CN104973827A - 彩色墙体预拌砂浆 - Google Patents
彩色墙体预拌砂浆 Download PDFInfo
- Publication number
- CN104973827A CN104973827A CN201410126930.1A CN201410126930A CN104973827A CN 104973827 A CN104973827 A CN 104973827A CN 201410126930 A CN201410126930 A CN 201410126930A CN 104973827 A CN104973827 A CN 104973827A
- Authority
- CN
- China
- Prior art keywords
- mortar
- pigment
- wall
- cement
- color
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及彩色墙体预拌砂浆,由以下以重量百分比计的原料组成:水泥15%-18%;硅灰1%-3%,砂子70%-80%,颜料2%-5%,纤维素醚0.012%-0.015%,胶粉1%-2%,触变润滑剂0.2%-0.5%,疏水剂0.2%-0.5%,纤维0.3%-0.5%。本发明彩色墙体预拌砂浆,在施工时一次成型,不脱落、不褪色,经雨水冲洗颜色更加鲜艳,并且能起到一定的保温作用。本发明从配料时已不同于普通的预拌砂浆,添加了多种韧性的材料,对温差的适应性更好,因此不易开裂,使得砂浆在附着于墙面时其附着力更好。砂浆表面形成一种特殊抗水结构(改变接触角)使砂浆表面具有极强的疏水、憎水、防水、提高遮味效果,且砂浆具有耐污性、耐擦洗性等性能。
Description
技术领域
本发明涉及一种砂浆,特别是彩色墙体预拌砂浆,属于建筑材料领域。
背景技术
目前由于技术上、材料上的原因,涂料本身附着在外墙面后耐候性不好,容易褪色,甚至产生脱皮、剥落等现象,且日后墙面易产生龟裂,出现渗水现象。现有的涂料基本在1—2年后易褪色、开裂、脱落,且不易冲洗,造成墙面美观度差的问题。
发明内容
为了解决上述问题,本发明是通过以下技术方案实现的:
彩色墙体预拌砂浆,由以下以重量百分比计的原料组成:水泥15%-18%;硅灰1%-3%,砂子70%-80%,颜料2%-5%,纤维素醚0.012%-0.015%,胶粉1%-2%,触变润滑剂0.2%-0.5%,疏水剂0.2%-0.5%,纤维0.3%-0.5%。
进一步的,水泥采用P0.425水泥。
进一步的,纤维素醚为羟丙基纤维素醚。
进一步的,颜料为氧化铁颜料、氧化锰颜料、氧化铬颜料、群青颜料、赭石颜料、普鲁士红颜料中的一种。
本发明彩色墙体预拌砂浆能替代建筑物外墙装饰用瓷砖及外墙装饰用各种颜色的涂料,可根据建筑物的需要调配颜色,施工过程中可根据需求调整砂浆厚度。
本发明彩色墙体预拌砂浆,在施工时一次成型,不脱落、不褪色,经雨水冲洗颜色更加鲜艳,并且能起到一定的保温作用。本发明所述彩色墙体预拌砂浆从配料时已不同于普通的预拌砂浆,添加了多种韧性的材料,对温差的适应性更好,因此不易开裂,使得砂浆在附着于墙面时其附着力更好。砂浆表面形成一种特殊抗水结构(改变接触角)使砂浆表面具有极强的疏水、憎水、防水、提高遮味效果,且砂浆具有耐污性、耐擦洗性等性能。
具体实施方式
以下实施例用于说明本发明,但不用来限制本发明的范围。
彩色墙体预拌砂浆,由以下以重量百分比计的原料组成:水泥15%-18%;硅灰1%-3%,砂子70%-80%,颜料2%-5%,纤维素醚0.012%-0.015%,胶粉1%-2%,触变润滑剂0.2%-0.5%,疏水剂0.2%-0.5%,纤维0.3%-0.5%。颜料为氧化铁颜料、氧化锰颜料、氧化铬颜料、群青颜料、赭石颜料、普鲁士红颜料中的一种。
实施例一
在本实施例中,砂浆由以下以重量百分比计的原料组成:水泥采用P0.425水泥,17%;硅灰2%,砂子76%,氧化铁颜料3%,纤维素采用羟丙基纤维素醚0.012%,胶粉1.288%,触变润滑剂0.2%,疏水剂0.2%,纤维0.3%。
将上述比例的各组分加入搅拌器中搅拌均匀,即可入袋封装形成预拌砂浆。使用时,将袋装的上述比例的各组分加入搅拌器中搅拌10分钟,均匀后加水搅拌。
实施例二
在本实施例中,砂浆由以下以重量百分比计的原料组成:水泥采用P0.425水泥,18%;硅灰3%,砂子75%,氧化铬颜料2%,纤维素采用羟丙基纤维素醚0.012%,胶粉1.288%,触变润滑剂0.2%,疏水剂0.2%,纤维0.3%。
将上述比例的各组分加入搅拌器中搅拌均匀,即可入袋封装形成预拌砂浆。使用时,将袋装的上述比例的各组分加入搅拌器中搅拌10分钟,均匀后加水搅拌。
在其他实施例中,也可以在前述设定的范围内采用其他比例进行配比,以调整砂浆的颜色或其他性能。
本发明彩色墙体预拌砂浆可适用于所有各类砖混及浇筑建筑物的外墙,能替代建筑物外墙装饰用瓷砖及外墙装饰用各种颜色的涂料,可根据建筑物的需要调配颜色,施工过程中可根据需求调整砂浆厚度。
本发明彩色墙体预拌砂浆,在施工时一次成型,不脱落、不褪色,经雨水冲洗颜色更加鲜艳,并且能起到一定的保温作用。本发明所述彩色墙体预拌砂浆从配料时已不同于普通的预拌砂浆,添加了多种韧性的材料,对温差的适应性更好,因此不易开裂,使得砂浆在附着于墙面时其附着力更好。砂浆表面形成一种特殊抗水结构(改变接触角)使砂浆表面具有极强的疏水、憎水、防水、提高遮味效果,且砂浆具有耐污性、耐擦洗性等性能。
以上所述仅是本发明的优选实施方式,应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明技术原理的前提下,还可以做出若干改进和变型,这些改进和变型也应视为本发明的保护范围。
Claims (5)
1.彩色墙体预拌砂浆,其特征在于,由以下以重量百分比计的原料组成:水泥15%-18%;硅灰1%-3%,砂子70%-80%,颜料2%-5%,纤维素醚0.012%-0.015%,胶粉1%-2%,触变润滑剂0.2%-0.5%,疏水剂0.2%-0.5%,纤维0.3%-0.5%。
2.根据权利要求1所述的彩色墙体预拌砂浆,其特征在于,水泥采用P0.425水泥。
3.根据权利要求1或2所述的彩色墙体预拌砂浆,其特征在于,纤维素醚为羟丙基纤维素醚。
4.根据权利要求1或2所述的彩色墙体预拌砂浆,其特征在于,颜料为氧化铁颜料、氧化锰颜料、氧化铬颜料、群青颜料、赭石颜料、普鲁士红颜料中的一种。
5.根据权利要求3所述的彩色墙体预拌砂浆,其特征在于,颜料为氧化铁颜料、氧化锰颜料、氧化铬颜料、群青颜料、赭石颜料、普鲁士红颜料中的一种。