CN105170430A - Archaistic wooden ware coating method - Google Patents
Archaistic wooden ware coating method Download PDFInfo
- Publication number
- CN105170430A CN105170430A CN201510379542.9A CN201510379542A CN105170430A CN 105170430 A CN105170430 A CN 105170430A CN 201510379542 A CN201510379542 A CN 201510379542A CN 105170430 A CN105170430 A CN 105170430A
- Authority
- CN
- China
- Prior art keywords
- woodenware
- spraying process
- coating
- modelled
- finish paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to an archaistic wooden ware coating method. The archaistic wooden ware coating method comprises the first coating step of spraying water-based transparent primer to the surface of wooden ware to be processed, conducting drying and forming a transparent primer layer; the second coating step of spraying water-based colored primer to the surface of the transparent primer layer, conducting drying and forming a colored primer layer; the third coating step of spraying water-based colored finish paint to the surface of the colored primer layer to form a first finish paint layer; the fourth coating step of mixing pearl powder and metal powder which is aluminum powder and/or gold powder, then mixing the mixture and water-based transparent primer at a preset proportion to form a coloring agent, and smearing the coloring agent to the first finish paint layer to color wood grains before the first finish paint layer is dried; and the fifth coating step of spraying water-based transparent finish paint to the surface of the first finish paint layer, conducting drying and forming a second finish paint layer. The method has the special bronzing or silvering effect different from the existing archaistic effect, the grade of furniture can be improved, and the construction process is simple and convenient to implement.
Description
Technical field
The present invention relates to woodwork coating technical field, be specifically related to a kind of woodenware coating process modelled after an antique.
Background technology
Pseudo-classic furniture construction on market generally comprises, and the destruction of substrate surface, wiping background color, Ge Lisi wipe look, beat the operations such as dry brush, finish paint, the visual experience of the main outstanding sedate low-key of pseudo-classic furniture, comfortable easiness.The Chinese invention patent being " CN103963508A " as the patent No. discloses a kind of finishing Technology for American Style Furniture antique-imitation method, the construction modelled after an antique of it and antique traditional furniture is similar, mainly by the destruction of base material with repair look process, make it the effect reaching antique-imitation, this similar technique generally all will through multiple working procedure, and technique is more complicated.
In addition, construction technology modelled after an antique in the market, all just has effect modelled after an antique, in the occasion that some hotel, villas etc. are high-grade, require that furniture has unusual and high-end, that air, class are high effect, current construction technology modelled after an antique is all difficult to meet this requirement.
Summary of the invention
Based on this, the invention provides a kind of woodenware coating process modelled after an antique, it has special bronzing or silver-colored effect, can be different from effect modelled after an antique at present, and can improve the class of furniture; Construction technology is easy.
In order to realize object of the present invention, the present invention by the following technical solutions:
Woodenware coating process modelled after an antique, it comprises the steps:
First spraying process: by aqueous transparent basecoat paint on pending woodenware surface, dry 1h-3h, forms clear primer layer;
Second spraying process: by the surface of aqueous pigmented basecoat paint in described clear primer layer, dry 2h-4h, is formed with color basecoat;
3rd spraying process: the surface having color basecoat described in being sprayed on by aqueous pigmented finish paint, forms first surface enamelled coating;
4th spraying process: pearl essence and metal powder are mixed, described metal powder is silver powder and/or bronze, mix with the mass ratio of 1:15-20 with described aqueous transparent priming paint again, form colouring agent, before the drying of described first surface enamelled coating, with described colouring agent obliterating on described first surface enamelled coating, make described wood grain painted;
5th spraying process: surface aqueous transparent finish paint being sprayed at described first surface enamelled coating, dry 2h-5h, forms the second top coat layer.
Wherein in an embodiment, in described 5th spraying process, described aqueous transparent finish paint is sprayed at the surface of described first surface enamelled coating with at least one " ten " font.
Wherein in an embodiment, after described pearl essence and described metal powder mix, fineness is 5 μm-20 μm.
Wherein in an embodiment, in described 4th spraying process, after obliterating terminates, unnecessary colouring agent is wiped.
Wherein in an embodiment, described drying carries out at following environment: temperature 15 DEG C-70 DEG C, relative humidity 20% ~ 80%.
Wherein in an embodiment, before described first spraying process, also there are following steps: burr and the sand trace of removing described woodenware surface.
Wherein in an embodiment, also there are following steps before removing the burr on described woodenware surface and the step of sand trace: described woodenware is carried out to stamp limit, beats and/or follows closely small holes caused by worms.
Wherein in an embodiment, also there are following steps between described first spraying process and described second spraying process: sanding is carried out to described clear primer layer; Also there are following steps between described second spraying process and described 3rd spraying process: have color basecoat to carry out sanding to described.
Wherein in an embodiment, also there are following steps between described 4th spraying process and described 5th spraying process: sanding is carried out to described first surface enamelled coating.
Wherein in an embodiment, in described 5th spraying process, the thickness of described second top coat layer is 15 μm-20 μm.
Woodenware coating process modelled after an antique of the present invention, its beneficial effect is compared to existing technology:
The present invention is by innovation construction technology, by spraying the step of transparent priming, colored paint and finish paint, and adding colouring agent, pearl essence, silver powder and/or bronze is added in colouring agent, as the colouring agent of wood grain, make the woodenware sprayed have the effect of bronzing or silver, change the present situation that traditional pseudo-classic furniture effect is single, and improve the class of woodenware; In addition, traditional obliterating technique is reduced to from three roads together, simplify construction technology, reduce production cost, be applicable to extensive batch construction.
Accompanying drawing explanation
Fig. 1 is the flow chart of the woodenware coating process modelled after an antique described in the embodiment of the present invention one.
Detailed description of the invention
For the ease of understanding the present invention, below in conjunction with accompanying drawing, the present invention is described more fully.But the present invention can realize in many different forms, is not limited to embodiment described herein.On the contrary, provide the object of these embodiments be make the understanding of disclosure of the present invention more comprehensively thorough.
Unless otherwise defined, all technology used herein and scientific terminology are identical with belonging to the implication that those skilled in the art of the present invention understand usually.The object of term used in the description of the invention herein just in order to describe specific embodiment, is not intended to be restriction the present invention.
Such as, a kind of woodenware coating process modelled after an antique, it comprises the steps: the first spraying process: by aqueous transparent basecoat paint on pending woodenware surface, and dry 1h-3h, forms clear primer layer; Second spraying process: by the surface of aqueous pigmented basecoat paint in described clear primer layer, dry 2h-4h, is formed with color basecoat; 3rd spraying process: the surface having color basecoat described in being sprayed on by aqueous pigmented finish paint, forms first surface enamelled coating; 4th spraying process: pearl essence and metal powder are mixed, described metal powder is silver powder and/or bronze, mix with the mass ratio of 1:15-20 with described aqueous transparent priming paint again, form colouring agent, before the drying of described first surface enamelled coating, with described colouring agent obliterating on described first surface enamelled coating, make described wood grain painted; Such as, with described colouring agent along the grain direction obliterating of described woodenware on described first surface enamelled coating, make described wood grain painted; 5th spraying process: surface aqueous transparent finish paint being sprayed at described first surface enamelled coating, dry 2h-5h, forms the second top coat layer.
In the 5th spraying process, preferably described aqueous transparent finish paint is sprayed at the surface of described first surface enamelled coating with at least one " ten " font, be preferably " ten " font, or multiple " ten " font is spaced, and forms neat hatching effect.
In 4th spraying process, after pearl essence and metal powder mix, fineness is 5 μm-20 μm, the powder coated of this fineness on woodenware after, can not seem too lofty, dazzling bronzing can be met again or wipe the effect of silver.
In 4th spraying process, after obliterating terminates, unnecessary colouring agent is wiped.Such as, described in obliterating during colouring agent, with the direction obliterating of hairbrush along described wood grain; And for example, after obliterating terminates, with white flannelette or lint-free calico, unnecessary colouring agent is wiped.
Drying carries out at following environment: temperature 15 DEG C-70 DEG C, relative humidity 20% ~ 80%.Best selective temperature 60 DEG C, relative humidity 20% carries out drying, and in such circumstances, rate of drying is very fast.
Before the first spraying process, also there are following steps: burr and the sand trace of removing described woodenware surface.Such as, first sand milling can be carried out with sand paper along the grain direction of woodenware when removing burr.
Also there are following steps before removing the burr on described woodenware surface and the step of sand trace: described woodenware is carried out to stamp limit, beats and/or follows closely small holes caused by worms.
Between the first spraying process and the second spraying process, also there are following steps: sanding is carried out to described clear primer layer; Also there are following steps between second spraying process and the 3rd spraying process: have color basecoat to carry out sanding to described.
Between the 4th spraying process and described 5th spraying process, also there are following steps: sanding is carried out to described first surface enamelled coating.
In the 5th spraying process, the thickness of described second top coat layer is 15 μm-20 μm, can be preferably 15 μm, and make woodenware surface more penetrating, texture display is more clear.
Embodiment one
With reference to Fig. 1, woodenware coating process modelled after an antique of the present invention, comprises the steps:
(1) pending woodenware is carried out stabbing limit, beat or follow closely in small holes caused by worms method one or more, thus destructions carried out to this woodenware process, make the antique effect of woodenware better.
(2) carry out sand milling with 240#TOA sand paper along the wood grain of pending woodenware, remove burr, the sand trace on woodenware surface.Woodenware surface more smooth can be ensured after sand milling, more level and smooth after follow-up spraying.
(3) 2.0mm is used, W-71 type spray gun is surperficial at pending woodenware by aqueous transparent basecoat paint, coating thickness 15 μm-20 μm, temperature 15 DEG C-70 DEG C, dry 1h-3h under the environment of relative humidity 20% ~ 80%, form clear primer layer, then adopt 600#TOA sand paper to carry out sanding to described clear primer layer.
(4) 2.0mm is used, W-71 type spray gun is by the surface of aqueous white basecoat paint in clear primer layer, coating thickness 15 μm-20 μm, then temperature 15 DEG C-70 DEG C, dry 2h-4h under the environment of relative humidity 20% ~ 80%, be formed with color basecoat, adopt 600#TOA sand paper to have color basecoat to carry out sanding to described.
(5) use 2.0mm, W-71 type spray gun aqueous pigmented finish paint to be sprayed on the surface of color basecoat, coating thickness 15 μm-20 μm, form first surface enamelled coating.
(6) pearl essence, silver powder and bronze are mixed, wherein the quality proportioning of pearl essence, silver powder and bronze is 1:1:2, mix with the mass ratio of 1:20 with aqueous transparent priming paint again, mixed fineness is 5 μm-20 μm, form colouring agent, before the drying of first surface enamelled coating, with this colouring agent along the grain direction obliterating of this woodenware on first surface enamelled coating, make wood grain painted; During scratch cover colorants, with the direction obliterating of hairbrush along described wood grain, after obliterating terminates, use lint-free calico, unnecessary colouring agent is wiped, then adopt 800#TOA sand paper to carry out sanding to this first surface enamelled coating.
(7) aqueous transparent finish paint is sprayed at the surface of this first surface enamelled coating, then temperature 15 DEG C-70 DEG C, dry 2h-5h under the environment of relative humidity 20% ~ 80%, forms the second top coat layer.Wherein, this aqueous transparent finish paint with at least one " ten " font even application in the surface of first surface enamelled coating.Be sprayed into " ten " font, make woodenware surface have hatching effect, Hepplewhite third dimension is stronger.
Below the painting effect of the present embodiment and comparative example one and comparative example two is contrasted, further illustrate effect of the present invention.
Comparative example one:
In this comparative example, construction method modelled after an antique is:
(1) material destroys process: material is carried out stabbing limit, beat or follow closely in small holes caused by worms method more than one, to reach a kind of furniture because of long and impaired natural effect service time;
(2) material sanding: adopt sand paper smooth to timber burr sand milling;
(3) background color spraying: with the color even application specially prepared;
The described color specially prepared, refers to the color being added dye combinations by nitro-diluent;
(4) polyurethane transparent primer spraying: with polyurethane diluent, polyurethane transparent primer is joined polyurethane primer curing agent, by 2: 1 weight ratios, viscosity being adjusted to is 15 ~ 16 seconds, even application " ten " word, dry 4-6 hour;
(5) sanding: smooth, smooth with sand paper sand milling;
(6) the clear priming paint of nitro: with nitro-diluent, nitrocellulose primer being adjusted to viscosity is 14-15 second, sprays " ten " word, dry 40-60 minute;
(7) paint stripper is brushed: with hairbrush, paint stripper is carried out local on the nitrocellulose primer surface sprayed and brush, position, corner is more than middle part;
(8) nitro white basecoat paint: with nitro-diluent, nitro white priming paint being adjusted to viscosity is 14-15 second, and spray " ten " word, dry 40-60 divides;
(9) come off process: with scouring pad, wiped clean is carried out at the position of brushing paint stripper;
(10) the clear priming paint of nitro: with nitro-diluent, nitrocellulose primer being adjusted to viscosity is 14-15 second, sprays " ten " word, dry 40-60 minute;
(11) nitro Ge Lisi: wipe in surface with nitro Ge Lisi, and then wiped clean;
(12) the clear priming paint of nitro: with nitro-diluent, nitrocellulose primer being adjusted to viscosity is 14-15 second, sprays " ten " word, dry 40-60 minute;
(13) light weight sand: smooth, smooth with sand paper sand milling, sand is not worn;
(14) the dry brush of nitro Ge Lisi: be stained with by Ge Lisi with hairbrush, do and beat surface, the color of local, edge is deeper than middle part, imitates old effect to reach color for the last time;
(15) the clear priming paint of nitro: with nitro-diluent, nitrocellulose primer being adjusted to viscosity is 14-15 second, sprays " ten " word, dry 40-60 minute;
(16) light weight sand: smooth, smooth with sand paper sand milling, sand is not worn;
(17) lacquer finish: with nitro-diluent, lacquer finish being adjusted to viscosity is 11-12 second, sprays " ten " word, dry 24 ~ 30 hours, obtains product.
Comparative example two
In this comparative example, construction method modelled after an antique is:
1) not holding any government official post's product surface destroys process;
2) material repaiies look;
3) background color process;
4) glue processes admittedly;
5) wiping process;
6) one prime treatment;
7) choose three and make models, manually to make at three according to the effect of colour table standard and models make respectively dry brush does old key element, oxtail does old key element and specking does old key element, form dry map brushing case, oxtail pattern and specking pattern respectively;
8) with scanner, the pattern that three make on model is scanned in computer respectively, then PaintShop and image graphic process software is utilized to process each pattern, the part done in each pattern beyond old key element is made to be pellucidity, finally set up pel material database, each pattern of process is deposited into wherein;
9) according to design size and the color requirement of product, corresponding pattern is extracted from pel material database, then by PaintShop and image graphic software, combination finishing is carried out to pattern, form the electronic pictures integrating dry brush, oxtail, specking and shade line required for product, and file;
10) by UV ink-jet printer, print on product by the pattern in the electronic pictures formed in step 9, what make the surface of product once form dry brush, oxtail and specking does old effect.
11) one finish paint process;
12) two coat finish process, makes finished product.
Table one is the embodiment of the present invention one and the painting effect correction data of comparative example one, comparative example two.
Table one
As can be seen from the above table, the relatively existing woodenware coating process modelled after an antique of the present invention, its outward appearance artistic feeling is comparatively strong, and operation is easy, and flow process controls well.
Embodiment two
In the present embodiment, woodenware coating process modelled after an antique of the present invention, comprises the steps:
(1) carry out sand milling with 240#TOA sand paper along the wood grain of pending woodenware, remove burr, the sand trace on woodenware surface.Woodenware surface more smooth can be ensured after sand milling, more level and smooth after follow-up spraying.
(2) 2.0mm is used, W-71 type spray gun is surperficial at pending woodenware by aqueous transparent basecoat paint, coating thickness 15 μm-20 μm, by this clear primer layer temperature 15 DEG C-70 DEG C, dry 1h-3h under the environment of relative humidity 20% ~ 80%, form clear primer layer, adopt 600#TOA sand paper to carry out sanding to described clear primer layer.
(3) 2.0mm is used, W-71 type spray gun is by the surface of aqueous white basecoat paint in clear primer layer, coating thickness 15 μm-20 μm, then temperature 15 DEG C-70 DEG C, dry 2h-4h under the environment of relative humidity 20% ~ 80%, be formed with color basecoat, adopt 600#TOA sand paper to have color basecoat to carry out sanding to described.
(4) use 2.0mm, W-71 type spray gun aqueous pigmented finish paint to be sprayed on the surface of color basecoat, coating thickness 15 μm-20 μm, form first surface enamelled coating.
(5) pearl essence of equivalent, silver powder and bronze are mixed, mix with the mass ratio of 1:18 with aqueous transparent priming paint again, mixed fineness is 5 μm-20 μm, form colouring agent, before the drying of first surface enamelled coating, with this colouring agent along the grain direction obliterating of this woodenware on first surface enamelled coating, make wood grain painted; During scratch cover colorants, with the direction obliterating of hairbrush along described wood grain, after obliterating terminates, use lint-free calico, unnecessary colouring agent is wiped, then adopt 800#TOA sand paper to carry out sanding to this first surface enamelled coating.
(6) aqueous transparent finish paint is sprayed at the surface of this first surface enamelled coating, then temperature 15 DEG C-70 DEG C, dry 2h-5h under the environment of relative humidity 20% ~ 80%, forms the second top coat layer.Wherein, this aqueous transparent finish paint with at least multiple " ten " font even application in the surface of first surface enamelled coating.Multiple " ten " font is evenly distributed, is sprayed into " ten " font, and make woodenware surface have hatching effect, Hepplewhite third dimension is stronger.
Below the painting effect of the present embodiment and comparative example one and comparative example two is contrasted, further illustrate effect of the present invention.
Table two is embodiment of the present invention two and the painting effect correction data of comparative example one, comparative example two.
Table two
As can be seen from the above table, the relatively existing woodenware coating process modelled after an antique of the present invention, its outward appearance artistic feeling is comparatively strong, and operation is easy, and flow process controls well.
Embodiment three
Woodenware coating process modelled after an antique of the present invention, comprises the steps:
(1) carry out stabbing limit, beaing or follow closely one in small holes caused by worms method to pending woodenware, thus destructions is carried out to this woodenware process, make the antique effect of woodenware better.
(2) carry out sand milling with 240#TOA sand paper along the wood grain of pending woodenware, remove burr, the sand trace on woodenware surface.Woodenware surface more smooth can be ensured after sand milling, more level and smooth after follow-up spraying.
(3) use 2.0mm, W-71 type spray gun by aqueous transparent basecoat paint on pending woodenware surface, coating thickness 15 μm, temperature 15 DEG C-70 DEG C, dry 2h under the environment of relative humidity 20% ~ 80%, forms clear primer layer; 600#TOA sand paper is adopted to carry out sanding to described clear primer layer.
(4) 2.0mm is used, W-71 type spray gun is by the surface of aqueous white basecoat paint in clear primer layer, coating thickness 20 μm, then temperature 15 DEG C-70 DEG C, dry 3h under the environment of relative humidity 20% ~ 80%, be formed with color basecoat, adopt 600#TOA sand paper to have color basecoat to carry out sanding to described.
(5) use 2.0mm, W-71 type spray gun aqueous pigmented finish paint to be sprayed on the surface of color basecoat, coating thickness 15 μm, form first surface enamelled coating.
(6) pearl essence of equivalent, silver powder and bronze are mixed, mix with the mass ratio of 1:15 with aqueous transparent priming paint again, mixed fineness is 5 μm-20 μm, form colouring agent, before the drying of first surface enamelled coating, with this colouring agent along the grain direction obliterating of this woodenware on first surface enamelled coating, make wood grain painted; During scratch cover colorants, with the direction obliterating of hairbrush along described wood grain, after obliterating terminates, use lint-free calico, unnecessary colouring agent is wiped, then adopt 800#TOA sand paper to carry out sanding to this first surface enamelled coating.
(7) aqueous transparent finish paint is sprayed at the surface of this first surface enamelled coating, then temperature 15 DEG C-70 DEG C, dry 2h-5h under the environment of relative humidity 20% ~ 80%, forms the second top coat layer.Wherein, this aqueous transparent finish paint with at least one " ten " font even application in the surface of first surface enamelled coating.Be sprayed into " ten " font, make woodenware surface have hatching effect, Hepplewhite third dimension is stronger.
Table three is embodiment of the present invention three and the painting effect correction data of comparative example one, comparative example two.
Table three
As can be seen from the above table, the relatively existing woodenware coating process modelled after an antique of the present invention, its outward appearance artistic feeling is comparatively strong, and operation is easy, and flow process controls well.
Embodiment four
Woodenware coating process modelled after an antique of the present invention, comprises the steps:
(1) pending woodenware is carried out stabbing limit, beat or follow closely in small holes caused by worms method one or more, thus destructions carried out to this woodenware process, make the antique effect of woodenware better.
(2) carry out sand milling with 240#TOA sand paper along the wood grain of pending woodenware, remove burr, the sand trace on woodenware surface.Woodenware surface more smooth can be ensured after sand milling, more level and smooth after follow-up spraying.
(3) 2.0mm is used, W-71 type spray gun is by aqueous transparent basecoat paint on pending woodenware surface, and coating thickness 20 μm, by this clear primer layer temperature 15 DEG C-70 DEG C, dry 1h-3h under the environment of relative humidity 20% ~ 80%, forms clear primer layer; 600#TOA sand paper is adopted to carry out sanding to described clear primer layer.
(4) 2.0mm is used, W-71 type spray gun is by the surface of aqueous white basecoat paint in clear primer layer, coating thickness 20 μm, then temperature 15 DEG C-70 DEG C, dry 2h-4h under the environment of relative humidity 20% ~ 80%, be formed with color basecoat, adopt 600#TOA sand paper to have color basecoat to carry out sanding to described.
(5) use 2.0mm, W-71 type spray gun aqueous pigmented finish paint to be sprayed on the surface of color basecoat, coating thickness 15 μm, form first surface enamelled coating.
(6) pearl essence, silver powder and bronze are mixed, wherein the quality proportioning of pearl essence, silver powder and bronze is 2:1:2, mix with the mass ratio of 1:20 with aqueous transparent priming paint again, mixed fineness is 5 μm-20 μm, form colouring agent, before the drying of first surface enamelled coating, with this colouring agent along the grain direction obliterating of this woodenware on first surface enamelled coating, make wood grain painted; During scratch cover colorants, with the direction obliterating of hairbrush along described wood grain, after obliterating terminates, use lint-free calico, unnecessary colouring agent is wiped, then adopt 800#TOA sand paper to carry out sanding to this first surface enamelled coating.
(7) aqueous transparent finish paint is sprayed at the surface of this first surface enamelled coating, then temperature 15 DEG C-70 DEG C, dry 2h-5h under the environment of relative humidity 20% ~ 80%, forms the second top coat layer.Wherein, this aqueous transparent finish paint with at least one " ten " font even application in the surface of first surface enamelled coating.Be sprayed into " ten " font, make woodenware surface have hatching effect, Hepplewhite third dimension is stronger.
Table four is embodiment of the present invention four and the painting effect correction data of comparative example one, comparative example two.
Table four
As can be seen from the above table, the relatively existing woodenware coating process modelled after an antique of the present invention, its outward appearance artistic feeling is comparatively strong, and operation is easy, and flow process controls well.
The above embodiment only have expressed several embodiment of the present invention, and it describes comparatively concrete and detailed, but therefore can not be interpreted as the restriction to the scope of the claims of the present invention.It should be pointed out that for the person of ordinary skill of the art, without departing from the inventive concept of the premise, can also make some distortion and improvement, these all belong to protection scope of the present invention.Therefore, the protection domain of patent of the present invention should be as the criterion with claims.
Claims (10)
1. woodenware coating process modelled after an antique, is characterized in that, comprise the steps:
First spraying process: by aqueous transparent basecoat paint on pending woodenware surface, dry 1h-3h, forms clear primer layer;
Second spraying process: by the surface of aqueous pigmented basecoat paint in described clear primer layer, dry 2h-4h, is formed with color basecoat;
3rd spraying process: the surface having color basecoat described in being sprayed on by aqueous pigmented finish paint, forms first surface enamelled coating;
4th spraying process: pearl essence and metal powder are mixed, described metal powder is silver powder and/or bronze, mix with the mass ratio of 1:15-20 with described aqueous transparent priming paint again, form colouring agent, before the drying of described first surface enamelled coating, with described colouring agent obliterating on described first surface enamelled coating, make described wood grain painted;
5th spraying process: surface aqueous transparent finish paint being sprayed at described first surface enamelled coating, dry 2h-5h, forms the second top coat layer.
2. woodenware coating process modelled after an antique according to claim 1, is characterized in that, in described 5th spraying process, described aqueous transparent finish paint is sprayed at the surface of described first surface enamelled coating with at least one " ten " font.
3. woodenware coating process modelled after an antique according to claim 1, is characterized in that, after described pearl essence and described metal powder mix, fineness is 5 μm-20 μm.
4. woodenware coating process modelled after an antique according to claim 1, is characterized in that, in described 4th spraying process, after obliterating terminates, is wiped by unnecessary colouring agent.
5. woodenware coating process modelled after an antique according to claim 1, is characterized in that, described drying carries out at following environment: temperature 15 DEG C-70 DEG C, relative humidity 20% ~ 80%.
6. woodenware coating process modelled after an antique according to claim 1, is characterized in that, also has following steps before described first spraying process: burr and the sand trace of removing described woodenware surface.
7. woodenware coating process modelled after an antique according to claim 6, is characterized in that, also has following steps: described woodenware is carried out to stamp limit, beats and/or follows closely small holes caused by worms before removing the burr on described woodenware surface and the step of sand trace.
8. woodenware coating process modelled after an antique according to claim 1, is characterized in that, also has following steps: carry out sanding to described clear primer layer between described first spraying process and described second spraying process; Also there are following steps between described second spraying process and described 3rd spraying process: have color basecoat to carry out sanding to described.
9. woodenware coating process modelled after an antique according to claim 1, is characterized in that, also has following steps: carry out sanding to described first surface enamelled coating between described 4th spraying process and described 5th spraying process.
10. woodenware coating process modelled after an antique according to claim 1, is characterized in that, in described 5th spraying process, the thickness of described second top coat layer is 15 μm-20 μm.