CN109505166A - A kind of ice oxygen bar summer subway takes the production technology of fabric - Google Patents
A kind of ice oxygen bar summer subway takes the production technology of fabric Download PDFInfo
- Publication number
- CN109505166A CN109505166A CN201910063453.1A CN201910063453A CN109505166A CN 109505166 A CN109505166 A CN 109505166A CN 201910063453 A CN201910063453 A CN 201910063453A CN 109505166 A CN109505166 A CN 109505166A
- Authority
- CN
- China
- Prior art keywords
- fabric
- desizing
- cloth
- agent
- production technology
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to the production technologies that a kind of ice oxygen bar summer subway takes fabric, include the following steps: Fabric Design, warping, starching and pass through, dozen reed of gaiting, woven fabric, fabric inspection, match cloth, cold dome, long vehicle desizing, dyeing, water-sprinkling sizing, middle inspection, technical performance inspection, pack.Ice oxygen bar summer subway of the present invention, which takes the fabric that fabric production technology is produced, has uvioresistant, comfortable and easy to wear, good permeability and certain water repellency, additionally it is possible to discharge anion and be effectively improved air quality, be the ideal fabric of summer subway clothes.
Description
Technical field
The present invention relates to the production technologies that fabric technical field more particularly to a kind of ice oxygen bar summer subway take fabric.
Background technique
With the rising of Global Temperature, day-light saving time is elongated and the increase of outdoor activities, and people are to sunscreen product demand
It is increasingly strong.And in big city, subway becomes the first-selected instrument of trip, outside subway, strong solar exposure, and ultraviolet radiation
By force;Into in subway carriage, and because environment relative closure, the crowd is dense, gravity-flow ventilation is insufficient, cause air quality poor.Closely
Over year aiming at the problem that ultraviolet light, many enterprises are limited only to UPF value and UVA value in actively research and development uvioresistant product,
The product of composite functional is few.
Existing sun protection clothing fabric, is mainly reached by auxiliary agent and postfinishing process, but wherein there is also problems.
Firstly, light color fabric difficulty reaches index, uneven color data difference is big, and water-fastness relatively poor, uvioresistant property is extremely unstable;
Secondly, some fabrics even promote uvioresistant coefficient with the technique of coating, causes fabric airtight, have when summer wears bored
Thermal sensation, comfort are poor;In addition functional relatively single, it is unable to satisfy yearning and demand of the people to good life.
Summary of the invention
Therefore, for the above content, the present invention provides the production technology that a kind of ice oxygen bar summer subway takes fabric, solves existing
Have technology sunscreen fabric uvioresistant effect it is unstable, it is airtight, wear uncomfortable problem.
In order to achieve the above objectives, the present invention is achieved by the following technical solutions: a kind of ice oxygen bar summer subway takes face
The production technology of material, the production technology of the fabric the following steps are included:
(1) Fabric Design: fabric warp thread selects N20D/24F FD DTY, and weft yarn selects N40D/36F SD DTY cool feeling
Yarn, weft density on machine 133/inch, upper machine breadth 180cm, porter 24;
(2) warping: warping is carried out using warping machine, warping requires to include total quantity of warps 12600, is divided into 10 disks
Head, each coiled hair 1260, every meter of yarn-using amount 28.1g/m of warp thread;
(3) starching: starching processing is carried out to 10 coiled hairs using polyamide fibre slurry WJ-98, the even tension of warp thread is controlled, protects
0.2~0.25 gram of every denier of wire vent is demonstrate,proved, 0.25~0.3 gram of every denier, curl tension -0.6 are batched;
(4) it and passes through: using and through machine by 10 coiled hairs and at a coiled hair, control the even tension of warp thread;
(5) it gaits and makes reed;
(6) woven fabric: will first gait to knit the good coiled hair of reed and draw to machine progress woven fabric, technological parameter on water-jet loom includes water spray
100 ° of angle, change 110 ° of yarn angle, leading angle is set as 10 ° of polyamide fibre;
(7) fabric is examined: will weave the case where fabric come tests, checks whether there is disconnected warp, sluff-offs, weft bar;
(8) match cloth: formulating " dyeing and finishing engineering control detail card " specified fabric, lot number, quantity arrangement according to our company;
(9) cold dome:
The proportion of press piece alkali 55-65g/L, desizing agent 15-25g/L, concise emulsifier 18-22g/L, stabilizer 3-7g/L,
The first desizing liquid for preparing 300L, is placed in hopper;
Above-mentioned resulting first desizing liquid is warming up to 56-65 DEG C, the fabric prepared is smooth from hopper process, then pass through
Padding machine sufficiently soaks and then breaks into a roll, stacking at room temperature 20-30h, 10 circles of revolving speed/min;
(10) long vehicle desizing:
The proportion of press piece alkali 30-50g/L, desizing agent 8-16g/L, concise emulsifier 6-14g/L, stabilizer 3-7g/L, match
Make the second desizing liquid;
By the good cloth of step (9) cold dome, by long vehicle desizing, for the control of hopper temperature at 90-100 DEG C, long vehicle speed is 25-
35M/min, padding machine pressure 1.5-2.5 ㎏, pay attention to cloth cover can not folding line, edge slack;
Cloth after desizing carries out desizing measure of merit, and test method is as follows: weighing the bright blue dyestuff 3g of cation, adds water to
Dissolution is sufficiently stirred in 500mL, then the desizing cloth of one piece of whole picture is taken to be dipped into dye liquor, and 5min, which takes out, sees that cloth cover dyeing effect is
It is no uniform;Illustrate that desizing works well if uniformly, on the contrary it will desizing again;
(11) it dyes:
Above-mentioned desizing cloth is sent into dye vat under room temperature, the dye liquor quality in the desizing cloth material to be dyed and dye vat
Bath raio is 1:10, is warming up to 36-45 DEG C by the heating curve of 2 DEG C/min, then be warming up to 75-85 DEG C by 1.5 DEG C/min, and keep the temperature
Then 10-15min is warming up to 96-104 DEG C by 1 DEG C/min, dyed after keeping the temperature 20-40min, is sampled after stained to color,
The woven fabric complete to color keeps the temperature 15-30min progress fixation in 75-85 DEG C of fixation liquid and washes, and fixation liquid rises to 75-85 by 2 DEG C/min
℃;
(12) water-sprinkling is formed:
Step1: C6 water-sprinkling agent 24-36g/L, hydrophilic softening agent 8-12g/L, bleeding agent 3-7g/L, glacial acetic acid 0.05- are pressed
The proportion of 0.15g/L, the mixed liquor for configuring 100L are placed in hopper;
Step2: cloth is sufficiently squeezed through padding machine after wetting again from hopper, padding machine pressure 1.5-3.5 ㎏, subsequently into fixed
Type machine baking oven high-temperature shaping, technological parameter are as follows: 150-170 DEG C of temperature, cloth speed 30-50M/min, air quantity 1400-1600m3/ S surpasses
Feed 3-5%;
Step3: fabric is sent to chill roll cooling, re-test waterproof effect compares feel after baking oven high-temperature shaping;
(13) inspection in: cloth cover quality is examined by American Standard four point system cloth test stone;
(14) technical performance is examined;
(15) it packs.
A further improvement is that: weft yarn is using two kinds of combinations in the step (5), and first latitude is by N40D/36F SD DTY ice
Cool yarn composition, second latitude is made of 2 ice-cold yarns of N40D/36F SD DTY, and weft yarn picking in a manner of 14 first latitude, 2 second latitude.
A further improvement is that: the main component of the desizing agent of step (9) and step (10) is isomerous tridecanol polyoxy second
Alkene ether, the main component of concise emulsifier are polyethenoxy ether, and the main component of stabilizer is sodium metasilicate.
A further improvement is that: in step (11) dye liquor include as mass fraction 0.02%-0.04% acid red,
Acid blue, 1%-3% UV resistant agent HTUV150,1%-2% level dyeing of 0.06%-0.10% Indian yellow, 0.10%-0.20%
Agent, remaining be water.
A further improvement is that: it further include 0.2g glacial acetic acid in every liter of dye liquor.
A further improvement is that: fixation liquid includes 2%-4% color fixing agent, 0.3%- as mass fraction in step (11)
0.7% glacial acetic acid, remaining be water.
A further improvement is that: the specification of the fabric is as follows: fabric through close 195/inch, fabric filling density 140/
Inch, fabric breadth 164cm, fabric weight per square meter 47g/m2, finished product through close 210/inch, 145/inch of finished product filling density,
Fabric width 148cm, finished product weight per square meter 56g/m2。
By using preceding solution, the beneficial effects of the present invention are: the fabric uvioresistant of (1) invention preparation reaches
Mark can effectively prevent skin and be tanned severely and cutaneous lesions;(2) the fabric contact cool feeling coefficient of invention preparation reaches
0.19J/ (cms) can be effectively improved summer high temperature bring discomfort;(3) the fabric good permeability of invention preparation
It can effectively perspire and rapid-curing cutback;(4) fabric of invention preparation has the effect of water repellency, it can be achieved that anti-light rain, it is ensured that dry and comfortable
Property;(5) release of anion can be effectively improved air quality.
Detailed description of the invention
Fig. 1 is the structural schematic diagram of line domain in the embodiment of the present invention.
Specific embodiment
Carry out the embodiment that the present invention will be described in detail below with reference to specific embodiment, how skill is applied to the present invention whereby
Art means solve technical problem, and the realization process for reaching technical effect can fully understand and implement.
Unless otherwise specified, the conventional hand that technological means employed in embodiment is well known to those skilled in the art
Section, used reagent and product are also available commercial.The source of agents useful for same, trade name and it is necessary to list it
Constituent person is indicated on the first occurrence.
Embodiment
A kind of ice oxygen bar summer subway takes the production technology of fabric, the production technology of the fabric the following steps are included:
(1) Fabric Design: fabric warp thread selects N20D/24F FD DTY, and weft yarn selects N40D/36F SD DTY cool feeling
Yarn, weft density on machine 133/inch, upper machine breadth 180cm, porter 24;
(2) warping: warping is carried out using warping machine, warping requires to include total quantity of warps 12600, is divided into 10 disks
Head, each coiled hair 1260, every meter of yarn-using amount 28.1g/m of warp thread;
(3) starching: starching processing is carried out to 10 coiled hairs using polyamide fibre slurry WJ-98, the even tension of warp thread is controlled, protects
0.25 gram of every denier of wire vent is demonstrate,proved, 0.3 gram of every denier, curl tension -0.6 are batched;
(4) it and passes through: using and through machine by 10 coiled hairs and at a coiled hair, control the even tension of warp thread;
(5) gait and make reed: for the mode for making reed of gaiting according to one textile processes table of table and with reference to Fig. 1, weft yarn uses two kinds of groups
It closes, first latitude is made of the ice-cold yarn of N40D/36F SD DTY, and second latitude is made of 2 ice-cold yarns of N40D/36F SD DTY, and latitude
Yarn picking in a manner of 14 first latitude, 2 second latitude;
(6) woven fabric: will first gait to knit the good coiled hair of reed and draw to machine progress woven fabric, technological parameter on water-jet loom includes water spray
100 ° of angle, change 110 ° of yarn angle, leading angle is set as 10 ° of polyamide fibre;
(7) fabric is examined: will weave the case where fabric come tests, checks whether there is disconnected warp, sluff-offs, weft bar;
(8) match cloth: formulating " dyeing and finishing engineering control detail card " specified fabric, lot number, quantity arrangement according to our company;
(9) cold dome:
The proportion of press piece alkali 60g/L, desizing agent 20g/L, concise emulsifier 20g/L are prepared the first desizing liquid of 300L, are put
It is placed in hopper;
Above-mentioned resulting first desizing liquid is warming up to 60 DEG C, fabric is smooth to be passed through from hopper, then is sufficiently moistened through padding machine
It is wet and then break into a roll, stacking at room temperature for 24 hours, 10 circles of revolving speed/min;
(10) long vehicle desizing:
The proportion of press piece alkali 40g/L, desizing agent 12g/L, concise emulsifier 10g/L, stabilizer 5g/L prepare the second desizing
Liquid;
By the good cloth of step (9) cold dome, by long vehicle desizing, for the control of hopper temperature at 95 DEG C, long vehicle speed is 30M/
Min, 2 ㎏ of padding machine pressure, pay attention to cloth cover can not folding line, edge slack;
Cloth after desizing carries out desizing measure of merit, and test method is as follows: weighing the bright blue dyestuff 3g of cation, adds water to
Dissolution is sufficiently stirred in 500mL, then the desizing cloth of one piece of whole picture is taken to be dipped into dye liquor, and 5min, which takes out, sees that cloth cover dyeing effect is
It is no uniform;Illustrate that desizing works well if uniformly, on the contrary it will desizing again;
The main component of first desizing liquid and the desizing agent in the second desizing liquid is isomerous tridecanol polyoxyethylene ether, concise
The main component of emulsifier is polyethenoxy ether, and the main component of stabilizer is sodium metasilicate;
(11) it dyes:
Above-mentioned desizing cloth is sent into dye vat under room temperature, the dye liquor quality in the desizing cloth material to be dyed and dye vat
Bath raio is 1:10, and dye liquor includes 0.03% acid red, 0.08% Indian yellow, 0.15% acid blue, 2% anti-purple as mass fraction
Outside line agent HTUV150,1.5% levelling agent, 96.24% water further include 0.2g glacial acetic acid in every liter of dye liquor;By the liter of 2 DEG C/min
Warm curve is warming up to 40 DEG C, then is warming up to 80 DEG C by 1.5 DEG C/min, and keep the temperature 10min, is then warming up to 100 by 1 DEG C/min
DEG C, it is dyed, is sampled after stained to color, the woven fabric complete to color keeps the temperature 20min in 80 DEG C of fixation liquid after keeping the temperature 30min
It carries out fixation to wash, assigns the good color fastness of fabric, fixation liquid rises to 80 DEG C by 2 DEG C/min, and fixation liquid wraps as mass fraction
Include 3% color fixing agent, 0.5% glacial acetic acid, 96.5% water;
(12) water-sprinkling is formed:
Step1: press C6 water-sprinkling agent 30g/L, hydrophilic softening agent 10g/L, bleeding agent 5g/L, the proportion of glacial acetic acid 0.1g/L,
The mixed liquor of configuration 100L is placed in hopper;
Step2: cloth is sufficiently squeezed through padding machine after wetting again from hopper, 2.5 ㎏ of padding machine pressure, subsequently into forming machine
Baking oven high-temperature shaping, technological parameter are as follows: 160 DEG C of temperature, cloth speed 40M/min, air quantity 1500m3/ S, overfeeding 4%;
Step3: it after the drying of baking oven high temperature, send to chill roll cooling, re-test waterproof effect compares feel;
(13) inspection in: cloth cover quality is examined by American Standard four point system cloth test stone;
(14) technical performance is examined: inspection result is shown in Table two;
(15) it packs.
The specification of the fabric is as follows: fabric is through close 195/inch, 140/inch of fabric filling density, fabric breadth
164cm, fabric weight per square meter 47g/m2, finished product through close 210/inch, finished product filling density 145/inch, Fabric width 148cm,
Finished product weight per square meter 56g/m2。
One textile processes table of table
Two technical performance examining report of table
The proportion of first desizing liquid can be in step (9) cold dome process of the present invention are as follows: piece alkali 55-65g/L, desizing agent
15-25g/L, concise emulsifier 18-22g/L, bleeding agent 3-7g/L;Resulting first desizing liquid is warming up to 56-65 DEG C, and fabric is flat
Whole passes through from the hopper containing the first desizing liquid, then sufficiently soaks and then break into a roll through padding machine, stacking at room temperature 20-30h;
The proportion of the second desizing liquid in step (10) long vehicle desizing process of the present invention can also be piece alkali 30-50g/L, move back
Starch agent 8-16g/L, concise emulsifier 6-14g/L, stabilizer 3-7g/L;The temperature of long vehicle desizing is 90-100 DEG C, keeps the temperature 20-
40min, padding machine pressure 1.5-2.5 ㎏,;
In step (11) dyeing process of the present invention formula for dye liquor include: as mass fraction 0.02%-0.04% acid red,
Acid blue, 1%-3% UV resistant agent HTUV150,1%-2% level dyeing of 0.06%-0.10% Indian yellow, 0.10%-0.20%
Agent, remaining be water, further include 0.2g glacial acetic acid in every liter of dye liquor;After desizing cloth is sent into dye vat by room temperature, by the heating of 2 DEG C/min
Curve is warming up to 36-45 DEG C, then is warming up to 75-85 DEG C by 1.5 DEG C/min, and keep the temperature 10-15min, then heats up by 1 DEG C/min
It to 96-104 DEG C, is dyed, is sampled after stained to color, the woven fabric complete to color is in 75-85 DEG C of fixation after keeping the temperature 20-40min
It keeps the temperature 15-30min progress fixation in liquid to wash, fixation liquid rises to 75-85 DEG C by 2 DEG C/min, and fixation liquid includes as mass fraction
2%-4% color fixing agent, 0.3%-0.7% glacial acetic acid, remaining be water;
Mixed liquor presses C6 water-sprinkling agent 24-36g/L, hydrophilic softening agent 8-12g/ in step (12) water-sprinkling shaping process of the present invention
L, bleeding agent 3-7g/L, glacial acetic acid 0.05-0.15g/L are prepared;Cloth is abundant through padding machine again after wetting from hopper
It squeezes, padding machine pressure 1.5-3.5 ㎏, subsequently into forming machine baking oven high-temperature shaping, technological parameter are as follows: 150-170 DEG C of temperature, cloth
Fast 30-50M/min, air quantity 1400-1600m3/ S, overfeeding 3-5%.
The foregoing descriptions are merely the embodiment using this origination techniques content, any those skilled in the art use this wound
Make done modifications and changes, all belong to the scope of the patents of this creation opinion, and is not limited to those disclosed embodiments.
Claims (7)
1. the production technology that a kind of ice oxygen bar summer subway takes fabric, which is characterized in that the production technology of the fabric include with
Lower step:
(1) Fabric Design: fabric warp thread selects N20D/24F FD DTY, and weft yarn selects N40D/36F SD DTY cool feeling yarn, on
Machine filling density 133/inch, upper machine breadth 180cm, porter 24;
(2) warping: warping is carried out using warping machine, warping requires to include total quantity of warps 12600, is divided into 10 coiled hairs, often
A coiled hair 1260, every meter of yarn-using amount 28.1g/m of warp thread;
(3) starching: starching processing is carried out to 10 coiled hairs using polyamide fibre slurry WJ-98, the even tension of warp thread is controlled, guarantees
0.2~0.25 gram of every denier of silk, batches 0.25~0.3 gram of every denier, curl tension -0.6;
(4) it and passes through: using and through machine by 10 coiled hairs and at a coiled hair, control the even tension of warp thread;
(5) it gaits and makes reed;
(6) woven fabric: will first gait to knit the good coiled hair of reed and draw to machine progress woven fabric, technological parameter on water-jet loom includes angle of spraying water
100 °, change 110 ° of yarn angle, leading angle is set as 10 ° of polyamide fibre;
(7) fabric is examined: will weave the case where fabric come tests, checks whether there is disconnected warp, sluff-offs, weft bar;
(8) match cloth;
(9) cold dome:
The proportion of press piece alkali 55-65g/L, desizing agent 15-25g/L, concise emulsifier 18-22g/L, stabilizer 3-7g/L are prepared
The first desizing liquid of 300L, is placed in hopper;
Above-mentioned resulting first desizing liquid is warming up to 56-65 DEG C, the fabric prepared is smooth from hopper process, then through padding machine
Sufficiently soak and then break into a roll, stacking at room temperature 20-30h, 10 circles of revolving speed/min;
(10) long vehicle desizing:
The proportion of press piece alkali 30-50g/L, desizing agent 8-16g/L, concise emulsifier 6-14g/L, stabilizer 3-7g/L prepare the
Two desizing liquids;
By the good cloth of step (9) cold dome, by long vehicle desizing, for the control of hopper temperature at 90-100 DEG C, long vehicle speed is 25-35M/
Min, padding machine pressure 1.5-2.5 ㎏;
Cloth after desizing carries out desizing measure of merit, and test method is as follows: weighing the bright blue dyestuff 3g of cation, adds water to 500mL
Dissolution is sufficiently stirred, then the desizing cloth of one piece of whole picture is taken to be dipped into dye liquor, 5min takes out see whether cloth cover dyeing effect is equal
It is even;Illustrate that desizing works well if uniformly, on the contrary it will desizing again;
(11) it dyes:
Above-mentioned desizing cloth is sent into dye vat under room temperature, the dye liquor quality bath raio in the desizing cloth material to be dyed and dye vat
For 1:10, it is warming up to 36-45 DEG C by the heating curve of 2 DEG C/min, then is warming up to 75-85 DEG C by 1.5 DEG C/min, and keep the temperature 10-
Then 15min is warming up to 96-104 DEG C by 1 DEG C/min, dyed after keeping the temperature 20-40min, is sampled after stained to color, right
The complete woven fabric of color keeps the temperature 15-30min progress fixation in 75-85 DEG C of fixation liquid and washes, and fixation liquid rises to 75-85 DEG C by 2 DEG C/min;
(12) water-sprinkling is formed:
Step1: C6 water-sprinkling agent 24-36g/L, hydrophilic softening agent 8-12g/L, bleeding agent 3-7g/L, glacial acetic acid 0.05-0.15g/ are pressed
The proportion of L, the mixed liquor for configuring 100L are placed in hopper;
Step2: cloth is sufficiently squeezed through padding machine after wetting again from hopper, padding machine pressure 1.5-3.5 ㎏, subsequently into forming machine
Baking oven high-temperature shaping, technological parameter are as follows: 150-170 DEG C of temperature, cloth speed 30-50M/min, air quantity 1400-1600m3/ S, overfeeding 3-
5%;
Step3: fabric is sent to chill roll cooling, re-test waterproof effect compares feel after baking oven high-temperature shaping;
(13) inspection in: cloth cover quality is examined by American Standard four point system cloth test stone;
(14) technical performance is examined;
(15) it packs.
2. the production technology that a kind of ice oxygen bar summer subway according to claim 1 takes fabric, which is characterized in that the step
Suddenly weft yarn is made of using two kinds of combinations, first latitude the ice-cold yarn of N40D/36F SD DTY in (5), and second latitude is by 2 N40D/36F SD
The ice-cold yarn composition of DTY, and weft yarn picking in a manner of 14 first latitude, 2 second latitude.
3. the production technology that a kind of ice oxygen bar summer subway according to claim 1 takes fabric, which is characterized in that step
(9) and the main component of the desizing agent of step (10) is isomerous tridecanol polyoxyethylene ether, and the main component of concise emulsifier is
Polyethenoxy ether, the main component of stabilizer are sodium metasilicate.
4. the production technology that a kind of ice oxygen bar summer subway according to claim 1 takes fabric, which is characterized in that step
(11) dye liquor includes 0.02%-0.04% acid red, 0.06%-0.10% Indian yellow, 0.10%- as mass fraction in
0.20% acid orchid, 1%-3% UV resistant agent HTUV150,1%-2% levelling agent, remaining be water.
5. the production technology that a kind of ice oxygen bar summer subway according to claim 4 takes fabric, which is characterized in that every liter of dye
It further include 0.2g glacial acetic acid in liquid.
6. the production technology that a kind of ice oxygen bar summer subway according to claim 1 takes fabric, which is characterized in that step
(11) in fixation liquid include as mass fraction 2%-4% color fixing agent, 0.3%-0.7% glacial acetic acid, remaining be water.
7. the production technology that a kind of ice oxygen bar summer subway according to claim 1 takes fabric, which is characterized in that the face
The specification of material is as follows: fabric is through close 195/inch, 140/inch of fabric filling density, fabric breadth 164cm, fabric weight per square meter
47g/m2, finished product is through close 210/inch, finished product filling density 145/inch, Fabric width 148cm, finished product weight per square meter 56g/m2。