CN105032744A - Brush coating construction process of transparent aqueous dye - Google Patents
Brush coating construction process of transparent aqueous dye Download PDFInfo
- Publication number
- CN105032744A CN105032744A CN201510602040.8A CN201510602040A CN105032744A CN 105032744 A CN105032744 A CN 105032744A CN 201510602040 A CN201510602040 A CN 201510602040A CN 105032744 A CN105032744 A CN 105032744A
- Authority
- CN
- China
- Prior art keywords
- paint
- coated
- clear
- glasss
- spraying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Provided in the invention is a brush coating construction process of transparent aqueous dye. The decoration method comprises: sanding, primer spaying, transparent aqueous dye coating, and aqueous paint spraying. The furniture decorated by using the provided decoration method has advantages of convenient operation, good tinting strength, high transparency, low odour, and convenient large-area construction and the like.
Description
Technical field
The present invention relates to water-based look essence, be specifically related to a kind of water-based look essence brush application technique.
Background technology
In recent years, paint field is more and more to the future development of low stain, low energy consumption, nuisanceless, functionalization, high solid, radiation curing, Water-borne modification.Wherein aqueous woodware paint is a topic more popular in industry, and the tremendous development of this and aqueous woodware paint technology has larger relation.It is generally adopt spraying coating process that current aqueous woodware paint comprises water-based look refine look, sprays and there are certain requirements the professional skill of workmen, and be not suitable for large-area construction.Current water-based look essence spraying coating process is also not suitable for constructing on oil primer.
Summary of the invention
The object of this invention is to provide a kind of water-based look essence brush coating process, water-based look refine look can be carried out on PU, NC, PE priming paint, both reduced construction difficulty, and again reduced the requirement to ground priming paint, and comparatively environmental protection.
The water-based look essence construction technology of the present invention's design, large-area construction is more convenient, and without pungent smell, and dry oil primer plate all can be constructed, and can adjust temporarily repair colour saturation, and furniture decoration method of the present invention comprises the following steps:
(1) sanding: with 240# sand paper along the grain sand milling, remove furniture surface burr, sand trace;
(2) priming paint: if the clear priming paint of the spraying clean taste of PU, then according to paint: curing agent: the ratio of diluent=1:0.5:0.5-0.8, it is 12 seconds/25 DEG C (being coated with two glasss) that working viscosity is adjusted to, even application two " ten " words.If the clear priming paint of spraying NC, then according to paint: the ratio of diluent=1:0.8-1.2, be adjusted to working viscosity 14 seconds/25 DEG C (being coated with two glasss), be evenly coated with two " ten " words.If the clear priming paint of spraying PE, then according to paint: diluent: the ratio of blue plain boiled water=1:0.3-0.4, be adjusted to working viscosity 17 seconds/25 DEG C (being coated with two glasss), be evenly coated with two " ten " words.
(3) dry more than 8 hours of normal temperature (25 DEG C, RH=50%).
(4) sand milling: 320# ~ 400# sand papering is smooth, smooth.
(5) priming paint: the clear priming paint of the spraying clean taste of PU, according to paint: curing agent: diluent=1:0.5:0.5-0.8, it is 12 seconds/25 DEG C (being coated with two glasss) that working viscosity is adjusted to, even application two " ten " words.If the clear priming paint of spraying NC, then according to paint: the ratio of diluent=1:0.8-1.2, be adjusted to working viscosity 14 seconds/25 DEG C (being coated with two glasss), be evenly coated with two " ten " words.Normal temperature (25 DEG C, RH=50%) dry more than 8 hours.If the clear priming paint of spraying PE, then according to paint: diluent: the ratio of blue plain boiled water=1:0.3-0.4, be adjusted to working viscosity 17 seconds/25 DEG C (being coated with two glasss), be evenly coated with two " ten " words.
(6) dry more than 8 hours of normal temperature (25 DEG C, RH=50%).
(7) sand milling: 320# ~ 400# sand papering is smooth, smooth.
(8) priming paint: the clear priming paint of the spraying clean taste of PU, according to paint: curing agent: diluent=1:0.5:0.5-0.8, it is 12 seconds/25 DEG C (being coated with two glasss) that working viscosity is adjusted to, even application two " ten " words.If the clear priming paint of spraying NC, then according to paint: the ratio of diluent=1:0.8-1.2, be adjusted to working viscosity 14 seconds/25 DEG C (being coated with two glasss), be evenly coated with two " ten " words.If the clear priming paint of spraying PE, then according to paint: diluent: the ratio of blue plain boiled water=1:0.3-0.4, be adjusted to working viscosity 17 seconds/25 DEG C (being coated with two glasss), be evenly coated with two " ten " words.
(9) dry 12 hours of normal temperature (25 DEG C, RH=50%).
(10) mix colours: color as required and colour saturation adjust the ratio of repairing look host and look essence, mix rear stand-by.
(11) brush: evenly brush water-based look essence along wood grain, leave standstill and treat that it permeates, with the dressing agent that dry cotton remains along wood grain erasing coating surface after 30 minutes, the dry time can be received according to temperature and the adjustment of humidity appropriateness.Time of penetration is longer, and color dyes is darker.
(12) dry more than 12 hours of normal temperature (25 DEG C, RH=50%).
(13) finish paint: spraying water-based clear finish, then according to paint: water=1: in right amount working viscosity be adjusted to 40-50 second/25 DEG C (being coated with four glasss), even application two crosses.
According to the present invention, described step 1) adopts 240# sand paper to carry out sand milling.
According to the present invention, described step (2) adopts the clean taste of the PU clear end or the NC clear end or the PE clear end.
According to the present invention, described step (4) adopts 320# ~ 400# sand paper to carry out sand milling.
According to the present invention, described step (10) adopts water-based to repair look host and water-based look essence.
According to the present invention, described step (13) adopts the clear face of water-based.
The furniture adopting trailing of the present invention to obtain, has ornamental and appreciation preferably, has environmental protection concurrently again simultaneously, meets the different demands of consumer.
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention will be further described.Should be understood that following examples only for illustration of the present invention but not for limiting the scope of the invention.
In the context of the present invention, described working viscosity detecting instrument all has dated, refers to by painting two glasss of viscosity surveyed.RH i.e. relative humidity at that time in literary composition.
Described spraying " ten " word, refers to longitudinally, laterally furniture respectively being sprayed one time, concrete, spray a cross and refers to and longitudinally from first to last furniture is sprayed one time comprehensively, and then laterally from first to last spraying one time comprehensively, presents " ten " word cross-like for twice.
The clear priming paint of clean taste PU adopted in an embodiment of the present invention, the clear priming paint of NC, the PE clear end, the clear face of water-based, water-based are repaiied look host and water-based look essence etc. and are commercially available prod, as the product of Shanghai Fuchen Chemical Co., Ltd.And the method that the allotment of various paint all adopts this area usually to adopt.
Furniture decoration method of the present invention, comprises the following steps:
Sanding: with sand paper along the grain sand milling, removes furniture surface burr, sand trace, and preferably adopt 240# sand paper to carry out sand milling, described furniture is preferably the furniture item of cherry lagging plate composition;
Spray clear priming paint: spray clear priming paint, even application two " ten " words, dry more than 8 hours, wherein said clear priming paint, working viscosity of the clean taste of the PU clear end is 12 seconds (being coated with 2 glasss), and the NC clear end is 14 seconds (being coated with 2 glasss), and the PE clear end is 17 seconds (being coated with 2 glasss);
Sand milling: smooth, smooth with sand paper sand milling, preferably adopts 320# ~ 400# sand paper to carry out sand milling;
Toning: plate face effect as required and color adjust the consumption repairing look host and look essence, and this is plate face look topmost influence factor;
Brush: evenly brush water-based look essence along wood grain, leave standstill and treat that it permeates, with the dressing agent that dry cotton remains along wood grain erasing coating surface after 30 minutes, the dry time can be received according to temperature and the adjustment of humidity appropriateness;
Spraying water-based clear finish: spraying water-based clear finish, even application two " ten " words, dry more than 24 hours, wherein, it was 40 ~ 50 seconds (being coated with four glasss) to working viscosity that described spraying water-based clear finish adds water allotment;
The present inventor, through extensive and deep research, reforms furniture decoration method, is proposed water-based look of the present invention essence brush coating process, and the decoration of the furniture item that above-mentioned trailing is formed for the lagging timber of shallow conduit.This novel trailing, repaiies look by oil primer and water-based and combines preferably, has the performance advantage of oil primer, holds concurrently again and all adopts water-based to repair color system, do not have the pollution that solvent volatilizees, more environmental protection.
Should be understood that to those skilled in the art, under the prerequisite not departing from the application's design, can make various changes or modifications the present invention, these equivalent form of values fall within the application's appended claims limited range equally.
Claims (6)
1. a water-based look essence brush application technique, is characterized in that, comprise the following steps:
Sanding: with 240# sand paper along the grain sand milling, remove furniture surface burr;
Priming paint: if the clear priming paint of the spraying clean taste of PU, then according to paint: curing agent: the ratio of diluent=1:0.5:0.5-0.8, working viscosity is adjusted to 12 seconds/25 DEG C (being coated with two glasss), even application two " ten " words; If the clear priming paint of spraying NC, then according to paint: the ratio of diluent=1:0.8-1.2, be adjusted to working viscosity 14 seconds/25 DEG C (being coated with two glasss), be evenly coated with two " ten " words; If the clear priming paint of spraying PE, then according to paint: diluent: the ratio of blue plain boiled water=1:0.3-0.4, be adjusted to working viscosity 17 seconds/25 DEG C (being coated with two glasss), be evenly coated with two " ten " words,
Normal temperature (25 DEG C, RH=50%) dry more than 8 hours,
Sand milling: 320# ~ 400# sand papering is smooth, smooth,
Priming paint: the clear priming paint of the spraying clean taste of PU, according to paint: curing agent: diluent=1:0.5:0.5-0.8, it is 12 seconds/25 DEG C (being coated with two glasss) that working viscosity is adjusted to, even application two " ten " words; If the clear priming paint of spraying NC, then according to paint: the ratio of diluent=1:0.8-1.2, be adjusted to working viscosity 14 seconds/25 DEG C (being coated with two glasss), be evenly coated with two " ten " words; Normal temperature (25 DEG C, RH=50%) dry more than 8 hours; If the clear priming paint of spraying PE, then according to paint: diluent: the ratio of blue plain boiled water=1:0.3-0.4, be adjusted to working viscosity 17 seconds/25 DEG C (being coated with two glasss), be evenly coated with two " ten " words,
Normal temperature (25 DEG C, RH=50%) dry more than 8 hours,
Sand milling: 320# ~ 400# sand papering is smooth, smooth,
Priming paint: the clear priming paint of the spraying clean taste of PU, according to paint: curing agent: diluent=1:0.5:0.5-0.8, it is 12 seconds/25 DEG C (being coated with two glasss) that working viscosity is adjusted to, even application two " ten " words; If the clear priming paint of spraying NC, then according to paint: the ratio of diluent=1:0.8-1.2, be adjusted to working viscosity 14 seconds/25 DEG C (being coated with two glasss), be evenly coated with two " ten " words; If the clear priming paint of spraying PE, then according to paint: diluent: the ratio of blue plain boiled water=1:0.3-0.4, be adjusted to working viscosity 17 seconds/25 DEG C (being coated with two glasss), be evenly coated with two " ten " words,
Normal temperature (25 DEG C, RH=50%) dry 12 hours,
Toning: color as required and colour saturation adjust the ratio of repairing look host and look essence, mix rear stand-by,
Brush: evenly brush water-based look essence along wood grain, leave standstill and treat that it permeates, with the dressing agent that dry cotton remains along wood grain erasing coating surface after 30 minutes, can receive the dry time according to temperature and the adjustment of humidity appropriateness, time of penetration is longer, and color dyes is darker,
Normal temperature (25 DEG C, RH=50%) dry more than 12 hours,
Finish paint: spraying water-based clear finish, then according to paint: water=1: in right amount working viscosity be adjusted to 40-50 second/25 DEG C (being coated with four glasss), even application one and half cross.
2. furniture decoration method according to claim 1, is characterized in that, described step (1) adopts 240# sand paper to carry out sand milling.
3. furniture decoration method according to claim 1, is characterized in that, described step (2) adopts the clean taste of the PU clear end or the NC clear end or the PE clear end.
4. furniture decoration method according to claim 1, is characterized in that, described step (4) adopts 320# ~ 400# sand paper to carry out sand milling.
5. according to furniture decoration method according to claim 1, it is characterized in that, described step (10) adopts water-based to repair look host and water-based look essence.
6. according to furniture decoration method according to claim 1, it is characterized in that, described step (13) adopts the clear face of water-based.