CN104549962A - Antique construction technology of polyurethane paint for PU foaming material of furniture - Google Patents
Antique construction technology of polyurethane paint for PU foaming material of furniture Download PDFInfo
- Publication number
- CN104549962A CN104549962A CN201310475478.5A CN201310475478A CN104549962A CN 104549962 A CN104549962 A CN 104549962A CN 201310475478 A CN201310475478 A CN 201310475478A CN 104549962 A CN104549962 A CN 104549962A
- Authority
- CN
- China
- Prior art keywords
- polyurethane
- word
- priming paint
- diluent
- viscosity
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an antique construction technology of a polyurethane paint for a PU foaming material of furniture. The antique construction technology is characterized by comprising the following steps: material treatment, treatment of a PU foaming material enhanced adhesion priming paint, treatment of a polyurethane priming paint, sanding, dry brushing of GLAZE, treatment of the polyurethane priming paint, sanding, color repairing of a dye, and treatment of a polyurethane f finishing coat, wherein the PU foaming material enhanced adhesion priming paint, the polyurethane priming paint, the polyurethane finishing coat, a curing agent, a diluent, the GLAZE, the dye and the like are all commercial products produced by Shanghai Fuchen Chemical Ltd or the similar products on the market, the GLAZE is a coloring system product formed by matching and grinding long oil alkyd resin and a transparent or semi-transparent inorganic pigment powder, and the viscosities are all subject to the 2# viscosity cup test. The antique construction technology has the advantages that the adhesive force problem after coating is solved, the coating cost is lowered, and conditions are created for wide application of the PU foaming material to the household products.
Description
Technical field
The present invention relates to a kind of construction technology modelled after an antique of polyurethane paint of the PU expanded material for furniture, belong to the technical field of application.
Background technology
Due to the scarcity of timber resources, Furniture manufacturing have employed a lot of other materials, reduces the dependence to timber, and except timber, bamboo, rattan, glass, plastics, UPE reverse mould material, PU foaming etc. are widely used.The application of bamboo, rattan, glass, plastics has its limitation, can only be used for local and decorate use, and can not replace timber and be widely used in flat board or carving position.UPE reverse mould material may be used for flat board or carving, but it is comparatively firmly crisp and thick and heavy, and application is subject to certain restrictions.And PU foaming has very good advantage: there is extraordinary intensity, various shape can be processed into, both can be used for flat board and also can be used for carving, good decorative property, environmental protection, low, the not perishable distortion of cost, can use for a long time.But it is tight that existing problems are PU expanded material chemical constitutions, and the coating varieties such as common nitro, polyurethane, epoxy, acrylic acid, alkyd paint cannot obtain good adhesive force on PU expanded material.
In today that personalization shows day by day, make PU expanded material increasingly extensive in the application demand of field of furniture, therefore inventing a kind of antique coating technology be directly coated on PU expanded material is have good market prospects, this technique has that rate of drying is fast, efficiency is high, adhesive force is extremely excellent, saves the advantage of painting cost.
Summary of the invention
The object of the invention is to, a kind of construction technology modelled after an antique of polyurethane paint of the PU expanded material for furniture is provided, to overcome the above-mentioned shortcoming and defect existing for prior art.
The present invention is designed for the construction technology modelled after an antique of the polyurethane paint of the PU expanded material of furniture, it is characterized in that being made up of following steps:
(1) material process: with cloth by the dust on bamboo product and foul wiped clean,
(2) attachment of PU expanded material strengthens priming paint: strengthen priming paint with the attachment of PU expanded material and add diluent, viscosity is adjusted to 9 ~ 10 seconds, even application " ten " word, treats dry 5 ~ 10 minutes,
(3) polyurethane primer: add curing agent, diluent with polyurethane primer, is adjusted to 13 ~ 14 seconds by viscosity, even application " ten " word, treats dry 1 ~ 2 hour,
(4) sanding: use sand paper sand milling, removes surface blot, preferred 400# sand paper,
(5) the dry brush of Ge Lisi: dip a small amount of Ge Lisi with hairbrush, make a little ducting effect along bamboo line, deep mixed Ge Lisi effect is made in edge, treats dry 30 ~ 40 minutes,
(6) polyurethane primer: add curing agent, diluent with polyurethane primer, is adjusted to 13 ~ 14 seconds by viscosity, even application " ten " word, treats dry 1 ~ 2 hour,
(7) sanding: use sand paper sand milling, by smooth for surperficial light weight sand, preferred 400# sand paper,
(8) look repaiied by dyestuff: repair integral color with repairing look, deepens the stereovision of integral color and increases the imitative old effect of bamboo product,
(9) polyurethane finish: add curing agent, diluent with polyurethane finish, is adjusted to 11 ~ 12 seconds by viscosity, even application " ten " word, treats dry more than 8 hours;
Described PU expanded material attachment strengthens priming paint, polyurethane primer, polyurethane finish, curing agent, diluent, lattice Liz, dyestuffs etc. are the like product that the commercially available prod (Ge Lisi refer to arrange in pairs or groups the coloring system product that grind to form with long oil alkyd resin and transparent or semitransparent inorganic pigment powder) of the production of Shanghai Fu Chen Co., Ltd or market are sold, described " ten " word, refer to that coated article part longitudinally sprays one time from the beginning to the end comprehensively, then laterally spray one time from the beginning to the end comprehensively, present " ten " word cross-like for twice, described viscosity is all as the criterion with the test of 2# rock field cup.Advantage of the present invention is the problem solving adhesive force after application, saves painting cost, for PU expanded material creates condition in the extensive application of household goods.
Detailed description of the invention
Implement 1
For the construction technology modelled after an antique of the polyurethane paint of the PU expanded material of furniture, it is characterized in that being made up of following steps:
(1) material process: with cloth by the dust on bamboo product and foul wiped clean,
(2) attachment of PU expanded material strengthens priming paint: strengthen priming paint with the attachment of PU expanded material and add diluent, viscosity is adjusted to 9 seconds, even application " ten " word, treats dry 5 minutes,
(3) polyurethane primer: add curing agent, diluent with polyurethane primer, is adjusted to 13 seconds by viscosity, even application " ten " word, treats dry 1 hour,
(4) sanding: use sand paper sand milling, removes surface blot, preferred 400# sand paper,
(5) the dry brush of Ge Lisi: dip a small amount of Ge Lisi with hairbrush, make a little ducting effect along bamboo line, deep mixed Ge Lisi effect is made in edge, treats dry 30 minutes,
(6) polyurethane primer: add curing agent, diluent with polyurethane primer, is adjusted to 13 seconds by viscosity, even application " ten " word, treats dry 1 hour,
(7) sanding: use sand paper sand milling, by smooth for surperficial light weight sand, preferred 400# sand paper,
(8) look repaiied by dyestuff: repair integral color with repairing look, deepens the stereovision of integral color and increases the imitative old effect of bamboo product,
(9) polyurethane finish: add curing agent, diluent with polyurethane finish, is adjusted to 11 seconds by viscosity, even application " ten " word, treats dry more than 8 hours;
Described PU expanded material attachment strengthens priming paint, polyurethane primer, polyurethane finish, curing agent, diluent, lattice Liz, dyestuffs etc. are the like product that the commercially available prod (Ge Lisi refer to arrange in pairs or groups the coloring system product that grind to form with long oil alkyd resin and transparent or semitransparent inorganic pigment powder) of the production of Shanghai Fu Chen Co., Ltd or market are sold, described " ten " word, refer to that coated article part longitudinally sprays one time from the beginning to the end comprehensively, then laterally spray one time from the beginning to the end comprehensively, present " ten " word cross-like for twice, described viscosity is all as the criterion with the test of 2# rock field cup.
Implement 2
For the construction technology modelled after an antique of the polyurethane paint of the PU expanded material of furniture, it is characterized in that being made up of following steps:
(1) material process: with cloth by the dust on bamboo product and foul wiped clean,
(2) attachment of PU expanded material strengthens priming paint: strengthen priming paint with the attachment of PU expanded material and add diluent, viscosity is adjusted to 10 seconds, even application " ten " word, treats dry 10 minutes,
(3) polyurethane primer: add curing agent, diluent with polyurethane primer, is adjusted to 14 seconds by viscosity, even application " ten " word, treats dry 2 hours,
(4) sanding: use sand paper sand milling, removes surface blot, preferred 400# sand paper,
(5) the dry brush of Ge Lisi: dip a small amount of Ge Lisi with hairbrush, make a little ducting effect along bamboo line, deep mixed Ge Lisi effect is made in edge, treats dry 40 minutes,
(6) polyurethane primer: add curing agent, diluent with polyurethane primer, is adjusted to 14 seconds by viscosity, even application " ten " word, treats dry 2 hours,
(7) sanding: use sand paper sand milling, by smooth for surperficial light weight sand, preferred 400# sand paper,
(8) look repaiied by dyestuff: repair integral color with repairing look, deepens the stereovision of integral color and increases the imitative old effect of bamboo product,
(9) polyurethane finish: add curing agent, diluent with polyurethane finish, is adjusted to 12 seconds by viscosity, even application " ten " word, treats dry more than 8 hours;
Described PU expanded material attachment strengthens priming paint, polyurethane primer, polyurethane finish, curing agent, diluent, lattice Liz, dyestuffs etc. are the like product that the commercially available prod (Ge Lisi refer to arrange in pairs or groups the coloring system product that grind to form with long oil alkyd resin and transparent or semitransparent inorganic pigment powder) of the production of Shanghai Fu Chen Co., Ltd or market are sold, described " ten " word, refer to that coated article part longitudinally sprays one time from the beginning to the end comprehensively, then laterally spray one time from the beginning to the end comprehensively, present " ten " word cross-like for twice, described viscosity is all as the criterion with the test of 2# rock field cup.
Implement 3
For the construction technology modelled after an antique of the polyurethane paint of the PU expanded material of furniture, it is characterized in that being made up of following steps:
(1) material process: with cloth by the dust on bamboo product and foul wiped clean,
(2) attachment of PU expanded material strengthens priming paint: strengthen priming paint with the attachment of PU expanded material and add diluent, viscosity is adjusted to 9 seconds, even application " ten " word, treats dry 10 minutes,
(3) polyurethane primer: add curing agent, diluent with polyurethane primer, is adjusted to 14 seconds by viscosity, even application " ten " word, treats dry 1 hour,
(4) sanding: use sand paper sand milling, removes surface blot, preferred 400# sand paper,
(5) the dry brush of Ge Lisi: dip a small amount of Ge Lisi with hairbrush, make a little ducting effect along bamboo line, deep mixed Ge Lisi effect is made in edge, treats dry 40 minutes,
(6) polyurethane primer: add curing agent, diluent with polyurethane primer, is adjusted to 13 seconds by viscosity, even application " ten " word, treats dry 2 hours,
(7) sanding: use sand paper sand milling, by smooth for surperficial light weight sand, preferred 400# sand paper,
(8) look repaiied by dyestuff: repair integral color with repairing look, deepens the stereovision of integral color and increases the imitative old effect of bamboo product,
(9) polyurethane finish: add curing agent, diluent with polyurethane finish, is adjusted to 11 seconds by viscosity, even application " ten " word, treats dry more than 8 hours;
Described PU expanded material attachment strengthens priming paint, polyurethane primer, polyurethane finish, curing agent, diluent, lattice Liz, dyestuffs etc. are the like product that the commercially available prod (Ge Lisi refer to arrange in pairs or groups the coloring system product that grind to form with long oil alkyd resin and transparent or semitransparent inorganic pigment powder) of the production of Shanghai Fu Chen Co., Ltd or market are sold, described " ten " word, refer to that coated article part longitudinally sprays one time from the beginning to the end comprehensively, then laterally spray one time from the beginning to the end comprehensively, present " ten " word cross-like for twice, described viscosity is all as the criterion with the test of 2# rock field cup.
Claims (1)
1., for the construction technology modelled after an antique of the polyurethane paint of the PU expanded material of furniture, it is characterized in that being made up of following steps:
(1) material process: with cloth by the dust on bamboo product and foul wiped clean,
(2) attachment of PU expanded material strengthens priming paint: strengthen priming paint with the attachment of PU expanded material and add diluent, viscosity is adjusted to 9 ~ 10 seconds, even application " ten " word, treats dry 5 ~ 10 minutes,
(3) polyurethane primer: add curing agent, diluent with polyurethane primer, is adjusted to 13 ~ 14 seconds by viscosity, even application " ten " word, treats dry 1 ~ 2 hour,
(4) sanding: use sand paper sand milling, removes surface blot, preferred 400# sand paper,
(5) the dry brush of Ge Lisi: dip a small amount of Ge Lisi with hairbrush, make a little ducting effect along bamboo line, deep mixed Ge Lisi effect is made in edge, treats dry 30 ~ 40 minutes,
(6) polyurethane primer: add curing agent, diluent with polyurethane primer, is adjusted to 13 ~ 14 seconds by viscosity, even application " ten " word, treats dry 1 ~ 2 hour,
(7) sanding: use sand paper sand milling, by smooth for surperficial light weight sand, preferred 400# sand paper,
(8) look repaiied by dyestuff: repair integral color with repairing look, deepens the stereovision of integral color and increases the imitative old effect of bamboo product,
(9) polyurethane finish: add curing agent, diluent with polyurethane finish, is adjusted to 11 ~ 12 seconds by viscosity, even application " ten " word, treats dry more than 8 hours;
Described PU expanded material attachment strengthens priming paint, polyurethane primer, polyurethane finish, curing agent, diluent, lattice Liz, dyestuffs etc. are the like product that the commercially available prod (Ge Lisi refer to arrange in pairs or groups the coloring system product that grind to form with long oil alkyd resin and transparent or semitransparent inorganic pigment powder) of the production of Shanghai Fu Chen Co., Ltd or market are sold, described " ten " word, refer to that coated article part longitudinally sprays one time from the beginning to the end comprehensively, then laterally spray one time from the beginning to the end comprehensively, present " ten " word cross-like for twice, described viscosity is all as the criterion with the test of 2# rock field cup.