CN105525427A - Preparation technology of stroller seat fabric - Google Patents
Preparation technology of stroller seat fabric Download PDFInfo
- Publication number
- CN105525427A CN105525427A CN201510859784.8A CN201510859784A CN105525427A CN 105525427 A CN105525427 A CN 105525427A CN 201510859784 A CN201510859784 A CN 201510859784A CN 105525427 A CN105525427 A CN 105525427A
- Authority
- CN
- China
- Prior art keywords
- parts
- soak
- preparation technology
- time
- stroller seat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a preparation technology of a stroller seat fabric, and relates to the technical field of seat fabrics. The preparation technology comprises the following steps of material preparation; pretreatment including the steps of respectively soaking white yarns and terry yarns in a soak solution, which comprises 3-4 parts of polyvinyl alcohol, 5-6 parts of polyacrylic acid, 1-3 parts of alkyl benzene sulfonic acid and 100-200 parts of water, for the first time for 5-6 hours, then pulling out the white yarns and terry yarns for secondary soak in another soak solution, which comprises, by weight, 1-2 parts of chlorendic acid, 3-4 parts of gold potassium chloride, 5-6 parts of tetrachlorophthalic anhydride, and 100-150 parts of water, in the temperature of 60-80 DEG C, and then pulling out and drying the white yarns and terry yarns after being soaked for two times; dyeing; weaving, fabric cutting, plaiting, needle detection and cropping; and composition. The stroller seat fabric has good flame-retardant effect, good environmental protection property, good elasticity, good hand feeling and strong toughness, and is not easy to bend.
Description
Technical field:
The present invention relates to seat-cover fabric technical field, particularly relate to a kind of preparation technology of stroller seat fabric.
Background technology:
It is main that children's seat fabric is generally textiles, in recent years, seat-cover fabric knitted fabric is low with its cost, be easy to the features such as die forming, lint set fastness is good, lightweight, computer jacquard potentiality are large, then children's seat fabric is higher for performance requirement, existing children's seat fabric all uses common weaving face fabric, flame retardant effect is poor, easily harmful substance is produced under high temperature or burning, more existing weaving face fabrics are poor in pliability, hardness is high, and toughness is low, poor flexibility, feel is poor, and bending is easily out of shape and is not easy to recover.
Summary of the invention:
It is good that technical problem to be solved by this invention is to provide a kind of feature of environmental protection, good springiness, good hand touch, and toughness is strong, and the preparation technology of yielding stroller seat fabric is not allowed in bending.
For solving the problems of the technologies described above, the present invention adopts following technical scheme:
A preparation technology for stroller seat fabric, is characterized in that: comprise the following steps,
(1), get the raw materials ready, select white yarn, terry yarn as raw material, the ratio of white yarn and terry yarn weight is 10:1 ~ 5;
(2), preliminary treatment, white yarn and terry yarn carried out respectively in soak first time and soak, soak time is 5 ~ 6 hours, soak polyvinyl alcohol 3 ~ 4 parts, polyacrylic acid 5 ~ 6 parts, alkyl benzene sulphonate 1 ~ 3 part and 100 ~ 200 parts, water when first time soaks; Then pull out and carry out second time immersion, soak when described second time is soaked comprises chlorendic acid 1 ~ 2 part, gold potassium chloride 3 ~ 4 parts, tetrachlorophthalic anhydride 5 ~ 6 parts and 100 ~ 150 parts, water by weight, temperature when second time is soaked is 60 ~ 80 DEG C, pulls out and dry after twice immersion;
(3), dyeing, dialogue yarn and terry yarn carry out dyeing and process respectively, during described dyeing process dyeing pigment also in add uvioresistant finishing agent;
(4), weave, cut open cloth, plaiting, test pin and cropping;
(5), compound, use sponge and base fabric to carry out compound by adhesive and the good cloth of cropping;
1, the preparation technology of a kind of stroller seat fabric according to claim 1, it is characterized in that: described uvioresistant finishing agent comprises nano zine oxide 3 ~ 5 parts, nano titanium oxide 1 ~ 2 part by weight, 1 ~ 2 part, adhesive and polyvinylpyrrolidone 0.5 ~ 1 part.
Cloth after described cropping needs to soak in hot water, and soak time is 1 ~ 2 hour.
Described binding agent comprises starch 100 parts by weight, borax 6 parts, 0.5 part, sodium thiosulfate and 100 parts, water.
Described carries out WATER REPELLENT TREATMENT to the cloth after compound, and the waterproofing agent being specially use 26 ~ 30g/L floods, and then dries setting.
In the present invention preliminary treatment first time soak employ polyvinyl alcohol 3 ~ 4 parts, polyacrylic acid 5 ~ 6 parts, alkyl benzene sulphonate 1 ~ 3 part have increases textiles elasticity and toughness, thus make seat-cover fabric good hand touch, bending is not easy distortion.
Soak the fire retardant of the number of chemical combinations of substances use employing good flame retardation effect in preliminary treatment first time in the present invention, chlorendic acid 1 ~ 2 part, gold potassium chloride 3 ~ 4 parts, tetrachlorophthalic anhydride 5 ~ 6 parts have better flame retardant effect, at high temperature or the lower harmful substance produced of burning less.
The invention has the beneficial effects as follows: good flame retardation effect of the present invention, the feature of environmental protection is good, good springiness, good hand touch, and toughness is strong, and bending is not easy.
Detailed description of the invention:
The present invention is further illustrated below by embodiment.
A preparation technology for stroller seat fabric, is characterized in that: comprise the following steps,
(1), get the raw materials ready, select white yarn, terry yarn as raw material, the ratio of white yarn and terry yarn weight is 10:1 ~ 5;
(2), preliminary treatment, white yarn and terry yarn carried out respectively in soak first time and soak, soak time is 5 ~ 6 hours, soak polyvinyl alcohol 3 ~ 4 parts, polyacrylic acid 5 ~ 6 parts, alkyl benzene sulphonate 1 ~ 3 part and 100 ~ 200 parts, water when first time soaks; Then pull out and carry out second time immersion, soak when second time is soaked comprises chlorendic acid 1 ~ 2 part, gold potassium chloride 3 ~ 4 parts, tetrachlorophthalic anhydride 5 ~ 6 parts and 100 ~ 150 parts, water by weight, temperature when second time is soaked is 60 ~ 80 DEG C, pulls out and dry after twice immersion;
(3), dyeing, dialogue yarn and terry yarn carry out dyeing and process respectively, during described dyeing process dyeing pigment also in add uvioresistant finishing agent;
(4), weave, cut open cloth, plaiting, test pin and cropping;
(5), compound, use sponge and base fabric to carry out compound by adhesive and the good cloth of cropping;
Uvioresistant finishing agent comprises nano zine oxide 3 ~ 5 parts, nano titanium oxide 1 ~ 2 part by weight, 1 ~ 2 part, adhesive and polyvinylpyrrolidone 0.5 ~ 1 part.
Cloth after cropping needs to soak in hot water, and soak time is 1 ~ 2 hour.
Binding agent comprises starch 100 parts by weight, borax 6 parts, 0.5 part, sodium thiosulfate and 100 parts, water.
Carry out WATER REPELLENT TREATMENT to the cloth after compound, the waterproofing agent being specially use 26 ~ 30g/L floods, and then dries setting.
The technical staff of the industry should understand; the present invention is not restricted to the described embodiments; what describe in above-described embodiment and description just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.Application claims protection domain is defined by appending claims and equivalent thereof.
Claims (5)
1. a preparation technology for stroller seat fabric, is characterized in that: comprise the following steps,
(1), get the raw materials ready, select white yarn, terry yarn as raw material, the ratio of white yarn and terry yarn weight is 10:1 ~ 5;
(2), preliminary treatment, white yarn and terry yarn carried out respectively in soak first time and soak, soak time is 5 ~ 6 hours, soak polyvinyl alcohol 3 ~ 4 parts, polyacrylic acid 5 ~ 6 parts, alkyl benzene sulphonate 1 ~ 3 part and 100 ~ 200 parts, water when first time soaks; Then pull out and carry out second time immersion, soak when described second time is soaked comprises chlorendic acid 1 ~ 2 part, gold potassium chloride 3 ~ 4 parts, tetrachlorophthalic anhydride 5 ~ 6 parts and 100 ~ 150 parts, water by weight, temperature when second time is soaked is 60 ~ 80 DEG C, pulls out and dry after twice immersion;
(3), dyeing, dialogue yarn and terry yarn carry out dyeing and process respectively, during described dyeing process dyeing pigment also in add uvioresistant finishing agent;
(4), weave, cut open cloth, plaiting, test pin and cropping;
(5), compound, use sponge and base fabric to carry out compound by adhesive and the good cloth of cropping.
2. the preparation technology of a kind of stroller seat fabric according to claim 1, it is characterized in that: described uvioresistant finishing agent comprises nano zine oxide 3 ~ 5 parts, nano titanium oxide 1 ~ 2 part by weight, 1 ~ 2 part, adhesive and polyvinylpyrrolidone 0.5 ~ 1 part.
3. the preparation technology of a kind of stroller seat fabric according to claim 1, is characterized in that: the cloth needs after described cropping soak in hot water, and soak time is 1 ~ 2 hour.
4. the preparation technology of a kind of stroller seat fabric according to claim 1, is characterized in that: described binding agent comprises starch 100 parts by weight, borax 6 parts, 0.5 part, sodium thiosulfate and 100 parts, water.
5. the preparation technology of a kind of stroller seat fabric according to claim 1, is characterized in that: described carries out WATER REPELLENT TREATMENT to the cloth after compound, and the waterproofing agent being specially use 26 ~ 30g/L floods, and then dries setting.