CN108587413A - A kind of exterior wall waterborne epoxy coatings - Google Patents
A kind of exterior wall waterborne epoxy coatings Download PDFInfo
- Publication number
- CN108587413A CN108587413A CN201810537418.4A CN201810537418A CN108587413A CN 108587413 A CN108587413 A CN 108587413A CN 201810537418 A CN201810537418 A CN 201810537418A CN 108587413 A CN108587413 A CN 108587413A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- exterior wall
- complex microsphere
- waterborne epoxy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of exterior wall waterborne epoxy coatings, raw material includes by weight：20 30 parts of bisphenol A type epoxy resin, 10 20 parts of epoxy polyurethane resin, 23 34 parts of novolac epoxy resin, between 13 parts of aminomethylamine, 12 parts of coalescents, 10 30 parts of packing strengthening agent, 12 parts of trbasic zinc phosphate, 29 parts of polyvinyl alcohol, 12 parts of antiseptic, 12 parts of dispersant, 0.2 1 parts of mould inhibitor, 0.2 0.5 parts of antifoaming agent, 12 parts of wetting agent, 50 100 parts of water.Packing strengthening agent includes by weight：2 10 parts of complex microsphere, 13 parts of expanded perlite, 24 parts of diatomite, 29 parts of flyash, 14 parts of aluminium borate whisker, 12 parts of zinc oxide.Waterproof of the present invention and adhesion property are extremely strong, and cheap, environmental protection, while can mitigate wall to the bearing load of coating and can get preferable heat insulation effect, and it is suitable for the constructions of the external wall waterproof of insulation system.
Description
Technical field
The present invention relates to technical field of coatings more particularly to a kind of exterior wall waterborne epoxy coatings.
Background technology
In each field, being widely used for coating is general, on exterior wall, industrial warehouse, and chemical industry, oil, food service industry class
Basin and pipe surface, the buildings such as workshop, modernization farm, freezer, residential house, office building are first-class.
Tradition is all the coating for organic solvent, and the pollution of the coating is serious, therefore, now everybody large area is opened
Begin to use water paint, especially waterborne epoxy coatings, and for exterior coating, the attachment of existing waterborne epoxy coatings
It is all not good enough with water resistance.
Invention content
Technical problems based on background technology, the present invention propose a kind of exterior wall waterborne epoxy coatings, waterproof and
Adhesion property is extremely strong, and cheap, environmental protection, fully biodegradable, at the same can mitigate wall to the bearing load of coating and
Preferable heat insulation effect is can get, it is suitable for the constructions of the external wall waterproof of insulation system.
A kind of exterior wall waterborne epoxy coatings proposed by the present invention, raw material include by weight：Bisphenol A type epoxy resin
20-30 parts, 10-20 parts of epoxy polyurethane resin, 23-34 parts of novolac epoxy resin, 1-3 parts of aminomethylamine, coalescents 1-2
Part, 10-30 parts of packing strengthening agent, 1-2 parts of trbasic zinc phosphate, 2-9 parts of polyvinyl alcohol, 1-2 parts of antiseptic, 1-2 parts of dispersant, mould inhibitor
0.2-1 parts, 0.2-0.5 parts of antifoaming agent, 1-2 parts of wetting agent, 50-100 parts of water.
Preferably, packing strengthening agent includes by weight：2-10 parts of complex microsphere, 1-3 parts of expanded perlite, diatomite 2-
4 parts, 2-9 parts of flyash, 1-4 parts of aluminium borate whisker, 1-2 parts of zinc oxide.
Preferably, complex microsphere is prepared using following technique：Epoxychloropropane, sorbester p17, atoleine are uniformly mixed
Obtain organic phase；Starch, humic acid, water being mixed, heating stirring, cooling, sodium hydroxide, which is added, under stirring is uniformly mixed,
It adds epoxychloropropane and is uniformly mixing to obtain water phase；Aqueous dispersions are stirred in organic phase, are filtered, filter residue uses epoxy successively
Ethane, absolute ethyl alcohol, water washing obtain complex microsphere.
Preferably, in the preparation process of complex microsphere, epoxychloropropane, sorbester p17, atoleine weight ratio be 2-4：
0.2-0.9：30-50.
Preferably, in the preparation process of complex microsphere, starch, humic acid, water, sodium hydroxide, epoxychloropropane weight
Than for 10-20：4-10：80-150：1-2：1-2.
Preferably, in the preparation process of complex microsphere, the weight ratio of water phase and organic phase is 20-40：80-100.
Preferably, in the preparation process of complex microsphere, starch, humic acid, water are mixed, are warming up to 92-98 DEG C of stirring 5-
15min is down to room temperature.
The present invention uses bisphenol A type epoxy resin, epoxy polyurethane resin and novolac epoxy resin compounding for major ingredient, processing
Function admirable, and aminomethylamine can control the open loop degree of major ingredient, adhesive force and water resistance are good after film-forming；The present invention
Complex microsphere in, water phase is wrapped up by organic phase, humic acid is fixed in starch and forms microballoon, cheap, environmental protection can be complete
Biodegradation, and it is good with expanded perlite, diatomite, flyash, aluminium borate whisker dispersion effect, it is internal not only to have very much
Cavity has very strong affinity with other raw materials, can significantly increase the waterproof and adhesion property of film；And complex microsphere with it is poly-
The miscible effect of vinyl alcohol is good, and the film after solidification has high crosslink density, the characteristics of high rigidity and fabulous water-fast, resistance to
Chemicals energy, and the light material of complex microsphere can mitigate wall to the bearing load of coating and can get preferable heat preservation
Effect, it is suitable for the constructions of the external wall waterproof of insulation system.
Specific implementation mode
In the following, technical scheme of the present invention is described in detail by specific embodiment.
Embodiment 1
A kind of exterior wall waterborne epoxy coatings, raw material include：Bisphenol A type epoxy resin 20kg, epoxy polyurethane resin
20kg, novolac epoxy resin 23kg, aminomethylamine 3kg, coalescents 1kg, packing strengthening agent 30kg, trbasic zinc phosphate 1kg, poly- second
Enol 9kg, antiseptic 1kg, dispersant 2kg, mould inhibitor 0.2kg, antifoaming agent 0.5kg, wetting agent 1kg, water 100kg；Filling is mended
Strong agent is 2 by weight by complex microsphere, expanded perlite, diatomite, flyash, aluminium borate whisker, zinc oxide：3：2：9：1：
2 compositions.
Complex microsphere is prepared using following technique：2kg epoxychloropropane, 0.9kg sorbester p17s, 30kg atoleines are mixed
Uniformly obtain organic phase；20kg starch, 4kg humic acid, 150kg water are mixed, 92 DEG C of stirring 15min is warming up to, is down to room temperature,
1kg sodium hydroxides are added under stirring to be uniformly mixed, adds 2kg epoxychloropropane and is uniformly mixing to obtain water phase；By 20kg
Aqueous dispersions stir 2h in 100kg organic phases, and filtering, filter residue is obtained with ethylene oxide, absolute ethyl alcohol, water washing compound successively
Microballoon.
Embodiment 2
A kind of exterior wall waterborne epoxy coatings, raw material include：Bisphenol A type epoxy resin 30kg, epoxy polyurethane resin
10kg, novolac epoxy resin 34kg, aminomethylamine 1kg, coalescents 2kg, packing strengthening agent 10kg, trbasic zinc phosphate 2kg, poly- second
Enol 2kg, antiseptic 2kg, dispersant 1kg, mould inhibitor 1kg, antifoaming agent 0.2kg, wetting agent 2kg, water 50kg；Packing strengthening agent
It is 10 by weight by complex microsphere, expanded perlite, diatomite, flyash, aluminium borate whisker, zinc oxide：1：4：2：4：1 group
At.
Complex microsphere is prepared using following technique：4kg epoxychloropropane, 0.2kg sorbester p17s, 50kg atoleines are mixed
Uniformly obtain organic phase；10kg starch, 10kg humic acid, 80kg water are mixed, 98 DEG C of stirring 5min is warming up to, is down to room temperature,
2kg sodium hydroxides are added under stirring to be uniformly mixed, adds 1kg epoxychloropropane and is uniformly mixing to obtain water phase；By 40kg
Aqueous dispersions stir 6h in 80kg organic phases, and filtering, filter residue is obtained with ethylene oxide, absolute ethyl alcohol, water washing compound successively
Microballoon.
Embodiment 3
A kind of exterior wall waterborne epoxy coatings, raw material include：Bisphenol A type epoxy resin 22kg, epoxy polyurethane resin
18kg, novolac epoxy resin 25kg, aminomethylamine 2.5kg, coalescents 1.2kg, packing strengthening agent 25kg, trbasic zinc phosphate
1.2kg, polyvinyl alcohol 8kg, antiseptic 1.2kg, dispersant 1.7kg, mould inhibitor 0.4kg, antifoaming agent 0.4kg, wetting agent
1.2kg, water 80kg；Packing strengthening agent is by complex microsphere, expanded perlite, diatomite, flyash, aluminium borate whisker, zinc oxide
It is 4 by weight：2.5：2.5：8：2：1.8 composition.
Complex microsphere is prepared using following technique：2.5kg epoxychloropropane, 0.8kg sorbester p17s, 35kg atoleines are mixed
Conjunction uniformly obtains organic phase；18kg starch, 6kg humic acid, 140kg water are mixed, 94 DEG C of stirring 12min is warming up to, is down to room
1.2kg sodium hydroxides are added under stirring and are uniformly mixed, adds 1.7kg epoxychloropropane and is uniformly mixing to obtain water phase for temperature；
25kg Aqueous dispersions are stirred into 3h in 95kg organic phases, are filtered, filter residue is obtained with ethylene oxide, absolute ethyl alcohol, water washing successively
To complex microsphere.
Embodiment 4
A kind of exterior wall waterborne epoxy coatings, raw material include：Bisphenol A type epoxy resin 28kg, epoxy polyurethane resin
12kg, novolac epoxy resin 30kg, aminomethylamine 1.5kg, coalescents 1.8kg, packing strengthening agent 15kg, trbasic zinc phosphate
1.8kg, polyvinyl alcohol 4kg, antiseptic 1.8kg, dispersant 1.3kg, mould inhibitor 0.8kg, antifoaming agent 0.3kg, wetting agent
1.8kg, water 60kg；Packing strengthening agent is by complex microsphere, expanded perlite, diatomite, flyash, aluminium borate whisker, zinc oxide
It is 8 by weight：1.5：3.5：4：3：1.2 composition.
Complex microsphere is prepared using following technique：3.5kg epoxychloropropane, 0.4kg sorbester p17s, 45kg atoleines are mixed
Conjunction uniformly obtains organic phase；12kg starch, 8kg humic acid, 100kg water are mixed, 96 DEG C of stirring 8min is warming up to, is down to room
1.8kg sodium hydroxides are added under stirring and are uniformly mixed, adds 1.3kg epoxychloropropane and is uniformly mixing to obtain water phase for temperature；
35kg Aqueous dispersions are stirred into 5h in 85kg organic phases, are filtered, filter residue is obtained with ethylene oxide, absolute ethyl alcohol, water washing successively
To complex microsphere.
Embodiment 5
A kind of exterior wall waterborne epoxy coatings, raw material include：Bisphenol A type epoxy resin 25kg, epoxy polyurethane resin
15kg, novolac epoxy resin 28kg, aminomethylamine 2kg, coalescents 1.5kg, packing strengthening agent 20kg, trbasic zinc phosphate 1.5kg,
Polyvinyl alcohol 6kg, antiseptic 1.5kg, dispersant 1.5kg, mould inhibitor 0.6kg, antifoaming agent 0.35kg, wetting agent 1.5kg, water
70kg；Packing strengthening agent by complex microsphere, expanded perlite, diatomite, flyash, aluminium borate whisker, zinc oxide by weight
It is 6：2：3：6：2.5：1.5 composition.
Complex microsphere is prepared using following technique：3kg epoxychloropropane, 0.6kg sorbester p17s, 40kg atoleines are mixed
Uniformly obtain organic phase；15kg starch, 7kg humic acid, 120kg water are mixed, 95 DEG C of stirring 10min is warming up to, is down to room temperature,
1.5kg sodium hydroxides are added under stirring to be uniformly mixed, adds 1.5kg epoxychloropropane and is uniformly mixing to obtain water phase；It will
30kg Aqueous dispersions stir 4h in 90kg organic phases, and filtering, filter residue is obtained with ethylene oxide, absolute ethyl alcohol, water washing successively
Complex microsphere.
5 gained exterior wall waterborne epoxy coatings of embodiment and commercially available common water borne epoxy coating are compared, result
It is as follows：
| Embodiment 5 | Commercially available common water borne epoxy coating | |
| Tensile strength, Mpa | 3.1 | 2.0 |
| Adhesive strength, Mpa | 1.6 | 1.2 |
| Impermeability (0.3Mpa, 30min) | It is waterproof | It is permeable |
| Impervious (mortar back side), Mpa | 1.0 | 0.8 |
| Heat resistance (100 DEG C of water, 5h) | Without cracking, peel off | Cracking peels off |
| Flexural strength (28 days), Mpa | 8.8 | 8.0 |
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Any one skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (7)
1. a kind of exterior wall waterborne epoxy coatings, which is characterized in that its raw material includes by weight：Bisphenol A type epoxy resin 20-
30 parts, 10-20 parts of epoxy polyurethane resin, 23-34 parts of novolac epoxy resin, 1-3 parts of aminomethylamine, 1-2 parts of coalescents,
10-30 parts of packing strengthening agent, 1-2 parts of trbasic zinc phosphate, 2-9 parts of polyvinyl alcohol, 1-2 parts of antiseptic, 1-2 parts of dispersant, mould inhibitor
0.2-1 parts, 0.2-0.5 parts of antifoaming agent, 1-2 parts of wetting agent, 50-100 parts of water.
2. exterior wall waterborne epoxy coatings according to claim 1, which is characterized in that packing strengthening agent includes by weight：
2-10 parts of complex microsphere, 1-3 parts of expanded perlite, 2-4 parts of diatomite, 2-9 parts of flyash, 1-4 parts of aluminium borate whisker, zinc oxide
1-2 parts.
3. exterior wall waterborne epoxy coatings according to claim 2, which is characterized in that complex microsphere uses following technique system
It is standby：Epoxychloropropane, sorbester p17, atoleine are uniformly mixed and obtain organic phase；Starch, humic acid, water are mixed, heating is stirred
It mixes, cools down, sodium hydroxide is added under stirring and is uniformly mixed, adds epoxychloropropane and is uniformly mixing to obtain water phase；By water
It is mutually dispersed in organic phase and stirs, filter, filter residue obtains complex microsphere with ethylene oxide, absolute ethyl alcohol, water washing successively.
4. exterior wall waterborne epoxy coatings according to claim 3, which is characterized in that in the preparation process of complex microsphere, ring
Oxygen chloropropane, sorbester p17, atoleine weight ratio be 2-4：0.2-0.9：30-50.
5. according to the exterior wall waterborne epoxy coatings of claim 3 or 4, which is characterized in that in the preparation process of complex microsphere,
Starch, humic acid, water, sodium hydroxide, epoxychloropropane weight ratio be 10-20：4-10：80-150：1-2：1-2.
6. according to exterior wall waterborne epoxy coatings described in claim 3-5, which is characterized in that in the preparation process of complex microsphere,
The weight ratio of water phase and organic phase is 20-40：80-100.
7. according to exterior wall waterborne epoxy coatings described in claim 3-6, which is characterized in that in the preparation process of complex microsphere,
Starch, humic acid, water are mixed, 92-98 DEG C of stirring 5-15min is warming up to, is down to room temperature.