CN108034268A - Asphalt cold repairing liquid and preparation method thereof - Google Patents
Asphalt cold repairing liquid and preparation method thereof Download PDFInfo
- Publication number
- CN108034268A CN108034268A CN201711430772.9A CN201711430772A CN108034268A CN 108034268 A CN108034268 A CN 108034268A CN 201711430772 A CN201711430772 A CN 201711430772A CN 108034268 A CN108034268 A CN 108034268A
- Authority
- CN
- China
- Prior art keywords
- cold repairing
- asphalt
- repairing liquid
- asphalt cold
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of asphalt cold repairing liquid, it is related to highway engineering technical field.Asphalt cold repairing liquid is made of matrix asphalt, diluent, styrene butadiene styrene block copolymer, additive, the preparation method of asphalt cold repairing liquid is by weighing raw material and being stirred, subsequent centering production product is sheared, then carry out insulation development and modified pitch is made, and then prepare additive, obtained additive, modified pitch and diluent are placed in container to be sheared, asphalt cold repairing liquid is prepared.The present invention provides a kind of asphalt cold repairing liquid and preparation method thereof, reduces asphalt cold repairing liquid production cost, and asphalt cold repairing liquid has preferable adhesion, and the cold repairing asphalt mixture being prepared has good construction workability and water stability.
Description
Technical field
The invention belongs to highway engineering technical field, is related to a kind of asphalt cold repairing liquid and preparation method thereof.
Background technology
In China, high-grade highway use scope is wider, and what is generally used is all the structure type of bituminous paving.Pitch
Road surface compared with cement pavement, have the characteristics that the construction time is short, noise is small, ride comfort, repairing it is convenient.But bituminous paving
Under traffic load and natural environment collective effect, some diseases such as track, crack, peeling easily occur.How to these diseases
Evil road surface carries out rapid-maintenance and open to traffic is highly important as early as possible.
Cold mixing cold-application technology is a huge progress of Chinese road repair technology, but compared with American-European countries, in
State's starting is than later, and the understanding to cold repairing asphalt mixture product is derived from imported product, its research is in Introduced From Abroad product
It is inchoate afterwards.Due to external product costly, some colleges and universities and business tie-up start to carry out cold repairing asphalt mixture
Research and development.Some experts of colleges and universities start to develop cold repairing asphalt mixture and it are applied in engineering, whether exist
Research or application all have accumulated substantial amounts of invaluable experience, the rapid development of China's Asphalt Pavement Damage repairing technique, economic benefit
With environmental benefit highly significant.But the performance of China's cold repairing asphalt mixture still has the deficiency of many so far, some are crucial
Property technology is not resolved, and construction workability and initial strength there is a problem, so this just needs to be constantly working into one
Step improves cold repairing asphalt mixture.
Cold repairing asphalt mixture performance depends primarily upon asphalt cold repairing liquid, and presently disclosed asphalt cold repairing liquid patent is seldom,
General cold repairing asphalt mixture publication is relatively more, so the research and development of asphalt cold repairing liquid are most important.Asphalt cold repairing liquid is by dripping
Green grass or young crops, diluent, additive, solvent etc. are prepared under certain preparation process condition.
Asphalt cold repairing liquid usually has three types, is respectively solvent-borne type, response type and emulsified asphalt type.Prepared by response type
Mixture intensity is higher, but operating difficulties, and difficulty is brought to construction.The mixture demulsification time prepared by emulsified asphalt type is not allowed
It is easy to control, cause difficulty to storing and reaching the shaping strength time.Solvent-borne type cold repairing asphalt mixture can be under room temperature, low temperature
Storage and construction, it is on-demand from seasonal effect, save material.Temperature is relatively low in preparation and work progress, not only saves energy
Source can also reduce environmental pollution.Therefore, in terms of maintenance of surface, solvent-borne type cold repairing asphalt mixture has good prospect.
Domestic common cold repairing additive has two kinds of an external import and self-control, external product superior performance, but expensive,
It is not readily available, often construction workability and initial strength can not balance mixture prepared by Domestic Additives very well, and water is stablized
Property and cohesiveness are poor.
Asphalt cold repairing liquid is to be prepared by pitch, diluent, additive under certain preparation process, it is main former
Reason be by adding diluent, improving the workability of cold repairing asphalt mixture, in use, as diluent volatilizees,
The strength of materials strengthens, water stability enhancing.Therefore the asphalt cold repairing liquid prepared will have a good water stability, workability and strong
Degree will be got well, and just can guarantee that the performance that asphalt cold repairing liquid has had.
The content of the invention
To achieve the above object, the present invention provides a kind of asphalt cold repairing liquid and preparation method thereof, solves in the prior art
The problem of asphalt cold repairing liquid construction workability and initial strength can not balance very well, water stability and poor cohesiveness.
The technical solution adopted in the present invention is asphalt cold repairing liquid, according to mass fraction, by 100 parts of matrix asphalt,
7~15 parts of 20~35 parts of diluent, 2~4 parts of Styrene-Butadiene-Styrene Block Copolymer, additive compositions.
Further, the diluent is 0# diesel oil.
Further, the additive by 2~4.5 parts C5C9 copolymer resinses, 2~4.5 parts of ethene-vinyl acetate is total to
Polymers, 2~4.5 parts of solvent, 0.5~0.8 part of antistripping agent composition.
Further, the solvent is oleic acid.
Further, the antistripping agent is PM-JL-06A type asphalt anti-stripping agents.
Another technical solution of the present invention is that the preparation method of asphalt cold repairing liquid, follows the steps below:
Load weighted matrix asphalt, Styrene-Butadiene-Styrene Block Copolymer, be added sequentially to by step 1
In reaction vessel, 150 ± 5 DEG C of temperature, heats and constantly stirs 0.5h with iron staff;
After the completion of step 2, step 1, reaction vessel is placed under high speed shear instrument, rotating speed 6000r/min, when shearing reacts
160 ± 5 DEG C, shear time 1h of vessel temp, step 2 whole process utilize electric furnace, thermometer temperature control;
After the completion of step 3, step 2, reaction vessel is taken out, after closed, is put into baking oven, 150 ± 5 DEG C of temperature, insulation
Time 0.5h, prepared by modified pitch completes;
C5C9 copolymer resinses, ethylene-vinyl acetate copolymer, be placed in reaction vessel by step 4, and is placed on constant temperature and is
2h in 150 ± 0.5 DEG C of baking oven, takes out reaction vessel, is directly added into solvent and antistripping agent and stirs evenly, be prepared into addition
Agent, additive are in yellow, viscous;
Step 5, by the modified pitch of preparation, be cooled to 135 ± 5 DEG C additive and diluent it is placed in the vessel, will be anti-
Container is answered to be placed under high speed shear instrument, rotating speed 4000r/min, 80 ± 5 DEG C, shear time 20min of reaction vessel temperature during shearing,
Asphalt cold repairing liquid is prepared using electric furnace, thermometer temperature control in step 4 whole process.
Further, the step 2 high speed boxshear apparatus model:LDGJQ—Ⅱ.
The beneficial effects of the invention are as follows a kind of asphalt cold repairing liquid and preparation method thereof is provided, the life of asphalt cold repairing liquid is reduced
Cost is produced, which has preferable adhesion, the cold repairing asphalt mixture construction workability and water stability of preparation
Preferably.
Brief description of the drawings
In order to illustrate more clearly about the embodiment of the present invention or technical scheme of the prior art, below will be to embodiment or existing
There is attached drawing needed in technology description to be briefly described, it should be apparent that, drawings in the following description are only this
Some embodiments of invention, for those of ordinary skill in the art, without creative efforts, can be with
Other attached drawings are obtained according to these attached drawings.
Fig. 1 is additive figure;
Fig. 2 is asphalt cold repairing liquid figure;
Fig. 3 is the preparation flow figure of asphalt cold repairing liquid.
Embodiment
Below in conjunction with the attached drawing in the embodiment of the present invention, the technical solution in the embodiment of the present invention is carried out clear, complete
Site preparation describes, it is clear that described embodiment is only part of the embodiment of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, those of ordinary skill in the art are obtained every other without making creative work
Embodiment, belongs to the scope of protection of the invention.
A kind of asphalt cold repairing liquid according to mass fraction by 100 parts of matrix asphalt, 20~35 parts of diluent, styrene-
2~4 parts of butadiene-styrene block copolymer (SBS), 7~15 parts of additive;Wherein additive is total to by 2~4.5 parts of C5C9
Poly resin, 2~4.5 parts of ethylene-vinyl acetate copolymer (EVA), 2~4.5 parts of solvent, 0.5~0.8 part of antistripping agent
Composition.
Matrix asphalt will meet code requirement as the main material for preparing asphalt cold repairing liquid, its technical indicator.
1 matrix pitch technical indicator of table
0# diesel oil can reduce asphalt viscosity, it is had certain mobility under room temperature, low temperature as diluent.
Since diesel oil volatilization is slow so that the cold repairing asphalt mixture storage time length of preparation.
SBS has soft segment, and intermolecular distance is larger, infiltration and SBS strand of the lightweight oil into SBS molecular networks
Diffusion of the section into pitch all relatively easily occurs, and makes the ratio that can become the part aromatic hydrocarbons heavy constituent of " constraint solvent " in residual oil
Rate increases, moreover, SBS can effectively absorb a part of saturation component (including wax point), so it can reduce the sense of albino bitumen
Warm nature.In pavement usage temperature range, SBS will keep very high elasticity in itself, can bear larger deformation without destroyed,
Part strain energy has been effectively absorbed at a lower temperature, so that modified pitch, has good low-temperature cracking-resistance.The opposing party
Face, SBS will have excellent dissolubility, intermiscibility, cementability, water resistance, weatherability, heat endurance, have chemistry to soda acid
Stability, with natural rubber (NR), synthetic rubber, polyethylene, styrene-isoprene-styrene block copolymer (SIS),
Styrene block copolymer (SEBS), EVA etc. will have good compatibility, to have peel off adhesive strength it is high, fast viscosity is good, be bonded
Performance is stable, melt viscosity is appropriate, heat-resist, good with the compatibility of high polymer matrix, the good characteristic of viscosity, have it is prominent just
Sticky energy.The SBS chosen herein has the characteristic of rubber and plastics, preferable with macromolecule resin compatibility.Itself again with compared with
The performances such as elasticity well, stretch-proof, can effectively improve the high-temperature stability and low-temperature cracking-resistance of cementitious matter.The high score chosen herein
The basic technical indicator of sub- Polymer SBS, is shown in Table 2.
2 SBS technical indicator tables of table
Numbering | Detection project | Unit | Inspection result |
1 | Fugitive constituent | % (m/m) | 0.3 |
2 | 300% stretches pulling force surely | (MPa) | 3.2 |
3 | Tensile strength | (MPa) | 20 |
4 | Elongation rate of tensile failure | (%) | 750 |
5 | Break permanent deformation | (%) | 18 |
6 | Melt flow rate (MFR) | (g/min) | 1 |
In practical applications, resinae is used not only to make cut-back asphalt that there is well first to stick as tackifier mostly
Property, and cohesive force of the asphalt cold repairing liquid to stone surface can be improved.In addition, tackifier can reduce asphalt cold repairing liquid surface
Power, soaks stone surface, produces adhesive force by diffusion into the surface and internal penetration, improves adhesion, extends asphalt cold repairing liquid
Stickiness working life and retention period.Reality of the performances such as good compatibility, increasing stick, heat resistance, water-fast and acid and alkali-resistance in pitch
Also it is very crucial in, C5C9 copolymer resinses, the resin extracted in oil;Relative density is generally 0.97-1.07;Softening point one
As be 90-140 DEG C;Chromatic value is less than normal, is generally less than 8;With good adhesive property, it has in adhesive widely should
With;It is good with phenolic resin, acrylic resin, natural rubber, synthetic rubber compatibility, it is especially compatible with butadiene-styrene rubber (SBR)
Property is excellent;Anti-aging property is preferable;Acetone, industrial naptha etc. are dissolved in, has preferable compatibility with most of organic solvent.Herein
The particular technique index of C5C9 copolymer resinses is chosen, is shown in Table 3.
3 C5C9 copolymer resins technical indicator tables of table
Numbering | Detection project | Unit | Testing result |
1 | Color number | YI | 1 |
Density | g/cm3 | 0.98 | |
2 | Softening point (ring and ball method) | ℃ | 103.1 |
3 | Acid number | mgKOH/g | 0.02 |
4 | Bromine number | gBr/100g | 1.13 |
5 | Melt viscosity | (190℃)m.Pa.s | 147 |
EVA is the copolymer of ethene and vinyl acetate, its property is shown huge with vinyl acetic acid (VA) changes of contents
Big difference, when VA contents are high, EVA is similar to rubber, is then similar to polyethylene (PE) when VA contents are low, in EVA in polymerization process
Vinegar key is introduced in macromolecular, thus there is internal plasticization.Larger side base is carried on EVA molecular cell segments, is increased
Intermolecular distance, is conducive to sub-chain motion, thus pliability is preferable, has to the high temperature performance of cold repairing asphalt mixture aobvious
The improvement of work.EVA simultaneously has preferable bond performance, and relative density is generally 0.92-0.95;Softening point is generally 63-64
℃;Crystallinity is low, and elasticity is big, in rubber-like, containing enough polyethylene crystallizations with physical crosslinking effect, has thermoplasticity
The characteristics of elastomer;With good flexibility, still there is preferable pliability at -50 DEG C.The transparency and glossiness are good, have good
Chemical stability well, resistance to ag(e)ing, nontoxicity.The particular technique index of the EVA chosen herein, is shown in Table 4.
4 EVA technology index table of table
Numbering | Detection project | Unit | Inspection result |
1 | Density | g/cm3 | 0.95 |
2 | Softening point (ring and ball method) | ℃ | 64 |
3 | Melt flow index | g/10min | 52 |
4 | VAC contents | % | 40 |
5 | Color | Range estimation | Water white transparency |
Since C5C9 copolymer resinses and EVA softening points are higher, it is directly added into asphalt cold repairing liquid and is unfavorable for the molten of resin
Solution, when shearing, are easily damaged instrument.The solvent selected herein is oleic acid, its molecular formula C18H34O2, it is colourless oil liquid, and
Selected solvent has lubricating action, it is possible to increase researches and develops the construction workability of product.
Antistripping agent selected by this paper resists for the commercially available PM-JL-06A types pitch of Jin Long Chemical Industry Science Co., Ltd of Shenzhen
Exfoliant, due to its special molecular structure, with asphalt cold repairing it is miscible after, the active group in molecule can make asphalt cold repairing liquid
Adsorption reaction occurs with mineral aggregate surface, asphalt cold repairing is improved by improving physics between pitch and mineral aggregate and chemisorbed power
Caking property between the adhesion and mixture particle of liquid and surface of aggregate, so that the water for strengthening cold repairing asphalt mixture is stablized
Property, the key technical indexes of antistripping agent is as shown in table 5.
5 antistripping agent the key technical indexes of table
Project | Index |
Appearance | Yellow powder |
Fusing point | 58~68 |
Density | 0.95~1.00g/cm3 |
Decomposition temperature (DEG C) | ﹥ 300 |
Dissolubility | There is good compatibility with hot-melt asphalt |
Security | It is safe and environment-friendly, nontoxic, free from extraneous odour, pollution-free, nonflammable |
Embodiment one
A kind of asphalt cold repairing liquid is made of according to mass fraction formula as below component:100 parts of matrix asphalt, 0# diesel oil
20 parts, 2 parts of Styrene-Butadiene-Styrene Block Copolymer (SBS), 7 parts of additive;Wherein additive is total to by 2 parts of C5C9
Poly resin, 2 parts of ethylene-vinyl acetate copolymer (EVA), 2 parts of oleic acid, 0.5 part of PM-JL-06A type asphalt anti-stripping agents
Composition.
Embodiment two
A kind of asphalt cold repairing liquid is made of according to mass fraction formula as below component:100 parts of matrix asphalt, 0# diesel oil
28 parts, 3 parts of Styrene-Butadiene-Styrene Block Copolymer (SBS), 11 parts of additive;Wherein additive is by 3.5 parts
C5C9 copolymer resinses, 3.5 parts of ethylene-vinyl acetate copolymer (EVA), 3.5 parts of oleic acid, the drip of 0.7 part of PM-JL-06A types
Blue or green antistripping agent composition.
Embodiment three
A kind of asphalt cold repairing liquid is made of according to mass fraction formula as below component:100 parts of matrix asphalt, 0# diesel oil
35 parts, 4 parts of Styrene-Butadiene-Styrene Block Copolymer (SBS), 15 parts of additive;Wherein additive is by 4.5 parts
C5C9 copolymer resinses, 4.5 parts of ethylene-vinyl acetate copolymer (EVA), 4.5 parts of oleic acid, the drip of 0.8 part of PM-JL-06A types
Blue or green antistripping agent composition.
Example IV
A kind of asphalt cold repairing liquid is made of according to mass fraction formula as below component:100 parts of matrix asphalt, 0# diesel oil
30 parts, 2 parts of Styrene-Butadiene-Styrene Block Copolymer (SBS), 11.1 parts of additive;Wherein additive is by 3.5 parts
C5C9 copolymer resinses, 3.5 parts of ethylene-vinyl acetate copolymer (EVA), 3.5 parts of oleic acid, the drip of 0.6 part of PM-JL-06A types
Blue or green antistripping agent composition.
Embodiment five
A kind of preparation method of asphalt cold repairing liquid, its flow chart is as shown in figure 3, specifically follow the steps below:
1st, load weighted matrix asphalt, SBS are added sequentially in reaction vessel (quality is accurate to 0.1g), temperature
150 ± 5 DEG C, heat and constantly stir 0.5h with iron staff;
2nd, after the completion of step 1, reaction vessel is placed under high speed shear instrument, rotating speed 6000r/min, reaction vessel during shearing
160 ± 5 DEG C, shear time 1h of temperature, step 2 whole process utilize electric furnace, thermometer temperature control;
3rd, after the completion of step 2, reaction vessel is taken out, after closed, is put into baking oven, 150 ± 5 DEG C of temperature, soaking time
0.5h, prepared by modified pitch completes;
4th, C5C9 copolymer resinses, EVA are placed in reaction vessel, and are placed on 2h in the baking oven that constant temperature is 150 ± 0.5 DEG C,
Reaction vessel is taken out, solvent and antistripping agent is directly added into and stirs evenly, be prepared into additive, additive is in clear yellow viscous
Shape, as shown in Figure 1;
5th, by the modified pitch of preparation, be cooled to 135 ± 5 DEG C additive and diluent it is placed in the vessel, will reaction hold
Device is placed under high speed shear instrument, rotating speed 4000r/min, 80 ± 5 DEG C, shear time 20min of reaction vessel temperature, step during shearing
Using electric furnace, thermometer temperature control asphalt cold repairing liquid is prepared, as shown in Figure 2 in 4 whole process.
During factorial praluction, conventional equipment of producing modified asphalt, can be used for preparing asphalt cold repairing liquid, asphalt cold repairing after cleaning
Liquid is thick in black at normal temperatures, has mobility, brookfield viscosity value is in 1.8Pa.s~2.5Pa.s.Asphalt cold repairing liquid and collection
Material has good adhesion, it is possible to increase the intensity and water stability of mixture.
High speed shear instrument model:LDGJQ-II, is to be combined using ultrasonic fusing technology with tradition shearing, super
When sonic generator works, ultrasonic energy is passed to soldering tip and produce high vibration with cutting die by ultrasonic transducer and is rubbed
Wipe, so as to reach the effect of shearing, shear product is had the advantages that more attractive, more firm, production efficiency is more efficient quick.
The application method of asphalt cold repairing liquid, prepares cold repairing asphalt mixture:By preparing asphalt cold repairing and mixing with gathering materials to mix and stir
Material is closed, for pavement patching.Mixing cold repairing asphalt mixture using asphalt cold repairing liquid, to obtain optimal performance as follows:
Construction workability:In the winter time or low temperature season, cold repairing asphalt mixture are used for pot holes mend, and under the conditions of loose
(keeping 24h in -10 DEG C of insulating box) can easily mix and stir without obvious clustering phenomena.
Adhesion:Using the adhesion of water-boiling method test cold repairing asphalt mixture, experiment shows that adhesion grade is 5 grades,
Meet requirement.
Cohesiveness:By cold repairing asphalt mixture 800g load marshal piece mould in, in 4 DEG C of health-preserving chambers health 2~
3h, it is two-sided after taking-up respectively to hit 5 times in fact, test specimen is made, is placed on after the demoulding on standard screen, square sieve aperture, diameter 26.5mm, along sieve
Frame rolls around 20 times vertically, residual rate 99.5%.
Initial strength:Cold repairing asphalt mixture 1200g or so (height of specimen of being subject to meets 63.5 ± 1.3mm) is taken,
Load die trial under room temperature, it is two-sided respectively to hit 75 times in fact, then demould, carry out Marshall strength test.Initial Marshall intensity level
2.42KN。
Shaping strength:Claim cold repairing asphalt mixture 1180g or so be fitted at normal temperatures in die trial (using height of specimen as
Subject to 63.5mm), two sides is respectively hit real 50 times, and is placed on 24h in 110 DEG C of insulating boxs in a manner of side is erect with one piece of die trial,
Two sides is hit respectively again 25 times in fact, hit real later erect die trial and be placed on health 24h in room temperature, demould and be placed on 60 DEG C of thermostatted waters
Cage breeding gives birth to 30min, and measure Marshall intensity level is 4.87KN.
The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the scope of the present invention.It is all
Any modification, equivalent replacement, improvement and so within the spirit and principles in the present invention, are all contained in protection scope of the present invention
It is interior.
Claims (7)
1. asphalt cold repairing liquid, it is characterised in that according to mass fraction, by 100 parts of matrix asphalt, 20~35 parts of diluent,
7~15 parts of 2~4 parts of Styrene-Butadiene-Styrene Block Copolymer, additive compositions.
2. asphalt cold repairing liquid according to claim 1, it is characterised in that the diluent is 0# diesel oil.
3. asphalt cold repairing liquid according to claim 1, it is characterised in that the additive is copolymerized by 2~4.5 parts of C5C9
Resin, 2~4.5 parts of ethylene-vinyl acetate copolymer, 2~4.5 parts of solvent, 0.5~0.8 part of antistripping agent composition.
4. asphalt cold repairing liquid according to claim 3, it is characterised in that the solvent is oleic acid.
5. asphalt cold repairing liquid according to claim 3, it is characterised in that the antistripping agent is PM-JL-06A type pitches
Antistripping agent.
6. the preparation method of a kind of asphalt cold repairing liquid as described in claim 1-5 any one, it is characterised in that according to following
Step carries out:
Step 1, by load weighted matrix asphalt, Styrene-Butadiene-Styrene Block Copolymer be added sequentially to react
In container, 150 ± 5 DEG C of temperature, heats and constantly stirs 0.5h with iron staff;
After the completion of step 2, step 1, reaction vessel is placed under high speed shear instrument, rotating speed 6000r/min, reaction vessel during shearing
160 ± 5 DEG C, shear time 1h of temperature, step 2 whole process utilize electric furnace, thermometer temperature control;
After the completion of step 3, step 2, reaction vessel is taken out, after closed, is put into baking oven, 150 ± 5 DEG C of temperature, soaking time
0.5h, prepared by modified pitch completes;
C5C9 copolymer resinses, ethylene-vinyl acetate copolymer, be placed in reaction vessel by step 4, and be placed on constant temperature for 150 ±
2h in 0.5 DEG C of baking oven, takes out reaction vessel, is directly added into solvent and antistripping agent and stirs evenly, be prepared into additive, add
It is in yellow, viscous to add agent;
Step 5, by the modified pitch of preparation, be cooled to 135 ± 5 DEG C additive and diluent it is placed in the vessel, will reaction hold
Device is placed under high speed shear instrument, rotating speed 4000r/min, 80 ± 5 DEG C, shear time 20min of reaction vessel temperature, step during shearing
Asphalt cold repairing liquid is prepared using electric furnace, thermometer temperature control in 4 whole process.
7. the preparation method of asphalt cold repairing liquid according to claim 6, it is characterised in that the step 2 high speed shearing
Instrument model:LDGJQ—Ⅱ.