CN105293994A - Coloured asphalt pavement mixture - Google Patents
Coloured asphalt pavement mixture Download PDFInfo
- Publication number
- CN105293994A CN105293994A CN201510722599.4A CN201510722599A CN105293994A CN 105293994 A CN105293994 A CN 105293994A CN 201510722599 A CN201510722599 A CN 201510722599A CN 105293994 A CN105293994 A CN 105293994A
- Authority
- CN
- China
- Prior art keywords
- asphalt pavement
- pavement mixture
- resin
- parts
- colorful asphalt
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a coloured asphalt pavement mixture. The coloured asphalt pavement mixture is prepared from the following raw materials in parts by weight: 20-40 parts of base oil, 15-40 parts of petroleum resin, 10-25 parts of terpene resin, 2-10 parts of a modifying agent, 1-15 parts of inorganic pigment and 15-30 parts of a pressure-sensitive diluent. The coloured asphalt pavement mixture only needs to be simply packaged in barrels or a tank car in transportation and can be mixed and used with stones at normal temperature without being heated before and after use, and then pavement spreading and roller compaction construction are carried out, so that a preparation process of the coloured asphalt pavement mixture is greatly simplified, and the construction of a coloured pavement is changed to be extremely simple and convenient. The coloured asphalt pavement mixture has pressure-sensitive property and is subjected to roller compaction by virtue of a road roller and transit vehicles, the bonding strength between asphalt and aggregate is improved, and the self strength of the mixture is improved.
Description
(1) technical field
The present invention relates to the colored pressure-sensitive modifying asphalt of a kind of cold construction, be specifically related to a kind of Colorful Asphalt Pavement mixture.
(2) background technology
In recent years, country is to improve city function, improve human settlement, continue city context, promote city taste, beautifying city view, to highlight city characteristic for focus, improve constantly afforestation planning, Construction and management level, while economy increases fast, make great efforts the harmonious development promoting human and environment, city taste is promoted further.Road is as a part for urban construction, and it beautifies degree and more will strengthen.And the general color asphalt that adopts is paved the way now, but need repeatedly to heat in existing color asphalt use procedure, have a strong impact on its result of use, need to improve.
(3) summary of the invention
The present invention is in order to make up the deficiencies in the prior art, provide a kind of Colorful Asphalt Pavement mixture, for liquid state can be flowed under this material normal temperature, can transport by normal temperature, can use with building stones mix at normal temperatures, then carry out the paving of road surface, roller compaction construction, realize cold mixing cold-application, greatly simplify the paving process of Colorful Asphalt Pavement, what the construction of colored road surface was become is more simple and convenient.
The present invention is achieved through the following technical solutions:
A kind of Colorful Asphalt Pavement mixture, its special character is: the raw material comprising following parts by weight:
Base oil 20-40 part, petroleum resin 15-40 part, terpine resin 10-25 part, properties-correcting agent 2-10 part, mineral dye 1-15 part, pressure-sensitive thinner 15-30 part.
Colorful Asphalt Pavement mixture of the present invention, base oil is at least one in aromatic hydrocarbon oil, viscous crude, distillate.
Colorful Asphalt Pavement mixture of the present invention, petroleum resin are at least one in group aliphatic resin, aromatic resin.
Colorful Asphalt Pavement mixture of the present invention, properties-correcting agent is at least one in styrene-butadiene-styrene block copolymer (SBS), powder styrene butadiene rubber (SBR).
Colorful Asphalt Pavement mixture of the present invention, mineral dye is at least one in iron oxide red pigment, chrome green pigment, iron phthalocyanine, titanium dioxide pigment, chrome yellow.
Colorful Asphalt Pavement mixture of the present invention, pressure-sensitive thinner be polyvalent alcohol, polyethers, acetate esters one or more.
The preparation method of the Colorful Asphalt Pavement mixture described in a kind of basis, it is characterized in that: comprise the following steps: base oil is heated to 160-180 DEG C, then petroleum resin, terpine resin, properties-correcting agent stirring is added, cool to 120-140 DEG C again, then add pressure-sensitive thinner to stir, finally add pigment as required and stir again and can obtain product.
Beneficial effect of the present invention: this material only needs bucket packaging or tank car simply to transport in transit, without the need to heating before and after using, can use with building stones mix at normal temperatures, then the paving of road surface, roller compaction construction is carried out, greatly simplify the preparation process of chromatic bitumen mixture, what the construction of colored road surface was become is very simple and convenient; This material has voltage-dependent characteristic, by street roller, the rolling of vehicular traffic, a pressure-sensitive dose of part is gathered materials absorption, improve pitch and the cohesive strength of gathering materials, a part is converted into macromole by rolling merit by small molecules, improve compound self-strength, also have part to vapor away, when rolling, surface layer will be more and more firm with the bonding of underpavement.
(4) embodiment
Embodiment 1:
The preparation method of Colorful Asphalt Pavement mixture, comprises the following steps:
First 20kg aromatic hydrocarbon oil is heated to 160 DEG C, then interpolation 15kg group aliphatic resin C5,10kg terpine resin, 2kg styrene-butadiene-styrene block copolymer (SBS) stir 2h, cool to 120 DEG C again, then 15kg polyvalent alcohol is added (as 1,2-propylene glycol) stir 1h, finally interpolation 1kg iron oxide red pigment stirs 1h again and can obtain product as required.
Embodiment 2:
The preparation method of Colorful Asphalt Pavement mixture, comprises the following steps:
First by 40kg heavy oil heating to 180 DEG C, then interpolation 40kg aromatic resin C9,25kg terpine resin, 10kg powder styrene butadiene rubber (SBR) stir 2h, cool to 140 DEG C again, then add 15kg polyethers and stir 2h, finally interpolation 15kg iron phthalocyanine stirs 1h again and can obtain product as required.
Embodiment 3:
The preparation method of Colorful Asphalt Pavement mixture, comprises the following steps:
First 30kg distillate is heated to 170 DEG C, then interpolation 10kg aromatic resin C9,20kg group aliphatic resin C5,20kg terpine resin, 4kg powder styrene butadiene rubber (SBR), 4kg styrene-butadiene-styrene block copolymer (SBS) stir 2h, cool to 130 DEG C again, then add 25kg ethyl acetate and stir 2h, finally interpolation 10kg chrome green pigment stirs 1h again and can obtain product as required.
Embodiment 4:
The preparation method of Colorful Asphalt Pavement mixture, comprises the following steps:
First by 10kg distillate, 10kg heavy oil heating to 170 DEG C, then interpolation 10kg aromatic resin C9,20kg group aliphatic resin C5,20kg terpine resin, 4kg powder styrene butadiene rubber (SBR), 4kg styrene-butadiene-styrene block copolymer (SBS) stir 2h, cool to 130 DEG C again, then add 10kg acetic ester, 5kg polyethers stirs 2h, finally interpolation 8kg titanium dioxide pigment stirs 1h again and can obtain product as required.
Embodiment 5:
The preparation method of Colorful Asphalt Pavement mixture, comprises the following steps:
First 10kg distillate, 10kg viscous crude, 10kg aromatic hydrocarbon oil are heated to 170 DEG C, then interpolation 10kg aromatic resin C9,20kg group aliphatic resin C5,20kg terpine resin, 4kg powder styrene butadiene rubber (SBR), 4kg styrene-butadiene-styrene block copolymer (SBS) stir 2h, cool to 130 DEG C again, then 10kg acetic ester, 5kg polyethers, 5kg polyvalent alcohol is added (as 1,2-propylene glycol) stir 2h, finally interpolation 8kg chrome yellow stirs 1h again and can obtain product as required.
Embodiment 6:
The preparation method of Colorful Asphalt Pavement mixture, comprises the following steps:
First 10kg distillate, 15kg viscous crude, 10kg aromatic hydrocarbon oil are heated to 170 DEG C, then interpolation 10kg aromatic resin C9,20kg group aliphatic resin C5,20kg terpine resin, 4kg powder styrene butadiene rubber (SBR), 4kg styrene-butadiene-styrene block copolymer (SBS) stir 2h, cool to 130 DEG C again, then 10kg acetic ester, 5kg polyethers, 5kg polyvalent alcohol is added (as 1,2-propylene glycol) stir 2h, finally interpolation 8kg chrome yellow, 1kg iron oxide red pigment stir 1h again and can obtain product as required.
Embodiment 7
Add 4kg chrome yellow, 1kg iron oxide red pigment, 2kg chrome green pigment, other are identical with embodiment 1.
Embodiment 8:
Add 2kg iron oxide red pigment, 2kg chrome green pigment, 2kg iron phthalocyanine, 1kg titanium dioxide pigment, 1kg chrome yellow, other are identical with embodiment 1.
Embodiment 9:
The preparation method of Colorful Asphalt Pavement mixture, comprises the following steps:
First 20kg aromatic hydrocarbon oil is heated to 160 DEG C, then interpolation 15kg group aliphatic resin C5,10kg terpine resin, 2kg styrene-butadiene-styrene block copolymer (SBS) stir 2h, cool to 120 DEG C again, then 15kg polyvalent alcohol is added (as 1,2-propylene glycol), broker wall bee pollen 2kg and clear cream stirs 1h, finally add 1kg iron oxide red pigment as required and stir 1h again and can obtain product.
Root of Indigowoad: antipyretic; Heat-clearing and detoxicating drug; Blood-cooling drugs nature and flavor are bitter, cold.Gui Jing: 1. " book on Chinese herbal medicine is just read ": enter liver, stomach blood system.2. " China's book on Chinese herbal medicine ": return liver; Stomach warp.Effect: heat-clearing, removing toxic substances, cool blood, relieve sore throat.Cure mainly: maculae caused by violent heat pathogen; High heat headache; Major part pestilence; Tongue is secretly dark reddish purple, scarlet fever; Erysipelas; Mumps; Larynx numbness; Sore is swollen, carbuncle swells; Varicella; Measles; Hepatitis; Influenza, epidemic meningitis, encephalitis, pneumonia, coma tells nosebleed, and pharynx is swollen, pinkeye, sore rash; Epidemic encephalitis type B, acute, chronic hepatitis, mumps, osteomyelitis can be prevented and treated.
Tea root: effect: cardiac stimulant diuresis; Promoting blood flow to regulate menstruation; Clearing heat and detoxicating.Cure mainly: heart trouble; Oedema; Hepatitis; Dysmenorrhoea; Sore swollen toxin; Aphtha; Soup fire is burnt; Zoster; Psoriasis.
The form of Lunate Peltate Sundew Herb is very changeable, the growth and not higher than 15 centimetres in rosette-stape of their great majority, some then can vertical growth to more than 20 centimetres, napiform root Lunate Peltate Sundew Herb ratio people that even can grow of some climbing growth is also high.The color of Lunate Peltate Sundew Herb blade generally is green, bright red or yellow-green colour can be presented under good irradiate light, shape is also very changeable, the leaf forked growth of such as fork blade Lunate Peltate Sundew Herb, the leaf of silk leaf Lunate Peltate Sundew Herb becomes linear vertical growth, and the most special may be the huge Lunate Peltate Sundew Herb of Australia, its form is just the same with tree, can grow to 1 meter high, the napiform root of underground can also grow to the diameter of 4 centimetres, and blade is then the same with many napiform root Lunate Peltate Sundew Herbs is " small bell " shape.The pharmacological action of pharmacological action 1, plumbagin is see Whiteflower Leadword Root bar.The extract of Lunate Peltate Sundew Herb at least comprises two kinds of naphthoquinone derivatives, has powerful spasmolysis.2, the glycerin extraction liquid of Lunate Peltate Sundew Herb herb and methanol extract liquid inject in frog thoracic lymph capsule and leg muscle, within 10 hours, check that there is hemorrhagic necrosis local later.Function cures mainly: treatment sore, scrofula are sick.Treat for stomachache, dysentery with red and white feces, infantile malnutrition, wound.
The Modified Bitumen Pavement material of this embodiment greatly reduces its toxicity to human body, and does not affect the result of use of Modified Bitumen Pavement material.
Embodiment 10:
Table 1: the technical indicator of the colored pressure-sensitive modified asphalt material of cold construction
Claims (7)
1. a Colorful Asphalt Pavement mixture, is characterized in that: the raw material comprising following parts by weight:
Base oil 20-40 part, petroleum resin 15-40 part, terpine resin 10-25 part, properties-correcting agent 2-10 part, mineral dye 1-15 part, pressure-sensitive thinner 15-30 part.
2. Colorful Asphalt Pavement mixture according to claim 1, is characterized in that: base oil is at least one in aromatic hydrocarbon oil, viscous crude, distillate.
3. Colorful Asphalt Pavement mixture according to claim 1, is characterized in that: petroleum resin are at least one in group aliphatic resin, aromatic resin.
4. Colorful Asphalt Pavement mixture according to claim 1, is characterized in that: properties-correcting agent is at least one in styrene-butadiene-styrene block copolymer (SBS), powder styrene butadiene rubber (SBR).
5. Colorful Asphalt Pavement mixture according to claim 1, is characterized in that: mineral dye is at least one in iron oxide red pigment, chrome green pigment, iron phthalocyanine, titanium dioxide pigment, chrome yellow.
6. the Colorful Asphalt Pavement mixture arbitrarily described according to claim 1, is characterized in that: pressure-sensitive thinner be polyvalent alcohol, polyethers, acetate esters one or more.
7. the preparation method according to Colorful Asphalt Pavement mixture described arbitrarily in claim 1 to 6, it is characterized in that: comprise the following steps: base oil is heated to 160-180 DEG C, then petroleum resin, terpine resin, properties-correcting agent stirring is added, cool to 120-140 DEG C again, then add pressure-sensitive thinner to stir, finally add pigment as required and stir again and can obtain product.