CN101339764B - Process for applying nitro crack antique effect on surface of electric guitar - Google Patents

Process for applying nitro crack antique effect on surface of electric guitar Download PDF

Info

Publication number
CN101339764B
CN101339764B CN 200710043560 CN200710043560A CN101339764B CN 101339764 B CN101339764 B CN 101339764B CN 200710043560 CN200710043560 CN 200710043560 CN 200710043560 A CN200710043560 A CN 200710043560A CN 101339764 B CN101339764 B CN 101339764B
Authority
CN
China
Prior art keywords
nitro
viscosity
diluent
effect
seconds
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN 200710043560
Other languages
Chinese (zh)
Other versions
CN101339764A (en
Inventor
钟华胜
刘林生
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHANGHAI ZHANCHEN PAINT Co.,Ltd.
Zhuhai zhanchen New Material Co., Ltd
Original Assignee
SHENZHEN ZHANCHENDA CHEMICAL INDUSTRY Co Ltd
Shanghai Fuchen Chemical Co Ltd
Beijing Zhanchen Chemical Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHENZHEN ZHANCHENDA CHEMICAL INDUSTRY Co Ltd, Shanghai Fuchen Chemical Co Ltd, Beijing Zhanchen Chemical Co Ltd filed Critical SHENZHEN ZHANCHENDA CHEMICAL INDUSTRY Co Ltd
Priority to CN 200710043560 priority Critical patent/CN101339764B/en
Publication of CN101339764A publication Critical patent/CN101339764A/en
Application granted granted Critical
Publication of CN101339764B publication Critical patent/CN101339764B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses a construction technology for nitro cracking archaizing painting effect on the surface of an electric guitar and is characterized by comprising the following procedures: (1) processing materials: a. destructive processing, b. sanding; (2) ground color spraying; (3) polyurethane primer spraying; (4) the polyurethane primer spraying; (5) nitro primer spraying; (6) the nitro cracking paint spraying; (7) the nitro primer spraying; (8) nitro gracing; (9) the nitro primer spraying; (10) nitro gracing dry brushing; (11) the nitro primer spraying; (12) the nitro primer spraying; (13) oxtailing and spot painting; (14) the nitro primer spraying; (15) the nitro primer spraying; (16) the nitro topcoat spraying. The construction technology of the invention can creat cracking archaizing effect on the electric guitar materials; therefore can meet the requirements of related stuffs.

Description

Nitro crack antique effect is in the construction technology on electric guitar surface
Technical field
The present invention relates to a kind of nitro crack antique coating construction process, be specifically related to the antique coating technology on the electric guitar base material.
Technical background
At present to make decorative effect more single for electric guitar, be mostly a kind of polyurethane/unsaturated polyester varnish minute surface, dodge silver-colored painting effect.Reason is that the former application is longer to the use of electric guitar, but along with people to spirit and material progress requirement when more and more higher, people begin ancient epoch a kind of cherished the memory of and pursue, and this pursuit people exactly enjoy on own employed furniture or article and pursue.So the former coating process can not satisfy modern's demand far away.(" wood processing machinery ", the second phase in 2004, Liu Xianzhong) the nitrate paint construction technology of Lun Shuing was that a kind of common bottom coloring, face are repaiied look technology to reference paper " the pine furniture nitrate paint is covered with paint, lacquer, colour wash, etc. industrial analysis ".List of references " development of nitro transparent priming and application " (" modern coating and application ", the first phase in 2002, Feng Shenyong, Qin Xiaolun) mention the application of nitrate paint, but two pieces of documents all do not have the natural antique effect of antique coating, therefore, the decorative effect of present electric guitar can not satisfy the relevant personnel's needs.
Summary of the invention
The technical issues that need to address of the present invention are to disclose the construction technology of a kind of nitro crack antique effect on the electric guitar surface, to satisfy people's needs.
Nitro crack antique effect of the present invention comprises the steps: in the construction technology on electric guitar surface
1. material is handled:
(1) destroys processing: with tool for destroying the bad intentional property of electric guitar hair is beaten, make it reach a kind of these article and be used overlong time and impaired natural effect;
(2) sanding:, remove material surface burr, sand trace etc. with sand paper sand milling along the grain; Preferred 240# sand paper;
2, background color: with the spraying of nitro colored paint, squirt, make it reach the grain of wood and embody effect;
3. polyurethane primer: transferring to viscosity with the clear priming paint of polyurethane by proportioning is 15～16 seconds, sprays one and half " ten " words, 4～6 hours drying times three times;
Said for viscosity is rock field-2# cup viscosity, down together;
4. sanding: along the grain sand milling is smooth, smooth with sand paper, preferred 320#～400# sand paper;
5. nitrocellulose primer: transferring nitrocellulose primer to viscosity with nitro-diluent is 12～13 seconds, sprays twice, one " ten " word, surface drying;
6, nitro crack lacquer: transferring nitro white crackle paint to viscosity with nitro-diluent is 11～12 seconds, evenly sprays " a ten " word, makes its effect that reaches a kind of natural cracking, dry 40～50 minutes;
7, nitrocellulose primer: transferring nitrocellulose primer to viscosity with nitro-diluent is 11～12 seconds, sprays " a ten " word, dry 50～60 minutes;
8, nitro Ge Lisi: use nitro Ge Lisi, wipe the face of taking temperature,, and slightly grab light and shade, make it reach a kind of deep mixed natural effect again with surperficial wiped clean;
9. nitrocellulose primer: transferring nitrocellulose primer to viscosity with nitro-diluent is 13～14 seconds, spray " a ten " word, drying 40～60 minutes;
10. do brush: be stained with nitro Ge Lisi tip-tap in the electric guitar edge with hairbrush, and in the middle of particular or destruction place, make it reach a kind of service time of the long and natural effect made dirty;
11. nitrocellulose primer: transferring nitrocellulose primer to viscosity with nitro-diluent is 14～16 seconds, sprays " a ten " word, dry 40～60 minutes;
12. sanding: level and smooth with the sand paper sand milling, sand is not worn, preferred 400# sand paper;
13. oxtail, specking: draw oxtail with nitro Ge Lisi, and do the specking effect, make it deepen natural effect modelled after an antique again with rifle;
14. nitrocellulose primer: transfer nitrocellulose primer to viscosity 14～16 seconds with nitro-diluent, spray " a ten " word, drying 40～60 minutes;
15. sanding: smooth, smooth with the sand paper sand milling; Sand is not worn, preferred 400# sand paper;
16. lacquer finish: transferring lacquer finish to viscosity with nitro-diluent is 12～13 seconds, sprays " a ten " word, gets final product in dry 36 hours.
Said material is maple, birch or linden;
Said nitro-diluent is by the two or more mixed solvents of forming in dimethylbenzene, isobutanol, ethylene glycol monobutyl ether or the butyl acetate etc.
Term " oxtail, specking " is term well known in the art, detailed description is arranged in American antique coating technology record.
Said nitro colored paint, the clear priming paint of polyurethane, nitrocellulose primer, nitro white crackle paint, nitro Ge Lisi and lacquer finish are the commercially available prod, as the product of the rich minister chemical industry in Shanghai Co., Ltd;
Adopt technology of the present invention, can form a kind of crack antique effect on the electric guitar surface, thereby can satisfy the relevant personnel's demand.
The specific embodiment
Embodiment 1
1. material is handled: material is a maple.
(1) destroys processing: with tool for destroying the bad intentional property of electric guitar hair is beaten, make it reach a kind of these article and be used overlong time and impaired natural effect;
(2) sanding: use 240# sand paper sand milling along the grain, remove material surface burr, sand trace etc.;
2, background color: with the spraying of nitro colored paint, squirt, make it reach the grain of wood and embody effect;
3. polyurethane primer: transferring to viscosity with the clear priming paint of polyurethane by proportioning is 15 seconds, sprays one and half " ten " words, 5 hours drying times three times;
Said for viscosity is rock field-2# cup viscosity, down together;
4. sanding: along the grain sand milling is smooth, smooth with 400# sand paper;
5. nitrocellulose primer: transferring nitrocellulose primer to viscosity with nitro-diluent is 12 seconds, sprays twice, one " ten " word, surface drying;
6, nitro crack lacquer: transferring nitro white crackle paint to viscosity with nitro-diluent is 12 seconds, evenly sprays " a ten " word, makes its effect that reaches a kind of natural cracking, dry 45 minutes;
7, nitrocellulose primer: transferring nitrocellulose primer to viscosity with nitro-diluent is 11 seconds, sprays " a ten " word, dry 1 hour;
8, nitro Ge Lisi: use nitro Ge Lisi, wipe the face of taking temperature,, and slightly grab light and shade, make it reach a kind of deep mixed natural effect again with surperficial wiped clean;
9. nitrocellulose primer: transferring nitrocellulose primer to viscosity with nitro-diluent is 13 seconds, spray " a ten " word, drying 50 minutes;
10. do brush: be stained with nitro Ge Lisi tip-tap in the electric guitar edge with hairbrush, and in the middle of particular or destruction place, make it reach a kind of service time of the long and natural effect made dirty;
11. nitrocellulose primer: transferring nitrocellulose primer to viscosity with nitro-diluent is 14 seconds, sprays " a ten " word, dry 50 minutes;
12. sanding: level and smooth with 400# sand paper sand milling, sand is not worn;
13. oxtail, specking: draw oxtail with nitro Ge Lisi, and do the specking effect, make it deepen natural effect modelled after an antique again with rifle;
14. nitrocellulose primer: transfer nitrocellulose primer to viscosity 14 seconds with nitro-diluent, spray " a ten " word, drying 50 minutes;
15. sanding: smooth, smooth with 400# sand paper sand milling; Sand is not worn;
16. lacquer finish: transferring lacquer finish to viscosity with nitro-diluent is 13 seconds, sprays " a ten " word, gets final product in dry hour.
Said nitro-diluent is the mixed solvent of being made up of dimethylbenzene and butyl acetate (1: 1, volume ratio).
Adopt above-mentioned technology, formed a kind of crack antique effect on the electric guitar surface.

Claims (3)

1. a nitro crack antique effect is characterized in that in the construction technology on electric guitar surface, comprises the steps:
(1) material is handled:
(a) destroy processing: with tool for destroying the bad intentional property of electric guitar hair is beaten, make it reach a kind of these article and be used overlong time and impaired natural effect;
(b) sanding:, remove wood surface burr, sand trace with sand paper sand milling along the grain;
(2) background color: with the spraying of nitro colored paint, squirt, make it reach the grain of wood and embody effect;
(3) polyurethane primer: transferring to viscosity with the clear priming paint of polyurethane by proportioning is 15～16 seconds, sprays one and half " ten " words, 4～6 hours drying times three times;
(4) sanding: along the grain sand milling is smooth, smooth with sand paper;
(5) nitrocellulose primer: transferring nitrocellulose primer to viscosity with nitro-diluent is 12～13 seconds, sprays twice, one " ten " word, surface drying;
(6) nitro crack lacquer: transferring nitro white crackle paint to viscosity with nitro-diluent is 11～12 seconds, evenly sprays " a ten " word, makes its effect that reaches a kind of natural cracking, dry 40～50 minutes;
(7) nitrocellulose primer: transferring nitrocellulose primer to viscosity with nitro-diluent is 11～12 seconds, sprays " a ten " word, dry 50～60 minutes;
(8) nitro Ge Lisi: use nitro Ge Lisi, wipe the face of taking temperature,, and slightly grab light and shade, make it reach a kind of deep mixed natural effect again with surperficial wiped clean;
(9) nitrocellulose primer: transferring nitrocellulose primer to viscosity with nitro-diluent is 13～14 seconds, sprays " a ten " word, dry 40～60 minutes;
(10) do brush: be stained with nitro Ge Lisi tip-tap in the electric guitar edge with hairbrush, and in the middle of particular or destruction place, make it reach a kind of service time of the long and natural effect made dirty;
(11) nitrocellulose primer: transferring nitrocellulose primer to viscosity with nitro-diluent is 14～16 seconds, sprays " a ten " word, dry 40～60 minutes;
(12) sanding: level and smooth with the sand paper sand milling, sand is not worn;
(13) oxtail, specking: draw oxtail with nitro Ge Lisi, and do the specking effect, make it deepen natural effect modelled after an antique again with rifle;
(14) nitrocellulose primer: transfer nitrocellulose primer to viscosity 14～16 seconds with nitro-diluent, spray " a ten " word, drying 40～60 minutes;
(15) sanding: smooth, smooth with the sand paper sand milling; Sand is not worn;
(16) lacquer finish: transferring lacquer finish to viscosity with nitro-diluent is 12～13 seconds, sprays " a ten " word, dry getting final product,
Described viscosity is rock field-2# cup viscosity.
2. nitro crack antique effect according to claim 1 is characterized in that in the construction technology on electric guitar surface said timber is maple, birch or linden.
3. nitro crack antique effect according to claim 1 is characterized in that in the construction technology on electric guitar surface, the mixed solvent that said nitro-diluent is made up of by 1: 1 volume ratio dimethylbenzene and butyl acetate.
CN 200710043560 2007-07-06 2007-07-06 Process for applying nitro crack antique effect on surface of electric guitar Active CN101339764B (en)