CN106311576A - Coating method - Google Patents

Coating method Download PDF

Info

Publication number
CN106311576A
CN106311576A CN201510402388.2A CN201510402388A CN106311576A CN 106311576 A CN106311576 A CN 106311576A CN 201510402388 A CN201510402388 A CN 201510402388A CN 106311576 A CN106311576 A CN 106311576A
Authority
CN
China
Prior art keywords
aqueous
priming paint
paint
consumption
coating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201510402388.2A
Other languages
Chinese (zh)
Inventor
佘学彬
沈乃强
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
GUANGDONG YINGRAN WOOD CO Ltd
Original Assignee
GUANGDONG YINGRAN WOOD CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by GUANGDONG YINGRAN WOOD CO Ltd filed Critical GUANGDONG YINGRAN WOOD CO Ltd
Priority to CN201510402388.2A priority Critical patent/CN106311576A/en
Publication of CN106311576A publication Critical patent/CN106311576A/en
Withdrawn legal-status Critical Current

Abstract

The invention discloses a coating method for furniture. A water-based coating and a UV coating which are jointly used are adopted in the method. The method comprises the following selected steps that firstly, a base material is provided; secondly, a water-based color wiping agent is applied to the surface of the base material, and the usage amount of the water-based color wiping agent is 8 g/m<2>-12 g/m<2>; thirdly, UV putty is applied, and the usage amount of the UV putty is 30 g/m<2>-40 g/m<2>; fourthly, UV primer is applied, and the usage amount of the UV primer is 30 g/m<2>-50 g/m<2>; fifthly, water-based primer is applied, and the usage amount of the water-based primer is 100 g/m<2>-110 g/m<2>; sixthly, a water-based color modifying agent is applied, and the usage amount of the color modifying agent is 20 g/m<2>-30 g/m<2>; and seventhly, water-based finish paint is applied, and the usage amount of the water-based finish paint is 100 g/m<2>-110 g/m<2>. In the third step, applying is finished through a roller painting manner. In the fourth step and the fifth step, applying is finished through one of a roller painting manner and a spraying manner or the combination manner of roller painting and spraying. In the sixth step, applying is finished through a spraying manner. In the seventh step, applying is finished through a spraying manner. The furniture is provided with a flat surface or a non-flat surface. By means of the coating method, the product performance is improved, environment friendliness is achieved, and implementation is easy.

Description

A kind of coating process
Technical field
The present invention relates to a kind of coating process, specifically, the present invention relates to a kind of use aqueous and UV is coated with The coating process of material.
Background technology
UV coating is a kind of ultraviolet-curing paint.Existing antique traditional furniture, painting wood door the most all use Traditional polyurethane (PU) dual-component coating, nitro paint equal solvent type coating carry out application, use this When class coating carries out the application of furniture etc., need bigger production area and paint solidification time long, and And this traditional polyurethane (PU) coating is containing organic solvent, can produce volatile organic matter, thus exist Coating process produces substantial amounts of Volatile organic emissions, and atmospheric environment is created and has a strong impact on, This is significantly to the about use of traditional coating process.Some factory has started to use UV coating, but only portion Coating is divided to use UV coating that the whole UV application of the most whole coating, and some UV coating still contain Organic solvent, still can produce higher Volatile organic emissions.Therefore, this area needs a kind of ring badly Protect and coating process easy to implement.
Summary of the invention
In order to solve the defect that prior art exists, the present invention provides a kind of coating process for furniture, Environmental protection and easy to implement.
The coating process for furniture that the embodiment of the present invention provides includes:
I) base material is provided;
Ii) applying aqueous wiping stain on the surface of described base material, the consumption of this aqueous wiping stain is 8-12g/m2;;
Iii) applying UV putty, the consumption of described UV putty is 30-40g/m2
Iv) applying UV priming paint, the consumption of described UV priming paint is 30-50g/m2
V) applying aqueous priming paint, the consumption of described aqueous priming paint is 100-110g/m2
Vi) applying aqueous dressing agent, the consumption of described aqueous dressing agent is 20-30g/m2
Vii) applying aqueous finish paint, the consumption of described aqueous finish paint is 100-110g/m2
Wherein,
In step iii, described in be applied through roll coating model and complete;
In step iv and step v, described in be applied through roller coat or spraying in a kind of mode or both groups Conjunction mode completes;
In step vi, described in be applied through spraying method and complete;
In step vii, described in be applied through spraying method and complete;
Further, wherein, described furniture has smooth surface or uneven surface.
Alternatively, in a kind of implementation of the present embodiment, in step i, described substrate surface is carried out Sanding processes.
Alternatively, in a kind of implementation of the present embodiment, the UV priming paint in step iv is selected from: UV Sanding priming paint, UV airless spraying priming paint, UV roller coat priming paint.
Alternatively, in a kind of implementation of the present embodiment, the aqueous priming paint in step v is selected from: water Property one-component primers, aqueous dual-component priming paint and UV type priming paint.
Alternatively, in a kind of implementation of the present embodiment, the aqueous finish paint in step vii is selected from: water Property one-component primers, aqueous dual-component priming paint and UV type priming paint.
Alternatively, in a kind of implementation of the present embodiment, described aqueous priming paint and described aqueous finish paint Comprise polyurethane coating and waterborne curing agent and deionized water.
Alternatively, in a kind of implementation of the present embodiment, the aqueous wiping stain in step ii comprises poly- Urethane.
Alternatively, in a kind of implementation of the present embodiment, described infrared radiation is carried out at 50-60 DEG C 10-90 minute.
The coating process using the embodiment of the present invention to provide, improves the stereovision of wood color, adds Hardness of paint film and richness, and lacquer painting third dimension is strong, feel is cunning, can obtain excellence visual effect and Sense of touch, drastically increases the aesthetics of product and enhances the protective value of product.Generally speaking, ring Protect and easy to implement.
Accompanying drawing explanation
Fig. 1 to Fig. 3 is shown and is obtained by the coating process of the present invention according to the embodiment of the present invention Timber flat board on coating structure schematic diagram.
Fig. 4 to Fig. 6 is shown and is obtained by the coating process of the present invention according to the embodiment of the present invention Shaped piece on coating structure schematic diagram.
Detailed description of the invention
For making the object, technical solutions and advantages of the present invention clearer, say the most by way of example Bright the present invention is described in detail, but embodiments of the present invention described below are only illustrated Bright, the present invention is not constituted any restriction.
Embodiment 1
The present embodiment provides a kind of exemplary method for application planar member, and described method includes as follows Step:
1) with 80#, 100#, 120# sand paper sanding element plate respectively;
2) with UV-aqueous wiping stain to step 1) the plain plate surface that processed carries out manual wiping color, consumption 8~12g/m2, 70 DEG C of drying in 10 minutes of infrared ray,
3) putty, consumption 30~40g/m are filled with putty roll coater coating UV-roller coat2, 150mJ/cm2UV Using 240# sand papering after solidification, continuous application 2 times is with filling timber eye;
4) with radium-shine roll coater coating UV-roller coat sanding priming paint, consumption 30~40g/m2, levelling 15 seconds, 80mJ/cm2UV semi-solid preparation, hands is slightly glued on surface;
5) it is coated with radium-shine roll coater with UV-radium-shine roller coat priming paint, consumption 40~50g/m2;Levelling 15 seconds, 180mJ/cm2400# sand papering is used after UV solidification;
6) spray with UV-aqueous spray-applied primer, consumption 100~110g/m2;Infrared ray dries 90 at 50 DEG C 150mJ/cm after minute2UV solidifies, and uses 600# sand papering after cooling;
7) spray with aqueous dressing agent, consumption 20~30g/m2;Infrared ray dries 10 minutes at 60 DEG C;
8) with the spraying sheen finish paint spraying of UV-aqueous, consumption 100~110g/m2;Infrared ray is 50 DEG C of bakings 250mJ/cm after 90 minutes2UV solidifies.
As it is shown in figure 1, wipe by using the method for the present embodiment to form UV-aqueous successively on base material 11 Colorant layer 12, UV-roller coat fills putty layer 13, UV-roller coat sanding prime coat 14, UV-radium-shine roller coat face Enamelled coating 15, UV-aqueous spray-applied primer layer 16, aqueous dressing agent layer 17, UV-aqueous spraying sheen finish paint Layer 18.
Embodiment 2
The present embodiment provides a kind of exemplary method for application planar member, its application step and enforcement Example 1 is identical, and simply UV-water paint is replaced by single-component water-based coating, specifically comprises the following steps that
1) with 80#, 100#, 120# sand paper sanding element plate respectively;
2) with aqueous PUD wiping stain to step 1) the plain plate surface that processed carries out manual wiping color, consumption 8~12g/m2, 70 DEG C of drying in 10 minutes of infrared ray,
3) putty, consumption 30~40g/m are filled with putty roll coater coating UV-roller coat2, 150mJ/cm2UV Using 240# sand papering after solidification, continuous application 2 times is with filling timber eye;
4) with radium-shine roll coater coating UV-roller coat sanding priming paint, consumption 30~40g/m2, levelling 15 seconds, 80mJ/cm2UV semi-solid preparation, hands is slightly glued on surface;
5) with radium-shine roll coater coating UV-radium-shine roller coat priming paint, consumption 40~50g/m2;Levelling 15 seconds, 180mJ/cm2400# sand papering is used after UV solidification;
6) spraying aqueous one-component spray-applied primer, consumption 100~110g/m2;Infrared ray dries 90 at 50 DEG C Minute, use 600# sand papering after cooling;
7) spraying aqueous dressing agent, consumption 20~30g/m2;Infrared ray dries 10 minutes at 60 DEG C;
8) spraying aqueous one-component spraying sheen finish paint, consumption 100~110g/m2;Infrared ray is 50 DEG C of bakings 90 minutes.
As in figure 2 it is shown, by using the method for the present embodiment to form aqueous PUD successively on base material 21 Wiping stain layer 22, UV-roller coat fills putty layer 23, UV-roller coat sanding prime coat 24, the radium-shine roller coat of UV- Top coat layer 25, aqueous spray-applied primer layer 26, aqueous dressing agent layer 27, aqueous spraying sheen top coat layer 28.
Embodiment 3
The present embodiment provides a kind of exemplary method for application planar member, its application step and enforcement Example 2 is identical, and the most single-component water-based coating is replaced by double-component water paint, specifically comprises the following steps that
1) with 80#, 100#, 120# sand paper sanding element plate respectively;
2) with aqueous PUD wiping stain to step 1) the plain plate surface that processed carries out manual wiping color, consumption 8~12g/m2, 70 DEG C of drying in 10 minutes of infrared ray,
3) putty, consumption 30~40g/m are filled with putty roll coater coating UV-roller coat2, 150mJ/cm2UV Using 240# sand papering after solidification, continuous application 2 times is with filling timber eye;
4) with radium-shine roll coater coating UV-roller coat sanding priming paint, consumption 30~40g/m2, levelling 15 seconds, 80mJ/cm2UV semi-solid preparation, hands is slightly glued on surface;
5) with radium-shine roll coater coating UV-radium-shine roller coat priming paint, consumption 40~50g/m2;Levelling 15 seconds, 180mJ/cm2400# sand papering is used after UV solidification;
6) spraying aqueous double-component spray-applied primer, consumption 100~110g/m2;Infrared ray dries 90 at 50 DEG C Minute, use 600# sand papering after cooling, this priming paint is by aqueous double-component spray-applied primer: waterborne curing agent: Deionized water is in harmonious proportion with the ratio of 80:10:10;
7) spraying aqueous dressing agent, consumption 20~30g/m2;Infrared ray dries 10 minutes at 60 DEG C;
8) spraying aqueous one-component spraying sheen finish paint, consumption 100~110g/m2;Infrared ray is 50 DEG C of bakings 90 minutes, this finish paint was by aqueous double-component spraying sheen finish paint: waterborne curing agent: deionized water=80:10:10 It is in harmonious proportion.
As it is shown on figure 3, by using the method for the present embodiment to form aqueous PUD successively on base material 31 Wiping stain layer 32, UV-roller coat fills putty layer 33, UV-roller coat sanding prime coat 34, the radium-shine roller coat of UV- Top coat layer 35, aqueous double-component spray-applied primer layer 36, aqueous dressing agent layer 37, aqueous double-component spraying is soft Bright finish enamelled coating 38.
Embodiment 4
The present embodiment provides a kind of exemplary method for application shaped piece, specifically comprises the following steps that
1) with 180#, 240#, 320# abnormity sand sanding element plate respectively;
2) with UV-aqueous wiping stain to step 1) the plain plate surface that processed carries out manual wiping color, consumption 8~12g/m2, 70 DEG C of drying in 10 minutes of infrared ray,
3) UV-airless spraying priming paint, consumption 40~60g/m are sprayed with vacuum spray painting machine2, 200mJ/cm2UV Polish with 400# abnormity sand after solidification, according to the needs of wood quality, continuous application 3 times with filling timber eye, Polish with 600# abnormity sand sand for 3rd time;
4) spraying UV-aqueous spray-applied primer, consumption 100~110g/m2;Infrared ray dries 90 minutes at 50 DEG C Rear 150mJ/cm2UV solidifies, and polishes with 600# abnormity sand after cooling;
5) spraying aqueous dressing agent, consumption 20~30g/m2;Infrared ray dries 10 minutes at 70 DEG C;
6) spraying UV-aqueous spraying sheen finish paint, consumption 100~110g/m2;Infrared ray dries 90 at 50 DEG C 250mJ/cm after minute2UV solidifies.
As shown in Figure 4, the method by using the present embodiment forms the wiping of UV-aqueous successively on base material 41 Colorant layer 42, UV-airless spraying prime coat 44, UV-aqueous spray-applied primer layer 46, aqueous dressing agent layer 47, UV-aqueous spraying sheen top coat layers 48.
Embodiment 5
The present embodiment provides a kind of exemplary method for application shaped piece, its step and embodiment 4 Identical, simply UV-water paint is replaced by single-component water-based coating, and the 3rd time spraying of airless spraying is more It is changed to spray thrower construction, specifically comprises the following steps that
1) with 180#, 240#, 320# abnormity sand sanding element plate respectively;
2) with aqueous PUD wiping stain to step 1) substrate surface that processed carries out manual wiping color, consumption 8~12g/m2, 70 DEG C of drying in 10 minutes of infrared ray,
3) UV-airless spraying priming paint, consumption 40~60g/m are sprayed with vacuum spray painting machine2, 200mJ/cm2UV Polish with 400# abnormity sand after solidification, according to the needs of wood quality, continuous application 2 times with filling timber eye, Spray with spray thrower for 3rd time, consumption 60~80g/m2, 200mJ/cm2With 600# abnormity sand after UV solidification Polishing;
4) spraying aqueous one-component spray-applied primer, consumption 100~110g/m2;Infrared ray dries 90 at 50 DEG C Minute, polish with 600# abnormity sand after cooling;
5) spraying aqueous dressing agent, consumption 20~30g/m2;Infrared ray dries 10 minutes at 70 DEG C;
6) spraying aqueous one-component spraying sheen finish paint, consumption 100~110g/m2;Infrared ray is 50 DEG C of bakings 90 minutes.
As it is shown in figure 5, by using the method for the present embodiment to form aqueous PUD successively on base material 51 Wiping stain layer 52, UV-airless spraying prime coat 54, aqueous one-component spray-applied primer layer 56, aqueous repaiies color Oxidant layer 57, aqueous one-component spraying sheen top coat layer 58.
Embodiment 6
The present embodiment provides a kind of exemplary method for application shaped piece, its step and embodiment 4 Identical, simply aqueous one-component coating is replaced by aqueous double-component coating, specifically comprises the following steps that
1) with 180#, 240#, 320# abnormity sand sanding element plate respectively;
2) with aqueous PUD wiping stain to step 1) the plain plate surface that processed carries out manual wiping color, consumption 8~12g/m2, 70 DEG C of drying in 10 minutes of infrared ray,
3) UV-airless spraying priming paint, consumption 40~60g/m are sprayed with vacuum spray painting machine2, 200mJ/cm2UV Polish with 400# abnormity sand after solidification, according to the needs of wood quality, continuous application 3 times with filling timber eye, Polish with 600# abnormity sand for 3rd time;
4) spraying aqueous double-component spray-applied primer, consumption 100~110g/m2;Infrared ray dries 90 at 50 DEG C Minute, polish with 600# abnormity sand after cooling;This priming paint is by aqueous double-component spraying sheen finish paint: aqueous Firming agent: deionized water=80:10:10 is in harmonious proportion;
5) spraying aqueous dressing agent, consumption 20~30g/m2;Infrared ray dries 10 minutes at 70 DEG C;
6) spraying aqueous double-component spraying sheen finish paint, consumption 100~110g/m2;Infrared ray is 50 DEG C of bakings 90 minutes, this finish paint was by aqueous double-component spraying sheen finish paint: waterborne curing agent: deionized water=80:10:10 It is in harmonious proportion.
As shown in Figure 6, the method by using the present embodiment forms aqueous PUD successively on base material 61 Wiping stain layer 62, UV-airless spraying prime coat 64, aqueous double-component spray-applied primer layer 66, aqueous repaiies color Oxidant layer 67, aqueous double-component spraying sheen top coat layer 68.
More than testing and provided coating and technical support by Jiangsu Himonia Technology Co., Ltd., wiping color is manual wiping Color, roller coat uses putty roll coater, and radium-shine roll coater is double radium-shine rollers of roller list, and hardness of rubber roll is 40 degree 55 Line, vacuum spray painting machine is-12 atmospheric pressure constructions, and spray thrower is Pneumatic pressure formula spray thrower, and flush coater is Reciprocating mixed paint formula flush coater, plane sanding uses built-in type sander, and shaped piece uses many Fructus Amomi abnormity Sander, the application of above mechanization and the collocation of novel environment friendly coating use, and make technique more advanced, carry The high percent of automatization of application, hence it is evident that improve the utilization rate of coating, effectively reduce coating and using The discharge of VOC in journey, reasonably combined by technique and coating, hence it is evident that improve the level of wood color Sense, adds hardness of paint film and richness, and lacquer painting third dimension is strong, feel is cunning, can obtain excellence Visual effect and sense of touch, drastically increase the aesthetics of product and enhance the protective value of product.This The method of invention is applicable to the application of timber, furniture.
After testing, the coating process of the present invention is used and the technical specification of the substrate of application is listed in the table below 1:
Table 1
By the present invention in that the UV coating of use environmental protection and the reasonably combined of water paint, select high efficiency Construction method, improves production efficiency, and adds hardness of paint film and richness, lacquer painting third dimension is strong, Feel is cunning, can obtain visual effect and the sense of touch of excellence, drastically increase aesthetics and the increasing of product The strong protective value of product.
Describing the present invention above in association with detailed description of the invention, these detailed description of the invention are only Exemplary, it is impossible to limiting protection scope of the present invention with this, those skilled in the art are without departing from this Various amendment can be carried out on the premise of bright essence, change or replace.Therefore, made according to the present invention Various equivalent variations, still fall within the scope that the present invention is contained.

Claims (9)

1., for a coating process for furniture, described method includes that water paint is used in combination and UV is coated with Material, described method includes selected from following step:
I) base material is provided;
Ii) applying aqueous wiping stain on the surface of described base material, the consumption of this aqueous wiping stain is 8-12g/m2
Iii) applying UV putty, the consumption of described UV putty is 30-40g/m2
Iv) applying UV priming paint, the consumption of described UV priming paint is 30-50g/m2
V) applying aqueous priming paint, the consumption of described aqueous priming paint is 100-110g/m2
Vi) applying aqueous dressing agent, the consumption of described aqueous dressing agent is 20-30g/m2
Vii) applying aqueous finish paint, the consumption of described aqueous finish paint is 100-110g/m2
Wherein,
In step iii, described in be applied through roll coating model and complete;
In step iv and step v, described in be applied through roller coat or spraying in a kind of mode or both groups Conjunction mode completes;
In step vi, described in be applied through spraying method and complete;
In step vii, described in be applied through spraying method and complete;
Further, wherein, described furniture has smooth surface or uneven surface.
The most the method for claim 1, wherein, in step i, described substrate surface is carried out at sanding Reason.
The most the method for claim 1, wherein each step in step ii to step vii completes Solidify afterwards, and, described solidification is completed by infrared radiation.
The most the method for claim 1, wherein the UV priming paint in step iv is selected from: at the bottom of UV sanding Paint, UV airless spraying priming paint, UV roller coat priming paint.
The most the method for claim 1, wherein the aqueous priming paint in step v is selected from: aqueous list group Divide priming paint, aqueous dual-component priming paint and UV type priming paint.
The most the method for claim 1, wherein the aqueous finish paint in step vii is selected from: aqueous list group Divide priming paint, aqueous dual-component priming paint and UV type priming paint.
7. the method as described in claim 5 or 6, wherein, described aqueous priming paint and described aqueous finish paint bag Containing polyurethane coating and waterborne curing agent and deionized water.
The most the method for claim 1, wherein the aqueous wiping stain in step ii comprises polyurethane.
9. method as claimed in claim 3, wherein, described infrared radiation carries out 10-90 at 50-60 DEG C Minute.
CN201510402388.2A 2015-07-09 2015-07-09 Coating method Withdrawn CN106311576A (en)