CN105478326A - UV coating construction process of edge band veneer elastic matte finishing paint - Google Patents
UV coating construction process of edge band veneer elastic matte finishing paint Download PDFInfo
- Publication number
- CN105478326A CN105478326A CN201510755274.6A CN201510755274A CN105478326A CN 105478326 A CN105478326 A CN 105478326A CN 201510755274 A CN201510755274 A CN 201510755274A CN 105478326 A CN105478326 A CN 105478326A
- Authority
- CN
- China
- Prior art keywords
- carry out
- coating
- drying time
- tic
- curing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a half-open UV coating construction process of edge band veneer elastic matte finishing paint. The half-open UV coating construction process comprises the following steps: (S1) a coiled natural veneer or technical veneer base material is sanded by a special veneer sanding machine; (S2) the roll coating is performed for special veneer elastic UV putty; the coating quantity is 30 g/m2; double mercury lamps are used for ultraviolet drying; the drying strength is 200 mJ; and the drying time is 3 seconds; (S3) the roll coating is performed for special veneer elastic UV elastic primer; the coating quantity is 70 g/m2; then, double mercury lamps are used for ultraviolet drying; the drying strength is 200 mJ; and the drying time is 3 seconds; (S4) the roll coating is performed for special veneer elastic UV sanding primer; the coating quantity is 30 g/m2; then, double mercury lamps are used for ultraviolet drying; the drying strength is 250 mJ; and the drying time is 3 seconds; and the like. The construction process needs no spraying, is free of paint mist, and can be suitable for batch production; and as the roll coating is performed for UV paint on the surface of the base material, subsequent coating treatment is not needed after a wood line is coated by a veneer painted by the elastic primer and finishing paint.
Description
Technical field
The present invention relates to coating application field, more specifically, relate to the wooden skin elasticity dull finishing coat UV coating construction process of a kind of edge band.
Background technology
Producing making wood twig main technique is in the market first directly be coated on making wood twig with the wooden skin without any application process, then through polishing, spraying at least twice priming paint (needing to polish after often spraying one deck priming paint), finally carries out finish paint spray-coating again.Harmful substance volatilization so in process of production, have a strong impact on healthy, and the production cycle is long, easy generation is split cruelly, plays the problems such as tangerine peel, and difficulty of simultaneously polishing is very big.
Summary of the invention
In order to solve traditional handicraft not environmentally, the polishing problems such as difficulty is large, the wooden skin elasticity dull finishing coat UV coating construction process of a kind of edge band of the present invention, comprises the following steps
S1, wooden skin Special sander is used to carry out the process of sand hair rolling natural veneer or Recombinant Wood scytoblastema material;
S2, roller coat wood skin dedicated elas-tic UV putty, coating weight is 25 ~ 30g/ ㎡, and then carry out UV curing with two mercury lamp, dry tenacity is 200mJ, and drying time is 1 ~ 3 second;
S3, roller coat wood skin dedicated elas-tic UV elastic primer, coating weight is 30 ~ 40g/ ㎡, and then carry out UV curing with two mercury lamp, dry tenacity is 200mJ, and drying time is 1 ~ 3 second;
S4, roller coat wood skin dedicated elas-tic UV sanding priming paint, coating weight is 25 ~ 30g/ ㎡, and then carry out UV curing with two mercury lamp, dry tenacity is 250mJ, and drying time is 1 ~ 3 second;
S5, wooden skin sander is used to carry out sanding, dedusting;
S6, roller coat wood skin dedicated elas-tic UV repaiies color bottom paint, and coating weight is 15 ~ 25g/ ㎡, and then carry out UV curing with two mercury lamp, dry tenacity is 300mJ, and drying time is 1 ~ 3 second;
S7, roller coat wood skin dedicated elas-tic UV dull finishing coat, coating weight is 15 ~ 25g/ ㎡, and then carry out UV curing with two mercury lamp, dry tenacity is 250mJ, and drying time is 1 ~ 3 second;
S8, last overlay film packaging, complete production.
The present invention has the following advantages:
1, after natural or scientific and technological veneer surface being processed paint by mechanized production apparatus, the paint wood skin of formation is used as coated or veneer processing again.
2, painting wooden skin is by bottom coloring, scrapes priming paint and the multiple operation such as colored paint and finish paint application completes, and has the sense of reality of natural veneer and the surface effect of traditional paint technique.
3, paint wooden micromicro and be processed into fixed width fixed length or fixed width endless web-like wood skin, the utilization rate of wooden skin can be improved, the operating efficiency of equipment can be improved.
4, after holding in the palm nonwoven surface paint process bottom this wooden skin, wooden skin is more pliable and tougher, and coated processing is more prone to operation, and complicated linetype covered effect is more obvious.
5, product is applicable to Surface coating, overlay film and the edge sealing process such as various moulding, section bar are coated, Composite door pocket, Compound door leaf, on-the-spot finishing.
6, paint wooden skin and overturned woodwork painting technology, can effectively solve traditional handicraft because of the spraying paint of continuous more than three times of minimum needs, polish and several days time production cycle and the recruitment demand that causes is large, place takies many problems.
7, wooden skin is first through elasticity UV primer painting, elasticity finish paint UV application is carried out again after sanding, the last making wood twig that carries out again is coated, such new technology can solve traditional handicraft not environmentally, the problem such as polishing difficulty is large, and film thickness and paint film planarization can be very significantly improved.
Detailed description of the invention
The present invention is further described below in conjunction with specific embodiment.Unless stated otherwise, the present invention adopts reagent, equipment and method are conventional commercial reagent, equipment and the conventional method used of the art.
Embodiment 1
The wooden skin elasticity dull finishing coat UV coating construction process of a kind of edge band, comprises the following steps
S1, wooden skin Special sander is used to carry out the process of sand hair rolling natural veneer or Recombinant Wood scytoblastema material;
S2, roller coat wood skin dedicated elas-tic UV putty, coating weight is 30g/ ㎡, and then carry out UV curing with two mercury lamp, dry tenacity is 200mJ, and drying time is 3 seconds;
S3, roller coat wood skin dedicated elas-tic UV elastic primer, coating weight is 40g/ ㎡, and then carry out UV curing with two mercury lamp, dry tenacity is 200mJ, and drying time is 3 seconds;
S4, roller coat wood skin dedicated elas-tic UV sanding priming paint, coating weight is 30g/ ㎡, and then carry out UV curing with two mercury lamp, dry tenacity is 250mJ, and drying time is 3 seconds;
S5, wooden skin sander is used to carry out sanding, dedusting;
S6, roller coat wood skin dedicated elas-tic UV repaiies color bottom paint, and coating weight is 25g/ ㎡, and then carry out UV curing with two mercury lamp, dry tenacity is 300mJ, and drying time is 3 seconds;
S7, roller coat wood skin dedicated elas-tic UV dull finishing coat, coating weight is 25g/ ㎡, and then carry out UV curing with two mercury lamp, dry tenacity is 250mJ, and drying time is 3 seconds;
S8, last overlay film packaging, complete production.
Embodiment 2
The wooden skin elasticity dull finishing coat UV coating construction process of a kind of edge band, comprises the following steps
S1, wooden skin Special sander is used to carry out the process of sand hair rolling natural veneer or Recombinant Wood scytoblastema material;
S2, roller coat wood skin dedicated elas-tic UV putty, coating weight is 25g/ ㎡, and then carry out UV curing with two mercury lamp, dry tenacity is 200mJ, and drying time is 1 second;
S3, roller coat wood skin dedicated elas-tic UV elastic primer, coating weight is 30g/ ㎡, and then carry out UV curing with two mercury lamp, dry tenacity is 200mJ, and drying time is 1 second;
S4, roller coat wood skin dedicated elas-tic UV sanding priming paint, coating weight is 25g/ ㎡, and then carry out UV curing with two mercury lamp, dry tenacity is 250mJ, and drying time is 1 second;
S5, wooden skin sander is used to carry out sanding, dedusting;
S6, roller coat wood skin dedicated elas-tic UV repaiies color bottom paint, and coating weight is 15g/ ㎡, and then carry out UV curing with two mercury lamp, dry tenacity is 300mJ, and drying time is 1 second;
S7, roller coat wood skin dedicated elas-tic UV dull finishing coat, coating weight is 15g/ ㎡, and then carry out UV curing with two mercury lamp, dry tenacity is 250mJ, and drying time is 1 second;
S8, last overlay film packaging, complete production.
Embodiment 3
The wooden skin elasticity dull finishing coat UV coating construction process of a kind of edge band, comprises the following steps
S1, wooden skin Special sander is used to carry out the process of sand hair rolling natural veneer or Recombinant Wood scytoblastema material;
S2, roller coat wood skin dedicated elas-tic UV putty, coating weight is 27g/ ㎡, and then carry out UV curing with two mercury lamp, dry tenacity is 200mJ, and drying time is 2 seconds;
S3, roller coat wood skin dedicated elas-tic UV elastic primer, coating weight is 35g/ ㎡, and then carry out UV curing with two mercury lamp, dry tenacity is 200mJ, and drying time is 2 seconds;
S4, roller coat wood skin dedicated elas-tic UV sanding priming paint, coating weight is 27g/ ㎡, and then carry out UV curing with two mercury lamp, dry tenacity is 250mJ, and drying time is 2 seconds;
S5, wooden skin sander is used to carry out sanding, dedusting;
S6, roller coat wood skin dedicated elas-tic UV repaiies color bottom paint, and coating weight is 20g/ ㎡, and then carry out UV curing with two mercury lamp, dry tenacity is 300mJ, and drying time is 2 seconds;
S7, roller coat wood skin dedicated elas-tic UV dull finishing coat, coating weight is 20g/ ㎡, and then carry out UV curing with two mercury lamp, dry tenacity is 250mJ, and drying time is 2 seconds;
S8, last overlay film packaging, complete production.
Construction technology of the present invention, without the need to spraying, does not have coating cloud, and can be applicable to batch production; Owing to being that UV paint roller is applied to substrate surface, paint film is coated with very uniform ground, strong adhesion, and the wooden suitcase after most importantly using elastic primer and finish paint application covers after making wood twig without the need to follow-up application process.
Claims (1)
1. the wooden skin elasticity dull finishing coat UV coating construction process of edge band, is characterized in that, comprise the following steps
S1, wooden skin Special sander is used to carry out the process of sand hair rolling natural veneer or Recombinant Wood scytoblastema material;
S2, roller coat wood skin dedicated elas-tic UV putty, coating weight is 25 ~ 30g/ ㎡, and then carry out UV curing with two mercury lamp, dry tenacity is 200mJ, and drying time is 1 ~ 3 second;
S3, roller coat wood skin dedicated elas-tic UV elastic primer, coating weight is 60 ~ 70g/ ㎡, and then carry out UV curing with two mercury lamp, dry tenacity is 200mJ, and drying time is 1 ~ 3 second;
S4, roller coat wood skin dedicated elas-tic UV sanding priming paint, coating weight is 25 ~ 30g/ ㎡, and then carry out UV curing with two mercury lamp, dry tenacity is 250mJ, and drying time is 1 ~ 3 second;
S5, wooden skin sander is used to carry out sanding, dedusting;
S6, roller coat wood skin dedicated elas-tic UV repaiies color bottom paint, and coating weight is 15 ~ 25g/ ㎡, and then carry out UV curing with two mercury lamp, dry tenacity is 300mJ, and drying time is 1 ~ 3 second;
S7, roller coat wood skin dedicated elas-tic UV dull finishing coat, coating weight is 15 ~ 25g/ ㎡, and then carry out UV curing with two mercury lamp, dry tenacity is 250mJ, and drying time is 1 ~ 3 second;
S8, last overlay film packaging, complete production.