CN105273547A - 一种水溶性阻燃型聚丙烯酸涂料的制备方法 - Google Patents

一种水溶性阻燃型聚丙烯酸涂料的制备方法 Download PDF

Info

Publication number
CN105273547A
CN105273547A CN201510270067.1A CN201510270067A CN105273547A CN 105273547 A CN105273547 A CN 105273547A CN 201510270067 A CN201510270067 A CN 201510270067A CN 105273547 A CN105273547 A CN 105273547A
Authority
CN
China
Prior art keywords
water
polyacrylic acid
preparation
resisting type
hydroxy
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510270067.1A
Other languages
English (en)
Inventor
杜隆超
王西弱
王西宇
王文本
徐国永
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Xingxin Chemical Science & Technology Co Ltd
Anhui University
Original Assignee
Anhui Xingxin Chemical Science & Technology Co Ltd
Anhui University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Xingxin Chemical Science & Technology Co Ltd, Anhui University filed Critical Anhui Xingxin Chemical Science & Technology Co Ltd
Priority to CN201510270067.1A priority Critical patent/CN105273547A/zh
Publication of CN105273547A publication Critical patent/CN105273547A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种水溶性阻燃型聚丙烯酸涂料的制备方法。该方法将水加入装有冷凝管的三颈瓶中，然后依次加入甲基丙烯酸、氯化石蜡、十二烷基硫酸钠，剧烈搅拌下加入2-羟基-2-甲基-1-苯基丙酮，并以2-羟基-2-甲基-1-苯基丙酮为紫外光引发剂，以15W低压汞灯为光源，升温反应，反应结束得到一种新型聚合物主链上键有氯化石蜡的水溶性阻燃型聚丙烯酸涂料。本发明的水溶性阻燃型聚丙烯酸涂料具有良好的物理化学性能、阻燃性能。

Description

一种水溶性阻燃型聚丙烯酸涂料的制备方法
技术领域
本发明涉及聚丙烯酸涂料的技术领域，具体地说，是一种水溶性阻燃型聚丙烯酸涂料的制备方法。
背景技术
丙烯酸树脂具有较好光泽度、耐候性、耐化学品性等，且生产安全，价格便宜，然而传统的丙烯酸树脂中有机溶剂的挥发会对环境造成污染。与有机溶剂型树脂相比，水性树脂具有廉价、安全、节能和无公害等特点。而由水溶性丙烯酸树脂制得的清漆具有无毒无味、耐酸碱、阻燃、光泽度高、附着力好、不掉色、耐候性好和耐化学品性好等特点，是一种低挥发性有机化合物(VOC)的绿色环保型产品。
氯化石蜡是石蜡烃的氯化衍生物，具有低挥发性、阻燃、电绝缘性良好、价廉等优点，可用作阻燃剂和聚氯乙烯辅助增塑剂。广泛用于生产电缆料、地板料、软管、人造革、橡胶等制品。以及应用于涂料、润滑油等的添加剂。但是氯化石蜡不溶于水，限制了它在涂料，粘合剂等领域中的使用。本发明扩展了氯化石蜡的使用范围，制备聚合物主链键有氯化石蜡的新型水溶性阻燃型聚丙烯酸涂料。
发明内容
本发明提供一种水溶性阻燃型聚丙烯酸涂料的制备方法,为实现上述目的，本发明采取的技术方案是：
一种水溶性阻燃型聚丙烯酸涂料的制备方法，其特征在于，由以下步骤制成：
包括以下按重量份计的原料组成：水100～300份；甲基丙烯酸60～80份；氯化石蜡1～20份；2-羟基-2-甲基-1-苯基丙酮0.1～3份；十二烷基硫酸钠0.8～2.6份。其中，氯化石蜡-52购自安徽星鑫化工科技有限公司，甲基丙烯酸、2-羟基-2-甲基-1-苯基丙酮、十二烷基硫酸钠购于国药集团化学试剂有限公司。
所述的一种水溶性阻燃型聚丙烯酸涂料的制备方法具体步骤如下：在500ml三颈瓶中加入水，剧烈搅拌下加入十二烷基硫酸钠、氯化石蜡和甲基丙烯酸，升温至60-100℃，加入2-羟基-2-甲基-1-苯基丙酮，以15W低压汞灯为光源，反应5-12小时，反应结束，得到水溶性阻燃型聚丙烯酸涂料。
所述的一种水溶性阻燃型聚丙烯酸涂料的制备方法，其特征在于，所述的紫外光引发剂为2-羟基-2-甲基-1-苯基丙酮。
所述的一种水溶性阻燃型聚丙烯酸涂料的制备方法，其特征在于，所述的乳化剂为十二烷基硫酸钠。
所述的一种水溶性阻燃型聚丙烯酸涂料的制备方法，其特征在于，所述的搅拌转速为1000～5000r/min。
所述的一种水溶性阻燃型聚丙烯酸涂料的制备方法，其特征在于，所述的紫外光源是以15W低压汞灯为光源。
本发明优点在于：
一种水溶性阻燃型聚丙烯酸涂料的制作方法，通过使用紫外光引发剂，促进了氯化石蜡键合在聚丙烯酸主链上，提供了一种新的水溶性阻燃涂料。
具体实施方式
下面结合具体实施例对本发明作进一步的说明。
实施例
①取水200g，甲基丙烯酸80g，氯化石蜡10g，2-羟基-2-甲基-1-苯基丙酮2g，十二烷基硫酸钠1.5g。
②在500ml三颈瓶中加入水，剧烈搅拌下加入十二烷基硫酸钠、氯化石蜡和甲基丙烯酸，升温至70℃，加入2-羟基-2-甲基-1-苯基丙酮，开启紫外光源，反应10小时，反应结束，得到水溶性阻燃型聚丙烯酸涂料。
所述的紫外光引发剂为2-羟基-2-甲基-1-苯基丙酮。
所述的乳化剂为十二烷基硫酸钠。
所述的搅拌转速为3000r/min。
所述的紫外光源是以15W低压汞灯为光源。
对比例
①取水200份，甲基丙烯酸80份，氯化石蜡10份，十二烷基硫酸钠1.5份。
②在500ml三颈瓶中加入水，剧烈搅拌下加入十二烷基硫酸钠、氯化石蜡和甲基丙烯酸，搅拌转速为3000r/min，升温至70℃，反应10小时，反应结束，得到阻燃型聚丙烯酸涂料。
项目 实施例 对比例
拉伸强度(MPa) 12 10
阻燃性能(UL94) V-0 V-1

Claims (6)

1.一种水溶性阻燃型聚丙烯酸涂料的制备方法，其特征在于，由以下步骤制成：
包括以下按重量份计的原料组成：水100～300份；甲基丙烯酸60～80份；氯化石蜡1～20份；2-羟基-2-甲基-1-苯基丙酮0.1～3份；十二烷基硫酸钠0.8～2.6份，其中，氯化石蜡-52购自安徽星鑫化工科技有限公司，甲基丙烯酸、2-羟基-2-甲基-1-苯基丙酮、十二烷基硫酸钠购于国药集团化学试剂有限公司。
2.所述的一种水溶性阻燃型聚丙烯酸涂料的制备方法具体步骤如下：在500ml三颈瓶中加入水，剧烈搅拌下加入十二烷基硫酸钠、氯化石蜡和甲基丙烯酸，升温至60-100℃，加入2-羟基-2-甲基-1-苯基丙酮，以15W低压汞灯为光源，反应5-12小时，反应结束，得到水溶性阻燃型聚丙烯酸涂料。
3.根据权利要求1所述的一种水溶性阻燃型聚丙烯酸涂料的制备方法，其特征在于，所述的紫外光引发剂为2-羟基-2-甲基-1-苯基丙酮。
4.根据权利要求1所述的一种水溶性阻燃型聚丙烯酸涂料的制备方法，其特征在于，所述的乳化剂为十二烷基硫酸钠。
5.根据权利要求1所述的一种水溶性阻燃型聚丙烯酸涂料的制备方法，其特征在于，所述的搅拌转速为1000～5000r/min。
6.根据权利要求1所述的一种水溶性阻燃型聚丙烯酸涂料的制备方法，其特征在于，所述的紫外光源是以15W低压汞灯为光源。
CN201510270067.1A 2015-05-26 2015-05-26 一种水溶性阻燃型聚丙烯酸涂料的制备方法 Pending CN105273547A (zh)