CN1673290A - Nanometer bactericidal outer wall paint - Google Patents
Nanometer bactericidal outer wall paint Download PDFInfo
- Publication number
- CN1673290A CN1673290A CN 200410098774 CN200410098774A CN1673290A CN 1673290 A CN1673290 A CN 1673290A CN 200410098774 CN200410098774 CN 200410098774 CN 200410098774 A CN200410098774 A CN 200410098774A CN 1673290 A CN1673290 A CN 1673290A
- Authority
- CN
- China
- Prior art keywords
- wall paint
- weight parts
- weight part
- bactericidal
- nanometer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The nanometer bactericidal outer wall paint consists of water, preservative, hydroxyethyl cellulose, pH regulator, dispresant A, dispersant B, moistening agent, defoaming agent A, defoaming agent B, filming agent, glycol, titanium dioxide, composite nanometer bactericidal powder, heavy calcium carbonate, talcum powder, thickener A, thickener B, reeologic modifier, and styrene-acrylic emulsion, acrylic emulsion, silicone propylene emulsion or elastic emulsion in certain proportion. It is used for outer wall of building, has bactericidal function.
Description
Technical field
The present invention relates to a kind of coating, particularly a kind of nanometer bactericidal outer wall paint that is applicable to exterior wall protection and decoration, the mildew-resistant of tool strong disinfecting and environmental protection effect.
Background technology
At present, the coating variety of selling on the market is many, purposes is wide, outstanding tool is an exterior coating, the multiple function of each tool, but when using all kinds of synthesis material, generally all contain harmful material, and discharge peculiar smell, as formaldehyde, VOC (volatile organic compounds), heavy metal, benzene etc. exceed standard and then environment and HUMAN HEALTH are produced a large amount of the murder by poisoning, virus and bacterium are always to have in our living space in addition, ubiquitous, the physical and mental health that everybody is perplexed always and threatened to the existence of virus and bacteria to the hazard rating of human body is as intestinal bacteria, streptococcus aureus, candida albicans, withered grass gemma etc. can cause infectation of bacteria to spread disease.
In view of this, in order to address the above problem, this creator is according to oneself practical experience and technical concept, and test has the present invention to produce eventually after deliberation.
Summary of the invention
The present invention will provide a kind of nanometer bactericidal outer wall paint, makes its toxicological harmless, free from extraneous odour with solution, has the technical problem of biocidal efficacies.
It is such solving the problems of the technologies described above the technical scheme that is adopted:
A kind of nanometer bactericidal outer wall paint is characterized in that: the base stock and the weight ratio of its prescription are:
Water 300～400 weight parts; Sanitas 0.6～2 weight part;
Natvosol 2～4 weight parts; PH regulator agent 0.6～2 weight part;
Dispersant A 0.6～2 weight part; Dispersant B 1～3 weight part;
Wetting agent 0.6～2 weight part; Defoamer A 1～3 weight part;
Defoamer B 0.6～2 weight part; Membrane-forming agent 10～14 weight parts;
Ethylene glycol 40～60 weight parts; Titanium dioxide 230～250 weight parts;
Composite Nano sterilization powder 0.05～25 weight part; Water-ground limestone 50～70 weight parts;
Talcum powder 10～30 weight parts; Thickening material A 0.6～1 weight part;
Thickening material B 0.3～0.6 weight part; Rheology modifier 3～5 weight parts.
Wherein add benzene emulsion 240～260 weight parts, constitute the styrene-acrylic nanometer bactericidal outer wall paint;
Wherein add pure-acrylic emulsion 240～260 weight parts, constitute the pure third type nanometer bactericidal outer wall paint;
Wherein add organosilicon crylic acid latex 240～260 weight parts, constitute the silicon third type nanometer bactericidal outer wall paint;
Wherein add elastic emulsion 240～260 weight parts, constitute the elastic type nanometer bactericidal outer wall paint;
The active ingredient of above-mentioned composite Nano sterilization powder is a nanometer silver, copper, zinc, manganese, the combination of the multiple metal particle of iron, its carrier is a titanium phosphate, zirconium phosphate or zeolite powder body material, sanitas is a nitrogen-containing heterocycle compound, the pH regulator agent is an organic ammonium, dispersant A is a polyacrylic acid sodium salt, dispersant B is a poly carboxylic acid sodium, wetting agent is a non-ionic wetting agent, defoamer A is the mixture of aliphatic hydrocarbon and emulsifying agent, defoamer B is the mixture of petroleum-type derivative and special assistant, membrane-forming agent is a pentanediol list isopropylformic acid fat, thickening material A is acrylate/nitrile amine copolymer thing, thickening material B is a polyether polyols with reduced unsaturation, the mixture of water and fourth oxygen three intoxicated alcohol, titanium dioxide are titanium dioxide powder, and rheology modifier is the nonionic polyoxyalkylene rheology modifier.
Benzene emulsion is a styrene acrylic resin copolymer emulsion among the present invention, and pure-acrylic emulsion is a pure acrylic acid ester emulsion, and organosilicon crylic acid latex is the organic silicon acrylic ester copolymer emulsion, and elastic emulsion is a pure acrylic acid ester elastomer emulsion.
The present invention has adopted composite Nano sterilization powder to add in the exterior coating, makes this coating have strong disinfecting mildew-resistant effect, thus solved make that its tool is tasteless, the technical problem of toxicological harmless, fungus and mildew resistance.
Advantage of the present invention is as follows:
1, product strong covering power of the present invention is constructed easily, and is nonpoisonous and tasteless, and the tool feature of environmental protection.
2, the present invention has increased the strong disinfecting antimildew function on the basis of the various exterior coatings that surpass national standard, and this function is a persistence, make the large-area body of wall of buildings become " sterilization bodyguard ", all reach more than 99.5% as sterilizing rate to streptococcus aureus, intestinal bacteria, candida albicans and withered grass gemma.
3, scrubbing resistance of the present invention is widely used in skins such as dwelling house, apartment, hospital, school, and the tool practicality.
Embodiment
The invention will be further described below by embodiment:
Embodiment 1, and its prescription is: water 348kg, sanitas 1kg, Natvosol 3kg, pH regulator agent 1kg, dispersant A 1kg, dispersant B 2kg, wetting agent 1kg, defoamer A 2kg, defoamer B 1kg, membrane-forming agent 12kg, ethylene glycol 50kg, titanium dioxide 240kg, composite Nano sterilization powder 8kg, water-ground limestone 60kg, talcum powder 20kg, thickening material A 0.8kg, thickening material B 0.5kg, rheology modifier 4kg and benzene emulsion 250kg constitute the styrene-acrylic nanometer bactericidal outer wall paint.
Embodiment 2, and its prescription is: water 348kg, sanitas 1kg, Natvosol 3kg, pH regulator agent 1kg, dispersant A 1kg, dispersant B 2kg, wetting agent 1kg, defoamer A 2kg, defoamer B 1kg, membrane-forming agent 12kg, ethylene glycol 50kg, titanium dioxide 240kg, composite Nano sterilization powder 8kg, water-ground limestone 60kg, talcum powder 20kg, thickening material A 0.8kg, thickening material B 0.5kg, rheology modifier 4kg and pure-acrylic emulsion 250kg constitute the pure third type nanometer bactericidal outer wall paint.
Embodiment 3, and its prescription is: water 348kg, sanitas 1kg, Natvosol 3kg, pH regulator agent 1kg, dispersant A 1kg, dispersant B 2kg, wetting agent 1kg, defoamer A 2kg, defoamer B 1kg, membrane-forming agent 12kg, ethylene glycol 50kg, titanium dioxide 240kg, composite Nano sterilization powder 8kg, water-ground limestone 60kg, talcum powder 20kg, thickening material A 0.8kg, thickening material B 0.5kg, rheology modifier 4kg and organosilicon crylic acid latex 250kg constitute the silicon third type nanometer bactericidal outer wall paint.
Embodiment 4, and its prescription is: water 348kg, sanitas 1kg, Natvosol 3kg, pH regulator agent 1kg, dispersant A 1kg, dispersant B 2kg, wetting agent 1kg, defoamer A 2kg, defoamer B 1kg, membrane-forming agent 12kg, ethylene glycol 50kg, titanium dioxide 240kg, composite Nano sterilization powder 8kg, water-ground limestone 60kg, talcum powder 20kg, thickening material A 0.8kg, thickening material B 0.5kg, rheology modifier 4kg and elastic emulsion 250kg constitute the elastic type nanometer bactericidal outer wall paint.
The active ingredient of above-mentioned composite Nano sterilization powder is a nanometer silver, copper, zinc, manganese, the combination of the multiple metal particle of iron, its carrier is a titanium phosphate, zirconium phosphate or zeolite powder body material, sanitas is a nitrogen-containing heterocycle compound, the pH regulator agent is an organic ammonium, dispersant A is a polyacrylic acid sodium salt, dispersant B is a poly carboxylic acid sodium, wetting agent is a non-ionic wetting agent, defoamer A is the mixture of aliphatic hydrocarbon and emulsifying agent, defoamer B is the mixture of petroleum-type derivative and special assistant, membrane-forming agent is a pentanediol list isopropylformic acid fat, thickening material A is acrylate/nitrile amine copolymer thing, thickening material B is a polyether polyols with reduced unsaturation, the mixture of water and fourth oxygen three intoxicated alcohol, titanium dioxide are titanium dioxide powder, and rheology modifier is the nonionic polyoxyalkylene rheology modifier, benzene emulsion is a styrene acrylic resin copolymer emulsion, pure-acrylic emulsion is a pure acrylic acid ester emulsion, and organosilicon crylic acid latex is the organic silicon acrylic ester copolymer emulsion, and elastic emulsion is a pure acrylic acid ester elastomer emulsion.
Preparation method of the present invention comprises: stir, grind, high speed dispersion is filtered, check, packing.
In sum, effect of the present invention has tangible lifting, and its fungus and mildew resistance effect tool practicality meets each important document of patent of invention, so propose application for a patent for invention in accordance with the law.
Claims (6)
1, a kind of nanometer bactericidal outer wall paint is characterized in that: the base stock and the weight ratio of its prescription are:
Water 300～400 weight parts; Sanitas 0.6～2 weight part;
Natvosol 2～4 weight parts; PH regulator agent 0.6～2 weight part;
Dispersant A 0.6～2 weight part; Dispersant B 1～3 weight part;
Wetting agent 0.6～2 weight part; Defoamer A 1～3 weight part;
Defoamer B 0.6～2 weight part; Membrane-forming agent 10～14 weight parts;
Ethylene glycol 40～60 weight parts; Titanium dioxide 230～250 weight parts;
Composite Nano sterilization powder 0.05～25 weight part; Water-ground limestone 50～70 weight parts;
Talcum powder 10～30 weight parts; Thickening material A 0.6～1 weight part;
Thickening material B 0.3～0.6 weight part; Rheology modifier 3～5 weight parts.
2, nanometer bactericidal outer wall paint according to claim 1 is characterized in that: wherein add benzene emulsion 240～260 weight parts, constitute the styrene-acrylic nanometer bactericidal outer wall paint.
3, nanometer bactericidal outer wall paint according to claim 1 is characterized in that: wherein add pure-acrylic emulsion 240～260 weight parts, constitute the pure third type nanometer bactericidal outer wall paint.
4, nanometer bactericidal outer wall paint according to claim 1 is characterized in that: wherein add organosilicon crylic acid latex 240～260 weight parts, constitute the silicon third type nanometer bactericidal outer wall paint.
5, nanometer bactericidal outer wall paint according to claim 1 is characterized in that: wherein add elastic emulsion 240～260 weight parts, constitute the elastic type nanometer bactericidal outer wall paint.
6, according to any described nanometer bactericidal outer wall paint in the claim 1 to 5, it is characterized in that: the active ingredient of this composite Nano sterilization powder is a nanometer silver, copper, zinc, manganese, the combination of the multiple metal particle of iron, its carrier is a titanium phosphate, zirconium phosphate or zeolite powder body material, sanitas is a nitrogen-containing heterocycle compound, the pH regulator agent is an organic ammonium, dispersant A is a polyacrylic acid sodium salt, dispersant B is a poly carboxylic acid sodium, wetting agent is a non-ionic wetting agent, defoamer A is the mixture of aliphatic hydrocarbon and emulsifying agent, defoamer B is the mixture of petroleum-type derivative and special assistant, membrane-forming agent is a pentanediol list isopropylformic acid fat, and thickening material A is acrylate/nitrile amine copolymer thing, and thickening material B is a polyether polyols with reduced unsaturation, the mixture of water and fourth oxygen three intoxicated alcohol, titanium dioxide is a titanium dioxide powder, and rheology modifier is the nonionic polyoxyalkylene rheology modifier.