CN108641378A - A kind of anti-aging color asphalt - Google Patents
A kind of anti-aging color asphalt Download PDFInfo
- Publication number
- CN108641378A CN108641378A CN201810291470.6A CN201810291470A CN108641378A CN 108641378 A CN108641378 A CN 108641378A CN 201810291470 A CN201810291470 A CN 201810291470A CN 108641378 A CN108641378 A CN 108641378A
- Authority
- CN
- China
- Prior art keywords
- parts
- color asphalt
- petropols
- base oil
- pigment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of anti-aging color asphalts, are made of the raw material of following parts by weight:15 20 parts of C5 Petropols, 20 30 parts of C9 Petropols, 30 35 parts of base oil, 38 parts of styrene butadiene rubber powder, 5 12 parts of inorganic pigment, 0.8 1.2 parts of age resister.The present invention can produce the color asphalt of various colors, improve vision, can be widely used in the different places such as street, pavement and landscape road, can not only meet the needs of various places, while can also beautify the environment.The present invention realizes the color asphalt product for being prepared have excellent performance at lower cost by being formulated global design.
Description
Technical field
The present invention relates to technical field of road engineering, more particularly to a kind of anti-aging color asphalt.
Background technology
Elasticity of the Colorful Asphalt Pavement with asphalt concrete is strong, damping strong and is easy to clean the formedness such as flushing
Can be outer, the monotonicity of plain asphalt road surface black is further improved, can be collocated with each other, coordinate with the building of surrounding, landscape, have
Apparent Landscape benefit.In addition, color asphalt increasingly obtains the organization and management effect of traffic the attention of people.Different colours
Bituminous paving, the recognition effect of driver can be improved, and the attention of driver can also be made more to concentrate, to play
Induce wagon flow, safe driving, the effect for making traffic administration intuitively change.It, can be with such as in the multiple location of Urban Road Traffic Accidents
Driver is intuitively reminded note that driving a vehicle with caution, to a certain extent than vertical traffic sign in making red or yellow road surface
And stroke markings are more preferable on track.
But the performance of existing color asphalt is still to be improved.
Invention content
In order to make up the defect of prior art, the present invention provides a kind of anti-aging color asphalt.
The technical problems to be solved by the invention are achieved by the following technical programs:
A kind of anti-aging color asphalt, is made of the raw material of following parts by weight:15-20 parts of C5 Petropols, C9 oil
20-30 parts of resin, 30-35 parts of base oil, 3-8 parts of styrene butadiene rubber powder, 5-12 parts of inorganic pigment, 0.8-1.2 parts of age resister.
Further, the base oil is mineral substance oil.
Further, inorganic pigment be iron oxide red pigment, chrome green pigment, iron green pigment, titanium dioxide pigment, in chrome yellow extremely
Few one kind.
Further, the age resister is ESCALOL 567 and 2,6- di-t-butyl -4- methyl
Phenol is with mass ratio 2:1 mixes.
Further, preparation method includes the following steps:Base oil is added according to the parts by weight, is heated to 160-
Under the conditions of 190 DEG C, styrene butadiene rubber powder stirring melting is added, be added after being completely dissolved C5 Petropols, C9 Petropols with it is anti-ageing
Agent is eventually adding inorganic pigment, is uniformly mixed.
The present invention has the advantages that:
The present invention can produce the color asphalt of various colors, improve vision, can be widely used in street, pavement and
The different places such as landscape road can not only meet the needs of various places, while can also beautify the environment.
The present invention realizes the color asphalt production for being prepared have excellent performance at lower cost by being formulated global design
Product.
Specific implementation mode
With reference to embodiment, the present invention will be described in detail, and embodiment is only the preferred embodiment of the present invention,
It is not limitation of the invention.
Embodiment 1
A kind of anti-aging color asphalt, is made of the raw material of following parts by weight:18 parts of C5 Petropols, C9 Petropols
25 parts, 32 parts of base oil, 5 parts of styrene butadiene rubber powder, 8 parts of inorganic pigment, 1 part of age resister.
Wherein, the base oil is mineral substance oil;Inorganic pigment is iron oxide red pigment;The age resister is 2- hydroxyls -4-
Methoxy benzophenone and 2,6 di tert butyl 4 methyl phenol are with mass ratio 2:1 mixes.
The color asphalt preparation method includes the following steps:Base oil is added according to the parts by weight, is heated to
Under the conditions of 160-190 DEG C, styrene butadiene rubber powder stirring melting is added, be added after being completely dissolved C5 Petropols, C9 Petropols with
Age resister is eventually adding inorganic pigment, is uniformly mixed.
Embodiment 2
A kind of anti-aging color asphalt, is made of the raw material of following parts by weight:15 parts of C5 Petropols, C9 Petropols
20 parts, 30 parts of base oil, 3 parts of styrene butadiene rubber powder, 5 parts of inorganic pigment, 0.8 part of age resister.
Wherein, the base oil is mineral substance oil;Inorganic pigment is chrome green pigment;The age resister is 2- hydroxyls -4-
Methoxy benzophenone and 2,6 di tert butyl 4 methyl phenol are with mass ratio 2:1 mixes.
The color asphalt preparation method includes the following steps:Base oil is added according to the parts by weight, is heated to
Under the conditions of 160-190 DEG C, styrene butadiene rubber powder stirring melting is added, be added after being completely dissolved C5 Petropols, C9 Petropols with
Age resister is eventually adding inorganic pigment, is uniformly mixed.
Embodiment 3
A kind of anti-aging color asphalt, is made of the raw material of following parts by weight:20 parts of C5 Petropols, C9 Petropols
30 parts, 35 parts of base oil, 8 parts of styrene butadiene rubber powder, 12 parts of inorganic pigment, 1.2 parts of age resister.
Wherein, the base oil is mineral substance oil;Inorganic pigment is titanium dioxide pigment;The age resister is 2- hydroxyls -4-
Methoxy benzophenone and 2,6 di tert butyl 4 methyl phenol are with mass ratio 2:1 mixes.
The color asphalt preparation method includes the following steps:Base oil is added according to the parts by weight, is heated to
Under the conditions of 160-190 DEG C, styrene butadiene rubber powder stirring melting is added, be added after being completely dissolved C5 Petropols, C9 Petropols with
Age resister is eventually adding inorganic pigment, is uniformly mixed.
Embodiments of the present invention above described embodiment only expresses, the description thereof is more specific and detailed, but can not
Therefore it is interpreted as the limitation to the scope of the claims of the present invention, as long as skill obtained in the form of equivalent substitutions or equivalent transformations
Art scheme should all be fallen within the scope and spirit of the invention.
Claims (5)
1. a kind of anti-aging color asphalt, is made of the raw material of following parts by weight:15-20 parts of C5 Petropols, C9 stones
20-30 parts of oleoresin, 30-35 parts of base oil, 3-8 parts of styrene butadiene rubber powder, 5-12 parts of inorganic pigment, 0.8-1.2 parts of age resister.
2. anti-aging color asphalt as described in claim 1, which is characterized in that the base oil is mineral substance oil.
3. anti-aging color asphalt as described in claim 1, which is characterized in that inorganic pigment is iron oxide red pigment, chrome green face
At least one of material, iron green pigment, titanium dioxide pigment, chrome yellow.
4. anti-aging color asphalt as described in claim 1, which is characterized in that the age resister is 2- hydroxyl -4- first
Oxygroup benzophenone and 2,6 di tert butyl 4 methyl phenol are with mass ratio 2:1 mixes.
5. anti-aging color asphalt as described in claim 1, which is characterized in that preparation method includes the following steps:It presses
Base oil is added according to the parts by weight, is heated under the conditions of 160-190 DEG C, styrene butadiene rubber powder stirring melting is added, it is completely molten
C5 Petropols, C9 Petropols and age resister are added after solution, is eventually adding inorganic pigment, is uniformly mixed.