CN105506973A - Fabric for airplane interior trimming - Google Patents

Fabric for airplane interior trimming Download PDF

Info

Publication number
CN105506973A
CN105506973A CN201610016569.6A CN201610016569A CN105506973A CN 105506973 A CN105506973 A CN 105506973A CN 201610016569 A CN201610016569 A CN 201610016569A CN 105506973 A CN105506973 A CN 105506973A
Authority
CN
China
Prior art keywords
fabric
soak
temperature
parts
prepared
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610016569.6A
Other languages
Chinese (zh)
Inventor
杨大明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Bo Langkaide Fabric Co Ltd
Original Assignee
Anhui Bo Langkaide Fabric Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Bo Langkaide Fabric Co Ltd filed Critical Anhui Bo Langkaide Fabric Co Ltd
Priority to CN201610016569.6A priority Critical patent/CN105506973A/en
Publication of CN105506973A publication Critical patent/CN105506973A/en
Pending legal-status Critical Current

Abstract

The invention discloses a fabric for airplane interior trimming, and relates to the technical field of fabrics for airplane interior trimming. The fabric for airplane interior trimming is prepared from PET, graphite, carbon fibers, glass fibers, a lubricating agent, anti-cracking pigment, terry yarn, a corrosion inhibitor, spinning oil, POY, wool and the like through processing production. According to the fabric for airplane interior trimming, the higher anti-static capacity is achieved, the fabric can be kept safe and sanitary due to the fact that sterilizing factors are contained, cleaning is convenient, the aid-sleeping function is achieved, and the wear-resisting function, the soiling-resisting function and the heat preservation function are achieved; the using comfort degree and the health maintenance effect of the fabric are improved, and the fabric is durable in use and has various beneficial functions.

Description

A kind of fabric for aircraft interior trim
Technical field:
The present invention relates to aircraft interior trim fabric technical field, be specifically related to a kind of fabric for aircraft interior trim.
Background technology:
Aircraft inner decoration facing needs to have comfortableness, security and ornamental feature, fabric is higher for performance requirement, the fabric of aircraft interior trim is generally textile cloth, dermatine and corium etc., but the weaving face fabric in existing aircraft inner decoration facing generally uses common weaving face fabric, only simply can meet the demand of general decor, then need the fabric of greater functionality feature to arrange in pairs or groups for high-end aircraft, a kind of fabric that this patent provides has antistatic, antibacterial, insulation, easy cleaning, has sleep-aid function, wear-resisting, the feature such as bear dirty.
Summary of the invention:
Technical problem to be solved by this invention is to provide one to have stronger anti-static ability, have sterilization factors can keep fabric safety and sanitation, convenient cleaning, there is sleep-aid function and have wear-resisting, bear dirty, the aircraft interior trim fabric of the function such as insulation.
Technical problem to be solved by this invention adopts following technical scheme to realize:
For a fabric for aircraft interior trim, step is processed by the following method:
1) basic silk is prepared, by mass fraction, PET30-40 part, graphite 20-25 part, carbon fiber 10-20 part, glass fibre 10-20 part, lubricant 10-15 part, crack resistence pigment 10-15 part, terry yarn 10-15 part, corrosion inhibitor 5-8 part, spinning oil 3-5 part are mixed and made into basic silk;
2) soak is prepared: perfluorocarboxylic acid 10-15 part, oxalic acid urea 5-8 part, triethanolamine 2-5 part, sodium metasilicate 2-5 part, polyvinylpyrrolidone 2-5 part, cocounut oil 10-15 part, tea seed powder 8-10 part and water 100-200 part mix and blend are prepared from by mass fraction, adopt the environment of 85-90 DEG C to carry out stirring during preparation and can use after keeping constant temperature 30-40 minute, the setting of constant temperature can be that the effectiveness between each composition of soak gives full play to;
3) basic silk is carried out process to soak, airing is taken out after soaking 8-10 hour with soak during immersion, dry for the first time by a dryer 40-50 DEG C temperature after airing 1-2 hour, first drying time is unsuitable long, temperature is also unsuitable too high, sum up through long-term experiment and show that the temperature of setting in 1-2 hour and 40-50 DEG C can increase the effectiveness of post-processed liquid and processing, and also can be conducive to initial stage basis silk to the abundant absorption of soak;
4) treatment fluid is prepared: by mass fraction by nano zine oxide 10-15 part, nano titanium oxide 5-8 part, adhesive 3-5 part, sulfamic acid 1-2 part, waterproofing agent 5-8 part and antioxidant 5-8 part mix and blend are prepared from, and adopt the environment of 85-90 DEG C to carry out stirring and can use after keeping constant temperature 30-40 minute during preparation;
5) carry out sprinkling with treatment fluid after drying to soak, put into after soaking in ultraviolet sterilising case and carry out sterilization, take out after sterilization 30-50 minute and again dry, dryer temperature is set in 50-60 DEG C, dry 40-50 minute, the secondary drying temperature higher time longer oven dry degree that can increase basic silk, facilitates follow-up braiding, and makes it absorb thoroughly to soak before;
6) after sterilization, basic silk is entered braiding machine to weave, during braiding, employing 20%POY, 30% wool become fabric with the common mixed weaving of 50% basic silk, together weave the comfort and result of use that can increase fabric with wool and POY;
7) enter in drawing machine after having woven and carry out drawing-off;
8) fabric braiding, drawing-off are soaked with soak after completing again, the time that secondary soaks is 3-4 hour, and during immersion, soak concentration is 50%, and secondary soaks and can make also can absorb soak in wool and POY, impel interaction, the effectiveness of soak is performed to maximum;
9) soak laggard in dryer dry 40 minutes, during oven dry, temperature is set as 80-90 DEG C, dry after take out stand-by;
10) sleeping liquid is prepared: by mass fraction, by amino acid, red date, tasteless son, pseudo-ginseng, caffeine, the tuber of dwarf lilyturf, Poria cocos, cassia seed, lavender, wheat flour, Jasmine, each 8 parts of honey, ginseng, each three parts of the stem of noble dendrobium joins in the goat milk of 50 parts and carries out stirring boiling, with the temperature boiling of 100-110 DEG C, after 1-1.5 hour, cooling is stand-by naturally, various sleeping composition carries out processing process together, be prepared from sleeping liquid to be absorbed by fabric, people can possess certain sleep-aid function in the process used, especially the stem of noble dendrobium, ginseng, amino acid plays facilitation especially to health,
11) fabric is put in sleeping liquid soak, stop when heating to temperature during immersion be gradually 85-90 DEG C heating, it is allowed naturally to cool, fabric is taken out when temperature drops to 35-40 DEG C, under strict limit temperature and time restriction, sleeping liquid is fully absorbed by fabric, then along with the various beneficiating ingredient that naturally reduces of temperature is merged the good phase result of use of absorption increase fabric by fabric;
12) by fabric spreading for cooling, oven dry after having soaked, vanning has been compiled;
Described soak and treatment fluid have the ability of the immersion grease reducing fabric, there is grease proofing effect, be convenient to the cleaning of fabric, and fabric can be made to have better flame retardant effect, at high temperature or the lower harmful substance produced of burning less, first basic silk is soaked, after fabric has woven, then again carry out secondary immersion the composition in soak can be made fully to be absorbed by fabric, increase the allomeric function of fabric and distinctive effectiveness;
By amino acid, red date, tasteless son, pseudo-ginseng, caffeine, the tuber of dwarf lilyturf, Poria cocos, cassia seed, lavender, wheat flour, Jasmine, each 8 parts of honey, each three parts of ginseng, the stem of noble dendrobium joins in the goat milk of 50 parts and carries out stirring boiling, with the temperature boiling of 100-110 DEG C, after 1-1.5 hour, cooling is stand-by naturally, various sleeping composition carries out processing process together, be prepared from sleeping liquid to be absorbed by fabric, people can possess certain sleep-aid function in the process used, and especially the stem of noble dendrobium, ginseng, amino acid play facilitation especially to health;
And in the preparation of basic silk, glass fibre, carbon fiber, wool, graphite etc. add the comfort that can not only increase later stage fabric can also increase fabric antistatic effect, increase the characteristics such as fabric tough wear-resistant hard, insulation;
The invention has the beneficial effects as follows provides one to have stronger anti-static ability, has sterilization factors and can keep fabric safety and sanitation, convenient cleaning, there is sleep-aid function and have wear-resisting, bear dirty, the aircraft interior trim fabric of the function such as insulation, add comfort and the health effect of fabric, and fabric is durable in use has various beneficial functions.
Detailed description of the invention:
The technological means realized to make the present invention, creation characteristic, reaching object and effect is easy to understand, below in conjunction with concrete example, setting forth the present invention further.
Embodiment 1:
For a fabric for aircraft interior trim, step is processed by the following method:
1) prepare basic silk, by mass fraction, PET40 part, 25 parts, graphite, 20 parts, carbon fiber, 20 parts, glass fibre, lubricant 15 parts, crack resistence pigment 15 parts, terry yarn 15 parts, corrosion inhibitor 8 parts, spinning oil 5 parts are mixed and made into basic silk;
2) soak is prepared: perfluorocarboxylic acid 15 parts, 8 parts, oxalic acid urea, triethanolamine 5 parts, sodium metasilicate 5 parts, polyvinylpyrrolidone 5 parts, cocounut oil 15 parts, 10 parts, tea seed powder and water 200 parts of mix and blends are prepared from by mass fraction, adopt the environment of 90 DEG C to carry out stirring during preparation and keep constant temperature can use after 40 minutes;
3) basic silk is carried out process to soak, take out airing after soaking 10 hours with soak during immersion, airing was dried for the first time by dryer 50 DEG C of temperature after 2 hours;
4) treatment fluid is prepared: by mass fraction by nano zine oxide 15 parts, nano titanium oxide 8 parts, 5 parts, adhesive, sulfamic acid 2 parts, waterproofing agent 8 parts and antioxidant 8 parts of mix and blends are prepared from, and adopt the environment of 90 DEG C to carry out stirring and keep constant temperature can use after 40 minutes during preparation;
5) carry out sprinkling with treatment fluid after drying to soak, put into after soaking in ultraviolet sterilising case and carry out sterilization, sterilization is taken out after 50 minutes and is again dried, and dryer temperature is set in 60 DEG C, dries 50 minutes;
6) after sterilization, basic silk is entered braiding machine to weave, during braiding, employing 20%POY, 30% wool become fabric with the common mixed weaving of 50% basic silk;
7) enter in drawing machine after having woven and carry out drawing-off;
8) fabric braiding, drawing-off are soaked with soak after completing again, and the time that secondary soaks is 4 hours, and during immersion, soak concentration is 50%;
9) soak laggard in dryer dry 40 minutes, during oven dry, temperature is set as 90 DEG C, dry after take out stand-by;
10) sleeping liquid is prepared: by mass fraction, by amino acid, red date, tasteless son, pseudo-ginseng, caffeine, the tuber of dwarf lilyturf, Poria cocos, cassia seed, lavender, wheat flour, Jasmine, each 8 parts of honey, each three parts of ginseng, the stem of noble dendrobium joins in the goat milk of 50 parts and carries out stirring boiling, and with the temperature boilings of 110 DEG C, after 1.5 hours, cooling is stand-by naturally;
11) fabric is put in sleeping liquid soak, stop heating when to heat to temperature be gradually 90 DEG C, allow it naturally cool during immersion, taking-up fabric when temperature drops to 40 DEG C;
12) by fabric spreading for cooling, oven dry after having soaked, vanning has been compiled;
Embodiment 2
For a fabric for aircraft interior trim, step is processed by the following method:
1) basic silk is prepared, by mass fraction, PET30 part, 20 parts, graphite, 10 parts, carbon fiber, 10 parts, glass fibre, lubricant 10 parts, crack resistence pigment 10 parts, terry yarn 10 parts, corrosion inhibitor 5 parts, spinning oil 3-5 part are mixed and made into basic silk;
2) soak is prepared: perfluorocarboxylic acid 10 parts, 5 parts, oxalic acid urea, triethanolamine 2 parts, sodium metasilicate 2 parts, polyvinylpyrrolidone 2 parts, cocounut oil 10 parts, 8 parts, tea seed powder and water 100 parts of mix and blends are prepared from by mass fraction, adopt the environment of 85 DEG C to carry out stirring during preparation and keep constant temperature can use after 30 minutes;
3) basic silk is carried out process to soak, take out airing after soaking 8 hours with soak during immersion, airing was dried for the first time by dryer 40 DEG C of temperature after 1 hour;
4) treatment fluid is prepared: by mass fraction by nano zine oxide 10 parts, nano titanium oxide 5 parts, 3 parts, adhesive, sulfamic acid 1 part, waterproofing agent 5 parts and antioxidant 5 parts of mix and blends are prepared from, and adopt the environment of 85 DEG C to carry out stirring and keep constant temperature can use after 30 minutes during preparation;
5) carry out sprinkling with treatment fluid after drying to soak, put into after soaking in ultraviolet sterilising case and carry out sterilization, sterilization is taken out after 30 minutes and is again dried, and dryer temperature is set in 50 DEG C, dries 40 minutes;
6) after sterilization, basic silk is entered braiding machine to weave, during braiding, employing 20%POY, 30% wool become fabric with the common mixed weaving of 50% basic silk;
7) enter in drawing machine after having woven and carry out drawing-off;
8) fabric braiding, drawing-off are soaked with soak after completing again, and the time that secondary soaks is 3 hours, and during immersion, soak concentration is 50%;
9) soak laggard in dryer dry 40 minutes, during oven dry, temperature is set as 80 DEG C, dry after take out stand-by;
10) sleeping liquid is prepared: by mass fraction, by amino acid, red date, tasteless son, pseudo-ginseng, caffeine, the tuber of dwarf lilyturf, Poria cocos, cassia seed, lavender, wheat flour, Jasmine, each 8 parts of honey, each three parts of ginseng, the stem of noble dendrobium joins in the goat milk of 50 parts and carries out stirring boiling, and with the temperature boilings of 100 DEG C, after 1 hour, cooling is stand-by naturally;
11) fabric is put in sleeping liquid soak, stop heating when to heat to temperature be gradually 85 DEG C, allow it naturally cool during immersion, taking-up fabric when temperature drops to 35 DEG C;
12) by fabric spreading for cooling, oven dry after having soaked, vanning has been compiled;
More than show and describe general principle of the present invention and principal character and advantage of the present invention.The technical staff of the industry should understand; the present invention is not restricted to the described embodiments; what describe in above-described embodiment and description just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.Application claims protection domain is defined by appending claims and equivalent thereof.

Claims (1)

1. for a fabric for aircraft interior trim, it is characterized in that: step is carried out processing and formed by the following method:
1) basic silk is prepared, by mass fraction, PET30-40 part, graphite 20-25 part, carbon fiber 10-20 part, glass fibre 10-20 part, lubricant 10-15 part, crack resistence pigment 10-15 part, terry yarn 10-15 part, corrosion inhibitor 5-8 part, spinning oil 3-5 part are mixed and made into basic silk;
2) prepare soak: perfluorocarboxylic acid 10-15 part, oxalic acid urea 5-8 part, triethanolamine 2-5 part, sodium metasilicate 2-5 part, polyvinylpyrrolidone 2-5 part, cocounut oil 10-15 part, tea seed powder 8-10 part and water 100-200 part mix and blend are prepared from by mass fraction, adopt the environment of 85-90 DEG C to carry out stirring during preparation and can use after keeping constant temperature 30-40 minute;
3) basic silk is carried out process to soak, take out airing after soaking 8-10 hour with soak during immersion, dry for the first time by a dryer 40-50 DEG C temperature after airing 1-2 hour;
4) treatment fluid is prepared: by mass fraction by nano zine oxide 10-15 part, nano titanium oxide 5-8 part, adhesive 3-5 part, sulfamic acid 1-2 part, waterproofing agent 5-8 part and antioxidant 5-8 part mix and blend are prepared from, and adopt the environment of 85-90 DEG C to carry out stirring and can use after keeping constant temperature 30-40 minute during preparation; 5) carry out sprinkling with treatment fluid after drying to soak, put into after soaking in ultraviolet sterilising case and carry out sterilization, take out after sterilization 30-50 minute and again dry, dryer temperature is set in 50-60 DEG C, dries 40-50 minute;
6) after sterilization, basic silk is entered braiding machine to weave, during braiding, employing 20%POY, 30% wool become fabric with the common mixed weaving of 50% basic silk;
7) enter in drawing machine after having woven and carry out drawing-off;
8) fabric braiding, drawing-off are soaked with soak after completing again, and the time that secondary soaks is 3-4 hour, and during immersion, soak concentration is 50%;
9) soak laggard in dryer dry 40 minutes, during oven dry, temperature is set as 80-90 DEG C, dry after take out stand-by;
10) sleeping liquid is prepared: by mass fraction, by amino acid, red date, tasteless son, pseudo-ginseng, caffeine, the tuber of dwarf lilyturf, Poria cocos, cassia seed, lavender, wheat flour, Jasmine, each 8 parts of honey, each three parts of ginseng, the stem of noble dendrobium joins in the goat milk of 50 parts and carries out stirring boiling, and with the temperature boiling of 100-110 DEG C, after 1-1.5 hour, cooling is stand-by naturally;
11) fabric is put in sleeping liquid soak, stop heating when to heat to temperature be gradually 85-90 DEG C, allow it naturally cool, taking-up fabric when temperature drops to 35-40 DEG C during immersion;
12) by fabric spreading for cooling, oven dry after having soaked, vanning has been compiled.
CN201610016569.6A 2016-01-06 2016-01-06 Fabric for airplane interior trimming Pending CN105506973A (en)