CN105177653A - 一种毛巾挂架表面复合镀层的制备方法 - Google Patents

一种毛巾挂架表面复合镀层的制备方法 Download PDF

Info

Publication number
CN105177653A
CN105177653A CN201510721778.6A CN201510721778A CN105177653A CN 105177653 A CN105177653 A CN 105177653A CN 201510721778 A CN201510721778 A CN 201510721778A CN 105177653 A CN105177653 A CN 105177653A
Authority
CN
China
Prior art keywords
layer
nickel layer
sulfate
plating
electroless nickel
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510721778.6A
Other languages
English (en)
Inventor
姜少群
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201510721778.6A priority Critical patent/CN105177653A/zh
Publication of CN105177653A publication Critical patent/CN105177653A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种毛巾挂架表面复合镀层的制备方法，该毛巾挂架材质为低碳钢，所述复合镀层包括与基材接触的电镀镍层以及电镀镍层外的电镀铬层，所述制备方法包括基材除油活化处理，电镀镍层以及电镀铬层步骤；其中电镀镍层的镀液包括硫酸镍、氯化镍、硼酸、硫酸铁、聚乙烯吡咯烷酮、电镀工艺参数为：pH为3.5-4.5，电流密度为10-12A/dm2，温度为40-44℃，时间为13-17min，其中电镀铬层的镀液包括硫酸铬、硫酸钠、硼酸、硫酸镁、十二烷基硫酸钠、甲酸、光亮剂MP-333、光亮剂MP-366、电镀工艺参数为：pH为3-4，温度,45-55℃，电流密度12-14A/dm2，电镀的时间为40-60min。

Description

一种毛巾挂架表面复合镀层的制备方法
技术领域
本发明涉及电镀技术领域，尤其涉及一种毛巾挂架表面复合镀层的制备方法。
背景技术
随着镍价格的不断攀升，在保证镀层功能的前提下，降低电镀镍层的厚度可直接降低电镀生产成本，减少废水排放，达到节能减排的目的。
在现代电镀技术的发展中，复合电镀是最活跃的部分，自20世纪30年代研究成功，60年代投产以来，发展极为迅速，应用领域不断扩大。同时在装饰电镀方面，人们为了获得高耐蚀的镀层，美国安美特公司发明了多层电镀，从双镍一直到今天的三层镍、四层镍，以提高装饰镀层的防腐蚀性能，为了进一步提高其耐蚀功能，把复合电镀用作镍封，即用极薄的复合镀层形成微孔铬来提高其防护性能。纳米复合电镀的防锈结构的原理是：把非导电性微粒子进行电镀，然后在其上面进行镀铬时就会产生无数的细孔。在此镀膜上腐蚀电流会被无限的分散开来，从而使得腐蚀的速度更加平稳缓慢。
据报道，在2001年10月，由重庆阿波罗机电技术开发公司自主开发的纳米电镀浆料及纳米电镀的工艺体系，不但能节约原材料，降低成本，而且其关键在于赋予镀层意想不到的耐磨等优良性能，该公司的纳米电镀浆料为α-A12O3组成的体系。但该镀层存在应力大等缺点。
目前这些复合镀层存在应力大、镀层厚和耐蚀性较差等缺点，迄今为止，还没有见到镀层很薄而耐蚀性优异为一体的复合功能镀层面市，也未见相关的专利和研究论文报道。
毛巾挂架经常处于潮湿的环境中，因此具有防腐蚀的要求，同时这些产品还具有装饰性美观的需求。因此亟需一种耐腐蚀性好，并且外观美观的复合镀层。
发明内容
本发明的目的在于提出一种毛巾挂架表面复合镀层的制备方法，该复合镀层具有良好的耐蚀性能，并且外观美观。
为达此目的，本发明采用以下技术方案：
一种毛巾挂架表面复合镀层的制备方法，该毛巾挂架材质为低碳钢，所述复合镀层包括与基材接触的电镀镍层以及电镀镍层外的电镀铬层，所述制备方法包括基材除油活化处理，电镀镍层以及电镀铬层步骤；其中电镀镍层的镀液组成为：硫酸镍为200-210g/L，氯化镍为65-75g/L，硼酸为50-54g/L，硫酸铁10-20g/L，聚乙烯吡咯烷酮0.1-0.2mol/L，电镀工艺参数为：pH为3.5-4.5，电流密度为10-12A/dm2，温度约为40-44℃，时间为13-17min，其中电镀铬层的镀液组成为：硫酸铬0.30-0.40mol/L，硫酸钠0.9-1.1mol/L，硼酸0.3-0.5mol/L，硫酸镁0.2-0.4mol/L，十二烷基硫酸钠0.0001-0.004mol/L，甲酸0.2-0.4mol/L，光亮剂MP-33320-30ml/L，光亮剂MP-36610-14ml/L，电镀工艺参数为：pH为3-4，温度约45-55℃，电流密度12-14A/dm2，电镀的时间为40-60min。
上述方案为本发明工艺方法的要点，其余如打磨除锈、清洗等等常规操作同现有技术，在此不再赘述。
本发明重点在于施镀镍层，特别是镍层中镀液组分中镍盐与铁盐的配比选择，使得镀液中二者的比例在上述组分中限定的范围内，才能获得优异的结合效果。为配合该镀镍层，对镀铬层的镀液组分也进行了优化和调整，使得适于与上述镀镍层在电镀过程中形成良好的冶金结合。同时，针对两种镀液成分的调整，选择了适合的电镀工艺条件。通过科学的复配，在理论和大量实验的基础上，创造性的确定了镀镍层镀液组分、镀铬层镀液组分、镀镍层电镀工艺、镀铬层电镀工艺四个变量的上述参数范围，达到协同技术效果，使得制备的镀层性能完美优异。
与现有技术相比，本发明具有如下有益效果：
1.通过增加镀镍层，使得镀层与基体结合力优异，可在浴室环境中持续使用8年以上不起皮，不剥落。
2.并且镀铬层耐腐蚀性能优异，盐雾试验200h以上未变色。
3.并且外观美观漂亮。完全可媲美不锈钢制品，但相比不锈钢制品的成本可降低40%以上。除了毛巾挂架外，还适合于卫浴用品的挂钩等产品。
具体实施方式
实施例一
一种毛巾挂架表面复合镀层的制备方法，该毛巾挂架材质为低碳钢，所述复合镀层包括与基材接触的电镀镍层以及电镀镍层外的电镀铬层，所述制备方法包括基材除油活化处理，电镀镍层以及电镀铬层步骤；其中电镀镍层的镀液组成为：硫酸镍为200g/L，氯化镍为75g/L，硼酸为50g/L，硫酸铁20g/L，聚乙烯吡咯烷酮0.1mol/L，电镀工艺参数为：pH为3.5-4.5，电流密度为10-12A/dm2，温度为40-44℃，时间为13min，其中电镀铬层的镀液组成为：硫酸铬0.30mol/L，硫酸钠1.1mol/L，硼酸0.3mol/L，硫酸镁0.4mol/L，十二烷基硫酸钠0.0001mol/L，甲酸0.4mol/L，光亮剂MP-33320ml/L，光亮剂MP-36614ml/L，电镀工艺参数为：pH为3-4，温度45-55℃，电流密度12-14A/dm2，电镀的时间为40min。
实施例二
一种毛巾挂架表面复合镀层的制备方法，该毛巾挂架材质为低碳钢，所述复合镀层包括与基材接触的电镀镍层以及电镀镍层外的电镀铬层，所述制备方法包括基材除油活化处理，电镀镍层以及电镀铬层步骤；其中电镀镍层的镀液组成为：硫酸镍为210g/L，氯化镍为65g/L，硼酸为54g/L，硫酸铁10g/L，聚乙烯吡咯烷酮0.2mol/L，电镀工艺参数为：pH为3.5-4.5，电流密度为10-12A/dm2，温度为40-44℃，时间为17min，其中电镀铬层的镀液组成为：硫酸铬0.40mol/L，硫酸钠0.9mol/L，硼酸0.5mol/L，硫酸镁0.2mol/L，十二烷基硫酸钠0.004mol/L，甲酸0.2mol/L，光亮剂MP-33330ml/L，光亮剂MP-36610ml/L，电镀工艺参数为：pH为3-4，温度45-55℃，电流密度12-14A/dm2，电镀的时间为60min。
实施例三
一种毛巾挂架表面复合镀层的制备方法，该毛巾挂架材质为低碳钢，所述复合镀层包括与基材接触的电镀镍层以及电镀镍层外的电镀铬层，所述制备方法包括基材除油活化处理，电镀镍层以及电镀铬层步骤；其中电镀镍层的镀液组成为：硫酸镍为205g/L，氯化镍为70g/L，硼酸为52g/L，硫酸铁15g/L，聚乙烯吡咯烷酮0.15mol/L，电镀工艺参数为：pH为3.5-4.5，电流密度为10-12A/dm2，温度为40-44℃，时间为15min，其中电镀铬层的镀液组成为：硫酸铬0.35mol/L，硫酸钠1.0mol/L，硼酸0.4mol/L，硫酸镁0.3mol/L，十二烷基硫酸钠0.00025mol/L，甲酸0.3mol/L，光亮剂MP-33325ml/L，光亮剂MP-36612ml/L，电镀工艺参数为：pH为3-4，温度45-55℃，电流密度12-14A/dm2，电镀的时间为50min。
申请人声明，本发明通过上述实施例来说明本发明的详细工艺设备和工艺流程，但本发明并不局限于上述详细工艺设备和工艺流程，即不意味着本发明必须依赖上述详细工艺设备和工艺流程才能实施。所属技术领域的技术人员应该明了，对本发明的任何改进，对本发明产品各原料的等效替换及辅助成分的添加、具体方式的选择等，均落在本发明的保护范围和公开范围之内。

Claims (1)

1.一种毛巾挂架表面复合镀层的制备方法，该毛巾挂架材质为低碳钢，所述复合镀层包括与基材接触的电镀镍层以及电镀镍层外的电镀铬层，所述制备方法包括基材除油活化处理，电镀镍层以及电镀铬层步骤；其中电镀镍层的镀液组成为：硫酸镍为200-210g/L，氯化镍为65-75g/L，硼酸为50-54g/L，硫酸铁10-20g/L，聚乙烯吡咯烷酮0.1-0.2mol/L，电镀工艺参数为：pH为3.5-4.5，电流密度为10-12A/dm2，温度约为40-44℃，时间为13-17min，其中电镀铬层的镀液组成为：硫酸铬0.30-0.40mol/L，硫酸钠0.9-1.1mol/L，硼酸0.3-0.5mol/L，硫酸镁0.2-0.4mol/L，十二烷基硫酸钠0.0001-0.004mol/L，甲酸0.2-0.4mol/L，光亮剂MP-33320-30ml/L，光亮剂MP-36610-14ml/L，电镀工艺参数为：pH为3-4，温度约45-55℃，电流密度12-14A/dm2，电镀的时间为40-60min。
CN201510721778.6A 2015-10-30 2015-10-30 一种毛巾挂架表面复合镀层的制备方法 Pending CN105177653A (zh)