CN106497427A - A kind of new wood wax oil and its coating processes - Google Patents
A kind of new wood wax oil and its coating processes Download PDFInfo
- Publication number
- CN106497427A CN106497427A CN201610928537.3A CN201610928537A CN106497427A CN 106497427 A CN106497427 A CN 106497427A CN 201610928537 A CN201610928537 A CN 201610928537A CN 106497427 A CN106497427 A CN 106497427A
- Authority
- CN
- China
- Prior art keywords
- parts
- wax
- wood
- wax oil
- oil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to the technical field of wood wax oil coating, especially a kind of new wood wax oil and its coating processes.Which includes following mass parts raw material composition：10～20 parts of Semen Ricini wax, 5～10 parts of Pseudotsuga menziesii (Mirbel) Franco wax, 6～8 parts of laurel wax, 8～12 parts of Oleum Ricini, 5～10 parts of Oleum Arachidis hypogaeae semen, 6～8 parts of quintessence oil, 4～6 parts of pine resin, 3～5 parts of kopol, 1～3 part of manganese dioxide, 0.5～0.8 part of anti-Pericarpium Citri Reticulatae levelling agent, 100 0.3～0.5 part of ORA.The wood wax oil is coated technique using three-layer type cross spraying process to timber, easy to operate, can strengthen and combine closely with timber itself, strengthens case hardness, and water proof anti-soil improves external aesthetics.
Description
Technical field
The present invention relates to the technical field of wood wax oil coating, especially a kind of new wood wax oil and its coating processes.
Background technology
In past general house decoration, the coating that paint is used as domestic wood furniture and woodwork is usually used.
Although paint can protect wood furniture and wood product surface very well, and can give people to a certain extent visually to produce
Certain is attractive in appearance, the penetrating odor that then paints and toxic brought very big harm, during finishing
Often just to can move in through long time, cause very big inconvenience.Wood wax oil is that vegetable oil Wax coatings are domestic to be commonly called as,
It is a kind of similar paint and the natural woodwork coating for being different from paint, it is with that is given birth to based on petrochemical industry class synthetic resin at present
The paint of product is entirely different, raw material mainly with the crude vegetals such as concise oleum lini, palm wax and vegetable wax and coordinate other one
A little natural component fusions are formed, and toning pigment used has also reached food stage.Therefore it is without triphen, formaldehyde and a huge sum of money
The toxic components such as category, do not have pungent abnormal smells from the patient, alternative paint to be used for house decoration and outdoor garden woodenware.Existing wood wax oil
Find in use, the hardness which is formed after coating on timber is low, and the distinctive lines gap-ratio of timber is larger, drop
Low external aesthetics.
Content of the invention
The technical problem to be solved in the invention is a kind of new wood wax oil and its painting proposed for above-mentioned technical problem
Coating process, haze tallow oil formula are simple, and the coating for carrying out monochromatic timber using wood wax oil is easy to operate, can strengthen and timber sheet
Combining closely for body, strengthens case hardness, and water proof anti-soil improves external aesthetics.
For solving above-mentioned technical problem, the invention provides a kind of new wood wax oil, constitutes including following mass parts raw material：
10～20 parts of Semen Ricini wax, 5～10 parts of Pseudotsuga menziesii (Mirbel) Franco wax, 6～8 parts of laurel wax, 8～12 parts of Oleum Ricini, 5～10 parts of Oleum Arachidis hypogaeae semen, essence
6～8 parts of oil, 4～6 parts of pine resin, 3～5 parts of kopol, 1～3 part of manganese dioxide, 0.5～0.8 part of anti-Pericarpium Citri Reticulatae levelling agent
With 0.3～0.5 part of ORA-100.
Further, constitute including following mass parts raw material：15～18 parts of Semen Ricini wax, 6～8 parts of Pseudotsuga menziesii (Mirbel) Franco wax, Laurel
7～8 parts of wax, 8～10 parts of Oleum Ricini, 8～10 parts of Oleum Arachidis hypogaeae semen, 7～8 parts of quintessence oil, 5～6 parts of pine resin, kopol 4～5
Part, 2～3 parts of manganese dioxide, 0.6～0.8 part and 0.4～0.5 part of ORA-100 of anti-Pericarpium Citri Reticulatae levelling agent.
Further, constitute including following mass parts raw material：18 parts of Semen Ricini wax, 7 parts of Pseudotsuga menziesii (Mirbel) Franco wax, 8 parts of laurel wax, castor
9 parts of Oleum Sesami, 9 parts of Oleum Arachidis hypogaeae semen, 7 parts of quintessence oil, 6 parts of pine resin, 5 parts of kopol, 3 parts of manganese dioxide, anti-Pericarpium Citri Reticulatae levelling agent 0.7
Part and ORA-1000.5 parts.
A kind of new wood wax oil coating processes, comprise the following steps to constitute：S1, solid wood furniture surface is adopted 240 first
～400 mesh sand paper are polished repeatedly, are polished 3～5 times along lumber grain in bruting process, until surfacing is smooth；
S2, opening wood wax oil, are stirred 5～10min using agitating device, dry up wood surface dust or impurity, using white not
Hair loss cotton carries out the spraying of first time cross spraying process, until wood wax oil drenches wood surface；S3, be placed on temperature for 20 DEG C～
Dry 1～2 hour in the environment of 30 DEG C；S4, wood surface polishing is carried out using 400～600 mesh sand paper, suitable in bruting process
Lumber grain to be polished, until surface is without obvious salient point；S5, wood surface dust or impurity is dried up, do not fallen using white
Velvet apple cloth carries out second cross spraying process spraying；S6, temperature is placed on for drying 1～2 hour in the environment of 20 DEG C～30 DEG C；
S7, carry out wood surface polishing using 600 mesh sand paper, polished along lumber grain in bruting process, until surface without
Obvious salient point；S8, wood surface dust or impurity is dried up, hair loss cotton does not carry out the spray of third time cross spraying process using white
Apply；S9, temperature is placed on for drying 5～8 hours in the environment of 20 DEG C～30 DEG C.
Further, in described S2, S5 and S8, cross spraying process is first laterally one layer of coating, again with not after 1～2min
Vertically one layer of the coating of the cotton of hair loss.
Further, the wood wax oil before spraying in the S5 and S8 is stirred 5～10min by agitating device.
Further, before cross spraying being carried out in described S2, S5 and S8 80～100 are adopted to the wood wax oil being stirred
Eye mesh screen is filtered.
Carried out after timber coating using the new wood wax oil of above-mentioned formula, easy to operate, can strengthen and timber itself
Combine closely, strengthen case hardness, water proof anti-soil improves external aesthetics.
Specific embodiment
The main composition portion of Semen Ricini wax in the present invention, Pseudotsuga menziesii (Mirbel) Franco wax, laurel wax, Oleum Ricini and Oleum Arachidis hypogaeae semen for wood wax oil
Point, formed by quality proportioning using vegetable oil and vegetable wax in the present invention, with the addition of manganese dioxide and ORA-100 is to promote
The intermiscibility entered between vegetable oil and vegetable wax, it is the abnormal smells from the patient in order to improve wood wax oil to add quintessence oil, and also for increasing, which is whole
The volatility of body；Add pine resin and kopol, be that the hardness that traditional wood wax oil is present is low, low intensity is asked in order to improve
Topic, these resins can form a tunic layer in wood surface after application, strengthen its film peel hardness, intensity and wear-resisting
Property.
Anti- Pericarpium Citri Reticulatae levelling agent can prevent wood wax oil surface skining in storage or use, and not change the property of wood wax oil
Energy.Anti- Pericarpium Citri Reticulatae levelling agent used in the present invention can be methyl ethyl ketoxime and diacetylmonoxime in one or two, its can with urge dry
The ionic metal moiety formation complex of agent loses drier and urges dry effect, and in film forming procedure, diacetylmonoxime volatilizees and makes
What complex decomposed and recovered drier urges dry effect.
The invention provides a kind of new wood wax oil, it is characterised in that constitute including following mass parts raw material：Semen Ricini wax
10～20 parts, 5～10 parts of Pseudotsuga menziesii (Mirbel) Franco wax, 6～8 parts of laurel wax, 8～12 parts of Oleum Ricini, 5～10 parts of Oleum Arachidis hypogaeae semen, 6～8 parts of quintessence oil,
4～6 parts of pine resin, 3～5 parts of kopol, 1～3 part of manganese dioxide, 0.5～0.8 part and ORA-100 of anti-Pericarpium Citri Reticulatae levelling agent
0.3～0.5 part.
A kind of new wood wax oil coating processes, comprise the following steps to constitute：S1, solid wood furniture surface is adopted 240 first
～400 mesh sand paper are polished repeatedly, are polished 3～5 times along lumber grain in bruting process, until surfacing is smooth；
S2, opening wood wax oil, are stirred 5～10min using agitating device, dry up wood surface dust or impurity, using white not
Hair loss cotton carries out the spraying of first time cross spraying process, until wood wax oil drenches wood surface；S3, be placed on temperature for 20 DEG C～
Dry 1～2 hour in the environment of 30 DEG C；S4, wood surface polishing is carried out using 400～600 mesh sand paper, suitable in bruting process
Lumber grain to be polished, until surface is without obvious salient point；S5, wood surface dust or impurity is dried up, do not fallen using white
Velvet apple cloth carries out second cross spraying process spraying；S6, temperature is placed on for drying 1～2 hour in the environment of 20 DEG C～30 DEG C；
S7, carry out wood surface polishing using 600 mesh sand paper, polished along lumber grain in bruting process, until surface without
Obvious salient point；S8, wood surface dust or impurity is dried up, hair loss cotton does not carry out the spray of third time cross spraying process using white
Apply；S9, temperature is placed on for drying 5～8 hours in the environment of 20 DEG C～30 DEG C.
In the present invention, agitating device can be stirred using blender or manual stirring bucket.
The present inventor is obtained when the wood wax oil of following mass components composition is adopted through test of many times, its overall film layer
Hardness, anti-shedding strength and wearability best results.
18 parts of Semen Ricini wax, 7 parts of Pseudotsuga menziesii (Mirbel) Franco wax, 8 parts of laurel wax, 9 parts of Oleum Ricini, 9 parts of Oleum Arachidis hypogaeae semen, 7 parts of quintessence oil, pinaster tree
6 parts of fat, 5 parts of kopol, 3 parts of manganese dioxide, 0.7 part and 0.5 part of ORA-100 of anti-Pericarpium Citri Reticulatae levelling agent.
The present inventor has carried out the coating experiment using above-mentioned formula to solid wood furniture：
First solid wood furniture surface is polished repeatedly using 240～400 mesh sand paper, along timber in bruting process
Lines is polished 5 times, until surfacing is smooth；Wood wax oil is opened, 10min is stirred using agitating device, timber table is dried up
Face dust or impurity, using white, hair loss cotton does not carry out the spraying of first time cross spraying process, until wood wax oil drenches timber table
Face；It is dry 2 hours in the environment of 28 DEG C to be placed on temperature.
The present inventor is detected have to the film layer anti-shedding strength after the spraying of first time cross, hardness and wearability
Body result is as follows：
Wood surface polishing is carried out using 400～600 mesh sand paper, is polished along lumber grain in bruting process,
Until surface is without obvious salient point；Wood surface dust or impurity is dried up, hair loss cotton does not carry out second cross spray using white
Coating is sprayed；It is dry 2 hours in the environment of 28 DEG C to be placed on temperature.
The present inventor is detected have to the film layer anti-shedding strength after second cross spraying, hardness and wearability
Body result is as follows：
Wood surface polishing is carried out using 600 mesh sand paper, is polished along lumber grain in bruting process, until table
Face is without obvious salient point；Wood surface dust or impurity is dried up, hair loss cotton does not carry out the spray of third time cross spraying process using white
Apply；It is dry 6 hours in the environment of 28 DEG C to be placed on temperature.
The present inventor is detected have to the film layer anti-shedding strength after the spraying of third time cross, hardness and wearability
Body result is as follows：
Find that its anti-shedding strength, hardness and wearability are all gradually increasing, the present inventor through three cross sprayings
Also for the test that other formula carry out correlation, it is found that its final performance parameter is below the effect that above-mentioned formula reaches.
Although the foregoing describing the specific embodiment of the present invention, those skilled in the art should be appreciated that this
It is merely illustrative of, various changes or modifications can be made to present embodiment, without departing from the principle and essence of the present invention,
Protection scope of the present invention is only limited by the claims that follow.
Claims (7)
1. a kind of new wood wax oil, it is characterised in that constitute including following mass parts raw material：10～20 parts of Semen Ricini wax, star-spangled banner
5～10 parts of loose wax, 6～8 parts of laurel wax, 8～12 parts of Oleum Ricini, 5～10 parts of Oleum Arachidis hypogaeae semen, 6～8 parts of quintessence oil, pine resin 4～6
Part, 3～5 parts of kopol, 1～3 part of manganese dioxide, 0.5～0.8 part and 0.3～0.5 part of ORA-100 of anti-Pericarpium Citri Reticulatae levelling agent.
2. a kind of new wood wax oil according to claim 1, it is characterised in that constitute including following mass parts raw material：Castor
15～18 parts of pockmarks wax, 6～8 parts of Pseudotsuga menziesii (Mirbel) Franco wax, 7～8 parts of laurel wax, 8～10 parts of Oleum Ricini, 8～10 parts of Oleum Arachidis hypogaeae semen, quintessence oil 7
～8 parts, 5～6 parts of pine resin, 4～5 parts of kopol, 2～3 parts of manganese dioxide, 0.6～0.8 part of anti-Pericarpium Citri Reticulatae levelling agent and
0.4～0.5 part of ORA-100.
3. a kind of new wood wax oil according to claim 1, it is characterised in that constitute including following mass parts raw material：Castor
18 parts of pockmarks wax, 7 parts of Pseudotsuga menziesii (Mirbel) Franco wax, 8 parts of laurel wax, 9 parts of Oleum Ricini, 9 parts of Oleum Arachidis hypogaeae semen, 7 parts of quintessence oil, 6 parts of pine resin, Ke Ba
5 parts of resin, 3 parts of manganese dioxide, 0.7 part and 0.5 part of ORA-100 of anti-Pericarpium Citri Reticulatae levelling agent.
4. a kind of new wood wax oil coating processes, it is characterised in that comprise the following steps to constitute：
S1, first solid wood furniture surface is polished repeatedly using 240～400 mesh sand paper, along timber in bruting process
Lines is polished 3～5 times, until surfacing is smooth；
S2, opening wood wax oil, are stirred 5～10min using agitating device, dry up wood surface dust or impurity, using white
Hair loss cotton does not carry out the spraying of first time cross spraying process to color, until wood wax oil drenches wood surface；
S3, temperature is placed on for drying 1～2 hour in the environment of 20 DEG C～30 DEG C；
S4, wood surface polishing is carried out using 400～600 mesh sand paper, polished along lumber grain, directly in bruting process
To surface without obvious salient point；
S5, wood surface dust or impurity is dried up, hair loss cotton does not carry out second cross spraying process spraying using white；
S6, temperature is placed on for drying 1～2 hour in the environment of 20 DEG C～30 DEG C；
S7, wood surface polishing is carried out using 600 mesh sand paper, polished along lumber grain in bruting process, until table
Face is without obvious salient point；
S8, wood surface dust or impurity is dried up, hair loss cotton does not carry out the spraying of third time cross spraying process using white；
S9, temperature is placed on for drying 5～8 hours in the environment of 20 DEG C～30 DEG C.
5. a kind of new wood wax oil coating processes according to claim 4, it is characterised in that：Ten in described S2, S5 and S8
Word spraying process is first laterally one layer of coating, again with cotton vertically one layer of the coating of not hair loss after 1～2min.
6. a kind of new wood wax oil coating processes according to claim 4, it is characterised in that：Before spraying in the S5 and S8
Wood wax oil 5～10min is stirred by agitating device.
7. a kind of new wood wax oil coating processes according to claim 6, it is characterised in that：Enter in described S2, S5 and S8
The wood wax oil being stirred is filtered using 80～100 eye mesh screens before the spraying of row cross.