CN106400480A - Production process of woven garment composite fabric - Google Patents

Production process of woven garment composite fabric Download PDF

Info

Publication number
CN106400480A
CN106400480A CN201610789991.5A CN201610789991A CN106400480A CN 106400480 A CN106400480 A CN 106400480A CN 201610789991 A CN201610789991 A CN 201610789991A CN 106400480 A CN106400480 A CN 106400480A
Authority
CN
China
Prior art keywords
parts
soak
drying
cotton
time
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610789991.5A
Other languages
Chinese (zh)
Inventor
杨双建
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Sanxin New Fiber Technology Co Ltd
Original Assignee
Anhui Sanxin New Fiber Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Sanxin New Fiber Technology Co Ltd filed Critical Anhui Sanxin New Fiber Technology Co Ltd
Priority to CN201610789991.5A priority Critical patent/CN106400480A/en
Publication of CN106400480A publication Critical patent/CN106400480A/en
Pending legal-status Critical Current

Abstract

The invention discloses a production process of a woven garment composite fabric, and relates to the technical field of garment fabrics. The production process comprises the following steps: material preparation, i.e., selecting cotton yarn and cotton-like dacron as raw materials; pretreatment, i.e., performing first-time immersion on the cotton yarn and the cotton-like dacron in immersion fluid respectively for 5-6 hours, wherein the immersion fluid for the first-time immersion is prepared from 3-5 parts of perfluorocarboxylic acid, 1-3 parts of oxalate urea, 1-2 parts of triethanolamine, 1-3 parts of sodium silicate and 100-200 parts of water; then pulling out for second-time immersion, wherein immersion fluid for the second-time immersion is prepared from the following components in parts by weight: 1-2 parts of chlorendic acid, 3-4 parts of gold potassium chloride, 2-3 parts of nonylphenol polyoxyethylene ether, 1-2 parts of polyvinylpyrrolidone and 100-150 parts of water; dyeing; drying to form; weaving, cutting cloth, plaiting and checking needles; compounding; steaming; and cleaning and drying. The production process disclosed by the invention has the advantages of good flame retardant efficiency, good environment friendliness, good anti-oil effect and convenience for cleaning as oily substances are difficult to immerse.

Description

A kind of production technology of the woven composite material of clothes
Technical field：
The present invention relates to garment material technical field, the production technology of the woven composite material of more particularly to a kind of clothes.
Background technology：
Garment material needs with comfortableness, security and ornamental feature, and fabric is higher for performance requirement, clothes Fabric be generally textile cloth, dermatine and corium etc., but the weaving face fabric in existing garment material generally uses Common weaving face fabric, flame retardant effect is poor, easily produces harmful substance under high temperature or burning, and garment material can touch A lot of things, be can frequently result in much greasy thing and are contacted with garment material, and the grease proofing of existing textile garment material prevents Dirty effect is poor, is unfavorable for cleaning.
Content of the invention：
The technical problem to be solved is to provide a kind of feature of environmental protection good, and grease proofing effect is good, is easy to the clothes cleaning The production technology of composite material is knitted in installation.
For solving above-mentioned technical problem, the present invention adopts following technical scheme：
A kind of production technology of the woven composite material of clothes it is characterised in that：Comprise the following steps,
(1), get the raw materials ready, select cotton yarn, imitative cotton terylene as raw material, cotton yarn, the ratio of Wool-Like terylene weight are 10:1 ～10；
(2), pre-process, carry out respectively soaking for the first time in soak by cotton yarn and imitative cotton terylene, soak time is 5 ～6 hours, 3～5 parts of soak perfluorocarboxylic acid when soaking for the first time, 1～3 part of oxalic acid urea, 1～2 part of triethanolamine, silicic acid 1～3 part of sodium and 100～200 parts of water；Then pull out and carry out second immersion, weight pressed by described soak when soaking for second Amount part includes 1～2 part of chlorendic acid, 3～4 parts of gold potassium chloride, 2～3 parts of NPE, polyvinylpyrrolidone 1～2 Part and 100～150 parts of water, second soak when temperature be 60～80 DEG C, pull out after soaking twice and dry；
(3), dye, respectively cotton yarn and imitative cotton terylene are carried out with dyeing process, in dyeing face when described dyeing is processed Material also middle addition uvioresistant finishing agent；
(4) setting, is dried, freezes at temperature is -1～-10 DEG C, then carry out drying and processing, temperature during drying is 50 ～60 DEG C；
(7), weave, cut open cloth, plaiting and test pin；
(8), it is combined, be combined by the adhesive cloth good with cropping using sponge and base fabric；
(9), gas steams, the cloth being combined enters promoting the circulation of qi steaming, and the time that gas steams is 2～3 hours；
(10), cleaning-drying.
Described uvioresistant finishing agent includes 3～5 parts of nano zine oxide, 1～2 part of nano titanium oxide by weight, 1～2 part of adhesive and 0.5～1 part of sulfamic acid.
Described binding agent includes 100 parts of starch, 6 parts of borax, 0.5 part of sodium thiosulfate and 100 parts of water by weight.
Described cleaning-drying is to be impregnated using the waterproofing agent of 26～30g/L, then dries setting.
Step (4) of the present invention can increase the stability of pigment, is not easy to fade during use.
Soak for the first time in pretreatment in the present invention and employ 3～5 parts of perfluorocarboxylic acid, 1～3 part of oxalic acid urea, three ethanol 1～2 part of amine, 1～3 part of sodium metasilicate have the ability of the immersion grease reducing fabric, have grease proofing effect, are easy to fabric Cleaning.
Soak for the first time in pretreatment in the present invention and employ the resistance that multiple combination of chemicals of good flame retardation effect use Combustion agent, 1～2 part of chlorendic acid, 3～4 parts of gold potassium chloride, 2～3 parts of NPE, 1～2 part of polyvinylpyrrolidone There is more preferable flame retardant effect, the harmful substance producing at high temperature or under burning is less.
The invention has the beneficial effects as follows：Good flame retardation effect of the present invention, the feature of environmental protection is good, and grease proofing effect is good, and greasy thing is difficult To immerse, it is easy to grease proofing, the good hand touch cleaned.
Specific embodiment：
To further illustrate the present invention below by embodiment.
A kind of production technology of the woven composite material of clothes, comprises the following steps,
(1), get the raw materials ready, select cotton yarn, imitative cotton terylene as raw material, cotton yarn, the ratio of Wool-Like terylene weight are 10:1 ～10；
(2), pre-process, carry out respectively soaking for the first time in soak by cotton yarn and imitative cotton terylene, soak time is 5 ～6 hours, 3～5 parts of soak perfluorocarboxylic acid when soaking for the first time, 1～3 part of oxalic acid urea, 1～2 part of triethanolamine, silicic acid 1～3 part of sodium and 100～200 parts of water；Then pull out and carry out second immersion, soak when soaking for second wraps by weight Include 1～2 part of chlorendic acid, 3～4 parts of gold potassium chloride, 2～3 parts of NPE, 1～2 part of polyvinylpyrrolidone and water 100～150 parts, second soak when temperature be 60～80 DEG C, pull out after soaking twice and dry；
(3), dye, respectively cotton yarn and imitative cotton terylene are carried out with dyeing process, in dyeing face when described dyeing is processed Material also middle addition uvioresistant finishing agent；
(4) setting, is dried, freezes at temperature is -1～-10 DEG C, then carry out drying and processing, temperature during drying is 50 ～60 DEG C；
(7), weave, cut open cloth, plaiting and test pin；
(8), it is combined, be combined by the adhesive cloth good with cropping using sponge and base fabric；
(9), gas steams, the cloth being combined enters promoting the circulation of qi steaming, and the time that gas steams is 2～3 hours；
(10), cleaning-drying.
Uvioresistant finishing agent includes 3～5 parts of nano zine oxide, 1～2 part of nano titanium oxide, adhesive 1 by weight ～2 parts and 0.5～1 part of sulfamic acid.
Binding agent includes 100 parts of starch, 6 parts of borax, 0.5 part of sodium thiosulfate and 100 parts of water by weight.
Cleaning-drying is to be impregnated using the waterproofing agent of 26～30g/L, then dries setting.
It should be understood by those skilled in the art that, the present invention is not restricted to the described embodiments, above-described embodiment and explanation Merely illustrating the principles of the invention described in book, without departing from the spirit and scope of the present invention, the present invention also has Various changes and modifications, these changes and improvements both fall within scope of the claimed invention.Claimed scope By appending claims and its equivalent thereof.

Claims (4)

1. a kind of woven composite material of clothes production technology it is characterised in that：Comprise the following steps,
(1), get the raw materials ready, select cotton yarn, imitative cotton terylene as raw material, cotton yarn, the ratio of Wool-Like terylene weight are 10:1～10；
(2), pre-process, carry out respectively soaking for the first time in soak by cotton yarn and imitative cotton terylene, soak time is 5～6 Hour, 3～5 parts of soak perfluorocarboxylic acid when soaking for the first time, 1～3 part of oxalic acid urea, 1～2 part of triethanolamine, sodium metasilicate 1 ～3 parts and 100～200 parts of water；Then pull out and carry out second immersion, described soak when soaking for second is by weight Including 1～2 part of chlorendic acid, 3～4 parts of gold potassium chloride, 2～3 parts of NPE, 1～2 part of polyvinylpyrrolidone and 100～150 parts of water, second soak when temperature be 60～80 DEG C, pull out after soaking twice and dry；
(3), dye, respectively cotton yarn and imitative cotton terylene are carried out with dyeing process, in dyeing pigment when described dyeing is processed Middle addition uvioresistant finishing agent；
(4) setting, is dried, freezes at temperature is -1～-10 DEG C, then carry out drying and processing, temperature during drying is 50～60 ℃；
(7), weave, cut open cloth, plaiting and test pin；
(8), it is combined, be combined by the adhesive cloth good with cropping using sponge and base fabric；
(9), gas steams, the cloth being combined enters promoting the circulation of qi steaming, and the time that gas steams is 2～3 hours；
(10), cleaning-drying.
2. a kind of woven composite material of clothes according to claim 1 production technology it is characterised in that：Described anti-purple Outside line finishing agent includes 3～5 parts of nano zine oxide, 1～2 part of nano titanium oxide, 1～2 part of adhesive and amino by weight 0.5～1 part of sulfonic acid.
3. a kind of woven composite material of clothes according to claim 1 production technology it is characterised in that：Described bonding Agent includes 100 parts of starch, 6 parts of borax, 0.5 part of sodium thiosulfate and 100 parts of water by weight.
4. the woven composite material of a kind of clothes according to claim 1 production technology it is characterised in that：Described is clear Washing drying is to be impregnated using the waterproofing agent of 26～30g/L, then dries setting.
CN201610789991.5A 2016-08-30 2016-08-30 Production process of woven garment composite fabric Pending CN106400480A (en)