CN105176451A - 一种水性瓷砖粘合剂及其制备方法和施工方法 - Google Patents
一种水性瓷砖粘合剂及其制备方法和施工方法 Download PDFInfo
- Publication number
- CN105176451A CN105176451A CN201510659230.3A CN201510659230A CN105176451A CN 105176451 A CN105176451 A CN 105176451A CN 201510659230 A CN201510659230 A CN 201510659230A CN 105176451 A CN105176451 A CN 105176451A
- Authority
- CN
- China
- Prior art keywords
- water
- tackiness agent
- tile
- adhesive
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种水性瓷砖粘合剂,其由以下重量百分比的组分制成:增粘剂:45-65%;有机溶剂:0.1-0.3%;水性颜料:0.1-0.5%;水:其余量。所述粘合剂的制备步骤包括:1)将增粘剂与有机溶剂于60-100℃下以1000-3000rpm的转速搅拌混合均匀形成混合组分A;2)将水性颜料与水于常温下搅拌混合均匀形成混合组分B;3)将步骤1)中的混合组分A与步骤2)中的混合组分B于40-60℃下以2000-4000rpm的转速搅拌混合均匀即可。其施工步骤包括:将所述粘合剂均匀涂刷在瓷砖的背面,待其固化呈半透明状态后,以水泥砂浆将瓷砖贴合于待贴合表面上即可。本发明的水性瓷砖粘合剂的制备方法简单、施工工艺简便、粘结力强,可有效解决瓷砖、大理石等上墙贴合后造成空鼓及脱落的问题。
Description
技术领域
本发明涉及一种粘合剂,具体涉及一种强粘结能力的水性瓷砖粘合剂及其制备方法,属于建材领域。
背景技术
随着近年来建筑业的快速发展,用于粘贴瓷砖、面砖、地砖等装饰材料的瓷砖粘合剂被大量应用于内外墙面、地面、浴室、厨房等建筑的饰面装饰场所。然而,现有的瓷砖粘合剂,大多属于刚性材料,导致水泥砂浆在成型后与瓷砖之间没有足够的附着力,在外部环境(如温度变化、地基或墙体下沉、裂缝、外力作用等)的影响下产生不同的应力和细微的移动,极易使得瓷砖和贴合面之间失去原有的粘结力,导致空鼓甚至瓷砖脱落的现象产生,不仅影响了建筑物的环境美观,甚至有可能威胁到人们的人身安全,存在着严重的不安全隐患。因此,开发一种具有强粘结力的瓷砖粘合剂是当前建材领域亟待解决的一个问题。
发明内容
本发明的目的在于克服现有技术的不足,提供一种具有强粘结力的水性瓷砖粘合剂,本发明的另一目的在于提供一种该粘合剂的制备方法。本发明的再一目的在于提供一种该粘合剂的施工工艺。
为实现上述目的,本发明采用以下技术方案:
本发明所述的水性瓷砖粘合剂,按重量百分比计,其由以下组成制成:
优选的是:按重量百分比计,所述水性瓷砖粘合剂由以下组分制成:
优选的是,所述增粘剂为聚丙烯酸丁酯和/或乙烯-醋酸乙烯共聚物。
优选的是,所述有机溶剂为甲苯;
优选的是,所述水性颜料水溶性颜料白、水溶性颜料黄、水性颜料蓝中的一种或几种。
本发明的另一目的,一种如上所述的水性瓷砖粘合剂的制备方法,包括以下制备步骤:
1)将增粘剂与有机溶剂于60-100℃下以1000-3000rpm的转速搅拌混合均匀形成混合组分A;
2)将水性颜料与水于常温下搅拌混合均匀形成混合组分B;
3)将步骤1)中的混合组分A与步骤2)中的混合组分B于40-60℃下以2000-4000rpm的转速搅拌混合均匀即得本发明所述的水性瓷砖粘合剂。
本发明的再一目的,一种如上所述的水性瓷砖粘合剂的施工方法,其步骤包括:将所述水性瓷砖粘合剂均匀涂刷在瓷砖/大理石的背面,待其固化呈半透明状态后,以水泥砂浆将瓷砖/大理石贴合于待贴合表面(如墙体)上即可。
进一步地,所述水性瓷砖粘合剂在瓷砖/大理石背面的涂刷厚度为0.5-2.5mm。
本发明的有益效果在于,本发明的水性瓷砖粘合剂的制备方法简单,粘结力强,可以解决当前瓷砖、大理石等上墙贴合后容易造成空鼓、脱落的安全问题,且施工工艺简便,仅需将本发明的水性瓷砖粘合剂均匀涂刷在瓷砖的背面,待其固化后,仅需通过水泥砂浆即可进行贴合,而无需使用现有其他任何的瓷砖胶。此外,本发明的粘合剂应用广泛,不仅适用于建筑装修过程中瓷砖、玻化砖、抛光砖、大理石、马赛克、玻璃等材料上墙或地面贴合,相比现在外墙干挂石材的施工会节省了大量成本及施工工期,节能环保。还可适用于墙面批灰(腻子)及水泥砂浆前期处理接着剂,并具有非常优异的防水性能。
具体实施方式
下面结合具体实施例对本发明的具体实施方式做进一步说明。但本发明并不仅限于下述实施例。若无特别说明,本发明各实施例中所采用的原料均可通过市场购买获得。
实施例1
一种水性瓷砖粘合剂,按重量百分比计,其由以下组分制成:聚丙烯酸丁酯:55%;甲苯:0.1%;水溶性颜料白:0.2%;水:其余量。
按照上述重量百分比的组成,所述粘合剂的制备步骤包括:
1)将聚丙烯酸丁酯与甲苯于80℃下以2500rpm的转速搅拌混合均匀形成混合组分A;
2)将水溶性颜料白与水于常温下搅拌混合均匀形成混合组分B;
3)将步骤1)中的混合组分A与步骤2)中的混合组分B于45℃下以3000rpm的转速搅拌混合均匀即得所述的水性瓷砖粘合剂。
经测试得,所制得的粘合剂的拉力为1.5-2.0千牛/5CM*5CM。
实施例2
一种水性瓷砖粘合剂,按重量百分比计,其由以下组分制成:聚丙烯酸丁酯:62%;甲苯:0.3%;水溶性颜料白:0.4%;水:其余量。
按照上述重量百分比的组成,所述粘合剂的制备步骤包括:
1)将聚丙烯酸丁酯与甲苯于75℃下以1500rpm的转速搅拌混合均匀形成混合组分A;
2)将水溶性颜料白与水于常温下搅拌混合均匀形成混合组分B;
3)将步骤1)中的混合组分A与步骤2)中的混合组分B于50℃下以2000rpm的转速搅拌混合均匀即得所述的水性瓷砖粘合剂。
经测试得,所制得的粘合剂的拉力为2.5-3.5千牛/5CM*5CM。
实施例3
一种水性瓷砖粘合剂,按重量百分比计,其由以下组分制成:乙烯-醋酸乙烯共聚物:45%;甲苯:0.1%;水溶性颜料黄:0.1%;水:其余量。
其制备过程同实施例1。
实施例4
一种水性瓷砖粘合剂,按重量百分比计,其由以下组分制成:聚丙烯酸丁酯:20%;乙烯-醋酸乙烯共聚物:30%;甲苯:0.3%;水溶性颜料蓝:0.2%;水:其余量。
其制备过程同实施例2。
上述实施例所制得的水性瓷砖粘合剂的施工过程包括:将所制得的水性瓷砖粘合剂均匀涂刷在瓷砖/大理石的背面,涂刷厚度为0.5-2.5mm,待其固化呈半透明状态后,以水泥砂浆将瓷砖/大理石贴合于待贴合表面(如墙体)上即可。此外,当在外墙高层使用时,可在待贴合墙体上按上述方法再涂刷一层厚度为0.5-2.5mm的粘合剂,然后再与涂刷有粘合剂的瓷砖进行贴合即可,以进一步增强贴合牢度。
本发明所描述的具体实施例只用于对该水性瓷砖粘合剂的具体实现过程的详细描述,而不是对其制备方法的限定。任何对此产品进行的修饰与改良,在专利范围或范畴内同类或相近物质的替代与使用,均属于本发明专利保护范围。
Claims (8)
1.一种水性瓷砖粘合剂,其特征在于:按重量百分比计,其由以下组分制成:
2.根据权利要求1所述的粘合剂,其特征在于:按重量百分比计,所述水性瓷砖粘合剂由以下组分制成:
3.根据权利要求1或2所述的粘合剂,其特征在于:所述增粘剂为聚丙烯酸丁酯和/或乙烯-醋酸乙烯共聚物。
4.根据权利要求1或2所述的粘合剂,其特征在于:所述有机溶剂为甲苯。
5.根据权利要求1或2所述的粘合剂,其特征在于:所述水性颜料水溶性颜料白、水溶性颜料黄、水性颜料蓝中的一种或几种。
6.一种如权利要求1或2所述的粘合剂的制备方法,其特征在于:包括以下制备步骤:
1)将增粘剂与有机溶剂于60-100℃下以1000-3000rpm的转速搅拌混合均匀形成混合组分A;
2)将水性颜料与水于常温下搅拌混合均匀形成混合组分B;
3)将步骤1)中的混合组分A与步骤2)中的混合组分B于40-60℃下以2000-4000rpm的转速搅拌混合均匀即可。
7.一种如权利要求1或2所述的粘合剂的施工方法,其特征在于:其施工步骤包括:将所述粘合剂均匀涂刷在瓷砖的背面,待其固化呈半透明状态后,以水泥砂浆将瓷砖贴合于待贴合表面上即可。
8.根据权利要求7所述的施工方法,其特征在于:所述粘合剂在瓷砖背面的涂刷厚度为0.5-2.5mm。