CN105350321A - 复合面料的整理工艺 - Google Patents

复合面料的整理工艺 Download PDF

Info

Publication number
CN105350321A
CN105350321A CN201510936284.XA CN201510936284A CN105350321A CN 105350321 A CN105350321 A CN 105350321A CN 201510936284 A CN201510936284 A CN 201510936284A CN 105350321 A CN105350321 A CN 105350321A
Authority
CN
China
Prior art keywords
parts
mass
stir
compound material
chloro
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510936284.XA
Other languages
English (en)
Inventor
严旭明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHANGSHU HUABO WOOLEN TEXTILE Co Ltd
Original Assignee
CHANGSHU HUABO WOOLEN TEXTILE Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGSHU HUABO WOOLEN TEXTILE Co Ltd filed Critical CHANGSHU HUABO WOOLEN TEXTILE Co Ltd
Priority to CN201510936284.XA priority Critical patent/CN105350321A/zh
Publication of CN105350321A publication Critical patent/CN105350321A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种复合面料的整理工艺，包括如下步骤：1）在19质量份去离子水中投入1～2质量份羟丙基纤维素、1.3质量份N,N-二正丁基二硫代氨基甲酸镍、2.6质量份2,4,4ˊ-三氯-2ˊ-羟基二苯醚8-羟基喹啉铜、1.7质量份羟基聚磷酸酯混合，搅拌均匀；2）再同时缓慢加入2.5质量份甘油单硬脂酸酯、0.8质量份酸性烷基膦酸酯、1.3质量份氯化二硬脂基二甲基铵、2.2质量份聚六亚甲基胍磷酸盐，继续搅拌，至充分混合均匀，制得整理液；3）将面料在整理液中浸轧处理，取出后恒温烘干。本发明复合面料的整理工艺，其整理后的面料具有优异的抗皱、抗菌、阻燃、防静电性能，且耐洗性强。

Description

复合面料的整理工艺
技术领域
本发明涉及复合面料的整理工艺。
背景技术
现有面料的抗皱、抗菌、阻燃、防静电性能和耐洗性能都有待提高。
发明内容
本发明的目的在于提供一种复合面料的整理工艺，其整理后的面料具有优异的抗皱、抗菌、阻燃、防静电性能，且耐洗性强。
为实现上述目的，本发明的技术方案是设计一种复合面料的整理工艺，包括如下步骤：
1）在19质量份去离子水中投入1～2质量份羟丙基纤维素、1.3质量份N,N-二正丁基二硫代氨基甲酸镍、2.6质量份2,4,4'-三氯-2'-羟基二苯醚8-羟基喹啉铜、1.7质量份羟基聚磷酸酯混合，搅拌均匀；
2）再同时缓慢加入2.5质量份甘油单硬脂酸酯、0.8质量份酸性烷基膦酸酯、1.3质量份氯化二硬脂基二甲基铵、2.2质量份聚六亚甲基胍磷酸盐，继续搅拌，至充分混合均匀，制得整理液；
3）将面料在整理液中浸轧处理，取出后恒温烘干。
优选的，复合面料的整理工艺，包括如下步骤：
1）在19质量份去离子水中投入1质量份羟丙基纤维素、1.3质量份N,N-二正丁基二硫代氨基甲酸镍、2.6质量份2,4,4'-三氯-2'-羟基二苯醚8-羟基喹啉铜、1.7质量份羟基聚磷酸酯混合，搅拌均匀；
2）再同时缓慢加入2.5质量份甘油单硬脂酸酯、0.8质量份酸性烷基膦酸酯、1.3质量份氯化二硬脂基二甲基铵、2.2质量份聚六亚甲基胍磷酸盐，继续搅拌，至充分混合均匀，制得整理液；
3）将面料在整理液中浸轧处理，取出后恒温烘干。
优选的，复合面料的整理工艺，包括如下步骤：
1）在19质量份去离子水中投入2质量份羟丙基纤维素、1.3质量份N,N-二正丁基二硫代氨基甲酸镍、2.6质量份2,4,4'-三氯-2'-羟基二苯醚8-羟基喹啉铜、1.7质量份羟基聚磷酸酯混合，搅拌均匀；
2）再同时缓慢加入2.5质量份甘油单硬脂酸酯、0.8质量份酸性烷基膦酸酯、1.3质量份氯化二硬脂基二甲基铵、2.2质量份聚六亚甲基胍磷酸盐，继续搅拌，至充分混合均匀，制得整理液；
3）将面料在整理液中浸轧处理，取出后恒温烘干。
本发明的优点和有益效果在于：提供一种复合面料的整理工艺，其整理后的面料具有优异的抗皱、抗菌、阻燃、防静电性能，且耐洗性强。
具体实施方式
下面结合实施例，对本发明的具体实施方式作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案，而不能以此来限制本发明的保护范围。
本发明具体实施的技术方案是：
实施例1
一种复合面料的整理工艺，包括如下步骤：
1）在19质量份去离子水中投入1～2质量份羟丙基纤维素、1.3质量份N,N-二正丁基二硫代氨基甲酸镍、2.6质量份2,4,4'-三氯-2'-羟基二苯醚8-羟基喹啉铜、1.7质量份羟基聚磷酸酯混合，搅拌均匀；
2）再同时缓慢加入2.5质量份甘油单硬脂酸酯、0.8质量份酸性烷基膦酸酯、1.3质量份氯化二硬脂基二甲基铵、2.2质量份聚六亚甲基胍磷酸盐，继续搅拌，至充分混合均匀，制得整理液；
3）将面料在整理液中浸轧处理，取出后恒温烘干。
实施例2
复合面料的整理工艺，包括如下步骤：
1）在19质量份去离子水中投入1质量份羟丙基纤维素、1.3质量份N,N-二正丁基二硫代氨基甲酸镍、2.6质量份2,4,4'-三氯-2'-羟基二苯醚8-羟基喹啉铜、1.7质量份羟基聚磷酸酯混合，搅拌均匀；
2）再同时缓慢加入2.5质量份甘油单硬脂酸酯、0.8质量份酸性烷基膦酸酯、1.3质量份氯化二硬脂基二甲基铵、2.2质量份聚六亚甲基胍磷酸盐，继续搅拌，至充分混合均匀，制得整理液；
3）将面料在整理液中浸轧处理，取出后恒温烘干。
实施例3
复合面料的整理工艺，包括如下步骤：
1）在19质量份去离子水中投入2质量份羟丙基纤维素、1.3质量份N,N-二正丁基二硫代氨基甲酸镍、2.6质量份2,4,4'-三氯-2'-羟基二苯醚8-羟基喹啉铜、1.7质量份羟基聚磷酸酯混合，搅拌均匀；
2）再同时缓慢加入2.5质量份甘油单硬脂酸酯、0.8质量份酸性烷基膦酸酯、1.3质量份氯化二硬脂基二甲基铵、2.2质量份聚六亚甲基胍磷酸盐，继续搅拌，至充分混合均匀，制得整理液；
3）将面料在整理液中浸轧处理，取出后恒温烘干。
以上所述仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明技术原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。

Claims (3)

1.复合面料的整理工艺，其特征在于，包括如下步骤：
1）在19质量份去离子水中投入1～2质量份羟丙基纤维素、1.3质量份N,N-二正丁基二硫代氨基甲酸镍、2.6质量份2,4,4'-三氯-2'-羟基二苯醚8-羟基喹啉铜、1.7质量份羟基聚磷酸酯混合，搅拌均匀；
2）再同时缓慢加入2.5质量份甘油单硬脂酸酯、0.8质量份酸性烷基膦酸酯、1.3质量份氯化二硬脂基二甲基铵、2.2质量份聚六亚甲基胍磷酸盐，继续搅拌，至充分混合均匀，制得整理液；
3）将面料在整理液中浸轧处理，取出后恒温烘干。
2.根据权利要求1所述的复合面料的整理工艺，其特征在于，包括如下步骤：
1）在19质量份去离子水中投入1质量份羟丙基纤维素、1.3质量份N,N-二正丁基二硫代氨基甲酸镍、2.6质量份2,4,4'-三氯-2'-羟基二苯醚8-羟基喹啉铜、1.7质量份羟基聚磷酸酯混合，搅拌均匀；
2）再同时缓慢加入2.5质量份甘油单硬脂酸酯、0.8质量份酸性烷基膦酸酯、1.3质量份氯化二硬脂基二甲基铵、2.2质量份聚六亚甲基胍磷酸盐，继续搅拌，至充分混合均匀，制得整理液；
3）将面料在整理液中浸轧处理，取出后恒温烘干。
3.根据权利要求1所述的复合面料的整理工艺，其特征在于，包括如下步骤：
1）在19质量份去离子水中投入2质量份羟丙基纤维素、1.3质量份N,N-二正丁基二硫代氨基甲酸镍、2.6质量份2,4,4'-三氯-2'-羟基二苯醚8-羟基喹啉铜、1.7质量份羟基聚磷酸酯混合，搅拌均匀；
2）再同时缓慢加入2.5质量份甘油单硬脂酸酯、0.8质量份酸性烷基膦酸酯、1.3质量份氯化二硬脂基二甲基铵、2.2质量份聚六亚甲基胍磷酸盐，继续搅拌，至充分混合均匀，制得整理液；
3）将面料在整理液中浸轧处理，取出后恒温烘干。
CN201510936284.XA 2015-12-16 2015-12-16 复合面料的整理工艺 Pending CN105350321A (zh)