Summary of the invention
The technical issues that need to address of the present invention are to disclose the construction method of a kind of gold dragon-skin antique effect in home decoration, and the application decorative effect of the method is given people a kind of visual experience of luxurious, honorable, style, to satisfy the relevant personnel's demand.
The construction method of gold dragon-skin antique effect of the present invention in indoor furniture is decorated comprises the steps:
1). material sanding: remove material surface burr, sand trace etc. with sand paper; Preferred 240# sand paper;
2). the spraying of polyurethane transparent priming paint: using polyurethane transparent priming paint to transfer to viscosity by proportioning is 15~16 seconds, sprays one and half " ten " words, 5~6 hours drying times then;
(said viscosity is rock field-2# cup viscosity, down together)
3). the sanding of polyurethane transparent priming paint: smooth, smooth with the sand paper sand milling, preferred 320# sand paper;
4). the golden priming paint spraying of polyurethane: with the copper bronze of polyurethane transparent priming paint adding 4~6%, transferring to viscosity by proportioning again is 15~16 seconds, spraying one and half " ten " words, dry 5~6 hours then;
5). the golden priming paint sanding of polyurethane: smooth, smooth with the sand paper sand milling, preferred 400# sand paper;
6). the nitrocellulose primer spraying: using nitro-diluent to transfer nitrate paint to viscosity is 12~13 seconds, sprays " a ten " word, then 20~30 minutes drying times;
7). the spraying of nitro white crackle paint: using nitro-diluent to transfer nitro white crackle paint viscosity is 11~12 seconds, evenly sprays " a ten " word, reaches a kind of imitative imperial bark effect, dry 30~40 minutes then;
8). copper-surfaced Jin Bo: be stained with the golden pool of copper glue with hairbrush material is brushed a time, after dry 10~20 minutes, again the copper gold is pasted on material surface, dry 7~8 hours then with mooring local irregularities;
9). nitrocellulose primer spraying: will not paste the glue scrub of copper Jin Bo with rosin, using nitro-diluent to transfer nitrocellulose primer to viscosity again is 14~15 seconds, spray " a ten " word, and drying is 50~60 minutes then;
10). nitro Ge Lisi: wipe examination material surface with nitro Ge Lisi,, and slightly grab light and shade, make it reach a kind of deep mixed natural decorative effect, dry 10~15 minutes then again with material surface wiped clean;
11). the nitrocellulose primer spraying: using nitro-diluent to transfer nitrocellulose primer to viscosity is 15~16 seconds, sprays " a ten " word, dry 50~60 minutes then;
12). the nitrocellulose primer sanding: extremely smooth with sand paper light weight sand material surface, preferred 400# sand paper;
13). nitro Ge Lisi does brush: be stained with nitro Ge Lisi tip-tap in the edge of material with hairbrush, and in the middle of particular, make it reach a kind of service time long and the deep mixed natural antique effect made dirty, 10~15 minutes drying times then;
14). the nitrocellulose primer spraying: using nitro-diluent to transfer nitrocellulose primer to viscosity is 14~15 seconds, sprays " a ten " word, dry 50~60 minutes then;
15). nitrocellulose primer sanding: use the sand paper light weight sand, remove the material surface particles, preferred 400# sand paper;
16). specking: with spray gun spray specking effect, make and deepen antique effect again, it is very long to reach a kind of service time, the dung point effect that the material surface has fly to stay;
17). the nitrocellulose primer spraying: using nitro-diluent to transfer nitrocellulose primer to viscosity is 14~15 seconds, sprays " a ten " word, 50~60 minutes drying times;
18). Bu Yinxiuse: be stained with cloth seal color with byssus and pat color effects, make it reach a deep mixed golden color effects, dry 10~15 minutes on the material surface;
19). the lacquer finish spraying: using nitro-diluent to transfer nitro dull finishing coat to viscosity is 11~12 seconds, sprays " a ten " word, gets final product in dry 36 hours.
Adopt technology of the present invention, can form a kind of antique effect of gold dragon-skin, make indoor decorative effect reach width of cloth wealth and rank, style, luxurious scene on indoor furniture surface.
The specific embodiment
For technological means, creation characteristic that the present invention is realized, reach purpose and effect and be easy to understand and understand, below in conjunction with the specific embodiment, further set forth the present invention.
The construction method of a kind of gold dragon-skin antique effect in home decoration carried out material sanding earlier, and specific practice is to remove material surface burr, sand trace etc., preferred 240# sand paper with sand paper.
Carry out the spraying of polyurethane transparent priming paint then, specific practice is to use polyurethane transparent priming paint to transfer to viscosity by proportioning to be 15~16 seconds, to spray one and half " ten " words, 5~6 hours drying times.
Then carrying out the sanding of polyurethane transparent priming paint, is smooth, smooth with the sand paper sand milling specifically, preferred 320# sand paper.
Next carrying out the golden priming paint spraying of polyurethane, is with the copper bronze of polyurethane transparent priming paint adding 5% specifically, transfers to 15~16 seconds spraying one and half " ten " words, dry 5~6 hours then again by proportioning.
Carry out the golden priming paint sanding of polyurethane then, specific practice is smooth, smooth with the sand paper sand milling, preferred 400# sand paper.
Carry out the nitrocellulose primer spraying then, specific practice is to use nitro-diluent to transfer nitrate paint to viscosity to be 12~13 seconds, to spray " a ten " word, dry 20~30 minutes then.
Then carrying out the spraying of nitro white crackle paint, is to use nitro-diluent to transfer nitro white crackle paint to viscosity to be 11~12 seconds, evenly to spray " a ten " word specifically, reaches a kind of imitative imperial bark effect, dry 30~40 minutes then.
Then carry out copper-surfaced Jin Bo, be stained with the golden pool of copper glue with hairbrush specifically material is brushed one time, after dry 10~20 minutes, again the copper gold is pasted on material surface, dry 7~8 hours then with mooring local irregularities.
Next carry out the nitrocellulose primer spraying, specific practice is the glue scrub that will not paste copper Jin Bo with rosin, and using nitro-diluent to transfer nitrocellulose primer to viscosity again is 14~15 seconds, sprays " a ten " word, then 50~60 minutes drying times.
Next carry out nitro Ge Lisi, specific practice is to wipe examination material surface with nitro Ge Lisi, again with material surface wiped clean, and slightly grabs light and shade, makes it reach a kind of deep mixed natural decorative effect, dry 10~15 minutes then.
Carrying out the nitrocellulose primer spraying then, is to use nitro-diluent to transfer nitrocellulose primer to viscosity to be 15~16 seconds, to spray " a ten " word, dry 50~60 minutes then specifically.
Carrying out the nitrocellulose primer sanding then, is extremely smooth with sand paper light weight sand material surface specifically, preferred 400# sand paper.
Then carry out nitro Ge Lisi and do brush; Specific practice is to be stained with the edge of nitro Ge Lisi tip-tap at material with hairbrush; And in the middle of particular, it is long and by the deep mixed natural antique effect made dirty to make it reach a kind of service time, dry 10~15 minutes then.
Next carry out the nitrocellulose primer spraying, specific practice is to use nitro-diluent to transfer nitrocellulose primer to concentration to be 14~15 seconds, to spray " a ten " word, dry 50~60 minutes.
Carrying out the nitrocellulose primer sanding then, is to use the sand paper light weight sand specifically, removes the material surface particles, preferred 400# sand paper.
Carrying out specking then, is to remove the specking effect with the spray gun spray specifically, makes and deepens antique effect again, and it is very long to reach a kind of service time, the dung point effect that makes the material surface have fly to stay.
Then carry out the nitrocellulose primer spraying, using nitro-diluent to transfer nitrocellulose primer to viscosity specifically is 14~15 seconds, sprays " a ten " word, 50~60 minutes drying times.
Then carry out Bu Yinxiuse, be stained with cloth seal color with byssus specifically and pat color effects, make it reach a deep mixed golden color effects, dry 10~15 minutes then on the material surface.
The lacquer finish spraying is carried out in final step, and specific practice is to use nitro-diluent to transfer nitro dull finishing coat to viscosity to be 11~12 seconds, to spray " a ten " word, gets final product in dry 36 hours.
Said material is the indoor furniture product.
The mixed solvent that said nitro-diluent is made up of chemical solvents such as xylenes, ethylene glycol monobutyl ether, butyl acetates.
Said viscosity is rock field-2# cup viscosity.
Said material is the indoor furniture product; Furniture item like birch, MDF composition.
The mixed solvent that said nitro-diluent is made up of chemical solvents such as xylenes, ethylene glycol monobutyl ether, butyl acetates.
Term " cross spraying process " is meant on by spray and from first to last sprays one time that intersection from first to last sprays one time then.
Term " specking, dried brush, Bu Yin " is term well known in the art, in American antique coating technology record, detailed description is arranged.
Said nitrocellulose primer, polyurethane transparent priming paint, nitro white crackle paint, nitro Ge Lisi and lacquer finish are the market sale product, like the product of the rich minister chemical industry in Shanghai Co., Ltd.
Adopt technology of the present invention, can form a kind of antique effect of gold dragon-skin, make the indoor furniture decorative effect reach width of cloth wealth and rank, style, luxurious scene, thereby can satisfy the relevant personnel's demand.
More than show and described basic principle of the present invention, principal character and advantage of the present invention.The technical staff of the industry should understand; The present invention is not restricted to the described embodiments; That describes in the foregoing description and the specification just explains principle of the present invention; The present invention also has various changes and modifications under the prerequisite that does not break away from spirit and scope of the invention, and these variations and improvement all fall in the scope of the invention that requires protection.The present invention requires protection domain to be defined by appending claims and equivalent thereof.