CN108440976A - A kind of high temperature resistant color asphalt - Google Patents
A kind of high temperature resistant color asphalt Download PDFInfo
- Publication number
- CN108440976A CN108440976A CN201810290047.4A CN201810290047A CN108440976A CN 108440976 A CN108440976 A CN 108440976A CN 201810290047 A CN201810290047 A CN 201810290047A CN 108440976 A CN108440976 A CN 108440976A
- Authority
- CN
- China
- Prior art keywords
- parts
- high temperature
- pigment
- temperature resistant
- petropols
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of high temperature resistant color asphalts, are made of the raw material of following parts by weight：30 38 parts of Petropols, 35 40 parts of aromatic naphtha, 10 20 parts of clay, 10 14 parts of rubber powder, 3 10 parts of polyurethane resin, 10 20 parts of inorganic pigment.The present invention can produce the color asphalt of various colors, improve vision, can be widely used in the different places such as street, pavement and landscape road, can not only meet the needs of various places, while can also beautify the environment.The present invention realizes and the excellent color asphalt product of high temperature resistance is prepared at lower cost by being formulated global design.
Description
Technical field
The present invention relates to technical field of road engineering, more particularly to a kind of high temperature resistant color asphalt.
Background technology
Elasticity of the Colorful Asphalt Pavement with asphalt concrete is strong, damping strong and is easy to clean the formedness such as flushing
Can be outer, the monotonicity of plain asphalt road surface black is further improved, can be collocated with each other, coordinate with the building of surrounding, landscape, have
Apparent Landscape benefit.In addition, color asphalt increasingly obtains the organization and management effect of traffic the attention of people.Different colours
Bituminous paving, the recognition effect of driver can be improved, and the attention of driver can also be made more to concentrate, to play
Induce wagon flow, safe driving, the effect for making traffic administration intuitively change.It, can be with such as in the multiple location of Urban Road Traffic Accidents
Driver is intuitively reminded note that driving a vehicle with caution, to a certain extent than vertical traffic sign in making red or yellow road surface
And stroke markings are more preferable on track.
But the performance of existing color asphalt is still to be improved.
Invention content
In order to make up the defect of prior art, the present invention provides a kind of high temperature resistant color asphalt.
The technical problems to be solved by the invention are achieved by the following technical programs：
A kind of high temperature resistant color asphalt, is made of the raw material of following parts by weight：30-38 parts of Petropols, aromatic naphtha 35-40
Part, 10-20 parts of clay, 10-14 parts of rubber powder, 3-10 parts of polyurethane resin, 10-20 parts of inorganic pigment.
Further, inorganic pigment be iron oxide red pigment, chrome green pigment, iron green pigment, titanium dioxide pigment, in chrome yellow extremely
Few one kind.
Further, the preparation method of the Petropols is：（1）With ethylene unit by-product pyrolysis c9 fraction in vacuum degree
, by rectification under vacuum, to intercept boiling point in 100-150 DEG C of C9 components as raw material A under the conditions of -0.085MPa；With ethylene unit
By-product pyrolysis c9 fraction or pyrolysis C 5 are existed under the conditions of vacuum degree is -0.090MPa by rectification under vacuum, interception boiling point
It is raw material B that 160-175 DEG C of fraction, which obtains dicyclopentadiene DCPD enriched compositions,；Above-mentioned raw materials A and B in mass ratio 2-6: 1 is mixed
Conjunction obtains reaction raw materials C；（2）In the reaction kettle with forced circulation, the reaction raw materials C of said ratio is put into advance, is enabled anti-
It answers material to be reacted 25-30 hours under the conditions of 180-240 DEG C, obtains polymer fluid；（3）Above-mentioned polymer fluid is entered in insulation still,
The composite antioxidant for accounting for polymer fluid mass ratio 2~5 ‰ is put into again, and keeps the temperature 10-15 hours under the conditions of 180-200 DEG C；（4）It will
It is -0.07MPa that the polymer fluid that step (3) obtains, which delivers into top vacuum degree, and the desolventizing that 90~120 DEG C of tower top temperature evaporates tower
Interior carry out solvent removal, control reflux ratio are 2；Tower top obtains solvent of the boiling point at 85-200 DEG C, and bottom of tower obtains resin liquid；（5）
Above-mentioned resin liquid is input into the extracting of row steam distillation, top vacuum degree -0.0850MPa extracts several equal molecules by stripping
Oligomer of the amount less than 400 is to get to Petropols.
Further, preparation method includes the following steps：（1）Aromatic naphtha is added according to the parts by weight, is heated to
Under the conditions of 165-190 DEG C, rubber powder stirring melting is added, Petropols, polyurethane resin and clay are added after being completely dissolved, most
After inorganic pigment is added, be uniformly mixed.
The present invention has the advantages that：
The present invention can produce the color asphalt of various colors, improve vision, can be widely used in street, pavement and
The different places such as landscape road can not only meet the needs of various places, while can also beautify the environment.
The present invention realizes and the excellent colored drip of high temperature resistance is prepared at lower cost by being formulated global design
Green product.
Specific implementation mode
With reference to embodiment, the present invention will be described in detail, and embodiment is only the preferred embodiment of the present invention,
It is not limitation of the invention.
Embodiment 1
A kind of high temperature resistant color asphalt, is made of the raw material of following parts by weight：32 parts of Petropols, 38 parts of aromatic naphtha, pottery
15 parts of soil, 12 parts of rubber powder, 8 parts of polyurethane resin, 15 parts of inorganic pigment.
Wherein, inorganic pigment is iron oxide red pigment.
Preparation method includes the following steps：（1）Aromatic naphtha is added according to the parts by weight, is heated to 165-190 DEG C
Under the conditions of, rubber powder stirring melting is added, Petropols, polyurethane resin and clay are added after being completely dissolved, is eventually adding nothing
Machine pigment, is uniformly mixed.
Embodiment 2
A kind of high temperature resistant color asphalt, is made of the raw material of following parts by weight：30 parts of Petropols, 35 parts of aromatic naphtha, pottery
10 parts of soil, 10 parts of rubber powder, 3 parts of polyurethane resin, 10 parts of inorganic pigment.
Wherein, inorganic pigment is chrome green pigment.
Preparation method includes the following steps：（1）Aromatic naphtha is added according to the parts by weight, is heated to 165-190 DEG C
Under the conditions of, rubber powder stirring melting is added, Petropols, polyurethane resin and clay are added after being completely dissolved, is eventually adding nothing
Machine pigment, is uniformly mixed.
Embodiment 3
A kind of high temperature resistant color asphalt, is made of the raw material of following parts by weight：38 parts of Petropols, 40 parts of aromatic naphtha, pottery
20 parts of soil, 14 parts of rubber powder, 10 parts of polyurethane resin, 20 parts of inorganic pigment.
Wherein, inorganic pigment is titanium dioxide pigment.
Preparation method includes the following steps：（1）Aromatic naphtha is added according to the parts by weight, is heated to 165-190 DEG C
Under the conditions of, rubber powder stirring melting is added, Petropols, polyurethane resin and clay are added after being completely dissolved, is eventually adding nothing
Machine pigment, is uniformly mixed.
Embodiments of the present invention above described embodiment only expresses, the description thereof is more specific and detailed, but can not
Therefore it is interpreted as the limitation to the scope of the claims of the present invention, as long as skill obtained in the form of equivalent substitutions or equivalent transformations
Art scheme should all be fallen within the scope and spirit of the invention.
Claims (4)
1. a kind of high temperature resistant color asphalt, is made of the raw material of following parts by weight：30-38 parts of Petropols, aromatic naphtha 35-
40 parts, 10-20 parts of clay, 10-14 parts of rubber powder, 3-10 parts of polyurethane resin, 10-20 parts of inorganic pigment.
2. high temperature resistant color asphalt as described in claim 1, which is characterized in that the inorganic pigment is iron oxide red pigment, chrome green
At least one of pigment, iron green pigment, titanium dioxide pigment, chrome yellow.
3. high temperature resistant color asphalt as described in claim 1, which is characterized in that the preparation method of the Petropols is：（1）
With ethylene unit by-product pyrolysis c9 fraction by rectification under vacuum under the conditions of vacuum degree is -0.085MPa, interception boiling point is in 100-
150 DEG C of C9 components are as raw material A；Be in vacuum degree with ethylene unit by-product pyrolysis c9 fraction or pyrolysis C 5-
Dicyclopentadiene DCPD enriched compositions are obtained in 160-175 DEG C of fraction by rectification under vacuum, interception boiling point under the conditions of 0.090MPa
For raw material B；Above-mentioned raw materials A and B in mass ratio 2-6: 1 is mixed to get reaction raw materials C；（2）In the reaction with forced circulation
In kettle, the reaction raw materials C of said ratio is put into advance, enables reaction mass be reacted 25-30 hours under the conditions of 180-240 DEG C, obtains
To polymer fluid；（3）Above-mentioned polymer fluid is entered in insulation still, then puts into the composite antioxidant for accounting for polymer fluid mass ratio 2~5 ‰,
And keep the temperature 10-15 hours under the conditions of 180-200 DEG C；（4）The polymer fluid that step (3) obtains is delivered into top vacuum degree
For -0.07MPa, the desolventizing that 90~120 DEG C of tower top temperature, which evaporates, carries out solvent removal in tower, control reflux ratio is 2；Tower top obtains
Solvent of the boiling point at 85-200 DEG C, bottom of tower obtains resin liquid；（5）Above-mentioned resin liquid is input into the extracting of row steam distillation, tower top
Vacuum degree -0.0850MPa extracts oligomer of the number-average molecular weight less than 400 to get to Petropols by stripping.
4. high temperature resistant color asphalt as described in claim 1, which is characterized in that preparation method includes the following steps：（1）It presses
Aromatic naphtha is added according to the parts by weight, is heated under the conditions of 165-190 DEG C, rubber powder stirring melting is added, after being completely dissolved
Petropols, polyurethane resin and clay is added, is eventually adding inorganic pigment, is uniformly mixed.