CN105176206A - Moldproof coating - Google Patents
Moldproof coating Download PDFInfo
- Publication number
- CN105176206A CN105176206A CN201510679593.3A CN201510679593A CN105176206A CN 105176206 A CN105176206 A CN 105176206A CN 201510679593 A CN201510679593 A CN 201510679593A CN 105176206 A CN105176206 A CN 105176206A
- Authority
- CN
- China
- Prior art keywords
- parts
- silver
- mould
- loaded
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses moldproof coating. The moldproof coating is prepared from silver-loaded calcium phosphate, silver-loaded, copper-loaded or zinc-loaded zeolite, hydroxyethyl cellulose, styrene-acrylate emulsion, polyethylene wax emulsion, diatomite, magnesium silicate, calcium sulfate, coloring pigment, a flatting agent, a defoaming agent, an anti-skinning agent, a coalescence solvent, diethylene glycol butyl ether, propylene glycol and deionized water. According to the moldproof coating disclosed by the invention, the silver-loaded calcium phosphate and the silver-loaded, copper-loaded or zinc-loaded zeolite are added in the moldproof coating, so that the moldproof coating has a moldproof sterilizing effect and a wide application prospect.
Description
Technical field
The present invention relates to a kind of building coating, be specifically related to a kind of mould-repellant coating.
Background technology
Mould-repellant coating is that its film can be bred by mould fungus inhibition, and the functional coating of growth, is mainly used in the moist place of improper ventilation, and is rich in nutraceutical shop building wall coating in environment, plays the effect beautifying and protect.At present, common mould-repellant coating mainly adds organic mould inhibitor if sodium pentachlorophenate, Phenylmercuric Acetate, derosal, m-tetrachlorophthalodinitrile, mould inhibitor etc. or inorganic mould inhibitor are as nanometer silver, Nanometer Copper, Nano-Zinc or multiple inorganic nano material doping techniques synthesis class powder etc., and organic mould-repellant coating is containing bio-toxicity medicine, inorganic mould-repellant coating just can not grow the one protection coating developed by mould fungus inhibition containing bio-toxicity medicine, the demand that more can meet market of inorganic mould-repellant coating, has wide application prospect.
Summary of the invention
The object of the invention is to, for prior art, provide a kind of mould-repellant coating, it has good sterilization antienzyme effect.
For achieving the above object, the present invention takes following technical scheme: a kind of mould-repellant coating, specifically by carrying silver-colored calcium phosphate, carry silver-colored or copper-loaded or year zinc zeolite, Natvosol, styrene-acrylate emulsion, polythene wax emulsion, diatomite, Magnesium Silicate q-agent, calcium sulfate, tinting pigment, flow agent, defoamer, anti skinning agent, agglomerated solvent, butyl carbitol, propylene glycol and a deionized water and make.
Wherein, the proportion by weight of each component of described mould-repellant coating is: year silver-colored calcium phosphate 5 ~ 10 part, year are silver-colored or copper-loaded or carry 7 ~ 8 parts, zinc zeolite, Natvosol 20 ~ 25 parts, styrene-acrylate emulsion 15 ~ 26 parts, polythene wax emulsion 10 ~ 15 parts, 30 ~ 50 parts, diatomite, Magnesium Silicate q-agent 20 ~ 30 parts, 22 ~ 25 parts, calcium sulfate, tinting pigment 5 ~ 10 parts, flow agent 8 ~ 9 parts, defoamer 5 ~ 8 parts, anti skinning agent 1 ~ 3 part, agglomerated solvent 3 ~ 6 parts, butyl carbitol 10 ~ 15 parts, propylene glycol 12 ~ 15 parts, deionized water 15 ~ 17 parts;
Further illustrate, described year silver (copper, a zinc) zeolite is by the aqueous solution of the argentiferous of high density (copper, zinc) ion, make the zeolite structured interior basic metal of silver (copper, zinc) ion exchange or alkaline-earth metal ions and the active anti-biotic material of a kind of globality made, wherein, the zeolite per-cent shared by silver, copper, zinc is respectively 2 ~ 5%, 10 ~ 15%, 10 ~ 15%.
Further illustrate, year silver-colored calcium phosphate carries out high temperature sintering with more than 1000 DEG C after being mixed with silver iron compound by calcium phosphate, then obtain after pulverizing, grinding.
Wherein, described tinting pigment is green wherein a kind of of zinc white, iron oxide yellow, molybdenum red, cadmium or the composite pigment by its several allotment.
Wherein, described anti skinning agent is the one of methyl ethyl ketoxime, butyraldehyde oxime, cyclohexanone-oxime.
Wherein, green wherein a kind of of described iron oxide yellow, molybdenum red, cadmium or the composite pigment by its several allotment.
The invention has the beneficial effects as follows: a kind of mould-repellant coating of the present invention adds year silver (copper, zinc) zeolite and carries silver-colored calcium phosphate two kinds of anti-fungus materials, has good mildew-resistant, sterilization effect.
Embodiment
Below in conjunction with specific embodiment, the present invention is further described.
Embodiment 1
Each component of a kind of mould-repellant coating of the present invention and proportion by weight be: carry 5 parts, silver-colored calcium phosphate, zeolite with carrying silver 7.5 parts, Natvosol 25 parts, styrene-acrylate emulsion 18 parts, polythene wax emulsion 10 parts, 40 parts, diatomite, Magnesium Silicate q-agent 20 parts, 25 parts, calcium sulfate, tinting pigment 10 parts, flow agent 8 parts, defoamer 7 parts, anti skinning agent 1 part, agglomerated solvent 6 parts, butyl carbitol 12 parts, propylene glycol 15 parts, deionized water 17 parts; In zeolite with carrying silver silver percentage composition be 3%.
Embodiment 2
Each component of a kind of mould-repellant coating of the present invention and proportion by weight be: carry 7 parts, silver-colored calcium phosphate, 7 parts, copper-loaded zeolite, Natvosol 22 parts, styrene-acrylate emulsion 26 parts, polythene wax emulsion 15 parts, 30 parts, diatomite, Magnesium Silicate q-agent 30 parts, 22 parts, calcium sulfate, tinting pigment 8 parts, flow agent 9 parts, defoamer 8 parts, anti skinning agent 2 parts, agglomerated solvent 3 parts, butyl carbitol 10 parts, propylene glycol 14 parts, deionized water 16 parts.Wherein, in copper-loaded zeolite copper percentage composition be 12%.
Embodiment 3
Each component of a kind of mould-repellant coating of the present invention and proportion by weight be: carry 8 parts, silver-colored calcium phosphate 10 part, year zinc zeolite, Natvosol 20 parts, styrene-acrylate emulsion 15 parts, polythene wax emulsion 13 parts, 50 parts, diatomite, Magnesium Silicate q-agent 25 parts, 24 parts, calcium sulfate, tinting pigment 5 parts, flow agent 8 parts, defoamer 5 parts, anti skinning agent 3 parts, agglomerated solvent 5 parts, butyl carbitol 15 parts, propylene glycol 12 parts, deionized water 15 parts.Wherein, carry zinc in zinc zeolite percentage composition be 15%.
Claims (6)
1. a mould-repellant coating, is characterized in that: its by carrying silver-colored calcium phosphate, carry silver-colored or copper-loaded or year zinc zeolite, Natvosol, styrene-acrylate emulsion, polythene wax emulsion, diatomite, Magnesium Silicate q-agent, calcium sulfate, tinting pigment, flow agent, defoamer, anti skinning agent, agglomerated solvent, butyl carbitol, propylene glycol and a deionized water and make.
2. a kind of mould-repellant coating according to claim 1, it is characterized in that: the proportion by weight of each component of described mould-repellant coating is: carry 5 ~ 10 parts, silver-colored calcium phosphate, carry silver-colored or copper-loaded or carry 7 ~ 8 parts, iron zeolite, Natvosol 20 ~ 25 parts, styrene-acrylate emulsion 15 ~ 26 parts, polythene wax emulsion 10 ~ 15 parts, 30 ~ 50 parts, diatomite, Magnesium Silicate q-agent 20 ~ 30 parts, 22 ~ 25 parts, calcium sulfate, tinting pigment 5 ~ 10 parts, flow agent 8 ~ 9 parts, defoamer 5 ~ 8 parts, anti skinning agent 1 ~ 3 part, agglomerated solvent 3 ~ 6 parts, butyl carbitol 10 ~ 15 parts, propylene glycol 12 ~ 15 parts, deionized water 15 ~ 17 parts.
3. a kind of mould-repellant coating according to claim 1 and 2, is characterized in that: described carries silver-colored or copper-loaded or carry in zinc zeolite, and the zeolite per-cent shared by silver, copper, zinc is respectively 2 ~ 5%, 10 ~ 15%, 10 ~ 15%.
4. a kind of mould-repellant coating according to claim 1 and 2, is characterized in that: described tinting pigment is green wherein a kind of of zinc white, iron oxide yellow, molybdenum red, cadmium or the composite pigment by its several allotment.
5. a kind of mould-repellant coating according to claim 1 and 2, is characterized in that: described anti skinning agent is the one of methyl ethyl ketoxime, butyraldehyde oxime, cyclohexanone-oxime.
6. a kind of mould-repellant coating according to claim 1 and 2, is characterized in that: described flow agent is polydimethylsiloxane or alkyl-modified organo-siloxane.