CN105293994B - A kind of Colorful Asphalt Pavement mixture - Google Patents
A kind of Colorful Asphalt Pavement mixture Download PDFInfo
- Publication number
- CN105293994B CN105293994B CN201510722599.4A CN201510722599A CN105293994B CN 105293994 B CN105293994 B CN 105293994B CN 201510722599 A CN201510722599 A CN 201510722599A CN 105293994 B CN105293994 B CN 105293994B
- Authority
- CN
- China
- Prior art keywords
- parts
- asphalt pavement
- pavement mixture
- colorful asphalt
- pigment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to a kind of Colorful Asphalt Pavement mixture, include the raw material of following parts by weight：20 40 parts of base oil, 15 40 parts of Petropols, 10 25 parts of terpene resin, 2 10 parts of modifying agent, 1 15 parts of inorganic pigment, 15 30 parts of pressure-sensitive diluent.This material only needs simply bucket packaging or tank car transport in transit, using front and rear without heating, it can be used at normal temperatures with building stones mix, then the paving of road surface, roller compaction construction are carried out, the preparation process of chromatic bitumen mixture is greatly simplify, the extremely simple convenience for becoming the construction of colored road surface；This material has voltage-dependent characteristic, is rolled by road roller, vehicular traffic, improves the adhesion strength of asphalt and aggregate, improves compound self-strength.
Description
（One）Technical field
The present invention relates to a kind of cold colored pressure-sensitive modified pitch of construction, and in particular to a kind of Colorful Asphalt Pavement mixture.
（Two）Background technology
In recent years, country with improve city function, improve human settlement, continue city context, lifting city taste, beautification
Urban landscape, to highlight city characteristic be focus, improves constantly afforestation planning, builds and managerial skills, economical fast
While speed increases, make great efforts to promote the harmonious development of human and environment, city taste is further lifted.Road is as urban construction
A part, its beautification degree will more strengthen.And typically now paved the way using color asphalt, but existing color asphalt
Need to heat repeatedly during use, have a strong impact on its using effect, it is necessary to improve.
（Three）The content of the invention
The present invention is in order to make up the deficiencies in the prior art, there is provided a kind of Colorful Asphalt Pavement mixture, the material normal temperature
Be flowable liquid down, can normal temperature transport, can be used at normal temperatures with building stones mix, then progress road surface paves, rolled
Construction, realizes cold mixing cold-application, greatly simplify the paving process of Colorful Asphalt Pavement, the construction of colored road surface is become more
It is simple and convenient.
The present invention is achieved through the following technical solutions：
A kind of Colorful Asphalt Pavement mixture, it is characterized in that：Include the raw material of following parts by weight：
Base oil 20-40 parts, 40 parts of Petropols 15-, 10-25 parts of terpene resin, modifying agent 2-10 parts, inorganic face
Expect 1-15 parts, pressure-sensitive diluent 15-30 parts.
The Colorful Asphalt Pavement mixture of the present invention, base oil are at least one of aromatic naphtha, viscous crude, distillate.
The Colorful Asphalt Pavement mixture of the present invention, Petropols are at least one in group aliphatic resin, aromatic resin
Kind.
The Colorful Asphalt Pavement mixture of the present invention, modifying agent is SBS
（SBS）, powder styrene butadiene rubber（SBR）At least one of.
The Colorful Asphalt Pavement mixture of the present invention, inorganic pigment are iron oxide red pigment, chrome green pigment, iron green pigment, titanium white
At least one of pigment, chrome yellow.
The Colorful Asphalt Pavement mixture of the present invention, pressure-sensitive diluent are polyalcohol, polyethers, acetate esters one kind or more
Kind.
A kind of preparation method of Colorful Asphalt Pavement mixture described in basis, it is characterised in that：Comprise the following steps：Will
Base oil is heated to 160-180 DEG C, then adds Petropols, terpene resin, modifying agent stirring, then cools to 120-140 DEG C,
Then pressure-sensitive diluent stirring is added, pigment is finally added as needed on and is stirred for can obtain product.
Beneficial effects of the present invention：This material only needs simply bucket packaging or tank car transport in transit, uses
It is front and rear to be used at normal temperatures with building stones mix, then carry out the paving of road surface, roller compaction construction without heating, it is greatly simple
The preparation process of chromatic bitumen mixture is changed, the extremely simple convenience for becoming the construction of colored road surface；This material has pressure-sensitive
Performance, rolled by road roller, vehicular traffic, a pressure-sensitive dose of part is gathered materials absorption, and the bonding for improving asphalt and aggregate is strong
Degree, a part are converted into macromolecular by rolling work(by small molecule, improve compound self-strength, also partly vapor away, grind
Surface layer will be more and more firm with the bonding of underpavement during pressure.
（Four）Embodiment
Embodiment 1：
The preparation method of Colorful Asphalt Pavement mixture, comprises the following steps：
20kg aromatic naphtha is first heated to 160 DEG C, then adds 15kg group aliphatic resin C5,10kg terpene resin, 2kg benzene
Ethylene-butadiene-styrene block copolymer（SBS）Stir 2h, then cool to 120 DEG C, then add 15kg polyalcohols (such as 1,
2- propane diols) stirring 1h, finally it is added as needed on 1kg iron oxide red pigments and is stirred for 1h can obtain product.
Embodiment 2：
The preparation method of Colorful Asphalt Pavement mixture, comprises the following steps：
First by 40kg heavy oil heatings to 180 DEG C, 40kg aromatic resin C9,25kg terpene resin, 10kg powder are then added
Last butadiene-styrene rubber（SBR）2h is stirred, then cools to 140 DEG C, 15kg polyethers stirring 2h is then added, is finally added as needed on
15kg iron green pigments are stirred for 1h and can obtain product.
Embodiment 3：
The preparation method of Colorful Asphalt Pavement mixture, comprises the following steps：
30kg distillates are first heated to 170 DEG C, then add 10kg aromatic resin C9,20kg group aliphatic resins C5,
20kg terpene resins, 4kg powder styrene butadiene rubbers（SBR）, 4kg SBSs（SBS）Stirring
2h, then 130 DEG C are cooled to, 25kg ethyl acetate stirring 2h is then added, 10kg chrome green pigment is finally added as needed on and stirs again
Mix 1h and can obtain product.
Embodiment 4：
The preparation method of Colorful Asphalt Pavement mixture, comprises the following steps：
First by 10kg distillates, 10kg heavy oil heatings to 170 DEG C, 10kg aromatic resins C9,20kg fat are then added
Hydroxy-aromatic resin C5,20kg terpene resin, 4kg powder styrene butadiene rubbers（SBR）, 4kg SBSs
（SBS）2h is stirred, then cools to 130 DEG C, 10kg acetic acid esters, 5kg polyethers stirring 2h is then added, is finally added as needed on
8kg titanium dioxide pigments are stirred for 1h and can obtain product.
Embodiment 5：
The preparation method of Colorful Asphalt Pavement mixture, comprises the following steps：
10kg distillates, 10kg viscous crude, 10kg aromatic naphtha are first heated to 170 DEG C, then add 10kg aromatic resins
C9,20kg group aliphatic resin C5,20kg terpene resin, 4kg powder styrene butadiene rubbers（SBR）, 4kg s-B-Ss
Block copolymer（SBS）Stir 2h, then cool to 130 DEG C, then add 10kg acetic acid esters, 5kg polyethers, 5kg polyalcohols (such as 1,
2- propane diols) stirring 2h, finally it is added as needed on 8kg chrome yellows and is stirred for 1h can obtain product.
Embodiment 6：
The preparation method of Colorful Asphalt Pavement mixture, comprises the following steps：
10kg distillates, 15kg viscous crude, 10kg aromatic naphtha are first heated to 170 DEG C, then add 10kg aromatic resins
C9,20kg group aliphatic resin C5,20kg terpene resin, 4kg powder styrene butadiene rubbers（SBR）, 4kg s-B-Ss
Block copolymer（SBS）Stir 2h, then cool to 130 DEG C, then add 10kg acetic acid esters, 5kg polyethers, 5kg polyalcohols (such as 1,
2- propane diols) stirring 2h, finally it is added as needed on 8kg chrome yellows, 1kg iron oxide red pigments are stirred for 1h and can obtain product.
Embodiment 7
4kg chrome yellows, 1kg iron oxide red pigments, 2kg chrome green pigment are added, other are same as Example 1.
Embodiment 8：
2kg iron oxide red pigments, 2kg chrome green pigment, 2kg iron green pigment, 1kg titanium dioxide pigments, 1kg chrome yellows are added, other
It is same as Example 1.
Embodiment 9：
The preparation method of Colorful Asphalt Pavement mixture, comprises the following steps：
20kg aromatic naphtha is first heated to 160 DEG C, then adds 15kg group aliphatic resin C5,10kg terpene resin, 2kg benzene
Ethylene-butadiene-styrene block copolymer（SBS）Stir 2h, then cool to 120 DEG C, then add 15kg polyalcohols (such as 1,
2- propane diols), broker wall bee pollen 2kg and clear cream stirring 1h, be finally added as needed on 1kg iron oxide red pigments and be stirred for 1h
Obtain product.
The Modified Bitumen Pavement material of the embodiment greatly reduces its toxicity to human body, and does not influence modified pitch road
The using effect of plane materiel material.
Embodiment 10：
Table 1：The technical indicator of the cold colored pressure-sensitive modified asphalt material of construction
Claims (2)
- A kind of 1. preparation method of Colorful Asphalt Pavement mixture, it is characterised in that：Colorful Asphalt Pavement mixture includes following The raw material of parts by weight：Base oil 20-40 parts, 40 parts of Petropols 15-, 10-25 parts of terpene resin, modifying agent 2-10 parts, inorganic pigment 1- 15 parts, pressure-sensitive diluent 15-30 parts；Base oil is at least one of aromatic naphtha, viscous crude, distillate；Petropols are at least one of group aliphatic resin, aromatic resin；Modifying agent is SBS（SBS）, powder styrene butadiene rubber（SBR）In at least one Kind；Pressure-sensitive diluent is polyalcohol, polyethers, acetate esters one or more；The preparation method of the Colorful Asphalt Pavement mixture：Comprise the following steps：Base oil is heated to 160-180 DEG C, then Petropols, terpene resin, modifying agent stirring are added, then cools to 120-140 DEG C, then adds pressure-sensitive diluent stirring, most After be added as needed on pigment and be stirred for can obtain product.
- 2. the preparation method of Colorful Asphalt Pavement mixture according to claim 1, it is characterised in that：Inorganic pigment is iron At least one of red, chrome green pigment, iron green pigment, titanium dioxide pigment, chrome yellow.