CN105462406A - 一种外墙涂料及其制备方法 - Google Patents
一种外墙涂料及其制备方法 Download PDFInfo
- Publication number
- CN105462406A CN105462406A CN201511015509.4A CN201511015509A CN105462406A CN 105462406 A CN105462406 A CN 105462406A CN 201511015509 A CN201511015509 A CN 201511015509A CN 105462406 A CN105462406 A CN 105462406A
- Authority
- CN
- China
- Prior art keywords
- parts
- exterior coating
- antioxidant
- triton
- tween
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种外墙涂料及其制备方法，其由以下重量份的组分组成：磷酸酯改性丙烯酸乳液41-48份、颜填料15-25份、十二烷基硫酸钠0.5-0.8份、小桐子生物柴油5-15份、抗氧化剂0.1-0.5份、成膜助剂1.5-2.3份、吐温-80？10-18份、曲拉通X-100？0.5-1.2份、水40-50份。本发明在各组分的科学匹配和协同作用下，采用非离子型表面活性剂吐温-80和曲拉通X-100，在小桐子生物柴油和抗氧化剂的协同作用下，增强了外墙涂料的性能，其具有很好的抗紫外线能力、耐候性能、耐化学腐蚀性、耐擦洗性等性能，远远满足了GB/T9755-2001合成树脂乳液外墙涂料的国家标准的要求。
Description
技术领域
本发明属于涂料技术领域，具体涉及一种外墙涂料及其制备方法。
背景技术
涂料是涂于物体表面能形成具有保护、装饰或特殊性能（如绝缘、防腐、标志等）的固态涂膜的一类液体或者固体材料的总称，包括油性漆、水性漆和粉末涂料。涂料作为家庭装饰和城市绿化的主材之一，在现代建筑装饰中占有很大的比例。随着人们生产和生活水平的不断提高，人们对涂料装饰性能和安全性能的要求也越来越高。
现有的外墙涂料功能比较单一，涂膜的耐候性、防水性、耐化学腐蚀性、耐擦洗性和耐人工老化等性能较差，由于建筑物的外墙长期受到阳光照射，其表面温度明显升高，直接影响到外墙的温度，以至于影响室内的温度；重要的是，外墙又经常饱受雨水的冲击；特别是在夏天，常常在高温照射后立即迎来暴风骤雨，这种阳光和雨水对外墙的交替冲刷和洗礼，使得外墙涂料提出了更高的要求，使其长期使用过程中存在褪色、脱落、掉粉等现象，不能满足外墙涂料的需求。
发明内容
本发明的目的在于提供一种工艺简单，组分配伍合理，不易脱落，使用寿命长的外墙涂料及其制备方法。
为实现上述目的，本发明所采用的技术方案是：
一种外墙涂料，其特征在于，由以下重量份的组分组成：磷酸酯改性丙烯酸乳液41-48份、颜填料15-25份、十二烷基硫酸钠0.5-0.8份、小桐子生物柴油5-15份、抗氧化剂0.1-0.5份、成膜助剂1.5-2.3份、吐温-8010-18份、曲拉通X-1000.5-1.2份、水40-50份。
优选的，由以下重量份的组分组成：磷酸酯改性丙烯酸乳液45份、颜填料20份、十二烷基硫酸钠0.7份、小桐子生物柴油10份、抗氧化剂0.3份、成膜助剂2份、吐温-8015份、曲拉通X-1000.8份、水45份。
优选的，所述颜填料为钛白粉、重钙粉、滑石粉、硫酸钡、云母粉和高岭土中的一种或多种。
优选的，所述抗氧化剂为二甲基对氨基苯甲酸辛酯或水杨酸辛酯。
优选的，所述的成膜助剂为丙二醇丁醚或丙二醇甲醚醋酸酯。
一种上述外墙涂料的制备方法，其特征在于包括以下步骤：（1）按配方称取各组分，在300-800转/分钟的搅拌速度下依次加入水、吐温-80、曲拉通X-100、抗氧化剂、十二烷基硫酸钠，充分搅拌10-30分钟；（2）在300-800转/分钟的搅拌速度下加入颜填料，混合均匀后，1000-2000转/分钟搅拌30-90分钟，得颜填料分散浆；（3）在300-800转/分钟的搅拌速度下加入磷酸酯改性丙烯酸乳液，然后在500-1000转/分钟搅拌速度下加入成膜助剂，搅拌20-60分钟，即得外墙涂料。
本发明具有的优点和积极效果是：
本发明在各组分的科学匹配和协同作用下，采用非离子型表面活性剂吐温-80和曲拉通X-100，在小桐子生物柴油和抗氧化剂的协同作用下，增强了外墙涂料的性能，其具有很好的抗紫外线能力、耐老化性能、耐候性能、耐化学腐蚀性、耐擦洗性等性能，远远满足了GB/T9755-2001合成树脂乳液外墙涂料的国家标准的要求，其耐水性、耐碱性、耐洗刷性、耐温变性和隔热性能均得到了很大程度的提高，延长了外墙涂料的使用寿命，增强了建筑物的装饰性能，克服了现有的外墙涂料容易出现褪色、开裂、甚至脱皮等现象而严重影响其使用效果和美观性能的问题，经济实用。本发明所用抗氧化剂是强有力的户外紫外光吸收剂，提供出色的吸收紫外线效果，且具有较低的成本，安全无毒，此外，抗氧化剂还能起到助溶剂的作用。
下面通过实施例对本发明进行具体描述和说明：
实施例1
一种外墙涂料，由以下重量份的组分组成：磷酸酯改性丙烯酸乳液41份、钛白粉15份、十二烷基硫酸钠0.5份、小桐子生物柴油5份、水杨酸辛酯0.1份、丙二醇丁醚1.5份、吐温-8010份、曲拉通X-1000.5份、水40份。
实施例2
一种外墙涂料，由以下重量份的组分组成：磷酸酯改性丙烯酸乳液48份、重钙粉25份、十二烷基硫酸钠0.8份、小桐子生物柴油15份、二甲基对氨基苯甲酸辛酯0.5份、丙二醇甲醚醋酸酯2.3份、吐温-8018份、曲拉通X-1001.2份、水50份。
实施例3
一种外墙涂料，由以下重量份的组分组成：磷酸酯改性丙烯酸乳液45份、滑石粉20份、十二烷基硫酸钠0.7份、小桐子生物柴油10份、二甲基对氨基苯甲酸辛酯0.3份、丙二醇甲醚醋酸酯2份、吐温-8015份、曲拉通X-1000.8份、水45份。
实施例4
一种外墙涂料，由以下重量份的组分组成：磷酸酯改性丙烯酸乳液43份、硫酸钡18份、十二烷基硫酸钠0.6份、小桐子生物柴油8份、二甲基对氨基苯甲酸辛酯0.2份、丙二醇甲醚醋酸酯1.8份、吐温-8012份、曲拉通X-1000.7份、水43份。
实施例5
一种外墙涂料，由以下重量份的组分组成：磷酸酯改性丙烯酸乳液47份、云母粉23份、十二烷基硫酸钠0.7份、小桐子生物柴油13份、水杨酸辛酯0.3份、丙二醇丁醚2.2份、吐温-8016份、曲拉通X-1001份、水47份。
实施例6
一种外墙涂料，由以下重量份的组分组成：磷酸酯改性丙烯酸乳液45份、滑石粉10份、高岭土10份、十二烷基硫酸钠0.7份、小桐子生物柴油10份、二甲基对氨基苯甲酸辛酯0.3份、丙二醇甲醚醋酸酯2份、吐温-8012份、曲拉通X-1001.2份、水45份。
以下是实施例1-6中外墙涂料的制备方法为：
实施例1-2所述外墙涂料的制备方法为：包括以下步骤：（1）按配方称取各组分，在300转/分钟的搅拌速度下依次加入水、吐温-80、曲拉通X-100、抗氧化剂、十二烷基硫酸钠，充分搅拌30分钟；（2）在300转/分钟的搅拌速度下加入颜填料，混合均匀后，1000转/分钟搅拌90分钟，得颜填料分散浆；（3）在300转/分钟的搅拌速度下加入磷酸酯改性丙烯酸乳液，然后在500转/分钟搅拌速度下加入成膜助剂，搅拌60分钟，即得外墙涂料。
实施例3-4所述外墙涂料的制备方法为：包括以下步骤：（1）按配方称取各组分，在500转/分钟的搅拌速度下依次加入水、吐温-80、曲拉通X-100、抗氧化剂、十二烷基硫酸钠，充分搅拌20分钟；（2）在500转/分钟的搅拌速度下加入颜填料，混合均匀后，1500转/分钟搅拌60分钟，得颜填料分散浆；（3）在500转/分钟的搅拌速度下加入磷酸酯改性丙烯酸乳液，然后在800转/分钟搅拌速度下加入成膜助剂，搅拌40分钟，即得外墙涂料。
实施例5-6所述外墙涂料的制备方法为：包括以下步骤：（1）按配方称取各组分，在800转/分钟的搅拌速度下依次加入水、吐温-80、曲拉通X-100、抗氧化剂、十二烷基硫酸钠，充分搅拌10分钟；（2）在800转/分钟的搅拌速度下加入颜填料，混合均匀后，2000转/分钟搅拌30分钟，得颜填料分散浆；（3）在800转/分钟的搅拌速度下加入磷酸酯改性丙烯酸乳液，然后在1000转/分钟搅拌速度下加入成膜助剂，搅拌20分钟，即得外墙涂料。
经检测，本发明的外墙涂料的光泽度均在75度以上，这是市售涂料无法企及的；本发明的涂料在水中浸渍250-300h均无异常，而市售涂料在浸水96h之后即出现变色现象；在强碱性溶液中，本发明的涂料浸渍150-200h均无异常，而市售涂料在强碱性溶液中48h后即出现明显变色现象；耐洗刷性试验结果表明，本发明涂料的耐洗刷能力可达8000-9000次，而市售涂料的耐洗刷能力仅有3000次左右；本发明涂料的耐温变性测试结果表明，其从烤箱转到冰箱这样来回循环8-9次均无任何异常，而市售涂料来回循环5次之后，其性能则显著下降；本发明涂料的耐人工气候老化性测试结果表明，本发明的涂料耐人工气候在800-900h均不起泡，未出现不良现象，而市售涂料在人工气候下600h即开始气泡，影响涂料的性能。
Claims (6)
1.一种外墙涂料，其特征在于，由以下重量份的组分组成：磷酸酯改性丙烯酸乳液41-48份、颜填料15-25份、十二烷基硫酸钠0.5-0.8份、小桐子生物柴油5-15份、抗氧化剂0.1-0.5份、成膜助剂1.5-2.3份、吐温-8010-18份、曲拉通X-1000.5-1.2份、水40-50份。
2.根据权利要求1所述的外墙涂料，其特征在于，由以下重量份的组分组成：磷酸酯改性丙烯酸乳液45份、颜填料20份、十二烷基硫酸钠0.7份、小桐子生物柴油10份、抗氧化剂0.3份、成膜助剂2份、吐温-8015份、曲拉通X-1000.8份、水45份。
3.根据权利要求1所述的外墙涂料，其特征在于，所述颜填料为钛白粉、重钙粉、滑石粉、硫酸钡、云母粉和高岭土中的一种或多种。
4.根据权利要求1所述的外墙涂料，其特征在于，所述抗氧化剂为二甲基对氨基苯甲酸辛酯或水杨酸辛酯。
5.根据权利要求1所述的外墙涂料，其特征在于，所述的成膜助剂为丙二醇丁醚或丙二醇甲醚醋酸酯。
6.一种权利要求1-5任一项所述外墙涂料的制备方法，其特征在于包括以下步骤：（1）按配方称取各组分，在300-800转/分钟的搅拌速度下依次加入水、吐温-80、曲拉通X-100、抗氧化剂、十二烷基硫酸钠，充分搅拌10-30分钟；（2）在300-800转/分钟的搅拌速度下加入颜填料，混合均匀后，1000-2000转/分钟搅拌30-90分钟，得颜填料分散浆；（3）在300-800转/分钟的搅拌速度下加入磷酸酯改性丙烯酸乳液，然后在500-1000转/分钟搅拌速度下加入成膜助剂，搅拌20-60分钟，即得外墙涂料。