CN106147527A - A kind of aqueous epoxy coating used for building exterior wall - Google Patents
A kind of aqueous epoxy coating used for building exterior wall Download PDFInfo
- Publication number
- CN106147527A CN106147527A CN201610573932.4A CN201610573932A CN106147527A CN 106147527 A CN106147527 A CN 106147527A CN 201610573932 A CN201610573932 A CN 201610573932A CN 106147527 A CN106147527 A CN 106147527A
- Authority
- CN
- China
- Prior art keywords
- parts
- exterior wall
- aqueous
- building exterior
- epoxy resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of aqueous epoxy coating used for building exterior wall, its raw material includes by weight: bisphenol A type epoxy resin 20 40 parts, aqueous acrylic modified epoxy resin 2 14 parts, styrene-acrylic emulsion 5 15 parts, tripolycyanamide 26 parts, coalescents 13 parts, Pulvis Talci 2 10 parts, activated carbon 5 15 parts, hollow glass microballoon 2 10 parts, calcinated argil 14 parts, aluminium silicate 28 parts, nano silicon 14 parts, zinc phosphate 27 parts, sodium hydroxide 16 parts, 13 parts of glacial acetic acid, polyvinyl alcohol 2 10 parts, anti-settling agent 12 parts, preservative 12 parts, defoamer 12 parts, 20 50 parts of water.The aqueous epoxy coating used for building exterior wall that the present invention proposes, gained coating heat stability, water resistance are good, and good toughness, and hardness is high.
Description
Technical field
The present invention relates to exterior coating technical field, particularly relate to a kind of aqueous epoxy coating used for building exterior wall.
Background technology
At present solvent-borne type is coated with coating and mostly contain organic solvent, as easy as rolling off a log volatilization in coating process, and severe contamination is greatly
Gas, destroys ecological environment, and nowadays environmental conservation increasingly comes into one's own, and water paint will replace traditional solvent-borne type and be coated with
Material, in coating used for building exterior wall, is widely used owing to aqueous epoxy coating adhesive force is good, shrinkage factor is low, but generally speaking
The heat stability of aqueous epoxy coating, waterproof, toughness and hardness and oiliness epoxy coating also have quite poor away from, how to prepare one
Kind of heat stability, water resistance are good, and good toughness, and the aqueous epoxy coating that hardness is high becomes and the technology of solution is presently required asks
Topic.
Summary of the invention
The technical problem existed based on background technology, the present invention proposes a kind of aqueous epoxy coating used for building exterior wall, institute
Coating heat stability, water resistance are good, and good toughness, hardness is high.
The one aqueous epoxy coating used for building exterior wall that the present invention proposes, its raw material includes by weight: bisphenol type epoxy
Resin 20-40 part, aqueous acrylic modified epoxy resin 2-14 part, styrene-acrylic emulsion 5-15 part, tripolycyanamide 2-6 part, film forming helps
Agent 1-3 part, Pulvis Talci 2-10 part, activated carbon 5-15 part, hollow glass microballoon 2-10 part, calcinated argil 1-4 part, aluminium silicate 2-8
Part, nano silicon 1-4 part, zinc phosphate 2-7 part, sodium hydroxide 1-6 part, glacial acetic acid 1-3 part, polyvinyl alcohol 2-10 part is anti-
Heavy agent 1-2 part, preservative 1-2 part, defoamer 1-2 part, water 20-50 part.
Preferably, bisphenol A type epoxy resin, aqueous acrylic modified epoxy resin, the weight ratio of styrene-acrylic emulsion are 25-
35:5-10:8-12.
Preferably, Pulvis Talci, activated carbon, hollow glass microballoon, calcinated argil, aluminium silicate, nano silicon, zinc phosphate
Weight ratio be 4-8:8-12:4-8:2-3:4-6:2-3:4-5.
Preferably, sodium hydroxide, glacial acetic acid, the weight ratio of polyvinyl alcohol are 3-5:1.5-2.5:4-8.
Preferably, anti-settling agent, preservative, the weight ratio of defoamer are 1.5-1.8:1.5-1.8:1.2-1.5.
Preferably, its raw material includes by weight: bisphenol A type epoxy resin 25-35 part, aqueous acrylic modified asphalt mixtures modified by epoxy resin
Fat 5-10 part, styrene-acrylic emulsion 8-12 part, tripolycyanamide 3-5 part, coalescents 1.5-2.5 part, Pulvis Talci 4-8 part, activated carbon 8-
12 parts, hollow glass microballoon 4-8 part, calcinated argil 2-3 part, aluminium silicate 4-6 part, nano silicon 2-3 part, zinc phosphate 4-5
Part, sodium hydroxide 3-5 part, glacial acetic acid 1.5-2.5 part, polyvinyl alcohol 4-8 part, anti-settling agent 1.5-1.8 part, preservative 1.5-1.8
Part, defoamer 1.2-1.5 part, water 30-40 part.
In the present invention, use bisphenol A type epoxy resin, aqueous acrylic modified epoxy resin, styrene-acrylic emulsion synergism,
Each other compatibility is good, and can supply a gap each other, heat-resisting, corrosion-resistant, ageing-resistant performance is excellent, in tripolycyanamide, film forming
Under the effect of auxiliary agent after film-forming, film layer is closely knit, and good toughness is the most easy to crack, and sodium hydroxide, glacial acetic acid, polyvinyl alcohol can
Effectively molecular weight after regulation solidification, on the premise of ensureing toughness, hardness is moderate, and the Pulvis Talci added, activated carbon, hollow glass
Glass microsphere, calcinated argil, aluminium silicate, nano silicon, zinc phosphate mating reaction, thermally-stabilised fabulous, and excellent in mechanical performance,
Wherein activated carbon is internal fabulous to rest materials adsorptivity containing a large amount of cavitys, and hollow glass microballoon hydrophobicity is good, and can have
Effect strengthens dispersibility between rest materials, activated carbon and hollow glass microballoon synergism, and goods water resistance is good, and divides each other
Dissipating closely knit, with bisphenol A type epoxy resin, aqueous acrylic modified epoxy resin, styrene-acrylic emulsion effect, toughness is with hardness the most relatively
Good, water resistance is excellent, and heat stability is fabulous.
Detailed description of the invention
Below, by specific embodiment, technical scheme is described in detail.
Embodiment 1
The one aqueous epoxy coating used for building exterior wall that the present invention proposes, its raw material includes by weight: bisphenol type epoxy
Resin 20 parts, aqueous acrylic modified epoxy resin 14 parts, styrene-acrylic emulsion 5 parts, tripolycyanamide 6 parts, coalescents 1 part, Talcum
10 parts of powder, activated carbon 5 parts, hollow glass microballoon 10 parts, calcinated argil 1 part, aluminium silicate 8 parts, nano silicon 1 part, phosphoric acid
7 parts of zinc, sodium hydroxide 1 part, 3 parts of glacial acetic acid, polyvinyl alcohol 2 parts, anti-settling agent 2 parts, preservative 1 part, defoamer 2 parts, 20 parts of water.
Embodiment 2
The one aqueous epoxy coating used for building exterior wall that the present invention proposes, its raw material includes by weight: bisphenol type epoxy
Resin 40 parts, aqueous acrylic modified epoxy resin 2 parts, styrene-acrylic emulsion 15 parts, tripolycyanamide 2 parts, coalescents 3 parts, Talcum
2 parts of powder, activated carbon 15 parts, hollow glass microballoon 2 parts, calcinated argil 4 parts, aluminium silicate 2 parts, nano silicon 4 parts, zinc phosphate
2 parts, sodium hydroxide 6 parts, 1 part of glacial acetic acid, polyvinyl alcohol 10 parts, anti-settling agent 1 part, preservative 2 parts, defoamer 1 part, 50 parts of water.
Embodiment 3
The one aqueous epoxy coating used for building exterior wall that the present invention proposes, its raw material includes by weight: bisphenol type epoxy
Resin 25 parts, aqueous acrylic modified epoxy resin 10 parts, styrene-acrylic emulsion 8 parts, tripolycyanamide 5 parts, coalescents 1.5 parts is sliding
Stone powder 8 parts, activated carbon 8 parts, hollow glass microballoon 8 parts, calcinated argil 2 parts, aluminium silicate 6 parts, nano silicon 2 parts, phosphoric acid
5 parts of zinc, sodium hydroxide 3 parts, 2.5 parts of glacial acetic acid, polyvinyl alcohol 4 parts, anti-settling agent 1.8 parts, preservative 1.5 parts, defoamer 1.5
Part, 30 parts of water.
Embodiment 4
The one aqueous epoxy coating used for building exterior wall that the present invention proposes, its raw material includes by weight: bisphenol type epoxy
Resin 35 parts, aqueous acrylic modified epoxy resin 5 parts, styrene-acrylic emulsion 12 parts, tripolycyanamide 3 parts, coalescents 2.5 parts is sliding
Stone powder 4 parts, activated carbon 12 parts, hollow glass microballoon 4 parts, calcinated argil 3 parts, aluminium silicate 4 parts, nano silicon 3 parts, phosphoric acid
4 parts of zinc, sodium hydroxide 5 parts, 1.5 parts of glacial acetic acid, polyvinyl alcohol 8 parts, anti-settling agent 1.5 parts, preservative 1.8 parts, defoamer 1.2
Part, 40 parts of water.
Embodiment 5
The one aqueous epoxy coating used for building exterior wall that the present invention proposes, its raw material includes by weight: bisphenol type epoxy
Resin 30 parts, aqueous acrylic modified epoxy resin 8 parts, styrene-acrylic emulsion 10 parts, tripolycyanamide 4 parts, coalescents 2 parts, Talcum
6 parts of powder, activated carbon 10 parts, hollow glass microballoon 6 parts, calcinated argil 2.5 parts, aluminium silicate 5 parts, nano silicon 2.5 parts, phosphorus
4.5 parts of zinc of acid, sodium hydroxide 4 parts, 2 parts of glacial acetic acid, polyvinyl alcohol 6 parts, anti-settling agent 1.6 parts, preservative 1.7 parts, defoamer 1.3
Part, 35 parts of water.
The above, the only present invention preferably detailed description of the invention, but protection scope of the present invention is not limited thereto,
Any those familiar with the art in the technical scope that the invention discloses, according to technical scheme and
Inventive concept equivalent or change in addition, all should contain within protection scope of the present invention.
Claims (6)
1. an aqueous epoxy coating used for building exterior wall, it is characterised in that its raw material includes by weight: bisphenol type epoxy tree
Fat 20-40 part, aqueous acrylic modified epoxy resin 2-14 part, styrene-acrylic emulsion 5-15 part, tripolycyanamide 2-6 part, coalescents
1-3 part, Pulvis Talci 2-10 part, activated carbon 5-15 part, hollow glass microballoon 2-10 part, calcinated argil 1-4 part, aluminium silicate 2-8 part,
Nano silicon 1-4 part, zinc phosphate 2-7 part, sodium hydroxide 1-6 part, glacial acetic acid 1-3 part, polyvinyl alcohol 2-10 part, anti-settling agent
1-2 part, preservative 1-2 part, defoamer 1-2 part, water 20-50 part.
Aqueous epoxy coating the most used for building exterior wall, it is characterised in that bisphenol A type epoxy resin, aqueous
Acrylic modified epoxy resin, the weight ratio of styrene-acrylic emulsion are 25-35:5-10:8-12.
Aqueous epoxy coating used for building exterior wall the most according to claim 1 or claim 2, it is characterised in that Pulvis Talci, activated carbon, in
Empty glass microsphere, calcinated argil, aluminium silicate, nano silicon, the weight ratio of zinc phosphate are 4-8:8-12:4-8:2-3:4-6:
2-3:4-5.
4. according to aqueous epoxy coating used for building exterior wall described in any one of claim 1-3, it is characterised in that sodium hydroxide, ice
Acetic acid, the weight ratio of polyvinyl alcohol are 3-5:1.5-2.5:4-8.
5. according to aqueous epoxy coating used for building exterior wall described in any one of claim 1-4, it is characterised in that anti-settling agent, anticorrosion
Agent, the weight ratio of defoamer are 1.5-1.8:1.5-1.8:1.2-1.5.
6. according to aqueous epoxy coating used for building exterior wall described in any one of claim 1-5, it is characterised in that its raw material is by weight
Part includes: bisphenol A type epoxy resin 25-35 part, aqueous acrylic modified epoxy resin 5-10 part, styrene-acrylic emulsion 8-12 part, three
Poly cyanamid 3-5 part, coalescents 1.5-2.5 part, Pulvis Talci 4-8 part, activated carbon 8-12 part, hollow glass microballoon 4-8 part, calcining
Potter's clay 2-3 part, aluminium silicate 4-6 part, nano silicon 2-3 part, zinc phosphate 4-5 part, sodium hydroxide 3-5 part, glacial acetic acid 1.5-
2.5 parts, polyvinyl alcohol 4-8 part, anti-settling agent 1.5-1.8 part, preservative 1.5-1.8 part, defoamer 1.2-1.5 part, water 30-40
Part.