CN106637632A - 150DQGB base cloth for automobile interior surface - Google Patents
150DQGB base cloth for automobile interior surface Download PDFInfo
- Publication number
- CN106637632A CN106637632A CN201610975496.3A CN201610975496A CN106637632A CN 106637632 A CN106637632 A CN 106637632A CN 201610975496 A CN201610975496 A CN 201610975496A CN 106637632 A CN106637632 A CN 106637632A
- Authority
- CN
- China
- Prior art keywords
- 150dqgb
- temperature
- dye vat
- pins
- speed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of automobile lining technologies, in particular to a 150DQGB base cloth for an automobile interior surface. The 150DQGB jacquard cloth is made through the following processes of 1 gray cloth weaving, 2 water washing pretreatment in a dye vat and 3 sizing aftertreatment. The 150DQGB base cloth has the advantages that by changing the needle arranging and sizing after finishing processes in a traditional knitting technology, the surface base cloth not only can meet the tension, tearing and static load tensile strength requirements, but also can decrease the gram weight and the thickness, and the using cost is reduced.
Description
Technical field
The present invention relates to inner lining of automobile technology field, is particularly used for the 150DQGB bases of automotive trim epidermis
Cloth.
Background technology
Automotive trim (Automotive Interior) is primarily referred to as the used automobile product of automotive interior repacking, relates to
And to the every aspect of automotive interior, such as automobile steering wheel cover, automobile cushion, automatic foot-mat, automobile perfume, automobile pendant,
Internal goods of furniture for display rather than for use, containing box etc. are all automotive trim products.Automotive trim described in our country, in fact in English
Interiors System.Because this partial automobile parts has certain dicoration, so common at present in the industry turn over
Translate and be all called " automotive trim ".But from English " Interiors ", we it is known that, this parts thereof not only only has
Decoration function, the feature, security and engineering attribute involved by them is very abundant.Wherein automotive trim table
Dermatome must have specific pulling force, tear and static load tensile strength according to different automobile types, and other specific physical property are required,
In Japanese auto project interior trim epidermis, need to such as reach physical property requirement and quality is qualified, the base fabric for using must will reach corresponding
Physical property standard specification, traditional handicraft appears in when meeting pulling force, tear and the physical property such as static load tensile strength and requiring, exists
Grammes per square metre lays particular stress on, thickness is bigger than normal, the higher situation of corresponding production cost.
Based on above reason, the new base fabric for automotive trim epidermis is needed to be devised, by changing to raw material
Enter, weaving process, the lifting of postfinishing process, develop meet Japanese auto project interior trim epidermis base fabric pulling force, tear and
While static load tensile strength, have in grammes per square metre and thickness and be significantly improved, reduce the cost of client, i.e., for automobile
The 150DQGB base fabrics of interior trim epidermis.
The content of the invention
In order to solve the technical problem that above-mentioned existing facecloth technique is present, the present invention is provided to automotive trim epidermis
150DQGB base fabrics.
The technical solution adopted for the present invention to solve the technical problems is：
For the 150DQGB base fabrics of automotive trim epidermis, including following technique：
The first step：Fabric is weaved.
Raw material：150D/48F DTY low stretch yarns；
Weaving board size：30 inches of diameter；
Knitting needle：Pin number is 24 pins/inch, and total needle amount is 2256 pieces；
Yarn is long：First, a length of 19cm/50 pins of four road yarns；
Second, three, five, six 11cm/50 pins；
Row's pin technique：
The mode of row's pin is A, B, B ﹑ A, by that analogy.
Second step：Pre-treatment dye vat is washed；
1) fabric enters dye vat；
2) dye vat temperature is set as 120 DEG C, and the speed that heats up is 2 DEG C/min, and temperature retention time is 30 minutes, and temperature retention time is arrived, and is opened
Begin to lower the temperature, cooling speed is 3 DEG C/min, and to normal temperature cylinder is gone out；
3) cleaning machine is cleaned 2 times；
4) processed is carried out with dewaterer；
3rd step：Post processing sizing；
1) punishment in advance is processed, and per 400kg water, plus 40kg fire retardants (10%) rear punishment in advance is blent.
2) heat treatment, Uneven Width width is set as 148cm during sizing, and oven temperature is 160 DEG C of first segment, second section 180
DEG C, remaining is 200 DEG C, and rotation speed of fan is 1000 revs/min, and speed is 18Y/ minutes, overfeeding -5 of shaping, thickness of shaping
0.86-0.91mm。
3) finished product clot is processed.
The invention has the beneficial effects as follows：The present invention is to arrange pin and Final finishing setting process by changing traditional knitting,
Make epidermis base fabric to meet pulling force, tear and static load tensile strength to require, reduction grammes per square metre and thickness can be reached again.Reduce
Use cost.
Description of the drawings
With reference to the accompanying drawings and examples the present invention is further described.
Fig. 1 is the knitting flow chart making of facecloth in the present invention；
Fig. 2 is pre-treatment dye vat washing process schematic diagram of the present invention；
Fig. 3 is present invention post processing sizing schematic flow sheet.
Specific embodiment
In order that the objects, technical solutions and advantages of the present invention become more apparent, it is right below in conjunction with drawings and Examples
The present invention is further elaborated.It should be appreciated that specific embodiment described herein is only to explain the present invention, and
It is not used in the restriction present invention.
As shown in Figure 1-Figure 3, the 150DQGB base fabrics for automotive trim epidermis of the present invention, including following technique：
The first step：Fabric is weaved.
Raw material：150D/48F DTY low stretch yarns；
Weaving board size：30 inches of diameter；
Knitting needle：Pin number is 24 pins/inch, and total needle amount is 2256 pieces；
Yarn is long：First, a length of 19cm/50 pins of four road yarns；
Second, three, five, six 11cm/50 pins；
Row's pin technique：
The mode of row's pin is A, B, B ﹑ A, by that analogy.
Second step：Pre-treatment dye vat is washed；
1) fabric enters dye vat；
2) dye vat temperature is set as 120 DEG C, and the speed that heats up is 2 DEG C/min, and temperature retention time is 30 minutes, and temperature retention time is arrived, and is opened
Begin to lower the temperature, cooling speed is 3 DEG C/min, and to normal temperature cylinder is gone out；
3) cleaning machine is cleaned 2 times；
4) processed is carried out with dewaterer；
3rd step：Post processing sizing；
1) punishment in advance is processed, and per 400kg water, plus 40kg fire retardants (10%) rear punishment in advance is blent.
2) heat treatment, Uneven Width width is set as 148cm during sizing, and oven temperature is 160 DEG C of first segment, second section 180
DEG C, remaining is 200 DEG C, and rotation speed of fan is 1000 revs/min, and speed is 18Y/ minutes, overfeeding -5 of shaping, thickness of shaping
0.86-0.91mm。
3) finished product clot is processed.
General principle, principal character and the advantages of the present invention of the present invention has been shown and described above.The technology of the industry
Personnel it should be appreciated that the present invention is not restricted to the described embodiments, the simply explanation described in above-described embodiment and specification this
The principle of invention, without departing from the spirit and scope of the present invention, the present invention also has various changes and modifications, these changes
Change and improvement is both fallen within scope of the claimed invention.The claimed scope of the invention by appending claims and its
Equivalent thereof.
Claims (1)
1. the 150DQGB base fabrics of automotive trim epidermis are used for, it is characterised in that including following technique：
The first step：Fabric is weaved.
Raw material：150D/48F DTY low stretch yarns；
Weaving board size：30 inches of diameter；
Knitting needle：Pin number is 24 pins/inch, and total needle amount is 2256 pieces；
Yarn is long：First, a length of 19cm/50 pins of four road yarns；
Second, three, five, six 11cm/50 pins；
Row's pin technique：
The mode of row's pin is A, B, B ﹑ A, by that analogy.
Second step：Pre-treatment dye vat is washed；
1) fabric enters dye vat；
2) dye vat temperature is set as 120 DEG C, and the speed that heats up is 2 DEG C/min, and temperature retention time is 30 minutes, and temperature retention time is arrived, and starts drop
Temperature, cooling speed is 3 DEG C/min, and to normal temperature cylinder is gone out；
3) cleaning machine is cleaned 2 times；
4) processed is carried out with dewaterer；
3rd step：Post processing sizing；
1) punishment in advance is processed, and per 400kg water, plus 40kg fire retardants (10%) rear punishment in advance is blent.
2) heat treatment, Uneven Width width is set as 148cm during sizing, and oven temperature is 160 DEG C of first segment, 180 DEG C of second section, its
Remaining to be 200 DEG C, rotation speed of fan is 1000 revs/min, and speed is 18Y/ minutes, overfeeding -5 of shaping, and shape thickness 0.86-
0.91mm。
3) finished product clot is processed.