CN105214623A - 一种微量重金属三醋酸纤维素多孔微球吸附剂的制备方法 - Google Patents

一种微量重金属三醋酸纤维素多孔微球吸附剂的制备方法 Download PDF

Info

Publication number
CN105214623A
CN105214623A CN201510722175.8A CN201510722175A CN105214623A CN 105214623 A CN105214623 A CN 105214623A CN 201510722175 A CN201510722175 A CN 201510722175A CN 105214623 A CN105214623 A CN 105214623A
Authority
CN
China
Prior art keywords
triafol
subsequently
parts
mass ratio
under
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201510722175.8A
Other languages
English (en)
Other versions
CN105214623B (zh
Inventor
仇颖超
高力群
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangdong Institute Of Analysis (china National Analytical Center Guangzhou)
Institute Of Testing And Analysis Guangdong Academy Of Sciences Guangzhou Analysis And Testing Center China
Zhongguang Testing (Zhongshan) Testing Technology Co.,Ltd.
Zhongshan Zhongce Weaving Industry Technology Research Center
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201510722175.8A priority Critical patent/CN105214623B/zh
Publication of CN105214623A publication Critical patent/CN105214623A/zh
Application granted granted Critical
Publication of CN105214623B publication Critical patent/CN105214623B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种微量重金属三醋酸纤维素多孔微球吸附剂的制备方法,属于吸附材料领域。本发明首先通过乙酸溶液高温活化棉浆泊,再在氮气环境下,通过乙酸酐对其乙酰化处理,制备三醋酸纤维素,再将三醋酸纤维素与碳酸钙颗粒和液体石蜡在超声振荡作用下,团聚形成三醋酸纤维素微球,再在盐酸腐蚀环境下,通过腐蚀碳酸钙颗粒,形成多孔结构制备一种微量重金属三醋酸纤维素多孔微球吸附剂,本发明制得的微量重金属三醋酸纤维素多孔微球吸附剂比表面积可达340m2/g以上,吸附效果显著,且可多次利用,解决资源。

Description

一种微量重金属三醋酸纤维素多孔微球吸附剂的制备方法
技术领域
本发明涉及一种微量重金属三醋酸纤维素多孔微球吸附剂的制备方法,属于吸附材料领域。
背景技术
在过去的几十年里,通过环境质量标准的实施,过滤、反渗透、化学沉淀、离子交换、电沉淀等技术的应用,水环境中的有毒重金属离子量已大大减少。这些手段对水环境中高浓度重金属的去除行之有效,然而对于水环境中低浓度重金属的去除效果较差,处理费用相对较高。环境中的微量重金属如铅和镍由于自身不能被自然降解,往往易通过食物链而累积,严重危害人类的身体健康。因此,如何有效去除水体中微量重金属离子已经成为当前十分迫切的任务。
纤维素是地球上最丰富的可再生资源,具有良好的生物降解性和环境协调性,其材料制品具有其它合成高分子材料不具有的优越性,因此,纤维素及其衍生物的改性越来越受到人们的欢迎与重视。醋酸纤维素中羟基及羰基的存在,对贵重金属有强烈亲和力,因此可作为贵重金属的吸附剂。由于醋酸纤维素可以微球、片状、膜以及溶液等不同形式出现。其中,三醋酸纤维素是一种高附加值的纤维素衍生品,具有对光稳定、不易燃烧、易加工成型、光泽好、强度高、韧性好、熔融流动性好的优点,所以制备一种三醋酸纤维素多孔微球吸附剂对微量重金属处理很有必要。
发明内容
本发明主要解决的技术问题:针对制备纤维素吸附剂过程中,无法完全水解形成纤维素溶液,从而无法完全利用纤维素制备吸附剂,且纤维素制备吸附剂吸附重金属离子后,无法回收利用的问题,提供了一种通过乙酸溶液高温活化棉浆泊,再在氮气环境下,通过乙酸酐对其乙酰化处理,制备三醋酸纤维素,再将三醋酸纤维素与碳酸钙颗粒和液体石蜡在超声振荡作用下,团聚形成三醋酸纤维素微球,再在盐酸腐蚀环境下,通过腐蚀碳酸钙颗粒,形成多孔结构制备一种微量重金属三醋酸纤维素多孔微球吸附剂,本发明制得的微量重金属三醋酸纤维素多孔微球吸附剂比表面积可达340m2/g以上,吸附效果显著,且可多次利用,解决资源。
为了解决上述技术问题,本发明所采用的技术方案:
(1)按质量比1:5计,将棉浆泊和乙酸加入三口烧瓶中,并对其搅拌升温至70~75℃,在1000~1200r/min下活化25~30min,待其活化完成后,按质量份数计,选取2~8份的四[β-(3,5-二叔丁基-4-羟基苯基)丙酸]季戊四醇酯,3~6份质量浓度为3.2mol/L的浓硫酸和89~92份的乙酸酐,搅拌混合10~15min;
(2)待其搅拌完成后,对其通入氮气,排除空气后,在氮气气氛下,加热升温至120~130℃,在1300~1500r/min下搅拌反应2~3h,随后停止加热静置冷却至20~30℃,随后对其过滤,收集滤渣并通过去离子水冲洗至pH为7.0,随后将其置于80~90℃烘箱中,干燥20~24h,制备得三醋酸纤维素;
(3)按质量比1:8将上述制备的三醋酸纤维素于丙酮,在200~300r/min下搅拌混合至三醋酸纤维素完全溶解,待其完全溶解后,制得三醋酸纤维素溶液,随后,提高搅拌器的速度至400~500r/min,并按质量比1:10将去离子水以12mL/min滴加至三醋酸纤维素溶液中,搅拌反应20~30min;
(4)按质量份数计,选取3~12份粒径大小为2μm的碳酸钙颗粒,1~2份聚氧乙烯脱水山梨醇单油酸酯和87~95份液体石蜡,使其在450~500r/min转速下。搅拌混合2~3h,制备得交联体系,随后按质量比1:1,将三醋酸纤维素溶液和交联体系,混合搅拌10~15min并以6mL/min的速度,缓慢滴加至超声波分散装置中,待其分散成型使其团聚后,用去离子水洗涤制备得三醋酸纤维素微球;
(5)在500mL的浓度为1mol/L的盐酸溶液中,加入100gNaCl,待NaCl完全溶解后,再将氯化钙混合搅拌添加至上述溶液,直至其呈饱和状态后,将上述制备的三醋酸纤维素微球按固液质量比1:2的比例,在200~250r/min下,缓慢搅拌溶解2~3h,随后对其过滤,收集滤渣并通过去离子水冲洗至pH为7.0,随后将其置于90~95℃烘箱中,干燥10~12h,即可制备得一种微量重金属三醋酸纤维素多孔微球吸附剂。
本发明的应用:取上述制备的吸附剂30~40g,加入2000~2500g铅离子含量为0.42mg/L,并对其进行曝气,8~10h后铅离子浓度降至0.02mg/L,吸附后对其热再生处理后,使用3~4次不发生解吸。
本发明的有益效果是:
(1)本发明制得的吸附剂对低浓度重金属吸附效果达95%以上;
(2)可多次吸附,吸附3~5次不发生解吸现象。
具体实施方式
首先按质量比1:5计,将棉浆泊和乙酸加入三口烧瓶中,并对其搅拌升温至70~75℃,在1000~1200r/min下活化25~30min,待其活化完成后,按质量份数计,选取2~8份的四[β-(3,5-二叔丁基-4-羟基苯基)丙酸]季戊四醇酯,3~6份质量浓度为3.2mol/L的浓硫酸和89~92份的乙酸酐,搅拌混合10~15min;待其搅拌完成后,对其通入氮气,排除空气后,在氮气气氛下,加热升温至120~130℃,在1300~1500r/min下搅拌反应2~3h,随后停止加热静置冷却至20~30℃,随后对其过滤,收集滤渣并通过去离子水冲洗至pH为7.0,随后将其置于80~90℃烘箱中,干燥20~24h,制备得三醋酸纤维素;按质量比1:8将上述制备的三醋酸纤维素于丙酮,在200~300r/min下搅拌混合至三醋酸纤维素完全溶解,待其完全溶解后,制得三醋酸纤维素溶液,随后,提高搅拌器的速度至400~500r/min,并按质量比1:10将去离子水以12mL/min滴加至三醋酸纤维素溶液中,搅拌反应20~30min;按质量份数计,选取3~12份粒径大小为2μm的碳酸钙颗粒,1~2份聚氧乙烯脱水山梨醇单油酸酯和87~95份液体石蜡,使其在450~500r/min转速下。搅拌混合2~3h,制备得交联体系,随后按质量比1:1,将三醋酸纤维素溶液和交联体系,混合搅拌10~15min并以6mL/min的速度,缓慢滴加至超声波分散装置中,待其分散成型使其团聚后,用去离子水洗涤制备得三醋酸纤维素微球;在500mL的浓度为1mol/L的盐酸溶液中,加入100gNaCl,待NaCl完全溶解后,再将氯化钙混合搅拌添加至上述溶液,直至其呈饱和状态后,将上述制备的三醋酸纤维素微球按固液质量比1:2的比例,在200~250r/min下,缓慢搅拌溶解2~3h,随后对其过滤,收集滤渣并通过去离子水冲洗至pH为7.0,随后将其置于90~95℃烘箱中,干燥10~12h,即可制备得一种微量重金属三醋酸纤维素多孔微球吸附剂。
实例1
首先按质量比1:5计,将棉浆泊和乙酸加入三口烧瓶中,并对其搅拌升温至70℃,在1000r/min下活化25min,待其活化完成后,按质量份数计,选取2份的四[β-(3,5-二叔丁基-4-羟基苯基)丙酸]季戊四醇酯,6份质量浓度为3.2mol/L的浓硫酸和92份的乙酸酐,搅拌混合10min;待其搅拌完成后,对其通入氮气,排除空气后,在氮气气氛下,加热升温至120℃,在1300r/min下搅拌反应2h,随后停止加热静置冷却至20℃,随后对其过滤,收集滤渣并通过去离子水冲洗至pH为7.0,随后将其置于80℃烘箱中,干燥20h,制备得三醋酸纤维素;按质量比1:8将上述制备的三醋酸纤维素于丙酮,在200r/min下搅拌混合至三醋酸纤维素完全溶解,待其完全溶解后,制得三醋酸纤维素溶液,随后,提高搅拌器的速度至400r/min,并按质量比1:10将去离子水以12mL/min滴加至三醋酸纤维素溶液中,搅拌反应20min;按质量份数计,选取3份粒径大小为2μm的碳酸钙颗粒,2份聚氧乙烯脱水山梨醇单油酸酯和95份液体石蜡,使其在450r/min转速下。搅拌混合2h,制备得交联体系,随后按质量比1:1,将三醋酸纤维素溶液和交联体系,混合搅拌10min并以6mL/min的速度,缓慢滴加至超声波分散装置中,待其分散成型使其团聚后,用去离子水洗涤制备得三醋酸纤维素微球;在500mL的浓度为1mol/L的盐酸溶液中,加入100gNaCl,待NaCl完全溶解后,再将氯化钙混合搅拌添加至上述溶液,直至其呈饱和状态后,将上述制备的三醋酸纤维素微球按固液质量比1:2的比例,在200r/min下,缓慢搅拌溶解2h,随后对其过滤,收集滤渣并通过去离子水冲洗至pH为7.0,随后将其置于90℃烘箱中,干燥10h,即可制备得一种微量重金属三醋酸纤维素多孔微球吸附剂。取上述制备的吸附剂30g,加入2000g铅离子含量为0.5mg/L,并对其进行曝气,8h后铅离子浓度降至0.03mg/L,吸附后对其热再生处理后,使用3次不发生解吸。
实例2
首先按质量比1:5计,将棉浆泊和乙酸加入三口烧瓶中,并对其搅拌升温至72℃,在1100r/min下活化27min,待其活化完成后,按质量份数计,选取5份的四[β-(3,5-二叔丁基-4-羟基苯基)丙酸]季戊四醇酯,5份质量浓度为3.2mol/L的浓硫酸和90份的乙酸酐,搅拌混合12min;待其搅拌完成后,对其通入氮气,排除空气后,在氮气气氛下,加热升温至125℃,在1400r/min下搅拌反应2.5h,随后停止加热静置冷却至25℃,随后对其过滤,收集滤渣并通过去离子水冲洗至pH为7.0,随后将其置于85℃烘箱中,干燥25h,制备得三醋酸纤维素;按质量比1:8将上述制备的三醋酸纤维素于丙酮,在250r/min下搅拌混合至三醋酸纤维素完全溶解,待其完全溶解后,制得三醋酸纤维素溶液,随后,提高搅拌器的速度至450r/min,并按质量比1:10将去离子水以12mL/min滴加至三醋酸纤维素溶液中,搅拌反应25min;按质量份数计,选取8份粒径大小为2μm的碳酸钙颗粒,2份聚氧乙烯脱水山梨醇单油酸酯和90份液体石蜡,使其在475r/min转速下。搅拌混合2.5h,制备得交联体系,随后按质量比1:1,将三醋酸纤维素溶液和交联体系,混合搅拌12min并以6mL/min的速度,缓慢滴加至超声波分散装置中,待其分散成型使其团聚后,用去离子水洗涤制备得三醋酸纤维素微球;在500mL的浓度为1mol/L的盐酸溶液中,加入100gNaCl,待NaCl完全溶解后,再将氯化钙混合搅拌添加至上述溶液,直至其呈饱和状态后,将上述制备的三醋酸纤维素微球按固液质量比1:2的比例,在225r/min下,缓慢搅拌溶解2.5h,随后对其过滤,收集滤渣并通过去离子水冲洗至pH为7.0,随后将其置于92℃烘箱中,干燥11h,即可制备得一种微量重金属三醋酸纤维素多孔微球吸附剂。取上述制备的吸附剂30~40g,加入2250g铅离子含量为0.4mg/L,并对其进行曝气,9h后铅离子浓度降至0.015mg/L,吸附后对其热再生处理后,使用4次不发生解吸。
实例3
首先按质量比1:5计,将棉浆泊和乙酸加入三口烧瓶中,并对其搅拌升温至75℃,在1200r/min下活化30min,待其活化完成后,按质量份数计,选取8份的四[β-(3,5-二叔丁基-4-羟基苯基)丙酸]季戊四醇酯,3份质量浓度为3.2mol/L的浓硫酸和89份的乙酸酐,搅拌混合15min;待其搅拌完成后,对其通入氮气,排除空气后,在氮气气氛下,加热升温至130℃,在1500r/min下搅拌反应3h,随后停止加热静置冷却至30℃,随后对其过滤,收集滤渣并通过去离子水冲洗至pH为7.0,随后将其置于90℃烘箱中,干燥24h,制备得三醋酸纤维素;按质量比1:8将上述制备的三醋酸纤维素于丙酮,在300r/min下搅拌混合至三醋酸纤维素完全溶解,待其完全溶解后,制得三醋酸纤维素溶液,随后,提高搅拌器的速度至500r/min,并按质量比1:10将去离子水以12mL/min滴加至三醋酸纤维素溶液中,搅拌反应30min;按质量份数计,选取12份粒径大小为2μm的碳酸钙颗粒,1份聚氧乙烯脱水山梨醇单油酸酯和87份液体石蜡,使其在500r/min转速下。搅拌混合3h,制备得交联体系,随后按质量比1:1,将三醋酸纤维素溶液和交联体系,混合搅拌15min并以6mL/min的速度,缓慢滴加至超声波分散装置中,待其分散成型使其团聚后,用去离子水洗涤制备得三醋酸纤维素微球;在500mL的浓度为1mol/L的盐酸溶液中,加入100gNaCl,待NaCl完全溶解后,再将氯化钙混合搅拌添加至上述溶液,直至其呈饱和状态后,将上述制备的三醋酸纤维素微球按固液质量比1:2的比例,在250r/min下,缓慢搅拌溶解3h,随后对其过滤,收集滤渣并通过去离子水冲洗至pH为7.0,随后将其置于95℃烘箱中,干燥12h,即可制备得一种微量重金属三醋酸纤维素多孔微球吸附剂。取上述制备的吸附剂40g,加入2500g铅离子含量为0.6mg/L,并对其进行曝气,10h后铅离子浓度降至0.03mg/L,吸附后对其热再生处理后,使用4次不发生解吸。

Claims (1)

1.一种微量重金属三醋酸纤维素多孔微球吸附剂的制备方法,其特征在于具体制备步骤为:
(1)按质量比1:5计,将棉浆泊和乙酸加入三口烧瓶中,并对其搅拌升温至70~75℃,在1000~1200r/min下活化25~30min,待其活化完成后,按质量份数计,选取2~8份的四[β-(3,5-二叔丁基-4-羟基苯基)丙酸]季戊四醇酯,3~6份质量浓度为3.2mol/L的浓硫酸和89~92份的乙酸酐,搅拌混合10~15min;
(2)待其搅拌完成后,对其通入氮气,排除空气后,在氮气气氛下,加热升温至120~130℃,在1300~1500r/min下搅拌反应2~3h,随后停止加热静置冷却至20~30℃,随后对其过滤,收集滤渣并通过去离子水冲洗至pH为7.0,随后将其置于80~90℃烘箱中,干燥20~24h,制备得三醋酸纤维素;
(3)按质量比1:8将上述制备的三醋酸纤维素于丙酮,在200~300r/min下搅拌混合至三醋酸纤维素完全溶解,待其完全溶解后,制得三醋酸纤维素溶液,随后,提高搅拌器的速度至400~500r/min,并按质量比1:10将去离子水以12mL/min滴加至三醋酸纤维素溶液中,搅拌反应20~30min;
(4)按质量份数计,选取3~12份粒径大小为2μm的碳酸钙颗粒,1~2份聚氧乙烯脱水山梨醇单油酸酯和87~95份液体石蜡,使其在450~500r/min转速下搅拌混合2~3h,制备得交联体系,随后按质量比1:1,将三醋酸纤维素溶液和交联体系,混合搅拌10~15min并以6mL/min的速度,缓慢滴加至超声波分散装置中,待其分散成型使其团聚后,用去离子水洗涤制备得三醋酸纤维素微球;
(5)在500mL的浓度为1mol/L的盐酸溶液中,加入100gNaCl,待NaCl完全溶解后,再将氯化钙混合搅拌添加至上述溶液,直至其呈饱和状态后,将上述制备的三醋酸纤维素微球按固液质量比1:2的比例,在200~250r/min下,缓慢搅拌溶解2~3h,随后对其过滤,收集滤渣并通过去离子水冲洗至pH为7.0,随后将其置于90~95℃烘箱中,干燥10~12h,即可制备得一种微量重金属三醋酸纤维素多孔微球吸附剂。
CN201510722175.8A 2015-10-31 2015-10-31 一种微量重金属三醋酸纤维素多孔微球吸附剂的制备方法 Active CN105214623B (zh)