CN107326673A - A kind of garment material environmentally friendly crease-shedding finishing agent and preparation method thereof - Google Patents
A kind of garment material environmentally friendly crease-shedding finishing agent and preparation method thereof Download PDFInfo
- Publication number
- CN107326673A CN107326673A CN201710635767.5A CN201710635767A CN107326673A CN 107326673 A CN107326673 A CN 107326673A CN 201710635767 A CN201710635767 A CN 201710635767A CN 107326673 A CN107326673 A CN 107326673A
- Authority
- CN
- China
- Prior art keywords
- parts
- finishing agent
- crease
- agent
- garment material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of garment material environmentally friendly crease-shedding finishing agent and preparation method thereof, the finishing agent includes the composition of following parts by weight：Butyl acrylate, Trimethyl phosphite, styrene, APEO：10 ~ 20 parts, microcrystalline cellulose, sodium carboxymethylcellulose, dimethyl phosphate, dimethicone, N methyl pyrrolidones, citric acid, nano zine oxide, thickener, surfactant, emulsifying agent, bacteriostatic agent, deionized water.The finishing agent low-yellowing, the original whiteness of fabric and coloured light are not influenceed, high temperature resistant, the moment dissolving in high temperature, fabric sofetening, fluffy, smooth feel can be assigned, whiteness, coloured light and color fastness are had no adverse effects, with good immediate water-solubility, flexible smooth, low spumescence, the soft finish of various fabrics, can assign plentiful, smooth, the soft feel of fabric and good water imbibition, assign fabric excellent antistatic property and anti pilling, wrinkle resistance, production cost is low, good in economic efficiency.
Description
Technical field
The invention belongs to garment material auxiliary agent technical field, and in particular to a kind of garment material with environmentally friendly crease-shedding finishing agent and
Its preparation method.
Background technology
Fabric is exactly the material for making clothes.As one of clothes three elements, fabric can not only annotate clothes
Style and characteristic, and directly left and right the color of clothes, the expression effect of moulding.
Clothes are made with fabric, and fabric is exactly the material for making clothes.It is used as one of clothes three elements, fabric
Can not only annotate the style and characteristic of clothes, and directly left and right the color of clothes, the expression effect of moulding.Presentation is come from
The noble quality of body is perfect, soft.
Modern times are produced on the clothes of formal social life institute wear, many blended yarn weaved fabrics from high-quality.And it is pure cotton, pure
The natural fabric such as hair, pure silk, pure fiber crops has become general cloth because there is the easily natural fabric such as wrinkle, yielding, compared with
It is few to be used as high-grade clothing materials.Blended yarn weaved fabric has natural fabric sweat-absorbing breathable, it is soft comfortable the characteristics of, chemical fibre face is absorbed again
Material is solid to wear well, overhangs the advantages of well-pressed, good luster color is vivid, has substantial amounts of high-grade high-quality blended yarn weaved fabric to be developed every year
Come.Sometimes, the clothes of the pure leatherwork of wear, are also allowed.
For the anti-crease finishing of garment material, the current country is primarily present following patent document：
Publication No. 106749956A Chinese patent discloses a kind of after-finishing of textile products very bullet finishing agent and its preparation side
Method, application method.Wherein described very to play finishing agent, its preparing raw material includes acrylate monomer 9% ~ 11%, vinyl monomer 15%
~ 20%, cationic monomer 0.1% ~ 1%, crosslinking agent 1% ~ 2%, cationic emulsifier 0.1% ~ 0.3%, acid auxiliary liquid 0.05% ~ 1%,
Polyethers monomer 0.1% ~ 1%, nonionic emulsifier 0.2% ~ 0.6%, water soluble starter 0.05% ~ 0.1% and deionized water 60%
~ 70%, wherein being weight percentage above is referred to the percentage of raw material components.A kind of after-finishing of textile products of the present invention is used
Finishing agent is very played, it can assign the good water resistance of fabric, well-pressed degree and splendid elasticity.However, the patent provided it is whole
Agent is managed, is not obviously improved for the wrinkle resistance of garment material.
The content of the invention
To solve above-mentioned problem, it is an object of the invention to provide a kind of garment material environmental protection crease-shedding finishing agent
And preparation method thereof, the finishing agent low-yellowing does not influence the original whiteness of fabric and coloured light, high temperature resistant, the moment in high temperature
Dissolving, can assign fabric sofetening, fluffy, smooth feel, whiteness, coloured light and color fastness are had no adverse effects, with good fast
Fast water-soluble, flexible smooth, low spumescence, the soft finish of various fabrics can assign that fabric is plentiful, smooth, softness
Feel and good water imbibition, assign fabric excellent antistatic property and anti pilling, wrinkle resistance, preparation technology letter
Single, production cost is low, good in economic efficiency.
To reach above-mentioned purpose, the technical scheme is that：
A kind of garment material includes the composition of following parts by weight with environmentally friendly crease-shedding finishing agent, the finishing agent：Butyl acrylate：20
~ 30 parts, Trimethyl phosphite：15 ~ 25 parts, styrene：10 ~ 15 parts, APEO：10 ~ 20 parts, microcrystalline cellulose：1~5
Part, sodium carboxymethylcellulose：5 ~ 10 parts, dimethyl phosphate：10 ~ 15 parts, dimethicone：5 ~ 10 parts, 1-METHYLPYRROLIDONE：
1 ~ 5 part, citric acid：1 ~ 5 part, nano zine oxide：1 ~ 3 part, thickener：1 ~ 5 part, surfactant：1 ~ 5 part, emulsifying agent：1~5
Part, bacteriostatic agent：1 ~ 5 part, deionized water：60 ~ 80 parts.
Further, the finishing agent includes the composition of following parts by weight：Butyl acrylate：25 ~ 30 parts, phosphorous acid front three
Ester：15 ~ 20 parts, styrene：10 ~ 13 parts, APEO：10 ~ 15 parts, microcrystalline cellulose：1 ~ 3 part, sodium carboxymethylcellulose：
5 ~ 7 parts, dimethyl phosphate：10 ~ 13 parts, dimethicone：7 ~ 10 parts, 1-METHYLPYRROLIDONE：1 ~ 3 part, citric acid：2 ~ 5 parts,
Nano zine oxide：2 ~ 3 parts, thickener：3 ~ 5 parts, surfactant：1 ~ 4 part, emulsifying agent：2 ~ 5 parts, deionized water：70 ~ 80 parts.
Preferably, the finishing agent includes the composition of following parts by weight：Butyl acrylate：25 parts, Trimethyl phosphite：20
Part, styrene：13 parts, APEO：15 parts, microcrystalline cellulose：2 parts, sodium carboxymethylcellulose：5 parts, dimethyl phosphate：
12 parts, dimethicone：8 parts, 1-METHYLPYRROLIDONE：2 parts, citric acid：4 parts, nano zine oxide：3 parts, thickener：4 parts,
Surfactant：3 parts, emulsifying agent：2 parts, deionized water：70 parts.
Preferably, the thickener elects aerosil as.
Preferably, the surfactant is AEO.
Preferably, the emulsifying agent is dihydroxy ethyl ammonio methacrylate or OTAC.
Preferably, the bacteriostatic agent is parachlorometaxylenol.
The preferred component of above additive, may be such that the finishing agent has a good immediate water-solubility, flexible smooth,
Low spumescence.
Meanwhile, the present invention also provides a kind of preparation method of the environmentally friendly crease-shedding finishing agent of garment material, the preparation method
Comprise the following steps：1) take stirred tank, add the butyl acrylate, Trimethyl phosphite, styrene, APEO, micro-
Crystalline cellulose, sodium carboxymethylcellulose, dimethyl phosphate, dimethicone, 1-METHYLPYRROLIDONE and 40 ~ 50% deionization
Water, is stirred 10 ~ 20 minutes, 30 ~ 40 DEG C of whipping temp under 600 ~ 800 revs/min of rotating speed；2) 60 ~ 80 DEG C are warming up to, lemon is added
Lemon acid, nano zine oxide, thickener, surfactant, emulsifying agent and remaining deionized water, under 800 ~ 900 revs/min of rotating speed
Stirring 15 ~ 20 minutes, stirring is cooled to room temperature after finishing, and produces the environmentally friendly crease-shedding finishing agent of the garment material.
The invention has the advantages that：
The finishing agent low-yellowing, the original whiteness of fabric and coloured light is not influenceed, high temperature resistant, the moment dissolving in high temperature can be assigned
Fabric sofetening, fluffy, smooth feel are given, whiteness, coloured light and color fastness are had no adverse effects, with good immediate water-solubility,
Flexible smooth, low spumescence, the soft finish of various fabrics can assign plentiful, smooth, the soft feel of fabric and good
Good water imbibition, assigns fabric excellent antistatic property and anti pilling, wrinkle resistance, and preparation technology is simple, production cost
It is low, it is good in economic efficiency.
Embodiment
Below by specific embodiment, the present invention is described further, but embodiment is not intended to limit the protection of the present invention
Scope.
A kind of garment material provided by the present invention includes following parts by weight with environmentally friendly crease-shedding finishing agent, the finishing agent
Composition：Butyl acrylate：20 ~ 30 parts, Trimethyl phosphite：15 ~ 25 parts, styrene：10 ~ 15 parts, APEO：10~20
Part, microcrystalline cellulose：1 ~ 5 part, sodium carboxymethylcellulose：5 ~ 10 parts, dimethyl phosphate：10 ~ 15 parts, dimethicone：5~10
Part, 1-METHYLPYRROLIDONE：1 ~ 5 part, citric acid：1 ~ 5 part, nano zine oxide：1 ~ 3 part, thickener：1 ~ 5 part, surface-active
Agent：1 ~ 5 part, emulsifying agent：1 ~ 5 part, bacteriostatic agent：1 ~ 5 part, deionized water：60 ~ 80 parts.
Further, the finishing agent includes the composition of following parts by weight：Butyl acrylate：25 ~ 30 parts, phosphorous acid front three
Ester：15 ~ 20 parts, styrene：10 ~ 13 parts, APEO：10 ~ 15 parts, microcrystalline cellulose：1 ~ 3 part, sodium carboxymethylcellulose：
5 ~ 7 parts, dimethyl phosphate：10 ~ 13 parts, dimethicone：7 ~ 10 parts, 1-METHYLPYRROLIDONE：1 ~ 3 part, citric acid：2 ~ 5 parts,
Nano zine oxide：2 ~ 3 parts, thickener：3 ~ 5 parts, surfactant：1 ~ 4 part, emulsifying agent：2 ~ 5 parts, deionized water：70 ~ 80 parts.
Preferably, the finishing agent includes the composition of following parts by weight：Butyl acrylate：25 parts, Trimethyl phosphite：20
Part, styrene：13 parts, APEO：15 parts, microcrystalline cellulose：2 parts, sodium carboxymethylcellulose：5 parts, dimethyl phosphate：
12 parts, dimethicone：8 parts, 1-METHYLPYRROLIDONE：2 parts, citric acid：4 parts, nano zine oxide：3 parts, thickener：4 parts,
Surfactant：3 parts, emulsifying agent：2 parts, deionized water：70 parts.
Preferably, the thickener elects aerosil as.
Preferably, the surfactant is AEO.
Preferably, the emulsifying agent is dihydroxy ethyl ammonio methacrylate or OTAC.
Preferably, the bacteriostatic agent is parachlorometaxylenol.
The preferred component of above additive, may be such that the finishing agent has a good immediate water-solubility, flexible smooth,
Low spumescence.
Meanwhile, the present invention also provides a kind of preparation method of the environmentally friendly crease-shedding finishing agent of garment material, the preparation method
Comprise the following steps：1) take stirred tank, add the butyl acrylate, Trimethyl phosphite, styrene, APEO, micro-
Crystalline cellulose, sodium carboxymethylcellulose, dimethyl phosphate, dimethicone, 1-METHYLPYRROLIDONE and 40 ~ 50% deionization
Water, is stirred 10 ~ 20 minutes, 30 ~ 40 DEG C of whipping temp under 600 ~ 800 revs/min of rotating speed；2) 60 ~ 80 DEG C are warming up to, lemon is added
Lemon acid, nano zine oxide, thickener, surfactant, emulsifying agent and remaining deionized water, under 800 ~ 900 revs/min of rotating speed
Stirring 15 ~ 20 minutes, stirring is cooled to room temperature after finishing, and produces the environmentally friendly crease-shedding finishing agent of the garment material.
A kind of garment material provided by the present invention does not influence fabric original white with environmentally friendly crease-shedding finishing agent, low-yellowing
Degree and coloured light, high temperature resistant, the moment dissolving in high temperature, can assign fabric sofetening, fluffy, smooth feel, to whiteness, coloured light and color
Fastness has no adverse effects, with good immediate water-solubility, flexible smooth, low spumescence, various fabrics it is soft whole
Reason, can assign plentiful, smooth, the soft feel of fabric and good water imbibition, assign the excellent antistatic property of fabric and
Anti pilling, wrinkle resistance, preparation technology are simple, and production cost is low, good in economic efficiency.
It should be noted that the above embodiments are merely illustrative of the technical solutions of the present invention and it is unrestricted.Although with reference to compared with
The present invention is described in detail good embodiment, it will be understood by those within the art that, can be to the technology of invention
Scheme is modified or equivalent substitution, and without departing from the scope of technical solution of the present invention, it all should cover the power in the present invention
In sharp claimed range.
Claims (8)
1. a kind of garment material environmental protection crease-shedding finishing agent, it is characterised in that the finishing agent includes the composition of following parts by weight：
Butyl acrylate：20 ~ 30 parts, Trimethyl phosphite：15 ~ 25 parts, styrene：10 ~ 15 parts, APEO：It is 10 ~ 20 parts, micro-
Crystalline cellulose：1 ~ 5 part, sodium carboxymethylcellulose：5 ~ 10 parts, dimethyl phosphate：10 ~ 15 parts, dimethicone：5 ~ 10 parts, N-
Methyl pyrrolidone：1 ~ 5 part, citric acid：1 ~ 5 part, nano zine oxide：1 ~ 3 part, thickener：1 ~ 5 part, surfactant：1~5
Part, emulsifying agent：1 ~ 5 part, bacteriostatic agent：1 ~ 5 part, deionized water：60 ~ 80 parts.
2. garment material according to claim 1 environmental protection crease-shedding finishing agent, it is characterised in that the finishing agent is included such as
The composition of lower parts by weight：Butyl acrylate：25 ~ 30 parts, Trimethyl phosphite：15 ~ 20 parts, styrene：10 ~ 13 parts, polyoxy second
Alkene ether：10 ~ 15 parts, microcrystalline cellulose：1 ~ 3 part, sodium carboxymethylcellulose：5 ~ 7 parts, dimethyl phosphate：10 ~ 13 parts, dimethyl
Silicone oil：7 ~ 10 parts, 1-METHYLPYRROLIDONE：1 ~ 3 part, citric acid：2 ~ 5 parts, nano zine oxide：2 ~ 3 parts, thickener：3 ~ 5 parts,
Surfactant：1 ~ 4 part, emulsifying agent：2 ~ 5 parts, deionized water：70 ~ 80 parts.
3. garment material according to claim 1 environmental protection crease-shedding finishing agent, it is characterised in that the finishing agent is included such as
The composition of lower parts by weight：Butyl acrylate：25 parts, Trimethyl phosphite：20 parts, styrene：13 parts, APEO：15 parts,
Microcrystalline cellulose：2 parts, sodium carboxymethylcellulose：5 parts, dimethyl phosphate：12 parts, dimethicone：8 parts, N- crassitudes
Ketone：2 parts, citric acid：4 parts, nano zine oxide：3 parts, thickener：4 parts, surfactant：3 parts, emulsifying agent：2 parts, deionization
Water：70 parts.
4. garment material according to claim 1 environmental protection crease-shedding finishing agent, it is characterised in that the thickener elects gas as
Aerosil.
5. garment material according to claim 1 is with environmentally friendly crease-shedding finishing agent, it is characterised in that the surfactant is
AEO.
6. garment material according to claim 1 environmental protection crease-shedding finishing agent, it is characterised in that the emulsifying agent is dihydroxy
Ethyl trimethyl ammonium chloride or OTAC.
7. garment material according to claim 1 environmental protection crease-shedding finishing agent, it is characterised in that the bacteriostatic agent is to chlorine
Meta-xylene phenol.
8. a kind of garment material as any one of claim 1 ~ 7 preparation method of environmentally friendly crease-shedding finishing agent, it is special
Levy and be, the preparation method comprises the following steps：1) stirred tank is taken, the butyl acrylate, Trimethyl phosphite, benzene is added
Ethene, APEO, microcrystalline cellulose, sodium carboxymethylcellulose, dimethyl phosphate, dimethicone, N- crassitudes
Ketone and 40 ~ 50% deionized water, are stirred 10 ~ 20 minutes, 30 ~ 40 DEG C of whipping temp under 600 ~ 800 revs/min of rotating speed；2) rise
Temperature adds citric acid, nano zine oxide, thickener, surfactant, emulsifying agent and remaining deionized water to 60 ~ 80 DEG C,
Stirred 15 ~ 20 minutes under 800 ~ 900 revs/min of rotating speed, stirring is cooled to room temperature after finishing, produce the garment material environmental protection
Crease-shedding finishing agent.