CN105062627B - 一种用于宽带钢轧机的轧制油组合物及制备方法 - Google Patents

一种用于宽带钢轧机的轧制油组合物及制备方法 Download PDF

Info

Publication number
CN105062627B
CN105062627B CN201510417100.9A CN201510417100A CN105062627B CN 105062627 B CN105062627 B CN 105062627B CN 201510417100 A CN201510417100 A CN 201510417100A CN 105062627 B CN105062627 B CN 105062627B
Authority
CN
China
Prior art keywords
parts
oil composition
rolling
rolling oil
strip mill
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201510417100.9A
Other languages
English (en)
Other versions
CN105062627A (zh
Inventor
胡卫东
喻选明
靳树林
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
WUHAN TONGSHENG FINE CHEMICAL TECHNOLOGY DEVELOPMENT Co Ltd
Original Assignee
WUHAN TONGSHENG FINE CHEMICAL TECHNOLOGY DEVELOPMENT Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by WUHAN TONGSHENG FINE CHEMICAL TECHNOLOGY DEVELOPMENT Co Ltd filed Critical WUHAN TONGSHENG FINE CHEMICAL TECHNOLOGY DEVELOPMENT Co Ltd
Priority to CN201510417100.9A priority Critical patent/CN105062627B/zh
Publication of CN105062627A publication Critical patent/CN105062627A/zh
Application granted granted Critical
Publication of CN105062627B publication Critical patent/CN105062627B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种轧制油组合物及制备方法，属于冶金轧机用油品领域，具体涉及一种用于宽带钢轧机的轧制油组合物及制备方法。其中，该用于宽带钢轧机的轧制油组合物包括如下重量份数的组分：三羟甲基丙烷椰油酸酯200份；油酸二乙醇酰胺20份；椰子油酸二乙醇酰胺40份；机油455份；防锈剂30份；抗氧化剂5份；硫化猪油50份；聚乙二醇400油酸酯200份。该轧制油组合物应用于四辊轧机及六辊轧机上，能满足高温下对轧钢润滑的要求保证轧钢过程的稳定性，而且在免清洗条件下能保证退火清净性，轧机清净性及防锈性。

Description

一种用于宽带钢轧机的轧制油组合物及制备方法
技术领域
本发明涉及一种轧制油组合物及制备方法，属于冶金轧机用油品领域，具体涉及一种用于宽带钢轧机的轧制油组合物及制备方法。
背景技术
钢板材加工是金属加工中一种重要的工艺。传统的钢轧机的轧制油在轧制钢板上容易引起过润滑，并且出现断带、钢板跑偏、甚至轧机震动等问题，即使降低浓度使用也不能从根本上解决问题，反而导致了防锈差等其他问题。
此外，传统的钢轧机的轧制油主皂化值高，并且动植物油挥发性较差的特点影响了轧制板面退火后的清净性，而且在冬季易产生凝固，使用不便，溅出的乳化液在轧机四周析油凝固，影响了轧机清净性，如降低浓度使用，非但不能解决问题，反而导致防锈性能变差等其他问题。
发明内容
本发明主要是解决现有技术所存在的上述的技术问题，提供了一种用于宽带钢轧机的轧制油组合物及制备方法。该轧制油组合物应用于四辊轧机及六辊轧机上，能满足高温下对轧钢润滑的要求保证轧钢过程的稳定性，而且在免清洗条件下能保证退火清净性，轧机清净性及防锈性。
为了解决上述问题，作为本发明的一方面，提供了一种用于宽带钢轧机的轧制油组合物，包含有如下重量份数的组分：
优化的，上述的一种用于宽带钢轧机的轧制油组合物，所述机油是150SN基础油。
优化的，上述的一种用于宽带钢轧机的轧制油组合物，所述防锈剂是T746防锈剂。
优化的，上述的一种用于宽带钢轧机的轧制油组合物，所述抗氧化剂是T501抗氧化剂。
为了解决上述问题，作为本发明的另一方面，提供了一种制备上述的用于宽带钢轧机的轧制油组合物的方法，包括：
步骤1，加入机油，升温至60-70℃，加入抗氧剂，搅拌至溶解；
步骤2，降温到60℃，加入三羟甲基丙烷椰油酸酯、油酸二乙醇酰胺、椰子油酸二乙醇酰胺、聚乙二醇400油酸酯、搅拌均匀；
步骤3，在50℃加入防锈剂、硫化猪油搅拌30分钟，即得本发明组合物。
因此，本发明具有如下优点：(1)润滑性能更好，有合理的皂化值，可满足窄带轧机轧钢对润滑的要求；(2)自主合成抗磨极压剂，保证高温高压条件下的润滑；(3)自主合成合成酯，并采用全合成酯配方，无导致退火不净的动植物油，保证了润滑和退火后板面的清净性，且凝固点较低；(4)配入高效特种防锈剂，保证钢材的防锈性能；(5)特有的乳化剂配比技术，控制乳化液颗粒度的大小和稳定性，更能保证轧钢过程的稳定性。
具体实施方式
下面通过实施例，对本发明的技术方案作进一步具体的说明。
实施例：
一种用于窄带钢轧机的轧制油组合物，包含有如下重量份数的组分：
本实施例中，机油是150SN基础油，防锈剂是T746防锈剂，抗氧化剂是T501抗氧化剂。
本实施例的轧制油组合物制备方法如下：
步骤1，加入机油，升温至60-70℃，加入抗氧剂，搅拌至溶解；
步骤2，降温到60℃，加入三羟甲基丙烷椰油酸酯、油酸二乙醇酰胺、椰子油酸二乙醇酰胺、聚乙二醇400油酸酯、搅拌均匀；
步骤3，在50℃加入防锈剂、硫化猪油搅拌30分钟，即得本发明组合物。
本发明轧制油组合物的指标数据如下表所示：
表1本发明组合物理化指标与典型指标对比
指标 取值
外观 棕红色透明液体
酸值(mgKOH/g) <10
皂化值(mgKOH/g) 75-85
运动粘度(mm2/s)40℃ 46-58
PH值(2％) 7.0-8.0
本发明首次采用全合成酯配方，满足中宽带四辊、六辊的专用轧制油的要求；采用乳化液颗粒可控技术，将轧制油中所有乳化剂替换成全天然可降解的酰胺性非离子乳化剂油酸二乙醇酰胺、椰子油酸二乙醇酰胺，从而使得乳化液颗粒相对较小，稳定性较好，防锈性也较采用了阳离子型的乳化剂好。
本文中所描述的具体实施例仅仅是对本发明精神作举例说明。本发明所属技术领域的技术人员可以对所描述的具体实施例做各种各样的修改或补充或采用类似的方式替代，但并不会偏离本发明的精神或者超越所附权利要求书所定义的范围。

Claims (5)

1.一种用于宽带钢轧机的轧制油组合物，其特征在于，包含有如下重量份数的组分：
2.根据权利要求1所述的一种用于宽带钢轧机的轧制油组合物，其特征在于，所述机油是150SN基础油。
3.根据权利要求1所述的一种用于宽带钢轧机的轧制油组合物，其特征在于，所述防锈剂是T746防锈剂。
4.根据权利要求1所述的一种用于宽带钢轧机的轧制油组合物，其特征在于，所述抗氧化剂是T501抗氧化剂。
5.一种制备权利要求1所述的用于宽带钢轧机的轧制油组合物的方法，其特征在于，包括：
步骤1，加入机油，升温至60-70℃，加入抗氧剂，搅拌至溶解；
步骤2，降温到60℃，加入三羟甲基丙烷椰油酸酯、聚乙二醇400油酸酯、搅拌均匀；
步骤3，在50℃加入防锈剂、硫化猪油搅拌30分钟，再加入油酸二乙醇酰胺、椰子油酸二乙醇酰胺搅拌30分钟即得本发明组合物。
CN201510417100.9A 2015-07-16 2015-07-16 一种用于宽带钢轧机的轧制油组合物及制备方法 Expired - Fee Related CN105062627B (zh)