CN103937348A - 一种导电涂料及其制备方法 - Google Patents

一种导电涂料及其制备方法 Download PDF

Info

Publication number
CN103937348A
CN103937348A CN201410107203.0A CN201410107203A CN103937348A CN 103937348 A CN103937348 A CN 103937348A CN 201410107203 A CN201410107203 A CN 201410107203A CN 103937348 A CN103937348 A CN 103937348A
Authority
CN
China
Prior art keywords
add
component
stir
coating
minute
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410107203.0A
Other languages
English (en)
Inventor
刘雪峰
陈新国
许金
张广宵
袁明
邹玉宏
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI LANKE COMPOSITE MATERIALS Co Ltd
Original Assignee
ANHUI LANKE COMPOSITE MATERIALS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI LANKE COMPOSITE MATERIALS Co Ltd filed Critical ANHUI LANKE COMPOSITE MATERIALS Co Ltd
Priority to CN201410107203.0A priority Critical patent/CN103937348A/zh
Publication of CN103937348A publication Critical patent/CN103937348A/zh
Pending legal-status Critical Current

Abstract

一种导电涂料,由下列重量份的原料制成:热塑性丙烯酸树脂32-36、纳米甲壳素3-5、聚乙烯醇1-2、纤维素纳米纤丝2-3、醇酸树脂4-6、过氯乙烯树脂8-10、鳞片石墨粉3-4、硅酸钾3-5、醇酯十二0.1-0.2、丙酮6-8、全氟辛基磺酸钠1-2、醋酸乙酯6-8、烷基改性有机硅氧烷0.2-0.3、附着助剂4-6;本发明的涂料具有良好的保光保色性、耐水耐化学性、干燥快、施工方便,通过添加纳米甲壳素、纤维素纳米纤丝,增加了漆膜的致密性,阻水和阻气性好,提高了耐腐蚀性,通过添加鳞片石墨粉,使得涂料具有导电性,防静电,该涂料易涂装、对材料的附着性好、不易燃烧。

Description

一种导电涂料及其制备方法
技术领域
本发明属于涂料领域,尤其涉及一种导电涂料及其制备方法。
背景技术
现在涂料的使用领域很多,由于经常暴露在大气之中,受到氧气、水分等的侵蚀,容易造成金属锈蚀、木材腐朽、水泥风化等现象,随着人们生活水平的提高,对涂料各方面的要求都有所提高,尤其是对涂料的硬度、耐磨性、丰满度、耐冲击性、耐老化性、防腐、防水、防油、耐化学品、耐光、耐温等性能等方面的要求越来越高,因此需要研究更加进步的涂料以满足人们的需要。
发明内容
本发明的目的在于提供一种导电涂料及其制备方法,该涂料本发明的涂料具有良好的保光保色性、耐水耐化学性、干燥快、施工方便,阻水和阻气性好,具有导电性,防静电,而且易涂装、对材料的附着性好、不易燃烧。
本发明的技术方案如下:
一种导电涂料,其特征在于由下列重量份的原料制成:热塑性丙烯酸树脂32-36、纳米甲壳素3-5、聚乙烯醇1-2、纤维素纳米纤丝2-3、醇酸树脂4-6、过氯乙烯树脂8-10、鳞片石墨粉3-4、硅酸钾3-5、醇酯十二0.1-0.2、丙酮6-8、全氟辛基磺酸钠1-2、醋酸乙酯6-8、烷基改性有机硅氧烷0.2-0.3、附着助剂4-6;
所述附着助剂由下列重量份的原料制成:烯丙基硫脲 0.2-0.3、硅烷偶联剂KH5500.4-0.6、丙烯酸丁酯3-5、1,6-己二醇二丙烯酸酯4-7、聚氨酯树脂6-8、氯化聚丙烯树脂7-9、没食子酸丙酯2-3、三聚磷酸钠2-3、过氧化二异丙苯0.1-0.2、丙烯酸异辛酯5-7、乙酸乙酯10-15、正丁醇10-15、亚麻油1-2、乳母果油1-2、琥珀酸0.2-0.3;制作方法为:将乙酸乙酯、正丁醇、亚麻油、乳母果油混合,在3000-4000转/分下加入聚氨酯树脂、氯化聚丙烯树脂,溶解后再加入丙烯酸丁酯、1,6-己二醇二丙烯酸酯,搅拌20-30分钟,加入其他剩余成分,加热至80-90℃,搅拌反应30-50分钟,即得。
所述的导电涂料的制备方法,其特征在于包括以下步骤:
(1)制备 A 组份 :将丙酮、醋酸乙酯混合,加热至60-70℃,在5000-6000转/分下加入纳米甲壳素、纤维素纳米纤丝,搅拌10-15分钟,再加入过氯乙烯树脂、醇酸树脂,搅拌1-2小时,超声分散7-10分钟,制得A组份;
(2)制备 B 组份 :将热塑性丙烯酸树脂加热至60-70℃,在5000-6000转/分下加入鳞片石墨粉、全氟辛基磺酸钠、聚乙烯醇,搅拌20-30分钟,分散并研磨至细度≤ 50μm ,制得B组份;
(3)将其他剩余成分混合均匀,加入A组份和B组份,搅拌均匀研磨成浆料即得。
本发明的有益效果
本发明的涂料具有良好的保光保色性、耐水耐化学性、干燥快、施工方便,通过添加纳米甲壳素、纤维素纳米纤丝,增加了漆膜的致密性,阻水和阻气性好,提高了耐腐蚀性,通过添加鳞片石墨粉,使得涂料具有导电性,防静电,该涂料易涂装、对材料的附着性好、不易燃烧。
具体实施方式
一种导电涂料,由下列重量份(公斤)的原料制成:热塑性丙烯酸树脂34、纳米甲壳素4、聚乙烯醇1.5、纤维素纳米纤丝2.5、醇酸树脂5、过氯乙烯树脂9、鳞片石墨粉3.5、硅酸钾4、醇酯十二0.1、丙酮7、全氟辛基磺酸钠1.5、醋酸乙酯7、烷基改性有机硅氧烷0.3、附着助剂5;
所述附着助剂由下列重量份(公斤)的原料制成:烯丙基硫脲 0.2、硅烷偶联剂KH5500.5、丙烯酸丁酯4、1,6-己二醇二丙烯酸酯5、聚氨酯树脂7、氯化聚丙烯树脂8、没食子酸丙酯2.5、三聚磷酸钠2.5、过氧化二异丙苯0.1、丙烯酸异辛酯6、乙酸乙酯13、正丁醇13、亚麻油1.5、乳母果油1.5、琥珀酸0.2;制作方法为:将乙酸乙酯、正丁醇、亚麻油、乳母果油混合,在3500转/分下加入聚氨酯树脂、氯化聚丙烯树脂,溶解后再加入丙烯酸丁酯、1,6-己二醇二丙烯酸酯,搅拌25分钟,加入其他剩余成分,加热至85℃,搅拌反应40分钟,即得。
所述的导电涂料的制备方法,包括以下步骤:
(1)制备 A 组份 :将丙酮、醋酸乙酯混合,加热至65℃,在5500转/分下加入纳米甲壳素、纤维素纳米纤丝,搅拌13分钟,再加入过氯乙烯树脂、醇酸树脂,搅拌1.5小时,超声分散9分钟,制得A组份;
(2)制备 B 组份 :将热塑性丙烯酸树脂加热至65℃,在5500转/分下加入鳞片石墨粉、全氟辛基磺酸钠、聚乙烯醇,搅拌25分钟,分散并研磨至细度为 50μm ,制得B组份;
(3)将其他剩余成分混合均匀,加入A组份和B组份,搅拌均匀研磨成浆料即得。
该涂料耐人工老化性3600小时,涂层在保持低光泽度和高耐磨性的前提下膜层厚度达到34微米以上,附着力为1 级,抗冲击强度≥55kg·cm,柔韧性为2mm。

Claims (2)

1.一种导电涂料,其特征在于由下列重量份的原料制成:热塑性丙烯酸树脂32-36、纳米甲壳素3-5、聚乙烯醇1-2、纤维素纳米纤丝2-3、醇酸树脂4-6、过氯乙烯树脂8-10、鳞片石墨粉3-4、硅酸钾3-5、醇酯十二0.1-0.2、丙酮6-8、全氟辛基磺酸钠1-2、醋酸乙酯6-8、烷基改性有机硅氧烷0.2-0.3、附着助剂4-6;
所述附着助剂由下列重量份的原料制成:烯丙基硫脲 0.2-0.3、硅烷偶联剂KH5500.4-0.6、丙烯酸丁酯3-5、1,6-己二醇二丙烯酸酯4-7、聚氨酯树脂6-8、氯化聚丙烯树脂7-9、没食子酸丙酯2-3、三聚磷酸钠2-3、过氧化二异丙苯0.1-0.2、丙烯酸异辛酯5-7、乙酸乙酯10-15、正丁醇10-15、亚麻油1-2、乳母果油1-2、琥珀酸0.2-0.3;制作方法为:将乙酸乙酯、正丁醇、亚麻油、乳母果油混合,在3000-4000转/分下加入聚氨酯树脂、氯化聚丙烯树脂,溶解后再加入丙烯酸丁酯、1,6-己二醇二丙烯酸酯,搅拌20-30分钟,加入其他剩余成分,加热至80-90℃,搅拌反应30-50分钟,即得。
2.根据权利要求1所述的导电涂料的制备方法,其特征在于包括以下步骤:
(1)制备 A 组份 :将丙酮、醋酸乙酯混合,加热至60-70℃,在5000-6000转/分下加入纳米甲壳素、纤维素纳米纤丝,搅拌10-15分钟,再加入过氯乙烯树脂、醇酸树脂,搅拌1-2小时,超声分散7-10分钟,制得A组份;
(2)制备 B 组份 :将热塑性丙烯酸树脂加热至60-70℃,在5000-6000转/分下加入鳞片石墨粉、全氟辛基磺酸钠、聚乙烯醇,搅拌20-30分钟,分散并研磨至细度≤ 50μm ,制得B组份;
(3)将其他剩余成分混合均匀,加入A组份和B组份,搅拌均匀研磨成浆料即得。
CN201410107203.0A 2014-03-21 2014-03-21 一种导电涂料及其制备方法 Pending CN103937348A (zh)