CN106497427B - A kind of wood wax oil and its coating processes - Google Patents
A kind of wood wax oil and its coating processes Download PDFInfo
- Publication number
- CN106497427B CN106497427B CN201610928537.3A CN201610928537A CN106497427B CN 106497427 B CN106497427 B CN 106497427B CN 201610928537 A CN201610928537 A CN 201610928537A CN 106497427 B CN106497427 B CN 106497427B
- Authority
- CN
- China
- Prior art keywords
- parts
- wax
- oil
- wood
- wood wax
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to the technical field of wood wax oil coating, especially a kind of wood wax oil and its coating processes.It includes following mass parts raw material composition：10~20 parts of castor bean wax, 5~10 parts of pesudotsuga taxifolia wax, 6~8 parts of laurel wax, 8~12 parts of castor oil, 5~10 parts of peanut oil, 6~8 parts of essential oil, 4~6 parts of pine resin, 3~5 parts of kopol, 1~3 part of manganese dioxide, 0.5~0.8 part of anti-tangerine peel levelling agent, 100 0.3~0.5 part of ORA.The wood wax oil carries out coating processes using three-layer type cross spray coating method to timber, easy to operate, can enhance and combine closely with timber itself, enhance case hardness, water proof anti-soil improves external aesthetics.
Description
Technical field
The present invention relates to the technical field of wood wax oil coating, especially a kind of wood wax oil and its coating processes.
Background technology
In past general house decoration, it is used as the coating of household wood furniture and woodwork usually using paint.
Although paint can protect wood furniture and wood product surface very well, and can visually be generated to people to a certain extent
Certain beauty, the penetrating odor then painted and it is toxic brought prodigious harm, during finishing
Often to pass through long time can just move in, and cause big inconvenience.Wood wax oil, which is that vegetable oil Wax coatings are domestic, to be commonly called as,
Be a kind of similar paint and be different from the natural woodwork coating of paint, it and that is given birth to based on petrochemical industry class synthetic resin at present
The paint of production is entirely different, and raw material mainly with the crude vegetals such as concise linseed oil, palm wax and vegetable wax and coordinates other one
A little natural components merge, and toning pigment used has also reached food-grade.Therefore it is free of triphen, formaldehyde and a huge sum of money
The toxic components such as category, the smell not being pungent, alternative paint are used for house decoration and outdoor garden woodenware.Existing wood wax oil
It finds in use, the hardness formed after being coated on timber is low, and the distinctive lines gap of timber is bigger, drop
Low external aesthetics.
Invention content
The technical problem to be solved in the invention is a kind of wood wax oil proposed in view of the above technical problems and its coating work
Skill, haze tallow oil formula is simple, and the coating of monochromatic timber is carried out using wood wax oil, easy to operate, can enhance and timber itself
It combines closely, enhances case hardness, water proof anti-soil improves external aesthetics.
In order to solve the above technical problems, the present invention provides a kind of wood wax oil, including following mass parts raw material composition：Castor-oil plant
10~20 parts of sub- wax, 5~10 parts of pesudotsuga taxifolia wax, 6~8 parts of laurel wax, 8~12 parts of castor oil, 5~10 parts of peanut oil, essential oil 6~
8 parts, 4~6 parts of pine resin, 3~5 parts of kopol, 1~3 part of manganese dioxide, 0.5~0.8 part of anti-tangerine peel levelling agent and ORA-
100 0.3~0.5 part.
Further, including following mass parts raw material forms：15~18 parts of castor bean wax, 6~8 parts of pesudotsuga taxifolia wax, bay
7~8 parts of wax, 8~10 parts of castor oil, 8~10 parts of peanut oil, 7~8 parts of essential oil, 5~6 parts of pine resin, kopol 4~5
0.4~0.5 part of part, 2~3 parts of manganese dioxide, 0.6~0.8 part of anti-tangerine peel levelling agent and ORA-100.
Further, including following mass parts raw material forms：18 parts of castor bean wax, 7 parts of pesudotsuga taxifolia wax, 8 parts of laurel wax, castor
9 parts of sesame oil, 9 parts of peanut oil, 7 parts of essential oil, 6 parts of pine resin, 5 parts of kopol, 3 parts of manganese dioxide, anti-tangerine peel levelling agent 0.7
0.5 part of part and ORA-100.
A kind of wood wax oil coating processes, include the following steps to form：S1, first by solid wood furniture surface use 240~400
Mesh sand paper is polished repeatedly, is polished 3~5 times along lumber grain in bruting process, until surfacing is smooth；S2, it beats
Wood wax oil is opened, 5~10min is stirred using agitating device, dries up wood surface dust or impurity, using white not hair loss cotton
Cloth carries out the spraying of first time cross spray coating method, until wood wax oil drenches wood surface；S3, temperature is placed on as 20 DEG C~30 DEG C
It is 1~2 hour dry under environment；S4, wood surface polishing is carried out using 400~600 mesh sand paper, along timber in bruting process
Lines is polished, until surface is without apparent salient point；S5, drying wood surface dust or impurity, using white not hair loss cotton
Carry out second of cross spray coating method spraying；S6, it is placed on drying 1~2 hour in the environment of temperature is 20 DEG C~30 DEG C；S7, it adopts
Wood surface polishing is carried out with 600 mesh sand paper, is polished along lumber grain in bruting process, until surface is without apparent convex
Point；S8, drying wood surface dust or impurity, using white, hair loss cotton does not carry out the spraying of third time cross spray coating method；S9, it puts
It sets 5~8 hours dry in the environment of temperature is 20 DEG C~30 DEG C.
Further, cross spray coating method is first laterally to coat one layer in described S2, S5 and S8, is used again not after 1~2min
Vertically one layer of the coating of the cotton of hair loss.
Further, the wood wax oil before being sprayed in the S5 and S8 is stirred 5~10min by agitating device.
Further, 80~100 are used to the wood wax oil being stirred before cross spraying is carried out in described S2, S5 and S8
Mesh screen is filtered.
It is easy to operate after carrying out timber coating using the wood wax oil of above-mentioned formula, it can enhance close with timber itself
In conjunction with enhancing case hardness, water proof anti-soil improves external aesthetics.
Specific implementation mode
Castor bean wax in the present invention, pesudotsuga taxifolia wax, laurel wax, castor oil and peanut oil are the main composition portion of wood wax oil
Point, it is all made of vegetable oil in the present invention and vegetable wax is formed by quality proportioning, it is to promote to be added to manganese dioxide and ORA-100
Into the intermiscibility between vegetable oil and vegetable wax, addition essential oil is to improve the smell of wood wax oil, and also for increasing, its is whole
The volatility of body；Pine resin and kopol are added, is that hardness existing for traditional wood wax oil is low, intensity is low asks in order to improve
Topic, these resins can form a tunic layer in wood surface after application, enhance its film peel hardness, intensity and wear-resisting
Property.
Anti- tangerine peel levelling agent can prevent wood wax oil surface skining in storage or use, and not change the property of wood wax oil
Energy.The anti-tangerine peel levelling agent used in the present invention can be one or both of methyl ethyl ketoxime and diacetylmonoxime, can with urge it is dry
The ionic metal moiety of agent, which forms complex compound drier is made to lose, urges dry effect, and in film forming procedure, diacetylmonoxime volatilizees and makes
Complex compound decomposes and that restores drier urges dry effect.
The present invention provides a kind of wood wax oils, which is characterized in that is formed including following mass parts raw material：Castor bean wax 10~
20 parts, 5~10 parts of pesudotsuga taxifolia wax, 6~8 parts of laurel wax, 8~12 parts of castor oil, 5~10 parts of peanut oil, 6~8 parts of essential oil, pine tree
4~6 parts of resin, 3~5 parts of kopol, 1~3 part of manganese dioxide, 0.5~0.8 part of anti-tangerine peel levelling agent and ORA-100 0.3
~0.5 part.
A kind of wood wax oil coating processes, include the following steps to form：S1, first by solid wood furniture surface use 240~400
Mesh sand paper is polished repeatedly, is polished 3~5 times along lumber grain in bruting process, until surfacing is smooth；S2, it beats
Wood wax oil is opened, 5~10min is stirred using agitating device, dries up wood surface dust or impurity, using white not hair loss cotton
Cloth carries out the spraying of first time cross spray coating method, until wood wax oil drenches wood surface；S3, temperature is placed on as 20 DEG C~30 DEG C
It is 1~2 hour dry under environment；S4, wood surface polishing is carried out using 400~600 mesh sand paper, along timber in bruting process
Lines is polished, until surface is without apparent salient point；S5, drying wood surface dust or impurity, using white not hair loss cotton
Carry out second of cross spray coating method spraying；S6, it is placed on drying 1~2 hour in the environment of temperature is 20 DEG C~30 DEG C；S7, it adopts
Wood surface polishing is carried out with 600 mesh sand paper, is polished along lumber grain in bruting process, until surface is without apparent convex
Point；S8, drying wood surface dust or impurity, using white, hair loss cotton does not carry out the spraying of third time cross spray coating method；S9, it puts
It sets 5~8 hours dry in the environment of temperature is 20 DEG C~30 DEG C.
Blender may be used in agitating device in the present invention or artificial agitator is stirred.
The present inventor obtains by test of many times when using the wood wax oil of following mass components composition, whole film layer
Hardness, anti-shedding strength and wearability best results.
18 parts of castor bean wax, 7 parts of pesudotsuga taxifolia wax, 8 parts of laurel wax, 9 parts of castor oil, 9 parts of peanut oil, 7 parts of essential oil, pine tree tree
0.5 part of 6 parts of fat, 5 parts of kopol, 3 parts of manganese dioxide, 0.7 part of anti-tangerine peel levelling agent and ORA-100.
The present inventor has carried out the coating experiment using above-mentioned formula to solid wood furniture：
Solid wood furniture surface is polished repeatedly using 240~400 mesh sand paper first, along timber in bruting process
Lines is polished 5 times, until surfacing is smooth；Wood wax oil is opened, 10min is stirred using agitating device, dries up timber table
Face dust or impurity, using white, hair loss cotton does not carry out the spraying of first time cross spray coating method, until wood wax oil drenches timber table
Face；It is placed on 2 hours dry in the environment of temperature is 28 DEG C.
Film layer anti-shedding strength, hardness and wearability after the present inventor sprays first time cross are detected, and are had
Body result is as follows：
| Test event | Anti-shedding strength（MPa） | Hardness（HRC） | Wearability（dL/dV） |
| It sprays for the first time | 15.2 | 5 | 10 |
Wood surface polishing is carried out using 400~600 mesh sand paper, is polished along lumber grain in bruting process,
Until surface is without apparent salient point；Wood surface dust or impurity are dried up, hair loss cotton does not carry out second of cross spray using white
Coating sprays；It is placed on 2 hours dry in the environment of temperature is 28 DEG C.
Film layer anti-shedding strength, hardness and wearability after second of cross spraying of the present inventor couple are detected, and are had
Body result is as follows：
| Test event | Anti-shedding strength（MPa） | Hardness（HRC） | Wearability（dL/dV） |
| Second of spraying | 28.2 | 16 | 16 |
Wood surface polishing is carried out using 600 mesh sand paper, is polished along lumber grain in bruting process, until table
Face is without apparent salient point；Wood surface dust or impurity are dried up, hair loss cotton does not carry out the spray of third time cross spray coating method using white
It applies；It is placed on 6 hours dry in the environment of temperature is 28 DEG C.
Film layer anti-shedding strength, hardness and wearability after the present inventor sprays third time cross are detected, and are had
Body result is as follows：
| Test event | Anti-shedding strength（MPa） | Hardness（HRC） | Wearability（dL/dV） |
| Third time sprays | 56.8 | 25 | 28 |
It sprays and finds by cross three times, anti-shedding strength, hardness and wearability are all gradually increasing, the present inventor
Relevant experiment is carried out also for other formulas, it is found that its final performance parameter is below the effect that above-mentioned formula reaches.
Although specific embodiments of the present invention have been described above, those skilled in the art should be appreciated that this
It is merely illustrative of, various changes or modifications can be made to present embodiment, without departing from the principle and substance of the present invention,
Protection scope of the present invention is only limited by the claims that follow.
Claims (3)
1. a kind of wood wax oil, which is characterized in that formed including following mass parts raw material：10~20 parts of castor bean wax, pesudotsuga taxifolia wax 5
~10 parts, 6~8 parts of laurel wax, 8~12 parts of castor oil, 5~10 parts of peanut oil, 6~8 parts of essential oil, 4~6 parts of pine resin, Ke
0.3~0.5 part of bar 3~5 parts of resin, 1~3 part of manganese dioxide, 0.5~0.8 part of anti-tangerine peel levelling agent and ORA-100.
2. a kind of wood wax oil according to claim 1, which is characterized in that formed including following mass parts raw material：Castor bean
15~18 parts of wax, 6~8 parts of pesudotsuga taxifolia wax, 7~8 parts of laurel wax, 8~10 parts of castor oil, 8~10 parts of peanut oil, essential oil 7~8
Part, 5~6 parts of pine resin, 4~5 parts of kopol, 2~3 parts of manganese dioxide, 0.6~0.8 part of anti-tangerine peel levelling agent and ORA-
100 0.4~0.5 part.
3. a kind of wood wax oil according to claim 1, which is characterized in that formed including following mass parts raw material：Castor bean
18 parts of wax, 7 parts of pesudotsuga taxifolia wax, 8 parts of laurel wax, 9 parts of castor oil, 9 parts of peanut oil, 7 parts of essential oil, 6 parts of pine resin, kopol
5 parts, 3 parts of manganese dioxide, 0.5 part of 0.7 part of anti-tangerine peel levelling agent and ORA-100.