CN105502954A - 一种半透明艺术玻璃加工工艺 - Google Patents

一种半透明艺术玻璃加工工艺 Download PDF

Info

Publication number
CN105502954A
CN105502954A CN201510849011.1A CN201510849011A CN105502954A CN 105502954 A CN105502954 A CN 105502954A CN 201510849011 A CN201510849011 A CN 201510849011A CN 105502954 A CN105502954 A CN 105502954A
Authority
CN
China
Prior art keywords
glass
pickle solution
sandblasting
parts
hydrofluoric acid
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510849011.1A
Other languages
English (en)
Inventor
吕建平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201510849011.1A priority Critical patent/CN105502954A/zh
Publication of CN105502954A publication Critical patent/CN105502954A/zh
Pending legal-status Critical Current

Abstract

本发明涉及玻璃深加工技术领域，具体指一种半透明艺术玻璃加工工艺。包括以下工艺步骤：a、首先将玻璃的非加工面封上保护膜，然后对玻璃的加工面进行喷砂处理；b、配制酸洗液，按重量比将55份氢氟酸(40％-45％)浓度的氢氟酸、45份(95％-98％)浓度的硫酸混合配制成酸洗液，并将酸洗液搅拌后静置30分钟；c、将酸洗液均匀浇淋在经过喷砂处理的玻璃加工面上，并使酸洗液在玻璃加工面上滞留30-60秒；d、用清水冲洗玻璃再撕去保护膜并晾干。本发明通过氢氟酸和硫酸配置成酸洗液与玻璃喷砂工艺有效结合，得到具有凹凸立体感、可实现层次图案设计、透光度可控、具有朦胧感的艺术玻璃加工方法，可与其他工艺组合加工，应用范围广、生产效率高。

Description

一种半透明艺术玻璃加工工艺
技术领域
本发明涉及玻璃深加工技术领域，具体指一种半透明艺术玻璃加工工艺。
背景技术
艺术玻璃是人们现实生活中对精神世界的一种形象反映，艺术玻璃的工艺种类多、工艺效果复杂，是现代高端装饰建材中不可或缺的品种。其中的压花玻璃一种具有半透明的、凹凸层次、琉璃彩色、漫反射效果的原片玻璃，应用非常广泛。但是压花玻璃是由碎玻颗粒回炉烧制的，然后辊压产生其表面的各种纹路和花纹。烧制后的压花玻璃内存在较多气泡、杂质，导致其强度较差、易碎，难以后期加工。而蒙砂玻璃是一种具有朦胧感的艺术玻璃，其表面通过化学药剂反应从而产生手感细腻的雾化效果，常用于隔断部位的装饰材料，但是蒙砂玻璃的层次感较差，且遇水透光，清洁和维护比较麻烦。因此，现有技术还有待于改进和发展。
发明内容
本发明的目的在于针对现有技术的缺陷和不足，提供一种透光透亮、层次清晰、具有颗粒感阻光隔视线的半透明艺术玻璃加工工艺。
为了实现上述目的，本发明采用以下技术方案：
本发明所述的一种半透明艺术玻璃加工工艺，包括以下工艺步骤：
a、首先将玻璃的非加工面封上保护膜，然后对玻璃的加工面进行喷砂处理；
b、配制酸洗液，按重量比将55份氢氟酸(40％-45％)浓度的氢氟酸、45份(95％-98％)浓度的硫酸混合配制成酸洗液，并将酸洗液搅拌后静置30分钟；
c、玻璃水平且待加工面朝上放置在操作台上，将酸洗液均匀浇淋在经过喷砂处理的玻璃加工面上，并使酸洗液在玻璃加工面上滞留30-60秒；
d、用清水冲洗玻璃加工面和非加工面以去除酸洗液残留，然后再撕去保护膜并晾干。
根据以上方案，所述喷砂处理的喷枪压力在5-6Kg之间，喷枪使用的金刚砂颗粒在30-80μm。
根据以上方案，所述经过酸洗液处理后的玻璃的透光度为T，酸洗液的酸洗滞留时间为S，则T与S呈正比，随着酸洗滞留时间的增加，玻璃喷砂面的透光度从半透明向全透明变化.
本发明有益效果为：本发明通过氢氟酸和硫酸配置成酸洗液与玻璃喷砂工艺有效结合，从而得到具有凹凸立体感、可实现层次图案设计、透光度可控、具有朦胧感的艺术玻璃加工方法，避免压花玻璃纹路的单一性和强度差问题，可与其他工艺组合加工，应用范围广、生产效率高，有效扩展玻璃装饰装潢设计的材质效果。
具体实施方式
下面结合实施例对本发明的技术方案进行说明。
本发明所述的一种半透明艺术玻璃加工工艺，其特征在于，包括以下工艺步骤：
a、首先将玻璃的非加工面封上保护膜，然后对玻璃的加工面进行喷砂处理；
b、配制酸洗液，按重量比将55份氢氟酸(40％-45％)浓度的氢氟酸、45份(95％-98％)浓度的硫酸混合配制成酸洗液，并将酸洗液搅拌后静置30分钟；
c、玻璃水平且待加工面朝上放置在操作台上，将酸洗液均匀浇淋在经过喷砂处理的玻璃加工面上，并使酸洗液在玻璃加工面上滞留30-60秒；
d、用清水冲洗玻璃加工面和非加工面以去除酸洗液残留，然后再撕去保护膜并晾干。
所述喷砂处理的喷枪压力在5-6Kg之间，喷枪使用的金刚砂颗粒在30-80μm。
所述经过酸洗液处理后的玻璃的透光度为T，酸洗液的酸洗滞留时间为S，则T与S呈正比，随着酸洗滞留时间的增加，玻璃喷砂面的透光度从半透明向全透明变化.
以上所述仅是本发明的较佳实施方式，故凡依本发明专利申请范围所述的构造、特征及原理所做的等效变化或修饰，均包括于本发明专利申请范围内。

Claims (4)

1.一种半透明艺术玻璃加工工艺，其特征在于，包括以下工艺步骤：
a、首先将玻璃的非加工面封上保护膜，然后对玻璃的加工面进行喷砂处理；
b、配制酸洗液，按重量比将55份氢氟酸(40％-45％)浓度的氢氟酸、45份(95％-98％)浓度的硫酸混合配制成酸洗液，并将酸洗液搅拌后静置30分钟；
c、玻璃水平且待加工面朝上放置在操作台上，将酸洗液均匀浇淋在经过喷砂处理的玻璃加工面上，并使酸洗液在玻璃加工面上滞留30-60秒；
d、用清水冲洗玻璃加工面和非加工面以去除酸洗液残留，然后再撕去保护膜并晾干。
2.根据权利要求1所述的半透明艺术玻璃加工工艺，其特征在于：所述喷砂处理的喷枪压力在5-6Kg之间，喷枪使用的金刚砂颗粒在30-80μm。
3.根据权利要求1所述的半透明艺术玻璃加工工艺，其特征在于：所述经过酸洗液处理后的玻璃的透光度为T，酸洗液的酸洗滞留时间为S，则T与S呈正比，随着酸洗滞留时间的增加，玻璃喷砂面的透光度从半透明向全透明变化。
4.根据权利要求1所述的半透明艺术玻璃加工工艺，其特征在于：所述酸洗液按重量比将80份氢氟酸(40％-45％)浓度的氢氟酸、20份(95％-98％)浓度的硫酸混时，酸洗液均匀浇淋在经过喷砂处理的玻璃加工面上，并使酸洗液在玻璃加工面上滞留20-40秒，所述玻璃的喷砂面呈朦胧的半透光效果。
CN201510849011.1A 2015-11-27 2015-11-27 一种半透明艺术玻璃加工工艺 Pending CN105502954A (zh)