CN105534741B - A kind of peelable nail polish glue and its synthetic method - Google Patents
A kind of peelable nail polish glue and its synthetic method Download PDFInfo
- Publication number
- CN105534741B CN105534741B CN201610038612.9A CN201610038612A CN105534741B CN 105534741 B CN105534741 B CN 105534741B CN 201610038612 A CN201610038612 A CN 201610038612A CN 105534741 B CN105534741 B CN 105534741B
- Authority
- CN
- China
- Prior art keywords
- byk
- nail polish
- polish glue
- irgacure
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a kind of peelable nail polish glue and its synthetic methods.The peelable nail polish glue of the present invention, in parts by weight, it is made of 50 80 parts of UV solidified resins A, 50 80 parts of UV solidified resins B, 50 80 parts of UV solidified resins C, 0.05 0.1 parts of levelling agents, 1 10 parts of wetting agent, 0.2 1 parts of antifoaming agent, 1 10 parts of UV mill bases and 35 parts of photoinitiator A and photoinitiator b.There are quick setting capabilities after the irradiation of 365nmUV LED light after the peelable nail polish glue film of the present invention, the technical fields such as the manicure of various people can be widely used.
Description
Technical field
The invention belongs to technical field of polymer materials, and in particular to a kind of peelable nail polish glue and its synthetic method, it should
Peelable nail polish glue is irradiated especially suitable for 365nm UV-LED light sources to be cured.
Background technology
Ms likes having deep love for derived from one kind to manicure.Nail polish glue using when with tool be applied to nail, by common UV light
Crosslink polymerisation after the light source treatment with irradiation of source, the nail polish adhesive curing object of generation is beautiful in colour, glittering and translucent full, change
It is infinite, it is the favorite of ladies.Compared with common UV light sources curing mode, UV-LED light sources have luminous efficiency height, long lifespan,
Many advantages, such as reaction speed is fast, heat release is few, energy-saving and environmental protection has gradually substituted common UV light sources.With enriching for city life
With the quickening of rhythm of life transformation, ladies have liked the allegro transformation nail of oneself.Peelable nail polish glue is easy to use,
Do not have to whole of cleaner energy when needing to remove to peel off, easily, is particularly suitable for child and uses.But current peelable nail polish glue
Generally aqueous, the transparent water that need to arrange in pairs or groups or sealing water use;It is not so good as oiliness nail polish glue in persistence, drying is slower, and can
Stripping nail polish glue is generally added to peelable component in the formula of nail polish glue, makes troubles to the production and use of nail polish glue.
Based on background above, need to develop one kind can rapid curing, have from stripping component and meanwhile have decorative effect,
The good peelable nail polish glue of peeling effect and its synthetic method.
Invention content
One of the object of the invention provide one kind can rapid curing, have from stripping component and meanwhile have decorative effect, stripping
The good peelable nail polish glue of peelable nail polish glue of effect.The two of the object of the invention provide a kind of above-mentioned synthesis of peelable nail polish glue
Method.
Technical scheme of the present invention is specifically described as follows.
A kind of peelable nail polish glue, in parts by weight, composition and content are as follows:
The wherein UV solidified resins A is a kind of quick-setting UV resins;
The chemical constitution of the UV solidified resins A is as follows:
Wherein:M is the integer within the scope of 1-30;N is the integer within the scope of 1-30.
The UV solidified resins B is selected from double pentaerythritol methacrylate, diethylene glycol diacrylate, tetrahydrofuran
Acrylate, pentaerythritol tetraacrylate, ethoxylated bisphenol A dimethylacrylates, two-trimethylolpropane tetras acid
Ester, three (2- ethoxys) isocyanuric acid triacrylates, pentaerythritol triacrylate, ethoxyquin trimethylolpropane tris propylene
Acid esters, the third oxidation trimethylolpropane trimethacrylate, ethoxyquin pentaerythritol tetraacrylate, isobornyl acrylate, three
Cyclodecane Dimethanol Diacrylate, third oxidation neopentylglycol diacrylate, ethoxyquin trimethylolpropane trimethacrylate,
Hyperbranched polyester acrylic ester, alkoxy acrylic ester, carbonic acid mono acrylic ester, imidazole radicals mono acrylic ester, cyclic carbonate ester list
One or more of acrylate, epoxy silicone monomer, silicone acrylate and vinyl ethers monomer;
The UV solidified resins C is toughened resin;
The levelling agent be selected from the high Tego Glide 410 of enlightening, Germany BYK Bi Ke BYK-UV3510, BYK-341,
One or more of BYK-344, BYK-345, BYK-346, BYK-347, BYK-348;
The wetting agent is selected from the aqueous wetting dispersing agent Silok-7117W of NP-100, Si Luoke-of Dow company
One or more of;
The antifoaming agent be selected from Germany BYK Bi Ke BYK-024, BYK-025, BYK-035, BYK-037, BYK-038,
One or more of BYK-044 or BYK-038;
The UV mill bases are in mill base indigo plant F4049, purple F612, red F3087, red F3095, orange F8010 or Huang F512
One or more;
The photoinitiator A be BASF Irgacure1173, Irgacure 184D, Irgacure TPO,
Irgacure 369, Irgacure 651, Irgacure 379, Irgacure 819, Irgacure 907 or macromolecular light
One or more of initiator Esacure KIP 150;
The photoinitiator b be selected from BASF BASF photoinitiators Irgacure 2959, IRGACURE500 or
It is one or more of in IRGACURE819DW;
In the present invention, in parts by weight, raw material composition and content are as follows by the UV solidified resins A:
The UV solidified resins A is prepared as follows:
Above-mentioned gained methyl and phenyl hydrogen-containing silicon oil and glycerol propoxylate triacrylate are proportionally added into reaction vessel
In, polymerization inhibitor is added, protective gas is passed through, stirs and heats, is warming up to 60~80 DEG C, catalyst is added, stirs lower constant temperature 3
~5h stops heating, waits for that temperature drops to room temperature to get UV solidified resins A.
The present invention also provides a kind of synthetic methods of peelable nail polish glue, are as follows:
According to formula, wetting agent, levelling agent, antifoaming agent are added in the high speed dispersor of control rotating speed 300-400r/min
With UV mill bases, rotating speed is down to 300r/min after disperseing 15-20min under 600-800r/min rotating speeds, UV solidified resins are added
A, UV solidified resins B, UV solidified resin C and photoinitiator A, photoinitiator b, continue disperse 5-10min, be uniformly mixed to get
To peelable nail polish glue.
The useful achievement of the present invention is as follows:
A kind of peelable nail polish glue of the present invention, makes it as a result of the UV solidified resins A of multi-functional acrylate
With the rapid capability under the irradiation of 365nmUV-LED lamp sources.
Further, after the peelable nail polish glue film of present invention gained peelable nail polish glue is precoated through UV nail polish light irradiations
The surface of glass slide, according to the fingers-touch method (surface of the peelable nail polish glue for the cured a period of time that press...withes one's finger, with tack-free work
For the standard being fully cured, when being fully cured with peelable nail polish glue the shortest time used characterize), after testing, the present invention
The peelable nail polish glue of quick-drying hardening time be 1-7s.
Further, the peelable nail polish glue addition of present invention gained has toughening effect UV solidified resin C, makes peelable
Nail polish glue has certain toughness.
Further, a kind of peelable nail polish glue of the invention, the UV solidified resin A molecular structures as main film forming substance
For organosilicon structures, there is very low surface energy, reduce the interaction between film and base material, is allowed to embody preferably from stripping
From property, it is not required to add stripping auxiliary agent again.Peel strength newly thinks carefully the CMT5104 electronic tension testers of company in room using Shenzhen
The lower peel test that 180 ° are carried out by GB/T2790-1995 standards " 180 ° of peeling strength test methods of adhesive " of temperature, stretches speed
Spend 50mm/min;It is 0.21~0.25kN/m to measure peel strength.
In conclusion a kind of peelable nail polish glue of the present invention, has quick solid under the irradiation of 365nmUV-LED lamp sources
Change ability has higher toughness, easily peelable after film.And preparation method is due to simple for process, it is easy to control, therefore have
There is the features such as technology maturation, quick, efficient, and is suitable for industrialized production.
Specific implementation mode
The present invention is described in further detail below by embodiment, but is not intended to limit the present invention.
In raw material used in various embodiments of the present invention in addition to the special producer shown and specification, other raw materials be it is commercially available,
Specification is that chemistry is pure.
The model of various equipment used in the present invention and the information of manufacturer are as follows:
GFJ-0.4 type high speed dispersors, the new promise experimental instruments and equipment limited production in Shanghai.
Embodiment 1
A kind of peelable nail polish glue, in parts by weight, raw material composition and content are as follows:
Wherein:In parts by weight, composition and content are as follows by the UV solidified resins A:
The UV solidified resins A is prepared as follows:20 parts of methyl and phenyl hydrogen-containing silicon oils and 10 part of third oxidation are sweet
Oily triacrylate adds 0.005 polymerization inhibitor by being added in the three-necked flask of 500ml, is passed through protective gas, stirring is simultaneously
Heating is warming up to 60 DEG C, and 0.03 part of catalyst is added, and stirs lower constant temperature 3h, stops heating, wait for that flask temperature drops to room temperature, i.e.,
Obtain UV solidified resins A.
The levelling agent is the high Tego Glide of enlightening 410;
The wetting agent is the NP-100 of Dow company;
The antifoaming agent is Germany BYK-035, BYK-037 in mass ratio 1:1 mixture;
The UV mill bases are one in mill base indigo plant F4049, purple F612, red F3087, red F3095, orange F8010, Huang F512
Kind or a variety of mixtures;
The photoinitiator A is that BASF Irgacure1173, Irgacure 184D, Irgacure TPO press quality
Than 1:1:The mixture of 1 composition;
The photoinitiator b be BASF BASF photoinitiators Irgacure 2959, IRGACURE500 in mass ratio
1:The mixture of 1 composition;
In the present embodiment, a kind of synthetic method of peelable nail polish glue specifically comprises the following steps:
According to formula, in the GFJ-0.4 types high speed dispersor for controlling rotating speed 300r/min, (the new promise instrument and equipment in Shanghai is limited
Company) 1 part of wetting agent of middle addition, 0.05 part of levelling agent, 0.2 part of antifoaming agent and 1 part of UV mill base, through disperseing under 600r/min rotating speeds
Rotating speed is down to 300r/min after 15min, 50 parts of UV solidified resins A, 50 parts of UV solidified resins B, 50 parts of UV solidified resins are added
C, 3 parts of photoinitiator A and 3 parts of photoinitiator bs continue to disperse 10min, be uniformly mixed to get to peelable nail polish glue.
The UV-LED light irradiations through 365nm precoat peelable nail polish glue after peelable nail polish glue film obtained by the present embodiment
Glass slide surface, according to the fingers-touch method (surface of the peelable nail polish glue for the cured a period of time that press...withes one's finger, with tack-free
As the standard being fully cured, when being fully cured with peelable nail polish glue the shortest time used characterize), after testing, this hair
The hardening time of the peelable nail polish glue of bright quick-drying is 1s.
Peel strength newly thinks carefully the CMT5104 electronic tension testers of company at room temperature by GB/T2790- using Shenzhen
1995 standards " 180 ° of peeling strength test methods of adhesive " carry out 180 ° of peel test, tensile speed 50mm/min;It measures
Peel strength is 0.25kN/m;
Higher curing rate after peelable nail polish glue film obtained by above the present embodiment, it is easily peelable.
Embodiment 2
A kind of peelable nail polish glue, in parts by weight, raw material composition and content are as follows:
Wherein:In parts by weight, composition and content are as follows by the UV solidified resins A:
The UV solidified resins A is prepared as follows:60 parts of methyl and phenyl hydrogen-containing silicon oils and 20 part of third oxidation are sweet
Oily triacrylate is added in the three-necked flask of 500ml, adds 0.01 part of polymerization inhibitor, is passed through protective gas, stirring is simultaneously
Heating is warming up to 80 DEG C, and 0.05 part of catalyst is added, and stirs lower constant temperature 5h, stops heating, wait for that flask temperature drops to room temperature, i.e.,
Obtain UV solidified resins A.
The levelling agent is Germany BYK-345, BYK-346 in mass ratio 1:The mixture of 1 composition;
The wetting agent is Germany BYK 333;
The antifoaming agent is Germany BYK Bi Ke BYK-024, BYK-025 in mass ratio 1:The mixture of 1 composition;
The UV mill bases are one in mill base indigo plant F4049, purple F612, red F3087, red F3095, orange F8010, Huang F512
Kind or a variety of mixtures;
The photoinitiator A is BASF Irgacure 184D, Irgacure TPO, Irgacure 369 press quality
Than 1:1:More than 1 kinds of mixture;
The photoinitiator b be BASF BASF photoinitiators Irgacure 2959, IRGACURE500 in mass ratio
2:The mixture of 1 composition;
In embodiment, a kind of synthetic method of peelable nail polish glue specifically comprises the following steps:
According to formula, in the GFJ-0.4 types high speed dispersor for controlling rotating speed 400r/min, (the new promise instrument and equipment in Shanghai is limited
Company) 10 parts of wetting agents of middle addition, 0.1 part of levelling agent, 1 part of antifoaming agent and 10 parts of UV mill bases, through disperseing under 800r/min rotating speeds
Rotating speed is down to 300r/min after 20min, 80 parts of UV solidified resins A, 80 parts of UV solidified resins B, 80 parts of UV solidified resins are added
C, 5 parts of photoinitiator A and 5 parts of photoinitiator bs continue to disperse 10min, be uniformly mixed to get to peelable nail polish glue.
The UV-LED light irradiations through 365nm precoat peelable nail polish glue after peelable nail polish glue film obtained by the present embodiment
Glass slide surface, according to the fingers-touch method (surface of the peelable nail polish glue for the cured a period of time that press...withes one's finger, with tack-free
As the standard being fully cured, when being fully cured with peelable nail polish glue the shortest time used characterize), after testing, this hair
The hardening time of the peelable nail polish glue of bright quick-drying is 7s.
Peel strength newly thinks carefully the CMT5104 electronic tension testers of company at room temperature by GB/T2790- using Shenzhen
1995 standards " 180 ° of peeling strength test methods of adhesive " carry out 180 ° of peel test, tensile speed 50mm/min;It measures
Peel strength is 0.21kN/m;
Higher curing rate after peelable nail polish glue film obtained by above the present embodiment, it is easily peelable.
In conclusion the peelable nail polish glue of the present invention is using UV curing formulas, the high speed curable of UV improves it
Curing rate, only 1~7s;The chameleon pigment of the peelable nail polish glue addition of gained of the invention comes to peelable nail polish adhesive tape
Ever-changing color, addition have toughening effect UV solidified resin C, peelable nail polish glue are made to have certain toughness.
UV solidified resin A molecular structures as main film forming substance are organosilicon structures, have very low surface energy, reduce film
Interaction between base material is allowed to embody preferable rippability, and peel strength is 0.21~0.25kN/m.Stripping is without residual
It stays.
Above said content is only the basic explanation under present inventive concept, and is appointed made by technical solution according to the present invention
What equivalent transformation, is within the scope of protection of the invention.
Claims (4)
1. a kind of peelable nail polish glue, which is characterized in that in parts by weight, raw material composition and content are as follows:
Wherein:The chemical constitution of the UV solidified resins A is as follows:
Wherein:M is the integer within the scope of 1-30;N is the integer within the scope of 1-30;
The UV solidified resins B is selected from double pentaerythritol methacrylate, diethylene glycol diacrylate, tetrahydrofuran propylene
Acid esters, pentaerythritol tetraacrylate, ethoxylated bisphenol A dimethylacrylates, two-trimethylolpropane tetra-acrylates,
Three (2- ethoxys) isocyanuric acid triacrylates, pentaerythritol triacrylate, ethoxyquin trimethylolpropane tris acrylic acid
Ester, the third oxidation trimethylolpropane trimethacrylate, ethoxyquin pentaerythritol tetraacrylate, isobornyl acrylate, tricyclic
Decane Dimethanol Diacrylate, ethoxyquin trimethylolpropane trimethacrylate, surpasses the third oxidation neopentylglycol diacrylate
Branched polyester acrylate, alkoxy acrylic ester, carbonic acid mono acrylic ester, imidazole radicals mono acrylic ester, cyclic carbonate ester list third
One or more of olefin(e) acid ester, epoxy silicone monomer, silicone acrylate and vinyl ethers monomer;
The UV solidified resins C is toughened resin;
The levelling agent be selected from the high Tego Glide 410 of enlightening, Germany BYK Bi Ke BYK-UV3510, BYK-341, BYK-344,
One or more of BYK-345, BYK-346, BYK-347, BYK-348;
The wetting agent is the NP-100 of Dow company;
The one kind of the UV mill bases in mill base indigo plant F4049, purple F612, red F3087, red F3095, orange F8010, Huang F512
Or it is a variety of;
The antifoaming agent is Germany BYK Bi Ke BYK-024, BYK-025, BYK-035, BYK-037, BYK-038, BYK-044
Or one or more of BYK-038;
The photoinitiator A is BASF Irgacure1173, Irgacure 184D, Irgacure TPO, Irgacure
369, Irgacure 651, Irgacure 379, Irgacure 819, Irgacure 907 or macromolecular photoinitiator
One or more of Esacure KIP 150;
The photoinitiator b be selected from BASF BASF photoinitiators Irgacure 2959, IRGACURE500 or
It is one or more of in IRGACURE819DW.
2. peelable nail polish glue as described in claim 1, which is characterized in that the UV solidified resins A is counted in parts by weight
It calculates, raw material and content are as follows:
The UV solidified resins A is prepared as follows:
Above-mentioned gained methyl and phenyl hydrogen-containing silicon oil and glycerol propoxylate triacrylate are proportionally added into reaction vessel, then
Polymerization inhibitor is added, is passed through protective gas, stirs and heat, is warming up to 60~80 DEG C, catalyst is added, stirs lower 3~5h of constant temperature,
Stop heating, waits for that temperature drops to room temperature to get UV solidified resins A.
3. peelable nail polish glue as claimed in claim 1 or 2, which is characterized in that hardening time 1-7s, in tensile speed
The peel strength measured when 50mm/min is 0.21~0.25kN/m.
4. a kind of synthetic method of peelable nail polish glue as described in claim 1, which is characterized in that be as follows:
According to formula, wetting agent, levelling agent, antifoaming agent and UV are added in the high speed dispersor of control rotating speed 300-400r/min
Rotating speed is down to 300r/min by mill base after disperseing 15-20min under 600-800r/min rotating speeds, and UV solidified resins A, UV are added
Solidified resin B, UV solidified resin C and photoinitiator A, photoinitiator b continue to disperse 5-10min, be uniformly mixed to get to can
Remove nail polish glue.