CN105315016A - 一种坭兴陶专用透明生料釉 - Google Patents
一种坭兴陶专用透明生料釉 Download PDFInfo
- Publication number
- CN105315016A CN105315016A CN201510299768.8A CN201510299768A CN105315016A CN 105315016 A CN105315016 A CN 105315016A CN 201510299768 A CN201510299768 A CN 201510299768A CN 105315016 A CN105315016 A CN 105315016A
- Authority
- CN
- China
- Prior art keywords
- glaze
- nixing pottery
- pottery
- nixing
- raw glaze
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种坭兴陶专用透明生料釉,该生料釉由硼酸钙、石英、长石、石灰石、维罗土、滑石、坭兴陶土,混合后经加水球磨,过筛,陈腐制成。该釉料烧成后呈现透明质感,对坭兴陶胚体的附着力强,铅化合物、镉化合物含量极低,其装饰效果既保留了坭兴陶的陶质特色,又有釉料的保护作用,使实用性和装饰性有机结合。
Description
技术领域
本发明涉及一种陶瓷釉料,具体涉及坭兴陶的一种釉料。
背景技术
坭兴陶属于含铁量较高的精陶,其胚体颜色一般呈铁红色,这类陶器胚体本身的铁元素就已经是着色剂,其固有色对其他着色剂有强烈的影响,其他着色剂不易覆盖。
现有的瓷器釉料中,适合于陶器烧成温度的釉料一般都是低温熔块釉,由于烧成温度低,所使用的熔块绝大多数含有一些有毒化合物,如铅化合物、镉化合物等,虽然这些化合物制成熔块以后毒素得到一定程度的有效地控制,但是有害物品的析出却在所难免,使用在坭兴陶上则有悖坭兴陶健康环保的产品理念;部分熔块的覆盖性不够强,不能完全覆盖含铁量较高的坭兴陶固有的铁红色,所以部分颜色显色不良,如蓝色系列、绿色系列等。且这类釉料釉层比较厚,釉层光亮平滑,掩盖了陶器特有的表面效果,不能突出陶器质地的美感。
发明内容
本发明要解决的技术问题是提供一种无毒的透明坭兴陶生料釉。
为解决本技术问题本发明采用的技术方案是提供一种坭兴陶生料釉,该生料釉由下列重量百分比的原料经加水、球磨、过筛、陈腐制成:硼酸钙34%、石英20%、长石23%、石灰石10%、维罗土6%、滑石5%、坭兴陶土2%。
釉式如下:
本发明的有益效果是烧制后呈现透明,对坭兴陶体的附着力强。本釉料的烧成温度是1080℃±25℃,与坭兴陶的烧成温度完全一致。完全放弃铅、镉等化合物,在原料上无毒无害,所选用的化合物元素均有利于人体健康,与坭兴陶作为绿色产品的环保理念相吻合,使消费者免除后顾之忧;本发明的釉料适合于氧化还原烧成,使用过程中保留了坭兴陶的大部分传统制作步骤,完全放弃打蜡的非环保环节,表面效果视情况选择打磨,既保留了坭兴陶的陶质特色,减轻工作量,又有釉料的装饰色彩效果。
具体实施方式
本生料釉的制作过程是将按下列重量百分比称量:硼酸钙34%、石英20%、长石23%、石灰石10%、维罗土6%、滑石5%、坭兴陶土2%。进行混合后加水球磨、检查细度、过筛、陈腐、待用。
称量环节中,各原料的精确度要达到0.1克,特别是硼酸钙的用量必须精确称量,因为它是最重要的助熔剂,硼的用量可以增加釉面的光洁感和平整感,但是用量过多则会导致过于光滑,没有陶器的手感,用量不足则会使釉面手感粗糙,滑石和坭兴陶土也需要十分具体的称量,因为它们的用量的细微差别会使釉色产生偏差;球磨环节则需要注意球、料、水的比例,一般球︰料︰水≈2︰1︰0.8,其中可以有0.1—0.2的误差,球磨时间根据料的多少决定,料越多球磨时间越长,料与球磨时间的比例控制在1千克/6—8小时,这一比例也会因为球磨机的功率和球磨罐的质量而有一些变化;细度检测环节一般只需手感检测即可,陶釉对细度的要求不做具体的严格要求。除铁环节可以使釉料的色泽更加纯正,减少铁质对油料色泽的影响,但是对陶釉来说这一环节不一定很严格,因为釉料中的铁杂质所对颜色产生的影响反而是陶的质地更加突出,虽然不必故意加入铁的成分,但是除了一些冷色,如蓝色系、绿色系、白色系以外,釉料中微量的铁所产生的则使釉料色泽有一种厚重感;过筛环节是为了使釉料细度200目以上;陈腐环节主要是对釉料进行调节,使其粘性更强以便施釉。
本釉料的烧成温度是1080℃±25℃,与坭兴陶的烧成温度完全一致。为了达到较低的烧成温度,本釉料以长石为熔融剂,硼酸钙、石灰石为助熔剂,石英和长石构成了透明釉的主体,硼酸钙提供的硼元素为矿化剂,维罗土和滑石则是调节釉的透明度和光洁度,使得釉有比较好的手感,区别于熔块釉的覆盖性和光洁感,突出陶的质感美,坭兴陶土在本釉料中起到药引的作用,既可以提供适量的铁元素,也可以使釉面与坭兴陶胚体的结合性更好。
实施例1
准确称量硼酸钙34克、石英20克、长石23克、石灰石10克、维罗土6克、滑石5克、坭兴陶土2克混合放入球磨机中加入80克水,进行球磨45分钟,球︰料≈2︰1。检查有料细度后,过200目筛,陈腐。将该经过陈腐后的生料釉喷涂在坭兴陶胚体表面,在1080℃烧成。
经国家陶瓷质量产品监督检测中心(江西)按照GB/T3532—2002《与食物接触的陶瓷制品铅、镉溶出量允许极限》标准进行检测,本釉的铅溶出量为<0.1mg/L,镉溶出量为<0.01mg/L,国家标准为铅溶出量0.5mg/L镉溶出量0.25mg/L,远低于国家标准,本检测数据为仪器检测线的极低值和未检出值;抗热震性按照GB/T3298—2008进行检测,结果为180℃/20℃热交换一次,所有样品均未开裂,符合国家标准;吸水率按照GB/T3298—2011进行检测,结果为10.01%,符合国家日用精陶标准;釉面硬度按照GB/T3731—1999进行检测,结果为5.1GPa,符合国家日用精陶标准。
各氧化物原料均为市售普通化学试剂,硼酸钙为土耳其进口,含量98%,购自山东济南辉煌化工有限公司;长石产自广西容县;石英、维罗土、石灰石均产自广西南宁周边;坭兴陶土产自广西钦州。
Claims (1)
1.一种坭兴陶专用透明生料釉,其特征在于该生料釉由下列重量百分比的原料经加水、球磨、过筛、陈腐制成:
硼酸钙34%、石英20%、长石23%、石灰石10%、维罗土6%、滑石5%、坭兴陶土2%。