CN105457873A - Environment-friendly coating method for producing wooden doors and furniture - Google Patents
Environment-friendly coating method for producing wooden doors and furniture Download PDFInfo
- Publication number
- CN105457873A CN105457873A CN201510754226.5A CN201510754226A CN105457873A CN 105457873 A CN105457873 A CN 105457873A CN 201510754226 A CN201510754226 A CN 201510754226A CN 105457873 A CN105457873 A CN 105457873A
- Authority
- CN
- China
- Prior art keywords
- water
- spraying
- coating
- consumption
- paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an environment-friendly coating method for producing wooden doors and furniture. According to the method, four types of UV (Ultraviolet) paints and four types of water-based paints are combined for coating, and construction of planar parts and straight line type special-shaped parts is implemented, wherein the four types of UV paints are respectively a UV-vacuum spray-coating priming paint, UV-roller-coating filling putty, UV-roller-coating sanded priming paint and a UV-laser roller-coating priming paint; the four types of water-based paints are respectively a water-based color wiping agent, a water-based spraying priming paint, a water-based embellishing agent and a water-based spraying soft-light finishing paint. According to the environment-friendly coating method disclosed by the invention, a coating technique and a construction method are improved to effectively reduce emission of VOC (Volatile Organic Compounds) during use of the paints coated on wooden doors and furniture; a product coated by using the method is good in plumpness and adhesive force and has a glossy and soft-light effect; the gloss of a paint film is controlled to be 30 degrees to 50 degrees; the decoration grade of the wooden doors and furniture is increased.
Description
Technical field
The present invention relates to and a kind of produce timber, furniture technique, specifically a kind of UV coating combine with water paint production timber, furniture environmentally-friendly coating method.
Background technology
UV is Ultraviolet(ultraviolet) english abbreviation, UV paint and ultraviolet-cured paint.Existing traditional furniture, painting wood door substantially all adopt traditional PU dual-component coating, nitro paint equal solvent type coating application, the painting effect that when using this type of coating application, production floor space is large, the paint solidification time is long, coating constrains production efficiency and product containing shortcomings such as organic solvents.Or some factory has brought into use UV coating, but be substantially all containing organic solvent, not environmentally; Or only have partial coating to adopt UV coating and the whole UV application of not whole coating.So existing coating application efficiency is low, it is large to take up an area, the feature of environmental protection is poor, whole lacquer painting effect is stiff, stiff, lacks aesthetic feeling, and VOC discharges a large amount of in process of production creates atmospheric environment and has a strong impact on.
Summary of the invention
The object of this invention is to provide a kind of environmentally-friendly coating method of producing timber, furniture, 8 kinds of coating that the method adopts UV coating and water paint to combine carry out application, can enhance productivity, save place, effectively reduce VOC discharge, can allow and use that the timber of this coating, family Ju's have more the feature of environmental protection and aesthetics, meet aesthetic trend instantly.
The object of the invention is to be achieved through the following technical solutions:
A kind of environmentally-friendly coating method of producing timber, furniture, it is characterized in that: 8 kinds of coating that the method adopts UV coating and water paint to combine carry out application, wherein 4 kinds of UV coating are UV-airless spraying priming paint, the filling of UV-roller coat putty, UV-roller coat sanding priming paint, the radium-shine roller coat priming paint of UV-respectively; 4 kinds of water paints are water-based wiping stain, water-based spray-applied primer, water-based dressing agent and water-based spraying sheen finish paint respectively, and specific requirement is as follows:
1) to planar member, adopt water-based wiping stain, UV-roller coat to fill putty, UV-roller coat sanding priming paint, the radium-shine roller coat priming paint of UV-, water-based spray-applied primer, water-based dressing agent and water-based spraying sheen finish paint and construct, concrete steps are as follows:
11) with sand paper sanding element plate;
12) use wiping stain substrate surface is manual wipes look, consumption 8 ~ 12g/m2, infrared baking, and this water-based wiping stain is wiping stain or the water-based PUD of UV type; (note: the wiping stain of UV type refers to the obtained a kind of water paint of the water-base resin of the band UV curing reaction double bond of acroleic acid esterification, and the wiping stain of water-based PUD refers to a kind of water paint that the polyurethane of use is obtained);
13) fill the coating of putty putty roll coater with UV-roller coat, consumption 30 ~ 40g/m2,150mj/cm2UV solidify rear sand papering, the populated wooden eye of continuous application;
14) be coated with the radium-shine roll coater of UV-roller coat sanding priming paint, consumption 30 ~ 40g/m2,80mj/cm2UV solidify rear sand papering;
15) be coated with the radium-shine roll coater of UV-radium-shine roller coat priming paint, consumption 40 ~ 50g/m2; 400# sand papering is used after 180mj/cm2UV solidification;
16) use spray-applied primer spraying, consumption 100 ~ 110g/m2; Infrared ray dries 90 minutes at 50 DEG C, use 600# sand papering after cooling, and this water-based spray-applied primer is UV type or aqueous one-component or aqueous double-component, UV type 50 DEG C dry within 90 minutes, remove moisture content after 150mj/cm2UV solidify; (note: the aqueous priming paint of UV type refers to the obtained a kind of water paint of the water-base resin of the band UV curing reaction double bond of acroleic acid esterification; Mono-component aqueous priming paint refer to that use emulsion resin obtains a kind of can a kind of water paint of self-curing; Bi-component waterborne priming paint refers to that use emulsion obtains but needs to add a kind of water paint that water-based TDI does curing agent mixing mediation);
17) use dressing agent spraying, consumption 20 ~ 30g/m2; Infrared ray dries 10 minutes at 60 DEG C;
18) use spraying sheen finish paint spraying, consumption 100 ~ 110g/m2; Infrared ray dries 90 minutes at 50 DEG C, and this water-based spraying sheen finish paint is UV type or aqueous one-component or aqueous double-component, UV type need 50 DEG C dry within 90 minutes, remove moisture content after 250mj/cm2UV solidification; (note: the aqueous priming paint of UV type refers to the obtained a kind of aqueous finish paint special coating of the water-base resin of the band UV curing reaction double bond of acroleic acid esterification; Mono-component aqueous priming paint refer to that use emulsion resin obtains a kind of can a kind of aqueous finish paint special coating of self-curing; Bi-component waterborne priming paint refers to that use emulsion obtains but needs to add a kind of aqueous finish paint special coating that water-based TDI does curing agent mixing mediation);
2) to straight shape lines shaped piece, adopt water-based wiping stain, UV-airless spraying priming paint, water-based spray-applied primer, water-based dressing agent and water-based spraying sheen finish paint to construct, concrete steps are as follows:
21) with sand paper sanding element plate;
22) use wiping stain substrate surface is manual wipes look, consumption 8 ~ 12g/m2, infrared baking, and this wiping stain is wiping stain and the water-based PUD of UV type;
23) with UV-airless spraying priming paint vacuum spray painting machine or spray thrower coating, consumption 40 ~ 60g/m2,200mj/cm2UV solidify rear sand papering, according to the needs of wood quality, and continuous application 2 ~ 3 populated wooden eyes;
24) use spray-applied primer spraying, consumption 100 ~ 110g/m2; Infrared ray dries 90 minutes at 50 DEG C, 600# sand papering is used after cooling, this water-based spray-applied primer is UV type or aqueous one-component or aqueous double-component, UV type need 50 DEG C dry within 60 minutes, remove moisture content after 150mj/cm2UV solidification (note: the aqueous priming paint of UV type refers to the obtained a kind of water paint of the water-base resin of the band UV curing reaction double bond of acroleic acid esterification; Mono-component aqueous priming paint refer to that use emulsion resin obtains a kind of can a kind of water paint of self-curing; Bi-component waterborne priming paint refers to that use emulsion obtains but needs to add a kind of water paint that water-based TDI does curing agent mixing mediation);
25) use dressing agent spraying, consumption 20 ~ 30g/m2; Infrared ray dries 10 minutes at 60 DEG C;
26) use spraying sheen finish paint spraying, consumption 100 ~ 110g/m2; Infrared ray dries 90 minutes at 50 DEG C, this water-based spraying sheen finish paint is UV type or aqueous one-component or aqueous double-component, UV type need 50 DEG C dry within 90 minutes, remove moisture content after 250mj/cm2UV solidification (note: the aqueous priming paint of UV type refers to the obtained a kind of aqueous finish paint special coating of the water-base resin of the band UV curing reaction double bond of acroleic acid esterification; Mono-component aqueous priming paint refer to that use emulsion resin obtains a kind of can a kind of aqueous finish paint special coating of self-curing; Bi-component waterborne priming paint refers to that use emulsion obtains but needs to add a kind of aqueous finish paint special coating that water-based TDI does curing agent mixing mediation).
8 kinds of coating that the present invention adopts UV coating and water paint to combine carry out application, and wherein 4 kinds of UV coating are UV-airless spraying priming paint, the filling of UV-roller coat putty, UV-roller coat sanding priming paint, the radium-shine roller coat priming paint of UV-respectively; Wherein 4 kinds of water paints are water-based wiping stain, water-based spray-applied primer, water-based dressing agent and water-based spraying sheen finish paint respectively, it can not be UV type that these 4 kinds of water paints remove water-based dressing agent, other coating can be UV type or the single, double component of water-based, this construction method can be enhanced productivity, save place, effectively reduce VOC discharge, can allow and use that the timber of this coating, family Ju's have more the feature of environmental protection and aesthetics, meet aesthetic trend instantly.
Compared with prior art; the present invention by improve UV coating and water paint with the use of construction method; adopt continuous productive process, improve production efficiency, improve the utilization rate in place; effectively reduce VOC discharge; add hardness of paint film and richness, and lacquer painting third dimension is strong, feel is cunning, excellent visual effect and sense of touch can be obtained; gloss of film controls in more than 30 ~ 50 degree, drastically increases the aesthetics of product and enhances the protective value of product.The present invention is applicable in timber, the plane of furniture and the construction of special-shaped lines.
Accompanying drawing explanation
Fig. 1 is the coating structure schematic diagram of the timber surface plate that embodiment 1 obtains.
Fig. 2 is the coating structure schematic diagram of the timber straight shape lines shaped piece that embodiment 4 obtains.
Detailed description of the invention
Below in conjunction with embodiment, the present invention is further described.
Embodiment 1
A kind of environmentally-friendly coating method of producing timber, furniture, the application of its planar member: the method adopts water-based wiping stain, UV-roller coat to fill putty, UV-roller coat sanding priming paint, the radium-shine roller coat priming paint of UV-, water-based spray-applied primer, water-based dressing agent and water-based spraying sheen finish paint and constructs, and concrete steps are as follows:
1) with 80#, 100#, 120# sand paper sanding element plate respectively;
2) wipe look, consumption 8 ~ 12g/m2 with UV-water-based wiping stain substrate surface is manual, infrared ray 70 DEG C is dried for 10 minutes,
3) fill the coating of putty putty roll coater with UV-roller coat, after consumption 30 ~ 40g/m2,150mj/cm2UV solidification, use 240# sand papering, continuous application 2 populated wooden eyes;
4) be coated with the radium-shine roll coater of UV-roller coat sanding priming paint, consumption 30 ~ 40g/m2, levelling 15 seconds, 80mj/cm2UV semi-solid preparation, the slight sticky hand in surface;
5) be coated with the radium-shine roll coater of UV-radium-shine roller coat priming paint, consumption 40 ~ 50g/m2; Levelling 15 seconds, uses 400# sand papering after 180mj/cm2UV solidification;
6) with the spraying of UV-water-based spray-applied primer, consumption 100 ~ 110g/m2; 150mj/cm2UV solidification after infrared ray dries 90 minutes at 50 DEG C, uses 600# sand papering after cooling;
7) use dressing agent spraying, consumption 20 ~ 30g/m2; Infrared ray dries 10 minutes at 60 DEG C;
8) with the spraying of UV-water-based spraying sheen finish paint, consumption 100 ~ 110g/m2; 250mj/cm2UV solidification after infrared ray dries 90 minutes at 50 DEG C.
As shown in Figure 1, sheet material comprises substrate layer 8, is coated on the UV-water-based wiping stain 1 of substrate layer successively, UV-roller coat fills the radium-shine roller coat finish paint 4 of putty 2, UV-roller coat sanding priming paint 3, UV-, UV-water-based spray-applied primer 5, water-based dressing agent 6, UV-water-based spraying sheen finish paint 7.
Embodiment 2
Another produces the environmentally-friendly coating method of timber, furniture, and the application step of its planar member is identical with embodiment 1, and just UV-water paint is replaced by single-component water-based coating, and concrete steps are as follows:
1) with 80#, 100#, 120# sand paper sanding element plate respectively;
2) use PUD wiping stain substrate surface is manual wipes look, consumption 8 ~ 12g/m2, and infrared ray 70 DEG C is dried for 10 minutes,
3) fill the coating of putty putty roll coater with UV-roller coat, after consumption 30 ~ 40g/m2,150mj/cm2UV solidification, use 240# sand papering, continuous application 2 populated wooden eyes;
4) be coated with the radium-shine roll coater of UV-roller coat sanding priming paint, consumption 30 ~ 40g/m2, levelling 15 seconds, 80mj/cm2UV semi-solid preparation, the slight sticky hand in surface;
5) be coated with the radium-shine roll coater of UV-radium-shine roller coat priming paint, consumption 40 ~ 50g/m2; Levelling 15 seconds, uses 400# sand papering after 180mj/cm2UV solidification;
6) use one-component spray-applied primer spraying, consumption 100 ~ 110g/m2; Infrared ray dries 90 minutes at 50 DEG C, uses 600# sand papering after cooling;
7) use dressing agent spraying, consumption 20 ~ 30g/m2; Infrared ray dries 10 minutes at 60 DEG C;
8) use one-component spraying sheen finish paint spraying, consumption 100 ~ 110g/m2; Infrared ray dries 90 minutes at 50 DEG C.
Embodiment 3
Another produces the environmentally-friendly coating method of timber, furniture, and the application step of its planar member is identical with embodiment 2, and just single-component water-based coating is replaced by double-component water paint, and concrete steps are as follows:
1) with 80#, 100#, 120# sand paper sanding element plate respectively;
2) use PUD wiping stain substrate surface is manual wipes look, consumption 8 ~ 12g/m2, and infrared ray 70 DEG C is dried for 10 minutes,
3) fill the coating of putty putty roll coater with UV-roller coat, after consumption 30 ~ 40g/m2,150mj/cm2UV solidification, use 240# sand papering, continuous application 2 populated wooden eyes;
4) be coated with the radium-shine roll coater of UV-roller coat sanding priming paint, consumption 30 ~ 40g/m2, levelling 15 seconds, 80mj/cm2UV semi-solid preparation, the slight sticky hand in surface;
5) be coated with the radium-shine roll coater of UV-radium-shine roller coat priming paint, consumption 40 ~ 50g/m2; Levelling 15 seconds, uses 400# sand papering after 180mj/cm2UV solidification;
6) use two component spray basecoat paint, consumption 100 ~ 110g/m2; Infrared ray dries 90 minutes at 50 DEG C, and use 600# sand papering after cooling, this coating needs use two component spray priming paint: waterborne curing agent: deionized water=80:10:10 is in harmonious proportion;
7) use dressing agent spraying, consumption 20 ~ 30g/m2; Infrared ray dries 10 minutes at 60 DEG C;
8) use two component spray sheen finish paint spraying, consumption 100 ~ 110g/m2; Infrared ray dries 90 minutes at 50 DEG C, and this coating needs use two component spray sheen finish paint: waterborne curing agent: deionized water=80:10:10 is in harmonious proportion;
Embodiment 4
A kind of environmentally-friendly coating method of producing timber, furniture, the application of its straight shape lines shaped piece: the method adopts UV-water-based wiping stain, UV-airless spraying priming paint, UV-water-based spray-applied primer, water-based dressing agent and UV-water-based spraying sheen finish paint to construct, and concrete steps are as follows:
1) with 180#, 240#, 320# abnormity sand sanding element plate respectively;
2) wipe look, consumption 8 ~ 12g/m2 with UV-water-based wiping stain substrate surface is manual, infrared ray 70 DEG C is dried for 10 minutes,
3) spray with UV-airless spraying priming paint vacuum spray painting machine, consumption 40 ~ 60g/m2,200mj/cm2UV solidification is rear with the polishing of 400# abnormity sand, and according to the needs of wood quality, continuous application 3 populated wooden eyes, polish with 600# abnormity sand sand for the 3rd time;
4) with the spraying of UV-water-based spray-applied primer, consumption 100 ~ 110g/m2; 150mj/cm2UV solidification after infrared ray dries 90 minutes removal moisture content at 50 DEG C, with the special-shaped sand polishing of 600# after cooling;
5) use dressing agent spraying, consumption 20 ~ 30g/m2; Infrared ray dries 10 minutes at 70 DEG C;
6) with the spraying of UV-water-based spraying sheen finish paint, consumption 100 ~ 110g/m2; 250mj/cm2UV solidification after infrared ray dries 90 minutes removal moisture content at 50 DEG C.
As shown in Figure 2, sheet material comprises substrate layer 10, is coated on UV-water-based wiping stain 11, UV-airless spraying priming paint 12, the UV-water-based spray-applied primer 13 of substrate layer successively, water-based dressing agent 14, UV-water-based spraying sheen finish paint 15.
Embodiment 5
Another produces the environmentally-friendly coating method of timber, furniture, the application step of its straight shape lines shaped piece is identical with embodiment 4, just UV-water paint is replaced by single-component water-based coating, and the 3rd time spraying of airless spraying is replaced by spray thrower construction, and concrete steps are as follows:
1) with 180#, 240#, 320# abnormity sand sanding element plate respectively;
2) use PUD wiping stain substrate surface is manual wipes look, consumption 8 ~ 12g/m2, and infrared ray 70 DEG C is dried for 10 minutes,
3) spray with UV-airless spraying priming paint vacuum spray painting machine, consumption 40 ~ 60g/m2, with the polishing of 400# abnormity sand after 200mj/cm2UV solidification, according to the needs of wood quality, continuous application 2 populated wooden eyes, with spray thrower spraying, after consumption 60 ~ 80g/m2,200mj/cm2UV solidification, use the polishing of 600# abnormity sand 3rd time;
4) use one-component spray-applied primer spraying, consumption 100 ~ 110g/m2; Infrared ray dries 90 minutes at 50 DEG C, with the polishing of 600# abnormity sand after cooling;
5) use dressing agent spraying, consumption 20 ~ 30g/m2; Infrared ray dries 10 minutes at 70 DEG C;
6) use one-component spraying sheen finish paint spraying, consumption 100 ~ 110g/m2; Infrared ray dries 90 minutes at 50 DEG C.
Embodiment 6
Another produces the environmentally-friendly coating method of timber, furniture, and the application step of its straight shape lines shaped piece is identical with embodiment 4, and just aqueous one-component coating is replaced by aqueous double-component coating, and concrete steps are as follows:
1) with 180#, 240#, 320# abnormity sand sanding element plate respectively;
2) use PUD wiping stain substrate surface is manual wipes look, consumption 8 ~ 12g/m2, and infrared ray 70 DEG C is dried for 10 minutes,
3) spray with UV-airless spraying priming paint vacuum spray painting machine, consumption 40 ~ 60g/m2,200mj/cm2UV solidification is rear with the polishing of 400# abnormity sand, and according to the needs of wood quality, continuous application 3 populated wooden eyes, polish with 600# abnormity sand for the 3rd time;
4) use two component spray basecoat paint, consumption 100 ~ 110g/m2; Infrared ray dries 90 minutes at 50 DEG C, with the polishing of 600# abnormity sand after cooling; This coating needs use two component spray sheen finish paint: waterborne curing agent: deionized water=80:10:10 is in harmonious proportion;
5) use dressing agent spraying, consumption 20 ~ 30g/m2; Infrared ray dries 10 minutes at 70 DEG C;
6) use two component spray sheen finish paint spraying, consumption 100 ~ 110g/m2; Infrared ray dries 90 minutes at 50 DEG C, and this coating needs use two component spray sheen finish paint: waterborne curing agent: deionized water=80:10:10 is in harmonious proportion.
More than test, wipe look and wipe look for manual, roller coat adopts putty roll coater, radium-shine roll coater is two radium-shine rollers of roller list, hardness of rubber roll is 40 degree of 55 line, vacuum spray painting machine is-12 atmospheric pressure constructions, spray thrower is Pneumatic pressure formula spray thrower, flush coater is reciprocating mixed paint formula flush coater, plane sanding adopts built-in type sander, shaped piece adopts many sand head irregular sanding machine, the application of above mechanization and the collocation of novel environment friendly coating use, make technique more advanced, improve the percent of automatization of application, significantly improve the utilization rate of coating, effectively reduce the discharge of coating in use VOC, reasonably combined by technique and coating, significantly improve the stereovision of wood color, add hardness of paint film and richness, and lacquer painting third dimension is strong, feel is cunning, excellent visual effect and sense of touch can be obtained, drastically increase the aesthetics of product and enhance the protective value of product.The present invention is applicable in the construction of timber, furniture.
After testing, use the technical indicator of the substrate of application of the present invention as following table 1:
Table 1
The present invention is by using the UV coating of environmental protection and the reasonably combined of water paint; select high efficiency construction method; improve production efficiency; and add hardness of paint film and richness; lacquer painting third dimension is strong, feel is cunning; can excellent visual effect and sense of touch be obtained, drastically increase the aesthetics of product and enhance the protective value of product.
Claims (2)
1. produce the environmentally-friendly coating method of timber, furniture for one kind, it is characterized in that: 8 kinds of coating that the method adopts UV coating and water paint to combine carry out application, wherein 4 kinds of UV coating are UV-airless spraying priming paint, the filling of UV-roller coat putty, UV-roller coat sanding priming paint, the radium-shine roller coat priming paint of UV-respectively; 4 kinds of water paints are water-based wiping stain, water-based spray-applied primer, water-based dressing agent and water-based spraying sheen finish paint respectively, and specific requirement is as follows:
1) to planar member, adopt water-based wiping stain, UV-roller coat to fill putty, UV-roller coat sanding priming paint, the radium-shine roller coat priming paint of UV-, water-based spray-applied primer, water-based dressing agent and water-based spraying sheen finish paint and construct, concrete steps are as follows:
11) with sand paper sanding element plate;
12) use wiping stain substrate surface is manual wipes look, consumption 8 ~ 12g/m2, infrared baking, and this water-based wiping stain is wiping stain or the water-based PUD of UV type;
13) fill the coating of putty putty roll coater with UV-roller coat, consumption 30 ~ 40g/m2,150mj/cm2UV solidify rear sand papering, the populated wooden eye of continuous application;
14) be coated with the radium-shine roll coater of UV-roller coat sanding priming paint, consumption 30 ~ 40g/m2,80mj/cm2UV solidify rear sand papering;
15) be coated with the radium-shine roll coater of UV-radium-shine roller coat priming paint, consumption 40 ~ 50g/m2; 400# sand papering is used after 180mj/cm2UV solidification;
16) use spray-applied primer spraying, consumption 100 ~ 110g/m2; Infrared ray dries 90 minutes at 50 DEG C, use 600# sand papering after cooling, and this water-based spray-applied primer is UV type or aqueous one-component or aqueous double-component, UV type 50 DEG C dry within 90 minutes, remove moisture content after 150mj/cm2UV solidify;
17) use dressing agent spraying, consumption 20 ~ 30g/m2; Infrared ray is 60 DEG C of oven dry;
18) use spraying sheen finish paint spraying, consumption 100 ~ 110g/m2; Infrared ray dries 90 minutes at 50 DEG C, and this water-based spraying sheen finish paint is UV type or aqueous one-component or aqueous double-component, UV type need 50 DEG C dry within 90 minutes, remove moisture content after 250mj/cm2UV solidification;
2) to straight shape lines shaped piece, adopt water-based wiping stain, UV-airless spraying priming paint, water-based spray-applied primer, water-based dressing agent and water-based spraying sheen finish paint to construct, concrete steps are as follows:
21) with sand paper sanding element plate;
22) use wiping stain substrate surface is manual wipes look, consumption 8 ~ 12g/m2, infrared baking, and this wiping stain is wiping stain and the water-based PUD of UV type;
23) with UV-airless spraying priming paint vacuum spray painting machine or spray thrower coating, consumption 40 ~ 60g/m2,200mj/cm2UV solidify rear sand papering, according to the needs of wood quality, and continuous application 2 ~ 3 populated wooden eyes;
24) use spray-applied primer spraying, consumption 100 ~ 110g/m2; Infrared ray dries 90 minutes at 50 DEG C, use 600# sand papering after cooling, and this water-based spray-applied primer is UV type or aqueous one-component or aqueous double-component, UV type need 50 DEG C dry within 60 minutes, remove moisture content after 150mj/cm2UV solidify;
25) use dressing agent spraying, consumption 20 ~ 30g/m2; Infrared ray is 60 DEG C of oven dry;
26) use spraying sheen finish paint spraying, consumption 100 ~ 110g/m2; Infrared ray dries 90 minutes at 50 DEG C, and this water-based spraying sheen finish paint is UV type or aqueous one-component or aqueous double-component, UV type need 50 DEG C dry within 90 minutes, remove moisture content after 250mj/cm2UV solidification.
2. the environmentally-friendly coating method of production timber according to claim 1, furniture, is characterized in that: step 17) and step 25) in, use dressing agent sprays, and infrared ray dries 10 minutes at 60 DEG C.