CN104527204A - Processing technology for waterproof fabric - Google Patents
Processing technology for waterproof fabric Download PDFInfo
- Publication number
- CN104527204A CN104527204A CN201410807310.4A CN201410807310A CN104527204A CN 104527204 A CN104527204 A CN 104527204A CN 201410807310 A CN201410807310 A CN 201410807310A CN 104527204 A CN104527204 A CN 104527204A
- Authority
- CN
- China
- Prior art keywords
- fabric
- processing technology
- proofing property
- water proofing
- catalyst
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a processing technology for a waterproof fabric. The processing technology comprises the following steps of (1) pretreating a fabric, namely whitening the fabric, and drying; (2) preparing a coating material from the following components in percentage by weight: 60-70% of polyurethane, 5-10% of a migration inhibitor, 3-5% of an anionic penetrant, 1-3% of a catalyst and the balance of water; (3) dipping the whitened and dried fabric into the coating material prepared in the step (2); and (4) drying the dipped fabric, and then, baking. A certain quantity of polyurethane and the anionic penetrant are added into the coating material and are matched with the migration inhibitor to generate chemical reaction; due to the adoption of the migration inhibitor, the softness of the fabric can be effectively improved; and due to the adoption of the anionic penetrant, the surface activity of the coating material can be improved, so that the waterproofness of the coating can be favorably improved.
Description
Technical field
The present invention relates to a kind of processing technology of water proofing property fabric, belong to technical field of textile production.
Background technology
Along with the development of science and technology, people are more and more higher for the functional requirement of garment material.Existing fabric does not have the function of waterproof usually, causes those staff often contacted with water usually to get wet in the course of the work oneself clothing, not only can affect normal work, and can bring various inconvenience to staff self.
Summary of the invention
Technical problem solved by the invention is to provide a kind of processing technology of water proofing property fabric, and the fabric processed can be made to have the function of waterproof, and the staff that the clothes made are applicable to contact with water for a long time wears, and effectively can play the function of waterproof.
To achieve the above object, the technical solution adopted in the present invention is as follows:
A processing technology for water proofing property fabric, is characterized in that: comprise the steps:
(1) fabric pre-treatment: by white for fabric refining, dry;
(2) coating material preparation: comprise following component according to percentage by weight: the polyurethane of 60%-70%, the anion-permeable membrane agent of migration inhibitor 5%-10%, 3%-5%, the catalyst of 1%-3%, all the other are water;
(3) white for refining fabric of drying is put into the coating material dipping that step (2) is prepared;
(4) fabric after dipping is dried, baked and banked up with earth.
The processing technology of aforesaid a kind of water proofing property fabric, is characterized in that: the dip time in described step (3) is 2.5 hours-3 hours, and dipping temperature controls between 35 DEG C-40 DEG C.
The processing technology of aforesaid a kind of water proofing property fabric, is characterized in that: the temperature that in described step (4), fabric is dried is 80 DEG C-90 DEG C, and the time is 0.2 hour-0.4 hour; The temperature of baking and banking up with earth is 200 DEG C-220 DEG C, and the time is 1.6 hours-2.0 hours.
The processing technology of aforesaid a kind of water proofing property fabric, is characterized in that: described anion-permeable membrane agent is the one in coconut oil, monoethanolamine, sodium sulphate.
The processing technology of aforesaid a kind of water proofing property fabric, is characterized in that: described polyurethane is 65%, migration inhibitor is 8%, coconut oil is 3.5%, and catalyst is 1.2%.
The processing technology of aforesaid a kind of water proofing property fabric, is characterized in that: described polyurethane is 68%, migration inhibitor is 7%, monoethanolamine is 4%, and catalyst is 1.4%.
The processing technology of aforesaid a kind of water proofing property fabric, is characterized in that: described catalyst is liquid catalyst.
The invention has the beneficial effects as follows: by adding a certain amount of polyurethane and anion-permeable membrane agent cooperation migration inhibitor generation chemical reaction in coating material, utilize migration inhibitor effectively can improve the pliability of fabric, utilize anion-permeable membrane agent to improve the surface-active of coating material, thus contribute to the water proofing property improving coating.
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention is further illustrated.
The invention provides a kind of processing technology of water proofing property fabric, comprise the steps:
(1) fabric pre-treatment: by white for fabric refining, dry;
(2) coating material preparation: comprise following component according to percentage by weight: the polyurethane of 60%-70%, the anion-permeable membrane agent of migration inhibitor 5%-10%, 3%-5%, the catalyst of 1%-3%, all the other are water;
(3) white for refining fabric of drying is put into the coating material dipping that step (2) is prepared;
(4) fabric after dipping is dried, baked and banked up with earth.
Wherein, the dip time in step (3) is 2.5 hours-3 hours, and dipping temperature controls between 35 DEG C-40 DEG C, and the temperature that in step (4), fabric is dried is 80 DEG C-90 DEG C, and the time is 0.2 hour-0.4 hour; The temperature of baking and banking up with earth is 200 DEG C-220 DEG C, and the time is 1.6 hours-2.0 hours.
Described anion-permeable membrane agent is the one in coconut oil, monoethanolamine, sodium sulphate, and described catalyst is liquid catalyst.
By adding a certain amount of polyurethane and anion-permeable membrane agent cooperation migration inhibitor generation chemical reaction in coating material, utilize migration inhibitor effectively can improve the pliability of fabric, utilize anion-permeable membrane agent to improve the surface-active of coating material, thus contribute to the water proofing property improving coating.
Embodiment 1
A processing technology for water proofing property fabric, comprises the steps:
(1) fabric pre-treatment: by white for fabric refining, dry;
(2) coating material preparation: comprise following component according to percentage by weight: the polyurethane of 65%, migration inhibitor 8%, the coconut oil of 3.5%, the catalyst of 1.2%, all the other are water;
(3) white for refining fabric of drying is put into fire retardant dipping 2.5 hours, dipping temperature is 37 DEG C;
(4) fabric after dipping is dried, baked and banked up with earth, the temperature of wherein drying is 85 DEG C, and the time is 0.3 hour; The temperature of baking and banking up with earth is 210 DEG C, and the time is 1.8 hours.
Embodiment 2
A processing technology for water proofing property fabric, comprises the steps:
(1) fabric pre-treatment: by white for fabric refining, dry;
(2) coating material preparation: comprise following component according to percentage by weight: the polyurethane of 68%, migration inhibitor 7%, the monoethanolamine of 4%, the catalyst of 1.4%, all the other are water;
(3) white for refining fabric of drying is put into fire retardant dipping 2.8 hours, dipping temperature is 35 DEG C;
(4) fabric after dipping is dried, baked and banked up with earth, the temperature of wherein drying is 86 DEG C, and the time is 0.25 hour; The temperature of baking and banking up with earth is 220 DEG C, and the time is 2.0 hours.
More than show and describe general principle of the present invention and principal character and advantage of the present invention.The technical staff of the industry should understand; the present invention is not restricted to the described embodiments; what describe in above-described embodiment and description just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.Application claims protection domain is defined by appending claims and equivalent thereof.
Claims (7)
1. a processing technology for water proofing property fabric, is characterized in that: comprise the steps:
(1) fabric pre-treatment: by white for fabric refining, dry;
(2) coating material preparation: comprise following component according to percentage by weight: the polyurethane of 60%-70%, the anion-permeable membrane agent of migration inhibitor 5%-10%, 3%-5%, the catalyst of 1%-3%, all the other are water;
(3) white for refining fabric of drying is put into the coating material dipping that step (2) is prepared;
(4) fabric after dipping is dried, baked and banked up with earth.
2. the processing technology of a kind of water proofing property fabric according to claim 1, is characterized in that: the dip time in described step (3) is 2.5 hours-3 hours, and dipping temperature controls between 35 DEG C-40 DEG C.
3. the processing technology of a kind of water proofing property fabric according to claim 2, is characterized in that: the temperature that in described step (4), fabric is dried is 80 DEG C-90 DEG C, and the time is 0.2 hour-0.4 hour; The temperature of baking and banking up with earth is 200 DEG C-220 DEG C, and the time is 1.6 hours-2.0 hours.
4. the processing technology of a kind of water proofing property fabric according to claim 3, is characterized in that: described anion-permeable membrane agent is the one in coconut oil, monoethanolamine, sodium sulphate.
5. the processing technology of a kind of water proofing property fabric according to claim 4, is characterized in that: described polyurethane is 65%, migration inhibitor is 8%, coconut oil is 3.5%, and catalyst is 1.2%.
6. the processing technology of a kind of water proofing property fabric according to claim 4, is characterized in that: described polyurethane is 68%, migration inhibitor is 7%, monoethanolamine is 4%, and catalyst is 1.4%.
7. according to the processing technology of a kind of water proofing property fabric described in claim 5 or 6, it is characterized in that: described catalyst is liquid catalyst.