CN105040929A - Construction method for strengthening bottom-painting putty via glue immersion on building pain wall surface - Google Patents
Construction method for strengthening bottom-painting putty via glue immersion on building pain wall surface Download PDFInfo
- Publication number
- CN105040929A CN105040929A CN201510575939.5A CN201510575939A CN105040929A CN 105040929 A CN105040929 A CN 105040929A CN 201510575939 A CN201510575939 A CN 201510575939A CN 105040929 A CN105040929 A CN 105040929A
- Authority
- CN
- China
- Prior art keywords
- putty
- wall surface
- metope
- glue
- construction method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a construction method for strengthening bottom-painting putty via glue immersion on a building pain wall surface. The construction method comprises steps of first, modularizing bottom-painting paint putty loosened after drying, then painting putty, second, grinding and flattening after wall surface putty dries, third, rolling-painting glue relapsed by water on the grinded and flattened wall surface via a wool roller cylinder and then penetrating glue into the putty painted on the wall surface for drying, fourth, conducting further grinding process for the putty strengthened due to immersed of glue and dried, and fifth, finally painting on the bottom-painted wall surface. By the use of the construction method, putty dries and solidifies, so the wall surface can be grinded and flattened; glue is immersed to strengthen the putty after grinding and flattening; a paint bottom-paint layer with high hardness is achieved at last; and paint can be easily attached to the wall surface; and problems of crack, bulge and wrapping of the paint surface layer due to looseness of the putty painted on the bottom can be effectively prevented.
Description
Technical field
The present invention relates to the construction technology that a kind of interior decoration is surface-veneer engineered, be specifically related to a kind of batch end putty strike-through strengthening construction method of building coating metope.
Background technology
In current technology, building coating metope carried out putty and criticizes end operation before doing coating, obtain the smooth further of coating bottom surface, it is the important prerequisite determining coating metope planarization effects simultaneously, for the putty modulation at batch end, if too loose after the putty dry solidification of modulation, though be convenient to the smooth polishing of husky skin but be unfavorable for the stickup adhesive power of coating, be easy to the minute crack producing coating surface, once metope makes moist, can ftracture, play the major defect such as drum, volume skin.If too hard after the putty dry solidification of modulation, though have stronger adhesive power for coating, add the difficulty that husky skin polishes flat, the planarization effects at the bottom of its batch is difficult to realize.
Summary of the invention
The object of the present invention is to provide a kind of batch end putty strike-through strengthening construction method of building coating metope, be convenient to polish flat after putty dry solidification, strike-through strengthening is carried out again on the basis being easy to smooth polishing, the painting charge bottom of final acquisition higher hardness, be conducive to the attachment of coating, effectively prevent the cracking of the loose paint topcoat caused because of batch end putty, play drum, roll up the phenomenons such as skin.
For achieving the above object, technical scheme of the present invention is batch end putty strike-through strengthening construction method of a kind of building coating metope of design, comprises the steps:
1) putty at the bottom of painting charge comparatively loose after modulating dry solidification, criticizing the metope in needing coating finish with batch cutter, reaching substantially smooth, solidification to be dried by this putty;
2), after wall surface putty drying, husky skin is adopted to polish flat process to loose wall surface putty, to reach level requirements;
3) water soluble adhesive no longer water-soluble after adopting drying, carrying out being watered dilution, carrying out roller coating by being watered the glue hair cylinder after dilution at the metope polished flat, and glue is infiltrated and pulls in the putty of metope, to be dried;
4) after the putty dry solidification that strike-through has been strengthened, more further husky skin grinding process is done, to obtain batch end metope of higher smooth precision;
5) coating finish is implemented at batch end metope.
Preferably, no longer water-soluble after described drying water soluble adhesive is white glue with vinyl.
Advantage of the present invention and beneficial effect are: batch end putty strike-through strengthening construction method providing a kind of building coating metope, be convenient to polish flat after putty dry solidification, strike-through strengthening is carried out again on the basis being easy to smooth polishing, the painting charge bottom of final acquisition higher hardness, be conducive to the attachment of coating, effectively prevent the cracking of the loose paint topcoat caused because of batch end putty, play drum, roll up the phenomenons such as skin.
Construction method of the present invention only increases strike-through technique in batch end polishing subitem work post of prior art, solve and to loosen the paint topcoat cracking caused, the phenomenon playing drum, volume skin because being coated with putty at the bottom of charge, particularly metope is even more serious after making moist, batch end putty is hard and be difficult to the contradiction that polishes flat, simple, practical.
Detailed description of the invention
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
The technical scheme that the present invention specifically implements is:
A batch end putty strike-through strengthening construction method for building coating metope, comprises the steps:
1) putty at the bottom of the dry rear loose painting charge of modulation, criticizing the metope in needing coating finish with batch cutter, reaching substantially smooth, solidification to be dried by this putty;
2), after wall surface putty drying, husky skin is adopted to polish flat process to loose wall surface putty, to reach level requirements;
3) water soluble adhesive no longer water-soluble after adopting drying, carrying out being watered dilution, carrying out roller coating by being watered the glue hair cylinder after dilution at the metope polished flat, and glue is infiltrated and pulls in the putty of metope, to be dried;
4) after the putty dry solidification that strike-through has been strengthened, more further husky skin grinding process is done, to obtain batch end metope of higher smooth precision;
5) coating finish is implemented at batch end metope.
Water soluble adhesive no longer water-soluble after above-mentioned drying can select white glue with vinyl.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (2)
1. batch end putty strike-through strengthening construction method of building coating metope, is characterized in that, comprise the steps:
1) putty at the bottom of the dry rear loose painting charge of modulation, criticizing the metope in needing coating finish with batch cutter, reaching substantially smooth, solidification to be dried by this putty;
2), after wall surface putty drying, husky skin is adopted to polish flat process to loose wall surface putty, to reach level requirements;
3) water soluble adhesive no longer water-soluble after adopting drying, carrying out being watered dilution, carrying out roller coating by being watered the glue hair cylinder after dilution at the metope polished flat, and glue is infiltrated and pulls in the putty of metope, to be dried;
4) after the putty dry solidification that strike-through has been strengthened, more further husky skin grinding process is done, to obtain batch end metope of higher smooth precision;
5) coating finish is implemented at batch end metope.
2. batch end putty strike-through strengthening construction method of building coating metope according to claim 1, it is characterized in that, water soluble adhesive no longer water-soluble after described drying is white glue with vinyl.