CN1050738A - 固体润滑剂分散液 - Google Patents
固体润滑剂分散液 Download PDFInfo
- Publication number
- CN1050738A CN1050738A CN 89107534 CN89107534A CN1050738A CN 1050738 A CN1050738 A CN 1050738A CN 89107534 CN89107534 CN 89107534 CN 89107534 A CN89107534 A CN 89107534A CN 1050738 A CN1050738 A CN 1050738A
- Authority
- CN
- China
- Prior art keywords
- solid lubricant
- nhr
- dispersing liquid
- consumption
- dispersion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及少量固体润滑剂(如石墨和二硫化钼
等)、增粘/分散剂和复合分散剂稳定地分散于大量
润滑基础油中的固体润滑剂分散液。该复合分散剂
包括(1)3～12C多元醇的5～24C饱和及不饱和羧
酸部分酯中选择的至少一种，(2)通式如下所示的聚
脲中选择的至少一种，R1NH(C(O)NHR4
NHC(O)NHR5NH)nC(O)NHR2NHC(O)NHR3这
里，n＝0或1；R1，R3＝2～24C一价烃基，R1和R3
可以相同或不相同；R2，R4＝6～18C二价烃基，R2和
R4可以相同或不相同；R5＝2～18C二价烃基。
Description
本发明涉及少量固体润滑剂（如石墨和二硫化钼等）、增粘/分散剂和复合分散剂稳定地分散于大量润滑基础油（如矿油和合成润滑油）中作润滑剂用的固体润滑剂分散液。
用作润滑剂的固体润滑剂分散液具有较全面的优点，即兼有固体润滑剂的优良的极压润滑性，液体润滑剂的良好的流动性、散热性和渗透性，在边界润滑条件下，能有效地降低摩擦面的摩擦和磨损。因此，固体润滑剂分散液，在汽车、船舶、印染及其它工业机械行业被广泛地用作润滑油和减摩添加剂。
然而，固体润滑剂分散液的一个技术关键还在于能否长期地稳定分散。因为若贮存和使用过程中固体颗粒凝聚和沉淀的话，那么在润滑中就会发生故障。为使分散液长期稳定，可以把固体颗粒破碎成尽可能小的尺寸和/或寻找优良的分散剂。
较早使用的分散剂有脂肪酸皂，聚丁二烯。1967年5月9日申请的美国专利3，384，580提出以乙烯-丙烯共聚物，乙烯-丙烯-二烯三元共聚物作分散剂。1978年4月3日申请的美国专利4，134，844提到以烯基丁二酰亚胺，聚甲基丙烯酸酯，氧化乙烯-丙烯共聚物及其与脂肪胺（或多胺）的反应产品作分散剂。
已知的各种分散剂确能在固体颗粒的破碎过程中帮助固体微粒分散，并有助于分散液稳定。但要进一步提高固体润滑剂颗粒的破碎分散效果和分散液的长期稳定性，还必须寻找更佳的分散剂及与之相适应的分散方法。
本发明的目的是提供一种新的稳定的固体润滑剂分散液。该分散液中含有复合分散剂。
本发明的固体润滑剂分散液包括少量固体润滑剂、常规的增粘/分散剂和复合分散剂及大量润滑基础油。
固体润滑剂，通常是从石墨、二硫化钼和二硫化钨等中选择的。最好从石墨和二硫化钼中选择固体润滑剂。
常规的增粘/分散剂，在分散液中主要起增粘作用，众所周知还起分散作用。此外，提高分散液的粘度，实际上也有利于固体润滑剂的稳定分散。
常规的增粘/分散剂，是从聚异丁烯、聚甲基丙烯酸酯和乙-丙共聚物等中选择的。通常，聚异丁烯的分子量为3，000～100，000;聚甲基丙烯酸酯的分子量为10，000～1，500，000;乙-丙共聚物的分子量为10，000～100，000。
复合分散剂，由（1）和（2）两种成分组成。（1）是极性较强的3～12C多元醇的5～24C饱和及不饱和羧酸部分酯（酯分子中至少含有一个羟基）中选择的至少一种。3～12C多元醇，可以从甘油、三羟甲基丙烷、季戊四醇、双季戊四醇和双三羟甲基丙烷中选择，最好从甘油、三羟甲基丙烷和季戊四醇中选择。5～24C饱和及不饱和羧酸，可以从戊酸、己酸、庚酸、辛酸、壬酸、癸酸、月桂酸、十四酸、十六酸、硬脂酸、油酸、亚油酸、二十酸、二十二酸和二十四酸中选择，最好从油酸和硬脂酸中选择。
（2）是通式如下所示的聚脲中选择的至少一种，
R1NH（C（O）NHR4NHC（O）NHR5NH）nC（O）NHR2NHC（O）NHR3
这里，n＝0或1;R1，R3＝2～24C一价烃基，如象乙基、丁基、戊基、己基、庚基、辛基、癸基、月桂基、十四烷基、十六烷基、十八烷基、二十烷基、二十二烷基和二十四烷基这样的烷烃基，苯基、甲苯基、萘基这样的芳烃基，环己基、乙基环己基、三甲基环己基这样的环烷烃基，R1和R3可以相同或不相同;当n＝0时，（2）是双脲，R2＝6～18C二价烃基，如象亚己基、三甲基亚己基、亚癸基、亚十八烷基这样的二价烷烃基，甲基亚苯基、亚甲基二苯基（-C6H4CH2C6H4-）这样的二价芳烃基;当n＝1时，R2，R4＝6～18C二价烃基，具体例子同上述的R2，R2和R4可以相同或不相同，R5＝2～18C二价烃基，如象亚乙基、亚丙基、亚己基、三甲基亚己基、亚癸基和亚十八烷基这样的二价烷烃基，甲基亚苯基、亚甲基二苯基这样的二价芳烃基。
润滑基础油，通常是从已知的矿油和合成油中选择的，最好是合成油。常用的合成油有阻化多元醇酯（如三羟甲基丙烷酯、季戊四醇酯和双季戊四醇酯）、双酯（如异壬基十二烷二酸酯）、复酯、聚二醇醚、聚硅氧烷和合成烃等。最好选择阻化多元醇酯。基础油的100℃运动粘度（V100）通常为3～24mm2/S，最好为4～8mm2/S。
本发明所用的固体润滑剂（如石墨和二硫化钼等）的平均粒子直径和用量，虽然都没有严格的限定，但通常其平均粒子直径在15μm以下，其质量是分散液总质量的0.1～20m%，最好是2～15m%。固体润滑剂的用量低于0.1m%时，分散液的极压润滑性变差;高于20m%时，分散液的流动性变差。
本发明所用的复合分散剂中，（1）和（2）的用量均按固体润滑剂的用量来确定，虽然都没有严格的限定，但（1）是甘油单油酸酯、甘油单硬脂酸酯或三羟甲基丙烷单油酸酯时，通常（1）的质量是固体润滑剂的质量的5～50m%，最好是10～50m%，低于5m%时，分散作用差，高于50m%时，无必要;通常（2）的质量是固体润滑剂的质量的5～50m%，最好是10～35m%，低于5m%时，分散作用差，高于50m%时，影响分散液的牛顿性能。
本发明的固体润滑剂分散液与各种常用的添加剂有很好的相容性。必要时，还可以把其它各种常用的添加剂，如抗氧剂和抗腐蚀剂等加入本发明的分散液中。
本发明的固体润滑剂分散液按下述步骤制备：第一，把适当量的石墨和/或二硫化钼等固体润滑剂和适当量的3～12C多元醇的5～24C饱和及不饱和羧酸部分酯以及部分润滑基础油于80℃下搅拌混合，再于常温下用三辊磨研磨，补加余量的润滑基础油后，用均化器进行均化;第二，再加入制备聚脲所需的原料（二异氰酸酯和胺;二异氰酸酯、二胺和胺），于80～150℃下充分反应，加入增粘/分散剂，必要时，还加入其它添加剂，最后于常温下用均化器进行第二步破碎分散。
虽然上述两步破碎分散制备本发明的固体润滑剂分散液的方法是最理想的，但也可以采用其它的制备方法。例如，采用预制聚脲粉和一步破碎分散的方法。
本发明的固体润滑剂分散液，因为含有复合分散剂，所以具有优良的分散稳定性和长期贮存稳定性。此外，本发明的固体润滑剂分散液还具有优良的耐高温性、抗磨和极压性。因此，本发明的固体润滑剂分散液广泛用作各种机械的极压润滑油，特别适于用作高温拉链油、齿轮油及其它节能润滑剂。
下述实施例更清楚地说明本发明，但并不意味着对本发明作任何特殊的限定。本发明的范围记载于权利要求中。
实施例1
把10gMoS2（0号）、5g甘油单油酸酯和10g双季戊四醇酯（V100＝7.5mm2/S）加入500ml容器中，加热至80℃，搅拌15min，冷到常温，用三辊磨研磨三遍，然后补加152g双季戊四醇酯，用均化器均化30min。在混合液中加入2.26g十八胺和0.74g甲苯基二异氰酸酯，于80～150℃下搅拌反应30min，加入20g聚异丁烯（分子量约3，000～4，000），冷到常温，最后用均化器均化15min，得到均匀稳定的固体润滑剂分散液。
实施例2～8和比较例1～4
按照实施例1相类似的方法制备了其它本发明的固体润滑剂分散液。实施例2、4、6和8的分散液含有n＝1的四脲;实施例1、3、5和7的分散液含有n＝0的双脲。
为了比较，制备了比较例1～4的分散液。在比较例中，除了删去本发明用的复合分散剂（1）和/或（2）成分以外，制备时采用的研磨和均化步骤与实施例1中采用的步骤基本相同。
本发明的实施例和参照的比较例的组成及分散稳定性试验结果分别列入表1和表2中。表中各成分的代号的含意-
GMOE：甘油单油酸酯
GMSE：甘油单硬脂酸酯
TMOE：三羟甲基丙烷单油酸酯
TDI：甲苯基二异氰酸酯
MDI：二苯基甲烷二异氰酸酯
PIB：聚异丁烯（分子量3，000～4，000）
PMA：聚甲基丙烯酸酯（分子量10，000～12，000）
OCP：乙-丙共聚物（国产T-604）
BPE：双季戊四醇酯（V100＝7.5mm2/S）
PE：季戊四醇酯（V100＝4.9mm2/S）
TMPE：三羟甲基丙烷酯（V100＝4.0mm2/S）
分散稳定性试验-
试验条件和方法：使用CL型试管离心机（国营北京仪器厂生产），把5ml分散液样品装于离心试管中，于常温、转速3，000r/min下离心15min，观察并记录上层清液层/下层沉淀层的ml数。
评价：清液层和沉淀层的体积越小越好。试验表明，当固体润滑剂用量为2～15m%时，只要上层无明显的清液层，下层沉淀层的体积小于0.25ml，那么该分散液就有优良的长期贮存稳定性。
表1
＊上层清液层的体积
＊＊下层沉淀层的体积
表2
＊上层清液层的体积
＊＊下层沉淀层的体积
Claims (7)
1、一种由少量固体润滑剂、增粘/分散剂和复合分散剂及大量润滑基础油组成的固体润滑剂分散液，其特征在于该复合分散剂由(1)和(2)两种成分组成，
(1)是3～12C多元醇的5～24C饱和及不饱和羧酸部分酯(酯分子中至少含有一个羟基)中选择的至少一种，
(2)是通式如下所示的聚脲中选择的至少一种，
R1NH(C(O)NHR4NHC(O)NHR5NH)nC(O)NHR2NHC(O)NHR3
这里，n=0或1；R1，R3=2～24C一价烃基，R1和R3可以相同或不相同；R2，R4=6～18C二价烃基，R2和R4可以相同或不相同；R5=2～18C二价烃基。
2、如权利要求1所述的固体润滑剂分散液，其特征在于（1）是固体润滑剂用量的5～50m%的甘油单油酸酯。
3、如权利要求1所述的固体润滑剂分散液，其特征在于（1）是固体润滑剂用量的5～50m%的甘油单硬脂酸酯。
4、如权利要求1所述的固体润滑剂分散液，其特征在于（1）是固体润滑剂用量的5～50m%的三羟甲基丙烷单油酸酯。
5、如权利要求1所述的固体润滑剂分散液，其特征在于（2）是固体润滑剂用量的5～50m%的n＝0的双脲。
6、如权利要求1所述的固体润滑剂分散液，其特征在于（2）是固体润滑剂用量的5～50m%的n＝1的四脲。
7、如权利要求1所述的固体润滑剂分散液，其特征在于（1）是固体润滑剂用量的10～50m%的甘油单油酸酯，（2）是固体润滑剂用量的10～35m%的n＝0的双脲。