CN105170430B - Woodenware coating process modelled after an antique - Google Patents
Woodenware coating process modelled after an antique Download PDFInfo
- Publication number
- CN105170430B CN105170430B CN201510379542.9A CN201510379542A CN105170430B CN 105170430 B CN105170430 B CN 105170430B CN 201510379542 A CN201510379542 A CN 201510379542A CN 105170430 B CN105170430 B CN 105170430B
- Authority
- CN
- China
- Prior art keywords
- woodenware
- coating
- spraying process
- modelled
- top coat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to woodenware coating process modelled after an antique, including the first spraying process：By aqueous transparent basecoat paint on pending woodenware surface, dry, form clear primer layer；Second spraying process：By aqueous pigmented basecoat paint in the surface of the clear primer layer, dry, be formed with color basecoat；3rd spraying process：Aqueous pigmented finish paint is sprayed on the surface for having a color basecoat, the first top coat layer is formed；4th coating step：Pearl essence is mixed with metal powder, metal powder is silver powder and/or bronze, then is mixed with aqueous transparent priming paint with preset ratio, form colouring agent, before the drying of the first top coat layer, with colouring agent erasing to first top coat layer, colour wood grain；5th spraying process：Aqueous transparent finish paint is sprayed to the surface of the coat of the 4th coating step formation, dried, the second top coat layer is formed.The present invention is different from effect modelled after an antique at present, and can improve the class of furniture with special bronzing or silver-colored effect；Construction technology is easy.
Description
Technical field
The present invention relates to woodwork coating technical field, and in particular to a kind of woodenware coating process modelled after an antique.
Background technology
The pseudo-classic furniture construction of in the market is generally comprised, the destruction of substrate surface, wipe background color, glaze wipe color, beat it is dry brush,
The processes such as finish paint, the sedate low-key of main prominent pseudo-classic furniture, comfortable easy visual experience.Such as Patent No.
The Chinese invention patent of " CN103963508A " discloses a kind of finishing Technology for American Style Furniture antique-imitation method, and it is with antique traditional furniture
Construction modelled after an antique is similar, is mainly by the destruction to base material and repaiies color processing, makes up to the effect of antique-imitation, this similar
Technique will typically pass through multiple working procedure, technique is more complicated.
In addition, construction technology modelled after an antique in the market, simply has effect modelled after an antique, in some hotels, villa etc.
High-grade occasion, it is desirable to which furniture has the high effect of unusual and high-end, air, class, current construction technology modelled after an antique is equal
It is difficult to meet this requirement.
The content of the invention
Based on this, the present invention provides a kind of woodenware coating process modelled after an antique, and it has special bronzing or silver-colored effect, can distinguish
In effect modelled after an antique at present, and the class of furniture can be improved；Construction technology is easy.
In order to realize the purpose of the present invention, the present invention uses following technical scheme：
Woodenware coating process modelled after an antique, it comprises the following steps：
First spraying process：By aqueous transparent basecoat paint on pending woodenware surface, 1h-3h is dried, is formed transparent
Prime coat；
Second spraying process：By aqueous pigmented basecoat paint in the surface of the clear primer layer, 2h-4h is dried, is formed
There is color basecoat；
3rd spraying process：Aqueous pigmented finish paint is sprayed on the surface for having a color basecoat, the first top coat layer is formed；
4th coating step：Pearl essence is mixed with metal powder, the metal powder be silver powder and/or bronze, then
With the aqueous transparent priming paint with 1：15-20 mass ratio mixing, forms colouring agent, it is dried in first top coat layer
Before, with grain direction erasing of the colouring agent along the woodenware to first top coat layer, colour the wood grain；
5th spraying process：Aqueous transparent finish paint is sprayed to the coating layer surface of the 4th coating step formation, done
Dry 2h-5h, forms the second top coat layer.
In one of the embodiments, in the 5th spraying process, by the aqueous transparent finish paint with least one
" ten " font is sprayed at the coating layer surface of the 4th coating step formation.
In one of the embodiments, after the pearl essence is mixed with the metal powder, fineness is 5 μm -20 μm.
In one of the embodiments, in the 4th coating step, after erasing terminates, unnecessary colouring agent is wiped.
In one of the embodiments, the drying is carried out in following environment：15 DEG C -70 DEG C of temperature, relative humidity
20%~80%.
In one of the embodiments, also had steps of before first spraying process：Remove the woodenware table
The burr in face and sand trace.
In one of the embodiments, also there is following step before removing the step of burr on the woodenware surface is with sand trace
Suddenly：Stamp side is carried out to the woodenware, beats and/or follows closely small holes caused by worms.
In one of the embodiments, also there is following step between first spraying process and second spraying process
Suddenly：Sanding is carried out to the clear primer layer；Also have between second spraying process and the 3rd spraying process as follows
Step：There is color basecoat to carry out sanding to described.
In one of the embodiments, also there is following step between the 4th coating step and the 5th spraying process
Suddenly：Coating layer surface to the 4th coating step formation carries out sanding.
In one of the embodiments, in the 5th spraying process, the thickness of second top coat layer is 15 μm of -20 μ
m。
Woodenware coating process modelled after an antique of the present invention, its beneficial effect compared with prior art is：
The present invention is by innovating construction technology, the step of by spraying transparent priming, colored paint and finish paint, and is adding
Pearl essence, silver powder and/or bronze are added in toner, colouring agent, the colouring agent of wood grain is used as so that the woodenware of spraying has bronzing
Or the effect of silver, the present situation of traditional pseudo-classic furniture single effect is changed, and improve the class of woodenware；In addition, will be traditional
Erasing technique is reduced to together from three roads, is simplified construction technology, is reduced production cost, is adapted to extensive batch and is constructed.
Brief description of the drawings
Fig. 1 is the flow chart of the woodenware coating process modelled after an antique described in the embodiment of the present invention one.
Embodiment
For the ease of understanding the present invention, the present invention is described more fully below in conjunction with accompanying drawing.But, the present invention
It can realize in many different forms, however it is not limited to embodiment described herein.On the contrary, providing these embodiments
Purpose is to make the understanding to the disclosure more thorough comprehensive.
Unless otherwise defined, all of technologies and scientific terms used here by the article is with belonging to technical field of the invention
The implication that technical staff is generally understood that is identical.Term used in the description of the invention herein is intended merely to description tool
The purpose of the embodiment of body, it is not intended that in the limitation present invention.
For example, a kind of woodenware coating process modelled after an antique, it comprises the following steps：First spraying process：By aqueous transparent priming paint
Pending woodenware surface is sprayed on, 1h-3h is dried, clear primer layer is formed；Second spraying process：Aqueous pigmented priming paint is sprayed
The surface of the clear primer layer is applied to, 2h-4h is dried, is formed with color basecoat；3rd spraying process：By aqueous pigmented finish paint
There is the surface of color basecoat described in being sprayed on, form the first top coat layer；4th coating step：Pearl essence is blended in metal powder
Together, the metal powder is silver powder and/or bronze, then with the aqueous transparent priming paint with 1：15-20 mass ratio mixing, shape
Into colouring agent, before first top coat layer drying, with colouring agent erasing to first top coat layer, make the wood
Line is coloured；For example, with grain direction erasing of the colouring agent along the woodenware to first top coat layer, making the wood
Line is coloured；5th spraying process：Aqueous transparent finish paint is sprayed to the coating layer surface of the 4th coating step formation, dried
2h-5h, forms the second top coat layer.
In the 5th spraying process, preferably the aqueous transparent finish paint is sprayed at at least one " ten " font described
The coating layer surface of 4th coating step formation, preferably one " ten " font, or multiple " ten " fonts are spaced, and are formed
Neat hatching effect.
In 4th coating step, after pearl essence is mixed with metal powder, fineness is 5 μm -20 μm, the powder of the fineness
It after being coated on woodenware, will not seem too lofty, dazzling bronzing can be met again or the effect of silver is wiped.
In 4th coating step, after erasing terminates, unnecessary colouring agent is wiped.For example, when rubbing the colouring agent, using
Hairbrush is rubbed along the direction of the wood grain；And for example,, will be unnecessary with white flannelette or lint-free calico after erasing terminates
Toner is wiped.
Drying is carried out in following environment：15 DEG C -70 DEG C of temperature, relative humidity 20%~80%.It is preferably selected temperature 60
DEG C, relative humidity 20% is dried, and in such circumstances, rate of drying is very fast.
Also had steps of before the first spraying process：Remove the burr and sand trace on the woodenware surface.For example, going
First it can be sanded during flash removed with sand paper along the grain direction of woodenware.
Also there are following steps before removing the step of burr on the woodenware surface is with sand trace：The woodenware is stabbed
Side, beat and/or follow closely small holes caused by worms.
Also there are following steps between the first spraying process and the second spraying process：Sand is carried out to the clear primer layer
Light；Also there are following steps between second spraying process and the 3rd spraying process：There is color basecoat to carry out sanding to described.
Also there are following steps between the 4th coating step and the 5th spraying process：To the 4th coating step
The coating layer surface of formation carries out sanding.
In the 5th spraying process, the thickness of second top coat layer is 15 μm -20 μm, is preferably 15 μm so that wood
Device surface is more fully apparent from, and texture display is apparent.
Embodiment one
Reference picture 1, woodenware coating process modelled after an antique of the present invention, comprises the following steps：
(1) is carried out by stamp side, beat or follows closely the one or more in small holes caused by worms method for pending woodenware, so as to the wood
Device carries out destruction processing so that the antique effect of woodenware is more preferable.
(2) wood grain with 240#TOA sand paper along pending woodenware is sanded, and removes burr, the sand trace on Wood-removing device surface.
Woodenware surface more smooth can be ensured after sand milling, it is smoother after follow-up spraying.
(3) 2.0mm is used, W-71 type spray guns are by aqueous transparent basecoat paint on pending woodenware surface, coating thickness
15 μm -20 μm, 1h-3h is dried in the environment of 15 DEG C -70 DEG C of temperature, relative humidity 20%~80%, clear primer layer is formed,
Then sanding is carried out to the clear primer layer using 600#TOA sand paper.
(4) 2.0mm is used, W-71 type spray guns are by aqueous white basecoat paint in the surface of clear primer layer, coating thickness
15 μm -20 μm, then in 15 DEG C -70 DEG C of temperature, 2h-4h is dried in the environment of relative humidity 20%~80%, coloured bottom is formed
Enamelled coating, has color basecoat to carry out sanding using 600#TOA sand paper to described.
(5) 2.0mm is used, aqueous pigmented finish paint is sprayed on the surface of color basecoat, coating thickness by W-71 type spray guns
15 μm -20 μm, form the first top coat layer.
(6) pearl essence, silver powder and bronze are mixed, wherein the quality proportioning of pearl essence, silver powder and bronze is 1:
1:2, then with aqueous transparent priming paint with 1：20 mass ratio mixing, mixed fineness is 5 μm -20 μm, forms colouring agent,
Before first top coat layer is dried, with grain direction erasing of the colouring agent along the woodenware to the first top coat layer, wood grain
Color；During scratch cover colorants, rubbed with hairbrush along the direction of the wood grain, after erasing terminates, use lint-free calico, will be unnecessary
Toner is wiped, and then carries out sanding to the coating layer surface formed after erasing using 800#TOA sand paper.
(7) aqueous transparent finish paint is sprayed at the coating layer surface that is formed after erasing, then in 15 DEG C -70 DEG C of temperature, phase
To drying 2h-5h in the environment of humidity 20%~80%, the second top coat layer is formed.Wherein, the aqueous transparent finish paint is with least one
Individual " ten " font even application is in the coating layer surface formed after erasing.It is sprayed into " ten " font so that woodenware surface has the moon
Shadow effect, Hepplewhite third dimension is stronger.
The present embodiment and the painting effect of comparative example one and comparative example two are contrasted below, this hair is further illustrated
Bright effect.
Comparative example one：
Construction method modelled after an antique is in the comparative example：
(1) material destruction is handled：Stamp side is carried out to material, beats or follows closely one or more of small holes caused by worms method, to reach one
Furniture is planted because of the long and impaired natural effect of use time；
(2) material sanding：Timber burr is sanded using sand paper smooth；
(3) background color is sprayed：With the color even application specially prepared；
The color specially prepared, refers to the color by nitro-diluent plus dye combinations；
(4) polyurethane transparent primer is sprayed：Polyurethane transparent primer is solidified with polyurethane primer with polyurethane diluent
Agent, by 2: 1 weight ratios, viscosity was adjusted to as 15~16 seconds, one " ten " word of even application is dried 4-6 hours；
(5) sanding：It is sanded with sand paper smooth, smooth；
(6) the clear priming paint of nitro：It is 14-15 seconds that nitrocellulose primer is adjusted into viscosity with nitro-diluent, sprays " ten " word,
Dry 40-60 minutes；
(7) paint stripper is brushed：Paint stripper is subjected to local brushing, corner on the nitrocellulose primer surface sprayed with hairbrush
Position is more than middle part；
(8) nitro white basecoat paint：It is 14-15 seconds that nitro white priming paint is adjusted into viscosity with nitro-diluent, spraying
One " ten " word, dries 40-60 points；
(9) come off processing：The position for brushing paint stripper is subjected to wiped clean with scouring pad；
(10) the clear priming paint of nitro：It is 14-15 seconds that nitrocellulose primer is adjusted into viscosity with nitro-diluent, sprays one " ten "
Word, is dried 40-60 minutes；
(11) nitro glaze：Wiped with nitro glaze in surface, then wiped clean again；
(12) the clear priming paint of nitro：It is 14-15 seconds that nitrocellulose primer is adjusted into viscosity with nitro-diluent, sprays one " ten "
Word, is dried 40-60 minutes；
(13) light weight sand：Smooth, smooth with sand paper sand milling, sand is not worn；
(14) the dry brush of nitro glaze：Glaze is stained with hairbrush, dry to beat surface, the local color in edge is deeper than centre
Position, to reach that color imitates old effect for the last time；
(15) the clear priming paint of nitro：It is 14-15 seconds that nitrocellulose primer is adjusted into viscosity with nitro-diluent, sprays one " ten "
Word, is dried 40-60 minutes；
(16) light weight sand：Smooth, smooth with sand paper sand milling, sand is not worn；
(17) lacquer finish：It is 11-12 seconds that lacquer finish is adjusted into viscosity with nitro-diluent, sprays " ten " word,
Dry 24~30 hours, obtain product.
Comparative example two
Construction method modelled after an antique is in the comparative example：
1) destruction of not holding any government official post's product surface is handled；
2) material repaiies color；
3) background color is handled；
4) glue is handled admittedly；
5) wiping is handled；
6) one of prime treatment；
7) three making models are chosen, is manually made according to the effect of colour table standard at three and makes dry brush on model respectively
Do that old key element, oxtail do old key element and specking does old key element, form dry map brushing case, oxtail pattern and specking pattern respectively；
8) make the pattern on model by three with scanner to scan in computer respectively, then utilize PaintShop
And image graphic processing software is handled each pattern, it is pellucidity to make to do the part beyond old key element in each pattern, most
After set up pel material database, each pattern of processing is deposited into wherein；
9) according to the design size of product and color requirement, corresponding pattern is extracted from pel material database, is then passed through
PaintShop and image graphic software are combined finishing to pattern, and the collection required for forming product does brush, oxtail, specking
With shade line in the electronic pictures of one, and achieve；
10) by UV ink-jet printers, the pattern in the electronic pictures formed in step 9 is printed on product, makes production
What the surface of product once formed dry brush, oxtail and specking does old effect.
11) one of finish paint processing；
12) two coat finish is handled, and finished product is made.
Table one is the embodiment of the present invention one and comparative example one, the painting effect correction data of comparative example two.
Table one
As can be seen from the above table, the relatively existing woodenware coating process modelled after an antique of the present invention, its outward appearance artistic feeling is stronger, process
Simplicity, flow is controlled well.
Embodiment two
In the present embodiment, woodenware coating process modelled after an antique of the present invention, comprises the following steps：
(1) wood grain with 240#TOA sand paper along pending woodenware is sanded, and removes burr, the sand trace on Wood-removing device surface.
Woodenware surface more smooth can be ensured after sand milling, it is smoother after follow-up spraying.
(2) 2.0mm is used, W-71 type spray guns are by aqueous transparent basecoat paint on pending woodenware surface, coating thickness
15 μm -20 μm, the clear primer layer is dried into 1h-3h in the environment of 15 DEG C -70 DEG C of temperature, relative humidity 20%~80%,
Clear primer layer is formed, sanding is carried out to the clear primer layer using 600#TOA sand paper.
(3) 2.0mm is used, W-71 type spray guns are by aqueous white basecoat paint in the surface of clear primer layer, coating thickness
15 μm -20 μm, then in 15 DEG C -70 DEG C of temperature, 2h-4h is dried in the environment of relative humidity 20%~80%, coloured bottom is formed
Enamelled coating, has color basecoat to carry out sanding using 600#TOA sand paper to described.
(4) 2.0mm is used, aqueous pigmented finish paint is sprayed on the surface of color basecoat, coating thickness by W-71 type spray guns
15 μm -20 μm, form the first top coat layer.
(5) pearl essence, silver powder and bronze of equivalent are mixed, then with aqueous transparent priming paint with 1：18 quality
Ratio is mixed, and mixed fineness is 5 μm -20 μm, forms colouring agent, before the drying of the first top coat layer, with the colouring agent edge
The grain direction for the woodenware is rubbed onto the first top coat layer, colours wood grain；During scratch cover colorants, with hairbrush along the wood
The direction erasing of line, after erasing terminates, uses lint-free calico, unnecessary colouring agent is wiped, then using 800#TOA sand paper to this
The coating layer surface formed after erasing carries out sanding.
(6) aqueous transparent finish paint is sprayed at the coating layer surface that is formed after erasing, then in 15 DEG C -70 DEG C of temperature, phase
To drying 2h-5h in the environment of humidity 20%~80%, the second top coat layer is formed.Wherein, the aqueous transparent finish paint is with least more
Individual " ten " font even application is in the coating layer surface formed after erasing.Multiple " ten " fonts are evenly distributed, are sprayed into " ten " word
Type so that woodenware surface has hatching effect, Hepplewhite third dimension is stronger.
The present embodiment and the painting effect of comparative example one and comparative example two are contrasted below, this hair is further illustrated
Bright effect.
Table two is the embodiment of the present invention two and comparative example one, the painting effect correction data of comparative example two.
Table two
As can be seen from the above table, the relatively existing woodenware coating process modelled after an antique of the present invention, its outward appearance artistic feeling is stronger, process
Simplicity, flow is controlled well.
Embodiment three
Woodenware coating process modelled after an antique of the present invention, comprises the following steps：
(1) is carried out by stamp side, beat or follows closely one kind in small holes caused by worms method for pending woodenware, so as to be carried out to the woodenware
Destruction is handled so that the antique effect of woodenware is more preferable.
(2) wood grain with 240#TOA sand paper along pending woodenware is sanded, and removes burr, the sand trace on Wood-removing device surface.
Woodenware surface more smooth can be ensured after sand milling, it is smoother after follow-up spraying.
(3) 2.0mm is used, W-71 type spray guns are by aqueous transparent basecoat paint on pending woodenware surface, coating thickness
15 μm, 2h is dried in the environment of 15 DEG C -70 DEG C of temperature, relative humidity 20%~80%, clear primer layer is formed；Using 600#
TOA sand paper carries out sanding to the clear primer layer.
(4) 2.0mm is used, W-71 type spray guns are by aqueous white basecoat paint in the surface of clear primer layer, coating thickness
20 μm, then in 15 DEG C -70 DEG C of temperature, 3h is dried in the environment of relative humidity 20%~80%, color basecoat is formed with, used
600#TOA sand paper has color basecoat to carry out sanding to described.
(5) 2.0mm is used, aqueous pigmented finish paint is sprayed on the surface of color basecoat, coating thickness by W-71 type spray guns
15 μm, form the first top coat layer.
(6) pearl essence, silver powder and bronze of equivalent are mixed, then with aqueous transparent priming paint with 1：15 quality
Ratio is mixed, and mixed fineness is 5 μm -20 μm, forms colouring agent, before the drying of the first top coat layer, with the colouring agent edge
The grain direction for the woodenware is rubbed onto the first top coat layer, colours wood grain；During scratch cover colorants, with hairbrush along the wood
The direction erasing of line, after erasing terminates, uses lint-free calico, unnecessary colouring agent is wiped, then using 800#TOA sand paper to wiping
The coating layer surface formed after painting carries out sanding.
(7) aqueous transparent finish paint is sprayed at the coating layer surface that is formed after erasing, then in 15 DEG C -70 DEG C of temperature, phase
To drying 2h-5h in the environment of humidity 20%~80%, the second top coat layer is formed.Wherein, the aqueous transparent finish paint is with least one
Individual " ten " font even application is in the coating layer surface formed after erasing.It is sprayed into " ten " font so that woodenware surface has the moon
Shadow effect, Hepplewhite third dimension is stronger.
Table three is the embodiment of the present invention three and comparative example one, the painting effect correction data of comparative example two.
Table three
As can be seen from the above table, the relatively existing woodenware coating process modelled after an antique of the present invention, its outward appearance artistic feeling is stronger, process
Simplicity, flow is controlled well.
Example IV
Woodenware coating process modelled after an antique of the present invention, comprises the following steps：
(1) is carried out by stamp side, beat or follows closely the one or more in small holes caused by worms method for pending woodenware, so as to the wood
Device carries out destruction processing so that the antique effect of woodenware is more preferable.
(2) wood grain with 240#TOA sand paper along pending woodenware is sanded, and removes burr, the sand trace on Wood-removing device surface.
Woodenware surface more smooth can be ensured after sand milling, it is smoother after follow-up spraying.
(3) 2.0mm is used, W-71 type spray guns are by aqueous transparent basecoat paint on pending woodenware surface, coating thickness
20 μm, the clear primer layer is dried into 1h-3h in the environment of 15 DEG C -70 DEG C of temperature, relative humidity 20%~80%, forms saturating
Bright prime coat；Sanding is carried out to the clear primer layer using 600#TOA sand paper.
(4) 2.0mm is used, W-71 type spray guns are by aqueous white basecoat paint in the surface of clear primer layer, coating thickness
20 μm, then in 15 DEG C -70 DEG C of temperature, 2h-4h is dried in the environment of relative humidity 20%~80%, color basecoat is formed with,
There is color basecoat to carry out sanding to described using 600#TOA sand paper.
(5) 2.0mm is used, aqueous pigmented finish paint is sprayed on the surface of color basecoat, coating thickness by W-71 type spray guns
15 μm, form the first top coat layer.
(6) pearl essence, silver powder and bronze are mixed, wherein the quality proportioning of pearl essence, silver powder and bronze is 2:
1:2, then with aqueous transparent priming paint with 1：20 mass ratio mixing, mixed fineness is 5 μm -20 μm, forms colouring agent,
Before first top coat layer is dried, with grain direction erasing of the colouring agent along the woodenware to the first top coat layer, wood grain
Color；During scratch cover colorants, rubbed with hairbrush along the direction of the wood grain, after erasing terminates, use lint-free calico, will be unnecessary
Toner is wiped, and then carries out sanding to the coating layer surface formed after erasing using 800#TOA sand paper.
(7) aqueous transparent finish paint is sprayed at the coating layer surface that is formed after erasing, then in 15 DEG C -70 DEG C of temperature, phase
To drying 2h-5h in the environment of humidity 20%~80%, the second top coat layer is formed.Wherein, the aqueous transparent finish paint is with least one
Individual " ten " font even application is in the coating layer surface formed after erasing.It is sprayed into " ten " font so that woodenware surface has the moon
Shadow effect, Hepplewhite third dimension is stronger.
Table four is the embodiment of the present invention four and comparative example one, the painting effect correction data of comparative example two.
Table four
As can be seen from the above table, the relatively existing woodenware coating process modelled after an antique of the present invention, its outward appearance artistic feeling is stronger, process
Simplicity, flow is controlled well.
Embodiment described above only expresses the several embodiments of the present invention, and it describes more specific and detailed, but simultaneously
Therefore the limitation to the scope of the claims of the present invention can not be interpreted as.It should be pointed out that for one of ordinary skill in the art
For, without departing from the inventive concept of the premise, various modifications and improvements can be made, these belong to the guarantor of the present invention
Protect scope.Therefore, the protection domain of patent of the present invention should be determined by the appended claims.
Claims (8)
1. woodenware coating process modelled after an antique, it is characterised in that comprise the following steps：
First spraying process：By aqueous transparent basecoat paint on pending woodenware surface, 1h-3h is dried, transparent priming is formed
Layer；
Second spraying process：By aqueous pigmented basecoat paint in the surface of the clear primer layer, 2h-4h is dried, is formed coloured
Prime coat；
3rd spraying process：Aqueous pigmented finish paint is sprayed on the surface for having a color basecoat, the first top coat layer is formed；
4th coating step：Pearl essence is mixed with metal powder, the pearl essence is mixed with the metal powder
Afterwards, fineness is 5 μm -20 μm；The metal powder is silver powder and/or bronze, then with the aqueous transparent priming paint with 1：15-20 matter
Amount ratio is mixed, and forms colouring agent, before first top coat layer drying, the wood grain with the colouring agent along the woodenware
Direction is rubbed onto first top coat layer, colours the wood grain；To be many after erasing terminates in 4th coating step
Remaining colouring agent is wiped；
5th spraying process：Aqueous transparent finish paint is sprayed to the coating layer surface of the 4th coating step formation, 2h- is dried
5h, forms the second top coat layer.
2. woodenware coating process modelled after an antique according to claim 1, it is characterised in that in the 5th spraying process, by institute
State the coating layer surface that aqueous transparent finish paint is sprayed at the 4th coating step formation with least one " ten " font.
3. woodenware coating process modelled after an antique according to claim 1, it is characterised in that the drying is entered in following environment
OK：15 DEG C -70 DEG C of temperature, relative humidity 20%~80%.
4. woodenware coating process modelled after an antique according to claim 1, it is characterised in that also have before first spraying process
There are following steps：Remove the burr and sand trace on the woodenware surface.
5. woodenware coating process modelled after an antique according to claim 4, it is characterised in that remove the burr on the woodenware surface with
Also there are following steps before the step of sand trace：Stamp side is carried out to the woodenware, beats and/or follows closely small holes caused by worms.
6. woodenware coating process modelled after an antique according to claim 1, it is characterised in that first spraying process and described the
Also there are following steps between two spraying process：Sanding is carried out to the clear primer layer；Second spraying process with it is described
Also there are following steps between 3rd spraying process：There is color basecoat to carry out sanding to described.
7. woodenware coating process modelled after an antique according to claim 1, it is characterised in that the 4th coating step and described the
Also there are following steps between five spraying process：Coating layer surface to the 4th coating step formation carries out sanding.
8. woodenware coating process modelled after an antique according to claim 1, it is characterised in that described in the 5th spraying process
The thickness of second top coat layer is 15 μm -20 μm.