯护套橡皮配方，它由以下原料组成：按分量计取，氯磺化聚乙烯30-45份、防老剂25-26份、二叔丁基28-36份、甲基苯酚18-26份、阻燃剂采用含氯20-40份、三氧化二锑10-20份、填充剂35-46份、超细滑石粉8.9-10.6份、高耐磨炭黑12-24份、氢氧化镁22-36份、低水硼酸锌15-17份、高岭土21-23份、硅灰石18-22份、蒙脱土、16-21份、云母粉中11-15份。
作为本发明的优选方案；本发明它由以下原料组成：按分量计取，氯磺化聚乙烯32份、防老剂26份、二叔丁基30份、甲基苯酚22份、阻燃剂采用含氯28份、三氧化二锑18份、填充剂37份、超细滑石粉10.2份、高耐磨炭黑15份、氢氧化镁26份、低水硼酸锌15份、高岭土22份、硅灰石21份、蒙脱土、18份、云母粉中13份。
尽管上文对本发明的具体实施方式给予了详细描述和说明，但是应该指明的是，我们可以依据本发明的构想对上述实施方式进行各种等效改变和修改，其所产生的功能作用仍未超出说明书所涵盖的精神时，均应在本发明的保护范围之内。

Claims (2)

1.一种防水电缆氯磺化聚乙烯护套橡皮配方，其特征在于，它由以下原料组成：按分量计取，氯磺化聚乙烯30-45份、防老剂25-26份、二叔丁基28-36份、甲基苯酚18-26份、阻燃剂采用含氯20-40份、三氧化二锑10-20份、填充剂35-46份、超细滑石粉8.9-10.6份、高耐磨炭黑12-24份、氢氧化镁22-36份、低水硼酸锌15-17份、高岭土21-23份、硅灰石18-22份、蒙脱土、16-21份、云母粉中11-15份。
2.根据权利要求1所述的一种防水电缆氯磺化聚乙烯护套橡皮配方，其特征在于，它由以下原料组成：按分量计取，氯磺化聚乙烯32份、防老剂26份、二叔丁基30份、甲基苯酚22份、阻燃剂采用含氯28份、三氧化二锑18份、填充剂37份、超细滑石粉10.2份、高耐磨炭黑15份、氢氧化镁26份、低水硼酸锌15份、高岭土22份、硅灰石21份、蒙脱土、18份、云母粉中13份。
CN201610054403.3A 2016-01-27 2016-01-27 一种防水电缆氯磺化聚乙烯护套橡皮配方 Pending CN105623131A (zh)